CN108484111A - 一种仿铁瓷器的制备方法 - Google Patents

一种仿铁瓷器的制备方法 Download PDF

Info

Publication number
CN108484111A
CN108484111A CN201810163156.XA CN201810163156A CN108484111A CN 108484111 A CN108484111 A CN 108484111A CN 201810163156 A CN201810163156 A CN 201810163156A CN 108484111 A CN108484111 A CN 108484111A
Authority
CN
China
Prior art keywords
prepared
ironware
ceramics
imitative
discarded
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201810163156.XA
Other languages
English (en)
Other versions
CN108484111B (zh
Inventor
周冬菊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dehua Dehua Ceramics Co Ltd
Original Assignee
Dehua Dehua Ceramics Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Dehua Dehua Ceramics Co Ltd filed Critical Dehua Dehua Ceramics Co Ltd
Priority to CN201810163156.XA priority Critical patent/CN108484111B/zh
Publication of CN108484111A publication Critical patent/CN108484111A/zh
Application granted granted Critical
Publication of CN108484111B publication Critical patent/CN108484111B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及陶瓷技术领域，具体的涉及一种仿铁瓷器的制备方法。该种利用废弃灰砖制备的仿铁器陶瓷的坯料由废弃灰砖粉、四班土、低温石、叶腊石、氧化铁、金红石、青金石制备而成；釉料由长石、废弃灰砖粉、石英、草木灰、氧化铁、硅酸锆、双飞粉、氧化钴、二氧化锰制备而成。该种仿铁器陶瓷，瓷器表面具有与锻打铁器相近的灰褐色，釉面光滑、细腻，在不同的光亮下能折射出彩色的光斑，具有粗犷、古朴的艺术效果，可以直接用于生产日用或艺术陶瓷；本发明的陶瓷材料可以解决陶瓷生产成本资金不断身高、陶瓷产品同质化的问题，在生产陶瓷的地方容易推广，为解决建筑废料提供了一条新的途径，符合可持续发展的要求。

Description

一种仿铁瓷器的制备方法
本申请是“利用废弃灰砖制备的仿铁瓷器及其制备方法”的分案申请，原 申请的申请日为2016年3月20日，申请号为：CN201610164835.X。
技术领域
本发明涉及陶瓷技术领域，具体的涉及一种仿铁瓷器的制备方法。
背景技术
随着城市建设，在拆迁过冲中长生了大量的废旧建筑材料，它不仅对城市 环境造成巨大压力，而且还限制了城市经济和环境的可持续发展，其中数量最 大的就是建房或铺路用的灰砖，现有的灰砖无法重新再次利用，因此通常破碎 后经直接填埋处理。
21世纪是环保的世纪，对环境保护提出了更高的要求，对建筑垃圾的综合 再生利用也是陶瓷工业环保的主要发展方向。我国作为世界上最大的陶瓷生产 国，如果将建筑垃圾充分利用起来，不但可以解决资源浪费问题，解决巨大的 环境危机，还可以实现社会和经济的可持续发展。此外如果能够在减少陶瓷原 料成本的同时制成高附加值的陶瓷，对于陶瓷生产企业来说具有十分重要的意 义。
发明内容
为克服现有技术中的不足，本发明提供一种仿铁瓷器的制备方法。
为实现上述目的，本发明采用的技术方案如下：
利用废弃灰砖制备的仿铁器陶瓷，其特征在于，
所述仿铁器陶瓷的坯料由以下重量份的原料制备而成：废弃灰砖粉20-50 份、四班土20-30份、低温石10-20份、叶腊石10-15份、氧化铁5-10份、金 红石1-5份、青金石1-5份；
所述仿铁器陶瓷的釉料由以下重量份的原料制备而成：长石30-40、废弃 灰砖粉10-30份、石英10-20、草木灰5-10、氧化铁5-10、硅酸锆5-10、双飞 粉5-10、氧化钴1-5、二氧化锰1-5。
优化的，仿铁器陶瓷的坯料由以下重量份的原料制备而成：废弃灰砖粉30 份、四班土28份、低温石15份、叶腊石12份、氧化铁8份、金红石4份、青 金石3份。
优化的，仿铁器陶瓷的釉料由以下重量份的原料制备而成：长石33、废弃 灰砖粉16份、石英16、草木灰5、氧化铁7、硅酸锆8、双飞粉8、氧化钴3、 二氧化锰4。
优化的，仿铁器陶瓷的坯料由以下重量份的原料制备而成：废弃灰砖粉46 份、四班土23份、低温石12份、叶腊石10份、氧化铁6份、金红石2份、青 金石1份。
优化的，仿铁器陶瓷的釉料由以下重量份的原料制备而成：长石30、废弃 灰砖粉28份、石英11、草木灰8、氧化铁5、硅酸锆6、双飞粉6、氧化钴5、 二氧化锰1。
优化的，仿铁器陶瓷的坯料由以下重量份的原料制备而成：废弃灰砖粉28 份、四班土26份、低温石17份、叶腊石15份、氧化铁6份、金红石4份、青 金石4份。
优化的，仿铁器陶瓷的釉料由以下重量份的原料制备而成：长石34、废弃 灰砖粉25份、石英11、草木灰6、氧化铁10、硅酸锆5、双飞粉5、氧化钴1、 二氧化锰3。
利用废弃灰砖制备的仿铁器陶瓷的制备工艺，其特征在于，制备上述任意 一项所述的利用废弃灰砖制备的仿铁器陶瓷，其具体步骤如下：
步骤1，集中收集废弃灰砖，废弃灰砖经清洗、干燥后破碎成块状备用；
步骤2，将块状灰砖煅烧，煅烧温度为500-800℃；
步骤3，煅烧后的块状灰砖破碎成废弃灰砖粉待用；
步骤4，使用步骤3所制备的废弃灰砖粉，并按照仿铁器陶瓷坯料和釉料的 重量份制备分别制备坯料和釉料；
步骤5，将坯料制备成坯体，待坯体干燥后直接施釉；
步骤6，窑炉升温，窑炉内转成还原气氛，烧成温度为950-1200℃；
步骤7，开炉，冷却后获得仿铁器陶瓷。
进一步的，坯料经压滤脱水、陈腐、真空练泥、成型后制成坯体。
进一步的，步骤4所述釉料使用湿球磨制成，其中料：球：水＝1：2：0.7。
由上述对本发明的描述可知，本发明提供的利用废弃灰砖制备的仿铁器陶 瓷，瓷器表面具有与锻打铁器相近的灰褐色，釉面光滑、细腻，在不同的光亮 下能折射出彩色的光斑，具有粗犷、古朴的艺术效果；本发明通过对建筑拆拆 迁所获得的青砖进行分析利用，得到一种可实现仿铁器效果的陶瓷，该种陶瓷 为可以直接用于生产日用或艺术陶瓷；本发明的陶瓷材料可以回收和再利用建 筑垃圾，从而解决陶瓷生产成本资金不断身高、陶瓷产品同质化的问题，在生 产陶瓷的地方容易推广，为解决建筑废料提供了一条新的途径，符合可持续发 展的要求。
具体实施方式
以下通过具体实施方式对本发明作进一步的描述。
为实现上述目的，本发明采用的技术方案如下：
利用废弃灰砖制备的仿铁器陶瓷，所述仿铁器陶瓷的坯料由以下重量份的 原料制备而成：废弃灰砖粉20-50份、四班土20-30份、低温石10-20份、叶 腊石10-15份、氧化铁5-10份、金红石1-5份、青金石1-5份；
所述仿铁器陶瓷的釉料由以下重量份的原料制备而成：长石30-40、废弃 灰砖粉10-30份、石英10-20、草木灰5-10、氧化铁5-10、硅酸锆5-10、双飞 粉5-10、氧化钴1-5、二氧化锰1-5。
具体实施例一：
仿铁器陶瓷的坯料由以下重量份的原料制备而成：废弃灰砖粉30份、四班 土28份、低温石15份、叶腊石12份、氧化铁8份、金红石4份、青金石3份；
釉料由以下重量份的原料制备而成：长石33、废弃灰砖粉16份、石英16、 草木灰5、氧化铁7、硅酸锆8、双飞粉8、氧化钴3、二氧化锰4。
制备上述的利用废弃灰砖制备的仿铁器陶瓷，其制备工艺具体步骤如下：
步骤1，集中收集废弃灰砖，废弃灰砖经清洗、干燥后破碎成块状备用；
步骤2，将块状灰砖煅烧，煅烧温度为700℃；
步骤3，煅烧后的块状灰砖破碎成废弃灰砖粉待用；
步骤4，使用步骤3所制备的废弃灰砖粉，并按照仿铁器陶瓷坯料和釉料的 重量份制备分别制备坯料和釉料，坯料经压滤脱水、陈腐、真空练泥、成型后 制成坯体，釉料使用湿球磨制成，其中料：球：水＝1：2：0.7；
步骤5，将坯料制备成坯体，待坯体干燥后直接施釉；
步骤6，窑炉升温，窑炉内转成还原气氛，烧成温度为1000℃；
步骤7，开炉，冷却后获得仿铁器陶瓷。
具体实施例二：
仿铁器陶瓷的坯料由以下重量份的原料制备而成：废弃灰砖粉46份、四班 土23份、低温石12份、叶腊石10份、氧化铁6份、金红石2份、青金石1份；
仿铁器陶瓷的釉料由以下重量份的原料制备而成：长石30、废弃灰砖粉28 份、石英11、草木灰8、氧化铁5、硅酸锆6、双飞粉6、氧化钴5、二氧化锰1。
制备上述的利用废弃灰砖制备的仿铁器陶瓷，其制备工艺具体步骤如下：
步骤1，集中收集废弃灰砖，废弃灰砖经清洗、干燥后破碎成块状备用；
步骤2，将块状灰砖煅烧，煅烧温度为750℃；
步骤3，煅烧后的块状灰砖破碎成废弃灰砖粉待用；
步骤4，使用步骤3所制备的废弃灰砖粉，并按照仿铁器陶瓷坯料和釉料的 重量份制备分别制备坯料和釉料，坯料经压滤脱水、陈腐、真空练泥、成型后 制成坯体，釉料使用湿球磨制成，其中料：球：水＝1：2：0.7；
步骤5，将坯料制备成坯体，待坯体干燥后直接施釉；
步骤6，窑炉升温，窑炉内转成还原气氛，烧成温度为1100℃；
步骤7，开炉，冷却后获得仿铁器陶瓷。
具体实施例三：
仿铁器陶瓷的坯料由以下重量份的原料制备而成：废弃灰砖粉28份、四班 土26份、低温石17份、叶腊石15份、氧化铁6份、金红石4份、青金石4份；
仿铁器陶瓷的釉料由以下重量份的原料制备而成：长石34、废弃灰砖粉25 份、石英11、草木灰6、氧化铁10、硅酸锆5、双飞粉5、氧化钴1、二氧化锰 3。
制备上述的利用废弃灰砖制备的仿铁器陶瓷，其制备工艺具体步骤如下：
步骤1，集中收集废弃灰砖，废弃灰砖经清洗、干燥后破碎成块状备用；
步骤2，将块状灰砖煅烧，煅烧温度为650℃；
步骤3，煅烧后的块状灰砖破碎成废弃灰砖粉待用；
步骤4，使用步骤3所制备的废弃灰砖粉，并按照仿铁器陶瓷坯料和釉料的 重量份制备分别制备坯料和釉料，坯料经压滤脱水、陈腐、真空练泥、成型后 制成坯体，釉料使用湿球磨制成，其中料：球：水＝1：2：0.7；
步骤5，将坯料制备成坯体，待坯体干燥后直接施釉；
步骤6，窑炉升温，窑炉内转成还原气氛，烧成温度为980℃；
步骤7，开炉，冷却后获得仿铁器陶瓷。
制备上述方法所制备的利用废弃灰砖制备的仿铁器陶瓷，瓷器表面具有与锻 打铁器相近的灰褐色，釉面光滑、细腻，在不同的光亮下能折射出彩色的光斑， 具有粗犷、古朴的艺术效果；本发明通过对建筑拆拆迁所获得的青砖进行分析 利用，得到一种可实现仿铁器效果的陶瓷，该种陶瓷为可以直接用于生产日用 或艺术陶瓷；本发明的陶瓷材料可以回收和再利用建筑垃圾，从而解决陶瓷生 产成本资金不断身高、陶瓷产品同质化的问题，在生产陶瓷的地方容易推广， 为解决建筑废料提供了一条新的途径，符合可持续发展的要求。
上述仅为本发明的若干具体实施方式，但本发明的设计构思并不局限于此， 凡利用此构思对本发明进行非实质性的改动，均应属于侵犯本发明保护范围的 行为。

Claims (3)

1.一种仿铁器陶瓷的制备工艺，其特征在于，其具体步骤如下：
步骤1，集中收集废弃灰砖，废弃灰砖经清洗、干燥后破碎成块状备用；
步骤2，将块状灰砖煅烧，煅烧温度为500-800℃；
步骤3，煅烧后的块状灰砖破碎成废弃灰砖粉待用；
步骤4，使用步骤3所制备的废弃灰砖粉，并按照仿铁器陶瓷坯料和釉料的重量份制备分别制备坯料和釉料；
步骤5，将坯料制备成坯体，待坯体干燥后直接施釉；
步骤6，窑炉升温，窑炉内转成还原气氛，烧成温度为950-1200℃；
步骤7，开炉，冷却后获得仿铁器陶瓷。
2.根据权利要求1所述的利用废弃灰砖制备的仿铁器陶瓷的制备工艺，其特征在于：所述坯料经压滤脱水、陈腐、真空练泥、成型后制成坯体。
3.根据权利要求1所述的利用废弃灰砖制备的仿铁器陶瓷的制备工艺，其特征在于：步骤4所述釉料使用湿球磨制成，其中料：球：水＝1：2：0.7。
CN201810163156.XA 2016-03-20 2016-03-20 一种仿铁瓷器的制备方法 Active CN108484111B (zh)