CN108468254A - A kind of moisture-proof paper furniture corrugated paper and preparation method thereof - Google Patents
A kind of moisture-proof paper furniture corrugated paper and preparation method thereof Download PDFInfo
- Publication number
- CN108468254A CN108468254A CN201810256255.2A CN201810256255A CN108468254A CN 108468254 A CN108468254 A CN 108468254A CN 201810256255 A CN201810256255 A CN 201810256255A CN 108468254 A CN108468254 A CN 108468254A
- Authority
- CN
- China
- Prior art keywords
- parts
- paper
- moisture
- corrugated paper
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of moisture-proof paper furniture corrugated papers, it is included in 100 parts of magma according to parts by weight and contains 15 parts of modifying agent and 13 parts of anti-blushing agents, wherein the modifying agent includes 50 60 parts of titanium dioxide, 10 15 parts of perlites, 10 15 parts of molybdenum disulfide and 15 parts of rare earth elements by weight；The anti-blushing agent includes 40 50 parts of paraffin, 20 30 parts of styrene, 10 15 parts of montmorillonite, 15 parts of tween, 15 parts of starch and 15 parts of graphene by weight.Obtained corrugated paper through the invention greatly strengthens the burst index and humidity resistance of corrugated paper so that this corrugated paper has higher intensity and moisture resistance, improves the service life of corrugated case by adding modifying agent and anti-blushing agent in paper making raw material.In addition the sizing agent for using independent research, further increases the intensity of corrugated paper.
Description
Technical field
The present invention relates to paper technology, especially a kind of moisture-proof paper furniture corrugated paper and preparation method thereof.
Background technology
Paper furniture, which is furniture of the material based on papery, can be referred to as paper furniture.Such as corrugated paper furniture.Paper furniture is normal
Material is corrugated paper, is distinguished in technique less with the carton in packaging logistics field, surface is exactly brown paper, is only selected
With best material, the bearing capacity of itself is stronger, and bigger load-bearing may be implemented by structure design.These furniture are most
All be import paper, water proofing property is fine, can waterproof 5 minutes or more, therefore be easy to clean, it is only necessary to be cleaned with wet cloth
Just.Compared to antique traditional furniture, the cost of paper furniture is not low, but relative to the antique traditional furniture for having brand, having design, some are general
The cost of logical paper furniture or lower, price is also much lower.But still there is certain ask in traditional paper furniture
Topic, as moisture resistance is not high.
Invention content
A kind of the main purpose of the present invention is to provide overall construction intensities higher, more environmentally friendly moisture-proof paper furniture
With corrugated paper and preparation method thereof.
To achieve the above objectives, the technical solution adopted by the present invention is：A kind of moisture-proof paper furniture corrugated paper, it is described
Corrugated paper is included in 100 parts of magma according to parts by weight and contains 1-5 parts of modifying agent and 1-3 parts of anti-blushing agents, wherein the modifying agent
Include 50-60 parts of titanium dioxide, 10-15 parts of perlites, 10-15 parts of molybdenum disulfide and 1-5 parts of rare earth elements by weight；It is described
Anti-blushing agent is by weight including 40-50 parts of paraffin, 20-30 parts of styrene, 10-15 parts of montmorillonite, 1-5 parts of tween, 1-5
The starch and 1-5 parts of graphene of part.
The surface of the corrugated paper is coated with sizing agent, and wherein sizing agent includes 20-30 parts of nanometer butyronitrile rubbers by weight
Glue, 10-15 part epoxy resin, 5-10 parts of phenol-formaldehyde resin modified, 5-10 parts of hydrogels, 20-30 parts of urea and 40-50 parts of water.
A kind of preparation method of moisture-proof paper furniture corrugated paper, includes the following steps：
Step 1: choosing paper making raw material, water is added to carry out bubble slurry, puts into pulper and crush, paper making raw material is made to dissociate into paper pulp；
Step 2: the paper pulp passes through pressurized screen successively and scummer removes impurity；
Step 3: the paper pulp after removal of impurities, which is input to mill, carries out mashing processing, magma is made；
Step 4: 1-5 parts of modifying agent and 1-3 parts of anti-blushing agents are added into 100 parts of magma by weight, it is sufficiently stirred, then
Moisture removal is removed, the copy paper that moisture content is 10-20% is obtained and starches,
Step 5: it is 15-25% that copy paper slurry, which is sent to wet end molding dehydration to mass dryness fraction,；
Step 6: slurry after molding is delivered to press section, the slurry press dewatering to mass dryness fraction is 40-50% by press section, so
Sizing agent is uniformly applied to by paper surface using sizing applicator afterwards；
Step 7: the sized corrugated paper semi-finished product in surface are put into drying cylinder, temperature is adjusted to 105-110 DEG C, moisture content is in 2-
4%, after being placed on indoor standing 24 hours, further takes out to be placed at aeration-drying and place 24 hours, you can obtain moisture-proof papery man
Tool corrugated paper.
The paper making raw material includes 20-30 parts of 70-80 parts of sawdust and waste paper by weight.
The preparation method of the modifying agent is by 50-60 parts of titanium dioxide, 10-15 parts of perlites, 10-15 parts of molybdenum disulfide
It is uniformly mixed, then heats while stirring, heating temperature is 200-250 DEG C, is pulverized after cooling with 1-5 parts of rare earth elements
End is up to modifying agent.
The preparation method of the anti-blushing agent be first by 40-50 parts of paraffin, 10-15 parts of montmorillonite, 1-5 parts of starch and
1-5 parts of graphene is uniformly mixed, and is then placed in reaction kettle, and heating temperature is 600-700 DEG C, and heating time 30min is waited for cold
But to after 200 DEG C again plus 20-30 part styrene, 1-5 part of tween, heating time 15min, it is cooling after grind into powder prevent to obtain the final product
Damp agent.
The preparation method of the sizing agent be by 20-30 parts of nanometer nitrile rubbers, 10-15 parts of epoxy resin, 5-10 parts
Phenol-formaldehyde resin modified, 5-10 part hydrogel, 20-30 parts of urea and 40-50 parts of water, 50-60 DEG C is heated to after stirring evenly makes respectively
Ingredient all dissolves, and waits for that temperature is reduced to room temperature naturally.
Titanium dioxide in the modifying agent can improve the adhesion strength between each raw material, pearl as binder
The effect of rock can do thermal insulation material, improve heat resistance, and molybdenum disulfide is used as lubricant, rare earth element promotion above-mentioned active ingredient is sent out
It waves, the final intensity for improving corrugated paper.
The organic anti-blushing agent of paraffin and styrene in the anti-blushing agent, montmorillonite and graphene for separate outer vapor with
Corrugated paper is in direct contact, and tween and starch then are used to improve the wetability of anti-blushing agent, at the same graphene can also promote it is moisture-proof
The effect of active ingredient, plays, and finally improves its moisture protection.The items of corrugated paper made from production method using the present invention
Performance and substance index comply fully with the requirements of corrugated paper.
Nanometer nitrile rubber, epoxy resin, phenol-formaldehyde resin modified in the sizing agent, can increase substantially top sizing
Effect, enhance corrugated paper ring crush intensity.In addition hydrogel is added in corrugated paper Cypres base-material, sizing can be improved
The hydrophobicity of paper after agent sizing, while the surface tension between various composition phases can also be improved, it is allowed to be formed uniform and stable
Dispersion.
The paper making raw material includes that sawdust and waste paper adapt to the whole society effectively using waste caused by every profession and trade
Energy conservation and environmental protection and the circular economy spirit advocated.
A kind of moisture-proof paper furniture corrugated paper and preparation method thereof that the present invention obtains, technique effect is by making
Modifying agent and anti-blushing agent are added in paper material, greatly strengthen the burst index and humidity resistance of corrugated paper so that this corrugated paper
Have higher intensity and moisture resistance, improves the service life of corrugated case.In addition the sizing agent for using independent research, into one
Step improves the intensity of corrugated paper.
Specific implementation mode
It is described below for disclosing the present invention so that those skilled in the art can realize the present invention.It is excellent in being described below
Embodiment is selected to be only used as illustrating, it may occur to persons skilled in the art that other obvious modifications.
Embodiment 1：
A kind of moisture-proof paper furniture corrugated paper provided in this embodiment, the corrugated paper are included in 100 parts according to parts by weight
Contain 3 parts of modifying agent and 3 parts of anti-blushing agents in magma, wherein the modifying agent includes 50 parts of titanium dioxide, 10 parts of treasure by weight
Zhu Yan, 10 parts of molybdenum disulfide and 1 part of rare earth element；The anti-blushing agent is by weight including 40 parts of paraffin, 20 parts of styrene, 10
The montmorillonite, 1 part of tween, 1 part of starch and 1 part of graphene of part.
The surface of the corrugated paper be coated with sizing agent, wherein sizing agent by weight include 20 parts of nanometer nitrile rubbers,
10 parts of epoxy resin, 5 parts of phenol-formaldehyde resin modified, 5 parts of hydrogels, 20 parts of urea and 40 parts of water.
A kind of preparation method of moisture-proof paper furniture corrugated paper, includes the following steps：
Step 1: choosing paper making raw material, water is added to carry out bubble slurry, puts into pulper and crush, paper making raw material is made to dissociate into paper pulp；
Step 2: the paper pulp passes through pressurized screen successively and scummer removes impurity；
Step 3: the paper pulp after removal of impurities, which is input to mill, carries out mashing processing, magma is made；
Step 4: 3 parts of modifying agent and 3 parts of anti-blushing agents are added into 100 parts of magma by weight, it is sufficiently stirred, then removes
Moisture obtains the copy paper that moisture content is 10-20% and starches；
Step 5: it is 15-25% that copy paper slurry, which is sent to wet end molding dehydration to mass dryness fraction,；
Step 6: slurry after molding is delivered to press section, the slurry press dewatering to mass dryness fraction is 40-50% by press section, so
Sizing agent is uniformly applied to by paper surface using sizing applicator afterwards；
Step 7: the sized corrugated paper semi-finished product in surface are put into drying cylinder, temperature is adjusted to 105-110 DEG C, moisture content is in 2-
4%, after being placed on indoor standing 24 hours, further takes out to be placed at aeration-drying and place 24 hours, you can obtain moisture-proof papery man
Tool corrugated paper.
The paper making raw material includes 30 parts of 70 parts of sawdust and waste paper by weight.
The preparation method of the modifying agent is by 50 parts of titanium dioxide, 10 parts of perlites, 10 parts of molybdenum disulfide and 1 part of rare earth
Element is uniformly mixed, and is then heated while stirring, and heating temperature is 200-250 DEG C, and grind into powder is up to modified after cooling
Agent.
The preparation method of the anti-blushing agent is first by 40 parts of paraffin, 10 parts of montmorillonite, 1 part of starch and 1 part of stone
Black alkene is uniformly mixed, and is then placed in reaction kettle, and heating temperature is 600-700 DEG C, and heating time 30min is cooled to 200 DEG C
Add 20 parts of styrene, 1 part of tween again afterwards, heating time 15min, grind into powder is up to anti-blushing agent after cooling.
The preparation method of the sizing agent is by 20 parts of nanometer nitrile rubbers, 10 parts of epoxy resin, 5 parts of modified phenolic resin
Fat, 5 parts of hydrogels, 20 parts of urea and 40 parts of water, 50-60 DEG C is heated to after stirring evenly makes each ingredient all dissolve, and waits for temperature
Naturally it is reduced to room temperature.
The pop strength of corrugated paper made from the present embodiment is 730Kpa, and ring crush index is 8.1 Nm/g, relatively wet
The side pressure mechanical strength spent under 85% state improves 28% or so than common cardboard.
Embodiment 2：
A kind of moisture-proof paper furniture corrugated paper provided in this embodiment and preparation method thereof is substantially same as Example 1,
It includes 60 parts of titanium dioxide, 15 parts of perlites, 15 parts of molybdenum disulfide and 5 parts of rare earths that difference, which is the modifying agent by weight,
Element.
The pop strength of corrugated paper made from the present embodiment is 700KPa, and ring crush index is 7.9 Nm/g, relatively wet
The side pressure mechanical strength spent under 85% state improves 28% or so than common cardboard.
Embodiment 3：
A kind of moisture-proof paper furniture corrugated paper provided in this embodiment and preparation method thereof substantially with 1 phase of embodiment
Together, difference be the anti-blushing agent by weight and include 50 parts paraffin, 30 parts of styrene, 15 parts of montmorillonite, 5 parts
Tween, 5 parts of starch and 5 parts of graphene.
The pop strength of corrugated paper made from the present embodiment is 710KPa, and ring crush index is 8.0 Nm/g, relatively wet
The side pressure mechanical strength spent under 85% state improves 28% or so than common cardboard.
Embodiment 4：
A kind of moisture-proof paper furniture corrugated paper provided in this embodiment and preparation method thereof is substantially same as Example 1,
It includes 30 parts of nanometer nitrile rubbers, 15 parts of epoxy resin, 10 parts of modified phenolic that difference, which is the sizing agent by weight,
Resin, 10 parts of hydrogels, 30 parts of urea and 50 parts of water.
The pop strength of corrugated paper made from the present embodiment is 750KPa, and ring crush index is 8.3 Nm/g, relatively wet
The side pressure mechanical strength spent under 85% state improves 28% or so than common cardboard.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and what is described in the above embodiment and the description is only the present invention
Principle, various changes and improvements may be made to the invention without departing from the spirit and scope of the present invention, these variation and
Improvement is both fallen in the range of claimed invention.The present invention claims protection domain by appended claims and its
Equivalent defines.
Claims (7)
1. a kind of moisture-proof paper furniture corrugated paper, which is characterized in that the corrugated paper is included in 100 parts of originals according to parts by weight
In slurry contain 1-5 part modifying agent and 1-3 parts of anti-blushing agents, wherein the modifying agent by weight including 50-60 parts of titanium dioxide,
10-15 parts of perlites, 10-15 parts of molybdenum disulfide and 1-5 parts of rare earth elements；The anti-blushing agent includes 40-50 parts by weight
Paraffin, 20-30 part styrene, 10-15 parts of montmorillonite, 1-5 parts of tween, 1-5 parts of starch and 1-5 parts of graphene.
2. a kind of moisture-proof paper furniture corrugated paper according to claim 1, which is characterized in that the table of the corrugated paper
Face is coated with sizing agent, and wherein sizing agent includes 20-30 parts of nanometer nitrile rubbers, 10-15 parts of epoxy resin, 5-10 by weight
The phenol-formaldehyde resin modified, 5-10 parts of hydrogels, 20-30 parts of urea and 40-50 parts of water of part.
3. a kind of preparation method of moisture-proof paper furniture corrugated paper as claimed in claim 1 or 2, which is characterized in that packet
Include following steps：
Step 1: choosing paper making raw material, water is added to carry out bubble slurry, puts into pulper and crush, paper making raw material is made to dissociate into paper pulp；
Step 2: the paper pulp passes through pressurized screen successively and scummer removes impurity；
Step 3: the paper pulp after removal of impurities, which is input to mill, carries out mashing processing, magma is made；
Step 4: 1-5 parts of modifying agent and 1-3 parts of anti-blushing agents are added into 100 parts of magma by weight, it is sufficiently stirred, then
Moisture removal is removed, the copy paper that moisture content is 10-20% is obtained and starches；
Step 5: it is 15-25% that copy paper slurry, which is sent to wet end molding dehydration to mass dryness fraction,；
Step 6: slurry after molding is delivered to press section, the slurry press dewatering to mass dryness fraction is 40-50% by press section, so
Sizing agent is uniformly applied to by paper surface using sizing applicator afterwards；
Step 7: the sized corrugated paper semi-finished product in surface are put into drying cylinder, temperature is adjusted to 105-110 DEG C, moisture content is in 2-
4%, after being placed on indoor standing 24 hours, further takes out to be placed at aeration-drying and place 24 hours, you can obtain moisture-proof papery man
Tool corrugated paper.
4. a kind of preparation method of moisture-proof paper furniture corrugated paper according to claim 4, it is characterised in that：It is described
Paper making raw material includes 20-30 parts of 70-80 parts of sawdust and waste paper by weight.
5. a kind of preparation method of moisture-proof paper furniture corrugated paper according to claim 4, it is characterised in that：It is described
The preparation method of modifying agent is by 50-60 parts of titanium dioxide, 10-15 parts of perlites, 10-15 parts of molybdenum disulfide and 1-5 parts of rare earths
Element is uniformly mixed, and is then heated while stirring, and heating temperature is 200-250 DEG C, and grind into powder is up to modified after cooling
Agent.
6. a kind of preparation method of moisture-proof paper furniture corrugated paper according to claim 4, it is characterised in that：It is described
The preparation method of anti-blushing agent is first by 40-50 parts of paraffin, 10-15 parts of montmorillonite, 1-5 parts of starch and 1-5 parts of graphite
Alkene is uniformly mixed, and is then placed in reaction kettle, and heating temperature is 600-700 DEG C, heating time 30min, after being cooled to 200 DEG C
Again plus 20-30 parts of styrene, 1-5 parts of tween, heating time 15min, it is cooling after grind into powder up to anti-blushing agent.
7. a kind of preparation method of moisture-proof paper furniture corrugated paper according to claim 4, it is characterised in that：It is described
The preparation method of sizing agent be by 20-30 parts of nanometer nitrile rubbers, 10-15 parts of epoxy resin, 5-10 parts of phenol-formaldehyde resin modified,
5-10 parts of hydrogels, 20-30 parts of urea and 40-50 parts of water, 50-60 DEG C is heated to after stirring evenly makes each ingredient all dissolve,
Wait for that temperature is reduced to room temperature naturally.