CN108486960A - A kind of preparation method of the moisture-proof rice paper of calligraphy and painting - Google Patents

A kind of preparation method of the moisture-proof rice paper of calligraphy and painting Download PDF

Info

Publication number
CN108486960A
CN108486960A CN201810315759.7A CN201810315759A CN108486960A CN 108486960 A CN108486960 A CN 108486960A CN 201810315759 A CN201810315759 A CN 201810315759A CN 108486960 A CN108486960 A CN 108486960A
Authority
CN
China
Prior art keywords
parts
calligraphy
painting
rice paper
added
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201810315759.7A
Other languages
Chinese (zh)
Inventor
胡翠霞
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jixi County Old Factory Hu Kai
Original Assignee
Jixi County Old Factory Hu Kai
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jixi County Old Factory Hu Kai filed Critical Jixi County Old Factory Hu Kai
Priority to CN201810315759.7A priority Critical patent/CN108486960A/en
Publication of CN108486960A publication Critical patent/CN108486960A/en
Withdrawn legal-status Critical Current

Abstract

The present invention relates to art work field of mounting, more particularly to the preparation method of the moisture-proof rice paper of calligraphy and painting, 12 parts of polyvinyl alcohol resin, 0.5 1 parts of sepiolite fibre are added in 8 10 parts of water and dissolved by heating completely for 35 40 DEG C, then pH is adjusted to 6.5 7.5,0.3 0.5 parts of 25 35 parts of mica powder, 20 25 parts of land plaster and Glycerin, mixed triester with caprylic acid capric acid is added and mixed at high speed is uniform, obtain polyvinyl alcohol resin mixed liquor, the object of the present invention is to provide a kind of preparation methods of the moisture-proof rice paper of calligraphy and painting, can will be controlled below 0.28% by wet rear average elongation.

Description

A kind of preparation method of the moisture-proof rice paper of calligraphy and painting
Technical field
The present invention relates to art work field of mounting, and in particular to a kind of preparation method of the moisture-proof rice paper of calligraphy and painting.
Background technology
The complete calligraphy and painting of one width needs to keep its more aesthetically pleasing, and is to be unable to do without mounting convenient for preserving, spreading and collect 's.Because calligraphy and painting be drawn in mostly on breakable rice paper or thin,tough silk class article on.Mounting is a kind of distinctive protection in China and U.S. The technology for changing painting and calligraphy and rubbings, can reach taller and bigger on aesthetic.Mounting is further divided into former mounting and again New mounting, original mounting are exactly that the picture newly finished is carried out mounting by the program of mounting.Remount be exactly to those original mounting it is bad or Be due to management collection keeping be not good at, occur ghost fall off, make moist it is mouldy, grain it is rotten fracture, damaged by rats of damaging by worms painting and calligraphy handed down from ancient times carry out Mounting.It is secured, beautiful by the painting and calligraphy of mounting, it is watched convenient for collection and arrangement.And the ancient painting remounted, it can also extend it Vitality.Either former mounting is still remounted, and the mountings such as calligraphy and painting are completed, it is desirable to reach secured, beautiful, convenient for collection and cloth It sets ornamental.Rice paper adds using Chu's bark or wingceltis bark or rice straw as raw material through several processes such as lime fermentation, grass bleaching, mashing Work, which is copied, to be made；With soft texture, water absorbing properties are good, and fiber is long, and toughness is big, colour the features such as firm, not only calligraphy and drawing It is be unable to do without rice paper, and rice paper is also indispensable material in mounting work.
Include following component application No. is the moisture-proof rice paper of calligraphy and painting disclosed in 201711022454.9：Chu's bark powder, dispersion are situated between Matter, wingceltis bark powder, reed straw powder, adhesive, atlapulgite, chitosan oligosaccharide-ceramic, modified meerschaum particle, polyethylene Alcohol resin, sepiolite fibre, N hydroxymethyl acrylamide, asbestos wool, mica powder, land plaster, nano medical stone powder, polyethylene Wax, lauric monoglyceride, Glycerin, mixed triester with caprylic acid capric acid, modified polyvinyl chloride lotion, sodium gluconate, carboxymethyl chitosan；This hair Bright to prepare the moisture-proof rice paper of calligraphy and painting, humidity resistance is stablized, and has good wet-heat resisting, ageing-resistant performance, preparation method is simple, technique Condition is easily realized, is obtained the moisture-proof rice paper of calligraphy and painting of performance stabilization, resting period length, be can be used for calligraphy and painting various forms mounting, and Production cost and maintenance cost are reduced, but the invention is still 0.4% by wet rear average elongation, it is clear that still have the sky of decline Between.
Invention content
The object of the present invention is to provide a kind of preparation method of the moisture-proof rice paper of calligraphy and painting, energy will be by wet rear average elongation control System is below 0.26%.
The present invention provides a kind of preparation methods of the moisture-proof rice paper of calligraphy and painting, it is characterised in that：The moisture-proof rice paper preparation side of calligraphy and painting Method, steps are as follows：
(1) 35-40 DEG C of heating for dissolving in 8-10 parts of water is added in 1-2 parts of polyvinyl alcohol resin, 0.5-1 parts of sepiolite fibre Completely, pH is then adjusted to 6.5-7.5,25-35 parts of mica powder, 20-25 parts of land plaster and Glycerin, mixed triester with caprylic acid capric acid 0.3-0.5 is added Simultaneously mixed at high speed is uniform for part, obtains polyvinyl alcohol resin mixed liquor；
(2) by 25-40 parts of Chu's bark powder, 23-35 parts of wingceltis bark powder, 5-12 parts of reed straw powder, chitosan oligosaccharide-ceramic 5-10 parts, 2-3 parts of modified meerschaum particle be added to the container jointly 93 DEG C reaction 3-5h, add 2-13 parts by weight step (1) Obtained polyvinyl alcohol resin mixed liquor stirs evenly at same temperature, and 3-5 parts of polyethylene wax, lauric acid list is added after cooling 0.1-0.3 parts of 0.3-0.5 parts of glyceride, 10-15 parts of modified polyvinyl chloride lotion and asbestos wool stirring 10-15min, obtain word Moisture-proof rice paper matrix is drawn, it is spare；
(3) 26-50 parts of decentralized medium, 50-80 parts of adhesive are poured into retort, then activity is added in vain into retort 15-20 parts native, 0.3-0.5 parts of N hydroxymethyl acrylamide, 2-4 parts of nano medical stone powder, are uniformly mixed, and stand 3-5h；
(4) again by 1-2 parts of sodium gluconate, 0.2-0.4 parts of carboxymethyl chitosan, the moisture-proof rice paper matrix of calligraphy and painting, which is added, reacts In tank, it is uniformly mixed；
(5) by retort sealing be placed in water-bath, heating water bath to constant temperature underwater curing 1-3h after 80 DEG C, after will consolidate Rice paper paper making equipment is added in material after change, prepares the moisture-proof rice paper of calligraphy and painting of different model.
The beneficial of the present invention is effectively：It can will be controlled below 0.26% by wet rear average elongation.
Specific implementation mode
A kind of preparation method of the moisture-proof rice paper of calligraphy and painting, it is characterised in that：The moisture-proof rice paper preparation method of calligraphy and painting, steps are as follows：
(1) 35-40 DEG C of heating for dissolving in 8-10 parts of water is added in 1-2 parts of polyvinyl alcohol resin, 0.5-1 parts of sepiolite fibre Completely, pH is then adjusted to 6.5-7.5,25-35 parts of mica powder, 20-25 parts of land plaster and Glycerin, mixed triester with caprylic acid capric acid 0.3-0.5 is added Simultaneously mixed at high speed is uniform for part, obtains polyvinyl alcohol resin mixed liquor；
(2) by 25-40 parts of Chu's bark powder, 23-35 parts of wingceltis bark powder, 5-12 parts of reed straw powder, chitosan oligosaccharide-ceramic 5-10 parts, 2-3 parts of modified meerschaum particle be added to the container jointly 93 DEG C reaction 3-5h, add 2-13 parts by weight step (1) Obtained polyvinyl alcohol resin mixed liquor stirs evenly at same temperature, and 3-5 parts of polyethylene wax, lauric acid list is added after cooling 0.1-0.3 parts of 0.3-0.5 parts of glyceride, 10-15 parts of modified polyvinyl chloride lotion and asbestos wool stirring 10-15min, obtain word Moisture-proof rice paper matrix is drawn, it is spare；
(3) 26-50 parts of decentralized medium, 50-80 parts of adhesive are poured into retort, then activity is added in vain into retort 15-20 parts native, 0.3-0.5 parts of N hydroxymethyl acrylamide, 2-4 parts of nano medical stone powder, are uniformly mixed, and stand 3-5h；
(4) again by 1-2 parts of sodium gluconate, 0.2-0.4 parts of carboxymethyl chitosan, the moisture-proof rice paper matrix of calligraphy and painting, which is added, reacts In tank, it is uniformly mixed；
(5) by retort sealing be placed in water-bath, heating water bath to constant temperature underwater curing 1-3h after 80 DEG C, after will consolidate Rice paper paper making equipment is added in material after change, prepares the moisture-proof rice paper of calligraphy and painting of different model.
It is of the invention can will by average elongation control after wet 0.26% hereinafter, and other data do not change relative to documents Become.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto, Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.

Claims (1)

1. a kind of preparation method of the moisture-proof rice paper of calligraphy and painting, it is characterised in that：Steps are as follows：
(1) 1-2 parts of polyvinyl alcohol resin, 0.5-1 parts of sepiolite fibre are added in 8-10 parts of water and have been dissolved by heating for 35-40 DEG C Entirely, pH is then adjusted to 6.5-7.5,0.3-0.5 parts of 25-35 parts of mica powder, 20-25 parts of land plaster and Glycerin, mixed triester with caprylic acid capric acid is added And mixed at high speed is uniform, obtains polyvinyl alcohol resin mixed liquor；
(2) by 25-40 parts of Chu's bark powder, 23-35 parts of wingceltis bark powder, 5-12 parts of reed straw powder, chitosan oligosaccharide-ceramic 5-10 Part, 2-3 parts of modified meerschaum particle are added to the container 93 DEG C of reaction 3-5h jointly, add 2-13 parts by weight step (1) and obtain Polyvinyl alcohol resin mixed liquor stirred evenly at same temperature, 3-5 parts of polyethylene wax, lauric monoglyceride is added after cooling 0.1-0.3 parts of 0.3-0.5 parts of ester, 10-15 parts of modified polyvinyl chloride lotion and asbestos wool stirring 10-15min, it is anti-to obtain calligraphy and painting Damp rice paper matrix, it is spare；
(3) 26-50 parts of decentralized medium, 50-80 parts of adhesive are poured into retort, then atlapulgite is added into retort 15-20 parts, 0.3-0.5 parts of N hydroxymethyl acrylamide, 2-4 parts of nano medical stone powder, be uniformly mixed, stand 3-5h；
(4) again by 1-2 parts of sodium gluconate, 0.2-0.4 parts of carboxymethyl chitosan, the moisture-proof rice paper matrix addition retort of calligraphy and painting In, it is uniformly mixed；
(5) by retort sealing be placed in water-bath, heating water bath to constant temperature underwater curing 1-3h after 80 DEG C, after will solidification after Rice paper paper making equipment is added in material, prepares the moisture-proof rice paper of calligraphy and painting of different model.
CN201810315759.7A 2018-04-10 2018-04-10 A kind of preparation method of the moisture-proof rice paper of calligraphy and painting Withdrawn CN108486960A (en)