CN108486582A - A kind of stainless steel work-piece paraffin removal cleaning agent and preparation method thereof that adds lustre to - Google Patents
A kind of stainless steel work-piece paraffin removal cleaning agent and preparation method thereof that adds lustre to Download PDFInfo
- Publication number
- CN108486582A CN108486582A CN201810570377.9A CN201810570377A CN108486582A CN 108486582 A CN108486582 A CN 108486582A CN 201810570377 A CN201810570377 A CN 201810570377A CN 108486582 A CN108486582 A CN 108486582A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- paraffin removal
- acid amide
- steel work
- removal cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of stainless steel work-piece paraffin removal cleaning agents and preparation method thereof that adds lustre to.The stainless steel work-piece raw material that the paraffin removal cleaning agent that adds lustre to includes following weight percent：Straight chain fatty acid amide 17 35%, organic acid 10 25%, softening agent 2 21%, builder 0.5 3%, the water of surplus.The stainless steel work-piece of the present invention is with the paraffin removal cleaning agent that adds lustre to using the principle and similar compatibility principle reacted using acid ion as foundation, the activating agent of paraffin removal compound preferably, and the processing that adds lustre to is carried out to stainless steel surface using organic acid, to realize paraffin removal and bright difunctional effect；Preparation method is simple, is advantageously implemented industrialized production.
Description
Technical field
The present invention relates to a kind of cleaning agent, specifically a kind of stainless steel work-piece paraffin removal cleaning agent and its preparation side of adding lustre to
Method.
Background technology
Stainless steel work-piece needs to clean up the wax dirt for being adhered to workpiece surface after scutching cotton piece buff and wax polishing；
Sometimes stainless steel kettle inner wall adds lustre to without polishing and by the way of directly cleaning, and reaches customer demand.Currently, city
Common stainless steel paraffin removal cleaning agent has polyethenoxy ether class, oleate soap, coconut oil diethanol amide and its phosphate ester salt on field,
Sulfonates；These stainless steel paraffin removal cleaning agents are neutral a bit or alkalinity, primarily serve paraffin removal cleaning performance, do not have
Light enhancing effect；Also some stainless steel paraffin removal cleaning agents are acid, primarily serve degreasing and rust removal light enhancing effect, but paraffin removal is clear
Wash power deficiency.Therefore, the present invention provides a kind of not only with degreasing and rust removal light enhancing effect but also with the stainless steel of paraffin removal cleaning performance
The workpiece paraffin removal cleaning agent and preparation method thereof that adds lustre to.
Invention content
The purpose of the present invention is to provide a kind of stainless steel work-piece paraffin removal cleaning agents and preparation method thereof that adds lustre to, to solve
The problems mentioned above in the background art.
To achieve the above object, the present invention provides the following technical solutions：
A kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece include following with the paraffin removal cleaning agent that adds lustre to
The raw material of weight percent：Straight chain fatty acid amide 17-35%, organic acid 10-25%, softening agent 2-21%, builder 0.5-
3%, the water of surplus.
As a further solution of the present invention：The straight chain fatty acid amide includes cerinic acid amide, lignin acid amide, flower
Raw acid amide, stearic amide, oleamide, rosin acid amide, floating oleamide, palmitamide, lauric amide, Pork and beans
The composition of cool acid amide, cocinic acid amide, certain herbaceous plants with big flowers acid amide and the 2-4 kinds in n-nonanoic acid amide.
As a further solution of the present invention：The organic acid includes formic acid, glacial acetic acid, tartaric acid, citric acid and fourth two
One or more compositions in acid.
As a further solution of the present invention：The builder includes one in boric acid, EDTA-2 sodium and sodium gluconate
Kind or a variety of compositions.
As a further solution of the present invention：The softening agent is using in OP10, peregal, a conduit made of long bamboo oil and polyethers activating agent
One or more compositions.
As a further solution of the present invention：Further include catalyst, the mass ratio of catalyst and straight chain fatty acid amide is
(5-10)：(17-35)；The catalyst uses inorganic base.
As a further solution of the present invention：The inorganic base uses sodium hydroxide or potassium hydroxide.
A kind of stainless steel work-piece preparation method for the paraffin removal cleaning agent that adds lustre to, includes the following steps：(1) according to above-mentioned formula
Each raw material is weighed, it is spare；(2) water is added into reaction kettle, adds other in addition to straight chain fatty acid amide and softening agent
Material, the stirring and dissolving in addition, then adds softening agent, finally adds straight chain fatty acid amide and is filled after the completion of material addition
Divide stirring curing 2-3h, dispensed after standing to obtain the final product.
As a further solution of the present invention：Step (2) is sufficiently stirred curing 2.5h, is dispensed after standing 0.5h.
Compared with prior art, the beneficial effects of the invention are as follows：
The principle and similar compatibility that the stainless steel work-piece of the present invention is reacted with paraffin removal cleaning agent is added lustre to using acid ion
Principle is foundation, to the activating agent of paraffin removal compound preferably, and carry out the processing that adds lustre to stainless steel surface using organic acid, from
And realize paraffin removal and bright difunctional effect；Preparation method is simple, is advantageously implemented industrialized production.
Specific implementation mode
The technical solution of this patent is described in more detail With reference to embodiment.
Embodiment 1
A kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece include following with the paraffin removal cleaning agent that adds lustre to
The raw material of weight percent：Straight chain fatty acid amide 17%, organic acid 10%, softening agent 8%, builder 0.5%, surplus
Water.The straight chain fatty acid amide includes cerinic acid amide and certain herbaceous plants with big flowers acid amide, and the mass ratio of cerinic acid amide and certain herbaceous plants with big flowers acid amide is 12：5；
The organic acid includes formic acid, glacial acetic acid and citric acid, and the mass ratio of formic acid, glacial acetic acid and citric acid is 2：3：5；Described help is washed
Agent includes EDTA-2 sodium；The softening agent is oily using peregal and an a conduit made of long bamboo, and the mass ratio of peregal and a conduit made of long bamboo oil is 5：3.
A kind of stainless steel work-piece preparation method for the paraffin removal cleaning agent that adds lustre to, includes the following steps：(1) according to above-mentioned formula
Each raw material is weighed, it is spare；(2) water is added into reaction kettle, adds other in addition to straight chain fatty acid amide and softening agent
Material, the stirring and dissolving in addition, then adds softening agent, finally adds straight chain fatty acid amide and is filled after the completion of material addition
Divide stirring curing 2h, dispensed after standing to obtain the final product.
Embodiment 2
A kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece include following with the paraffin removal cleaning agent that adds lustre to
The raw material of weight percent：Straight chain fatty acid amide 25%, organic acid 16%, softening agent 14%, builder 1%, the water of surplus.
The straight chain fatty acid amide includes cerinic acid amide and certain herbaceous plants with big flowers acid amide, and the mass ratio of cerinic acid amide and certain herbaceous plants with big flowers acid amide is 15：10；Institute
It includes formic acid, glacial acetic acid and citric acid to state organic acid, and the mass ratio of formic acid, glacial acetic acid and citric acid is 3：5：8；The builder
Including EDTA-2 sodium；The softening agent is oily using peregal and an a conduit made of long bamboo, and the mass ratio of peregal and a conduit made of long bamboo oil is 8：6.
A kind of stainless steel work-piece preparation method for the paraffin removal cleaning agent that adds lustre to, includes the following steps：(1) according to above-mentioned formula
Each raw material is weighed, it is spare；(2) water is added into reaction kettle, adds other in addition to straight chain fatty acid amide and softening agent
Material, the stirring and dissolving in addition, then adds softening agent, finally adds straight chain fatty acid amide and is filled after the completion of material addition
Divide stirring curing 3h, dispensed after standing to obtain the final product.
Embodiment 3
A kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece include following with the paraffin removal cleaning agent that adds lustre to
The raw material of weight percent：Straight chain fatty acid amide 20%, organic acid 15%, softening agent 8%, builder 1.5%, surplus
Water.The straight chain fatty acid amide includes lignin acid amide, rosin acid amide and certain herbaceous plants with big flowers acid amide, lignin acid amide, rosin
The mass ratio of sour amide and certain herbaceous plants with big flowers acid amide is 12：5：3；The organic acid includes formic acid and citric acid；The matter of formic acid and citric acid
Amount is than being 5：10；The builder includes boric acid and EDTA-2 sodium, and the mass ratio of boric acid and EDTA-2 sodium is 1：0.5；It is described soft
Agent uses OP10 and polyethers activating agent, and the mass ratio of OP10 and polyethers activating agent is 5：3.
A kind of stainless steel work-piece preparation method for the paraffin removal cleaning agent that adds lustre to, includes the following steps：(1) according to above-mentioned formula
Each raw material is weighed, it is spare；(2) water is added into reaction kettle, adds other in addition to straight chain fatty acid amide and softening agent
Material, the stirring and dissolving in addition, then adds softening agent, finally adds straight chain fatty acid amide and is filled after the completion of material addition
Divide stirring curing 2.5h, dispensed after standing to obtain the final product.
Embodiment 4
A kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece include following with the paraffin removal cleaning agent that adds lustre to
The raw material of weight percent：Straight chain fatty acid amide 30%, organic acid 23%, softening agent 14%, builder 3%, the water of surplus.
The straight chain fatty acid amide includes lignin acid amide, rosin acid amide and certain herbaceous plants with big flowers acid amide, lignin acid amide, rosin acid acyl
The mass ratio of amine and certain herbaceous plants with big flowers acid amide is 15：10：5；The organic acid includes formic acid and citric acid；The mass ratio of formic acid and citric acid
It is 8：15；The builder includes boric acid and EDTA-2 sodium, and the mass ratio of boric acid and EDTA-2 sodium is 2：1；The softening agent is adopted
With OP10 and polyethers activating agent, the mass ratio of OP10 and polyethers activating agent is 8：6.
A kind of stainless steel work-piece preparation method for the paraffin removal cleaning agent that adds lustre to, includes the following steps：(1) according to above-mentioned formula
Each raw material is weighed, it is spare；(2) water is added into reaction kettle, adds other in addition to straight chain fatty acid amide and softening agent
Material, the stirring and dissolving in addition, then adds softening agent, finally adds straight chain fatty acid amide and is filled after the completion of material addition
Divide stirring curing 2.1h, dispensed after standing to obtain the final product.
Embodiment 5
A kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece include following with the paraffin removal cleaning agent that adds lustre to
The raw material of weight percent：Straight chain fatty acid amide 17%, organic acid 15%, softening agent 13%, builder 0.5%, surplus
Water.The straight chain fatty acid amide includes rosin acid amide and floating oleamide, the quality of rosin acid amide and floating oleamide
Than being 12:5；The organic acid includes glacial acetic acid and citric acid, and the mass ratio of glacial acetic acid and citric acid is 10:5；The builder
Including EDTA-2 sodium；The softening agent is using peregal, a conduit made of long bamboo oil and polyethers activating agent, peregal, a conduit made of long bamboo oil and polyethers activating agent
Mass ratio is 5:3:5.
A kind of stainless steel work-piece preparation method for the paraffin removal cleaning agent that adds lustre to, includes the following steps：(1) according to above-mentioned formula
Each raw material is weighed, it is spare；(2) water is added into reaction kettle, adds other in addition to straight chain fatty acid amide and softening agent
Material, the stirring and dissolving in addition, then adds softening agent, finally adds straight chain fatty acid amide and is filled after the completion of material addition
Divide stirring curing 2.3h, dispensed after standing to obtain the final product.
Embodiment 6
A kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece include following with the paraffin removal cleaning agent that adds lustre to
The raw material of weight percent：Straight chain fatty acid amide 25%, organic acid 25%, softening agent 21%, builder 1%, the water of surplus.
The straight chain fatty acid amide includes rosin acid amide and floating oleamide, and the mass ratio of rosin acid amide and floating oleamide is
15:10；The organic acid includes glacial acetic acid and citric acid, and the mass ratio of glacial acetic acid and citric acid is 15:10；The builder packet
Include EDTA-2 sodium；The softening agent using peregal, an a conduit made of long bamboo oil and polyethers activating agent, peregal, an a conduit made of long bamboo oil and polyethers activating agent matter
Amount is than being 8:5:8.
A kind of stainless steel work-piece preparation method for the paraffin removal cleaning agent that adds lustre to, includes the following steps：(1) according to above-mentioned formula
Each raw material is weighed, it is spare；(2) water is added into reaction kettle, adds other in addition to straight chain fatty acid amide and softening agent
Material, the stirring and dissolving in addition, then adds softening agent, finally adds straight chain fatty acid amide and is filled after the completion of material addition
Divide stirring curing 2.7h, dispensed after standing to obtain the final product.
Embodiment 7
As different from Example 1, a kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece is with adding lustre to
Paraffin removal cleaning agent includes the raw material of following weight percent：Straight chain fatty acid amide 35%, organic acid 12%, catalyst 5% are soft
Agent 2%, builder 1.2%, the water of surplus；The catalyst uses inorganic base.The straight chain fatty acid amide includes peanut
The composition that sour amide, stearic amide, oleamide and palmitamide are mixed according to arbitrary proportion.The organic acid uses
Tartaric acid.The builder includes the composition that boric acid, EDTA-2 sodium and sodium gluconate are mixed according to arbitrary proportion.The nothing
Machine alkali uses sodium hydroxide.The softening agent uses OP10.
Embodiment 8
As different from Example 1, a kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece is with adding lustre to
Paraffin removal cleaning agent includes the raw material of following weight percent：Straight chain fatty acid amide 28%, organic acid 22%, catalyst 10%,
Softening agent 5%, builder 2%, the water of surplus；The catalyst uses inorganic base.The straight chain fatty acid amide includes bay
The composition that sour amide, myristic acid amide, cocinic acid amide and n-nonanoic acid amide are mixed according to arbitrary proportion.The organic acid
The composition mixed according to arbitrary proportion including formic acid, glacial acetic acid, citric acid and succinic acid.The builder include boric acid,
The composition that EDTA-2 sodium and sodium gluconate are mixed according to arbitrary proportion.The inorganic base uses potassium hydroxide.The softening
The composition that agent is mixed using OP10, peregal, a conduit made of long bamboo oil and polyethers activating agent according to arbitrary proportion.
Embodiment 9
As different from Example 1, a kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, the stainless steel work-piece is with adding lustre to
Paraffin removal cleaning agent includes the raw material of following weight percent：Straight chain fatty acid amide 30%, organic acid 19%, catalyst 6% are soft
Agent 10%, builder 0.8%, the water of surplus；The catalyst uses inorganic base.The straight chain fatty acid amide includes rosin
The composition that sour amide, floating oleamide, palmitamide, cocinic acid amide are mixed according to arbitrary proportion.The organic acid
The composition mixed according to arbitrary proportion including formic acid, glacial acetic acid, tartaric acid, citric acid and succinic acid.The builder includes
The composition that boric acid and sodium gluconate are mixed according to arbitrary proportion.The inorganic base uses sodium hydroxide.The softening agent is adopted
The composition mixed according to arbitrary proportion with OP10, a conduit made of long bamboo oil and polyethers activating agent.
Experimental example
Test comparison is carried out to embodiment 1-6 and conventional wax removing agent, as a result see the table below shown.
Table test comparison result
To sum up test, embodiment 1-6 is compared with conventional wax removing agent, not only shortens the paraffin removal time, and deoiling effect and
Luminosity also reaches requirement, and wherein embodiment 1-2 integration capabilities are preferable.
The better embodiment of this patent is explained in detail above, but this patent is not limited to above-mentioned embodiment party
Formula, one skilled in the relevant art within the scope of knowledge, can also be under the premise of not departing from this patent objective
Various changes can be made.
Claims (9)
1. a kind of stainless steel work-piece paraffin removal cleaning agent that adds lustre to, which is characterized in that the stainless steel work-piece is cleaned with the paraffin removal that adds lustre to
Agent includes the raw material of following weight percent：Straight chain fatty acid amide 17-35%, organic acid 10-25%, softening agent 2-21% are helped and are washed
Agent 0.5-3%, the water of surplus.
2. the stainless steel work-piece according to claim 1 paraffin removal cleaning agent that adds lustre to, which is characterized in that the straight chain fatty acid
Amide includes cerinic acid amide, lignin acid amide, arachidamide, stearic amide, oleamide, rosin acid amide, oil slick
In sour amide, palmitamide, lauric amide, myristic acid amide, cocinic acid amide, certain herbaceous plants with big flowers acid amide and n-nonanoic acid amide
The composition of 2-4 kinds.
3. the stainless steel work-piece according to claim 1 paraffin removal cleaning agent that adds lustre to, which is characterized in that the organic acid includes
One or more compositions in formic acid, glacial acetic acid, tartaric acid, citric acid and succinic acid.
4. the stainless steel work-piece according to claim 1 paraffin removal cleaning agent that adds lustre to, which is characterized in that the builder includes
One or more compositions in boric acid, EDTA-2 sodium and sodium gluconate.
5. the stainless steel work-piece according to claim 1 paraffin removal cleaning agent that adds lustre to, which is characterized in that the softening agent uses
One or more compositions in OP10, peregal, a conduit made of long bamboo oil and polyethers activating agent.
6. the stainless steel work-piece according to claim 1 paraffin removal cleaning agent that adds lustre to, which is characterized in that further include catalyst,
The mass ratio of catalyst and straight chain fatty acid amide is（5-10）：（17-35）；The catalyst uses inorganic base.
7. the stainless steel work-piece according to claim 6 paraffin removal cleaning agent that adds lustre to, which is characterized in that the inorganic base uses
Sodium hydroxide or potassium hydroxide.
8. a kind of preparation method according to any stainless steel work-piece paraffin removal cleaning agents that add lustre to of claim 1-7, special
Sign is, includes the following steps：（1）Each raw material is weighed according to above-mentioned formula, it is spare；（2）Water is added into reaction kettle, is added
Unclassified stores in addition to straight chain fatty acid amide and softening agent, the stirring and dissolving in addition, then adds softening agent, finally adds
Add straight chain fatty acid amide, after the completion of material addition, be sufficiently stirred curing 2-3h, dispensed after standing to obtain the final product.
9. the stainless steel work-piece according to claim 8 preparation method for the paraffin removal cleaning agent that adds lustre to, which is characterized in that step
（2）It is sufficiently stirred curing 2.5h, is dispensed after standing 0.5h.