CN108468208A - A kind of silica aerogel insulation quilt of environment-friendly and green - Google Patents
A kind of silica aerogel insulation quilt of environment-friendly and green Download PDFInfo
- Publication number
- CN108468208A CN108468208A CN201810279613.1A CN201810279613A CN108468208A CN 108468208 A CN108468208 A CN 108468208A CN 201810279613 A CN201810279613 A CN 201810279613A CN 108468208 A CN108468208 A CN 108468208A
- Authority
- CN
- China
- Prior art keywords
- silica aerogel
- friendly
- green
- environment
- insulation quilt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of silica aerogel insulation quilt of environment-friendly and green proposed by the present invention, using soft felt as substrate, the impregnating agent that collocation is mixed with silica aerogel toner is impregnated, it is multi-layer bonded after impregnation drying, and carry out coating treatment and be made, silica aerogel insulation quilt is made and has certain silica aerogel characteristic, its density is low, hole is small, and heat-insulating property is outstanding, and manufacture craft is simple, it is of low cost, contamination-free generates in manufacturing process, environment-friendly and green, is suitble to industrialization promotion.
Description
Technical field
The present invention relates to aeroge production application field, the silica aerogel insulation quilt of especially a kind of environment-friendly and green.
Background technology
Aerosil has nanoaperture, is a kind of porous solid material, has low-density, high porosity
Design feature has superinsulation performance.Using silica aerosil microballoon and coating membrane-forming materials combine, formation has
The coating of super heat-insulating property.
Insulation quilt currently sold on the market, the defect that generally existing hole is big, density is high, in similar product, heat preservation effect
Fruit is not outstanding, and need to largely be handled, and pollutant is serious in processing procedure, not only of high cost, and environmental pollution is also very
Seriously.
Invention content
The present invention is in view of the above-mentioned problems, the invention discloses a kind of silica aerogel insulation quilts of environment-friendly and green.
Specific technical solution is as follows:
A kind of silica aerogel insulation quilt of environment-friendly and green, which is characterized in that preparation method, including step in detail below:
1, using soft felt as substrate, specified specification is cut into;
2, impregnating agent is added in dipping tank, and the silica aerogel toner used is added, be heated to 40 DEG C and stir evenly;
3, the soft felt cut is put into dipping tank, is impregnated, dipping duration 10 minutes, repeated impregnations are three times;
4, after the completion of impregnating, processing is dried to soft felt;
5, after the completion of dry, multiple soft felts is bonded by bonding agent and are superimposed;
6, the soft felt of heap poststack carries out face coat processing to get a kind of silica aerogel insulation quilt of environment-friendly and green;
Wherein, the silica aerogel toner is made by silica aerogel and epoxy resin, and specific preparation method is as follows:
A, it takes silica aerogel crushing grinding at powder, crosses 250 mesh sieve, obtain silica aerogel powder,
B, the silica aerogel powder of gained in step a is added in epoxy resin, is uniformly mixed at 35 DEG C, it is then dry
Dry processing obtains silica aerogel resin mass;
C, the silica aerogel resin crushing grinding of gained in step b is crossed into 250 mesh sieve to get silica aerogel toner at powder.
The silica aerogel insulation quilt of above-mentioned a kind of environment-friendly and green, wherein the impregnating agent is impregnating with silane agent.
The silica aerogel insulation quilt of above-mentioned a kind of environment-friendly and green, wherein the silica aerogel powder and asphalt mixtures modified by epoxy resin lipid
Amount is than being 1:50~70.
The silica aerogel insulation quilt of above-mentioned a kind of environment-friendly and green, wherein the epoxy resin is aqueous epoxy resins.
The silica aerogel insulation quilt of above-mentioned a kind of environment-friendly and green, wherein coating used in face coat described in step 6 is
A kind of or both mixture in water-soluble resin glue, phenolic resin.
Beneficial effects of the present invention are:
A kind of silica aerogel insulation quilt of environment-friendly and green proposed by the present invention, using soft felt as substrate, collocation is mixed with silica aerogel
The impregnating agent of toner is impregnated, multi-layer bonded after impregnation drying, and is carried out coating treatment and be made, and silica aerogel is made
Insulation quilt has certain silica aerogel characteristic, and density is low, hole is small, and heat-insulating property is outstanding, and manufacture craft is simple, cost
Cheap, contamination-free generates in manufacturing process, environment-friendly and green, is suitble to industrialization promotion.
Specific implementation mode
It is clear to make technical scheme of the present invention be more clear, below the present invention is described further, it is any to this
The technical characteristic of inventive technique scheme carries out the scheme that equivalencing is obtained with conventional reasoning and each falls within the scope of the present invention.
Embodiment one
A kind of silica aerogel insulation quilt of environment-friendly and green, which is characterized in that preparation method, including step in detail below:
1, using soft felt as substrate, specified specification is cut into;
2, impregnating agent is added in dipping tank, and the silica aerogel toner used is added, be heated to 40 DEG C and stir evenly;
3, the soft felt cut is put into dipping tank, is impregnated, dipping duration 10 minutes, repeated impregnations are three times;
4, after the completion of impregnating, processing is dried to soft felt;
5, after the completion of dry, multiple soft felts is bonded by bonding agent and are superimposed;
6, the soft felt of heap poststack carries out face coat processing to get a kind of silica aerogel insulation quilt of environment-friendly and green;
Wherein, the silica aerogel toner is made by silica aerogel and epoxy resin, and specific preparation method is as follows:
A, it takes silica aerogel crushing grinding at powder, crosses 250 mesh sieve, obtain silica aerogel powder,
B, the silica aerogel powder of gained in step a is added in epoxy resin, is uniformly mixed at 35 DEG C, it is then dry
Dry processing obtains silica aerogel resin mass;
C, the silica aerogel resin crushing grinding of gained in step b is crossed into 250 mesh sieve to get silica aerogel toner at powder.
Wherein, the impregnating agent is impregnating with silane agent, and the silica aerogel powder is 1 with epoxy resin mass ratio:50, institute
Epoxy resin is stated as aqueous epoxy resins, coating used in face coat described in step 6 is water-soluble resin glue.
Embodiment two
A kind of silica aerogel insulation quilt of environment-friendly and green, which is characterized in that preparation method, including step in detail below:
1, using soft felt as substrate, specified specification is cut into;
2, impregnating agent is added in dipping tank, and the silica aerogel toner used is added, be heated to 40 DEG C and stir evenly;
3, the soft felt cut is put into dipping tank, is impregnated, dipping duration 10 minutes, repeated impregnations are three times;
4, after the completion of impregnating, processing is dried to soft felt;
5, after the completion of dry, multiple soft felts is bonded by bonding agent and are superimposed;
6, the soft felt of heap poststack carries out face coat processing to get a kind of silica aerogel insulation quilt of environment-friendly and green;
Wherein, the silica aerogel toner is made by silica aerogel and epoxy resin, and specific preparation method is as follows:
A, it takes silica aerogel crushing grinding at powder, crosses 250 mesh sieve, obtain silica aerogel powder,
B, the silica aerogel powder of gained in step a is added in epoxy resin, is uniformly mixed at 35 DEG C, it is then dry
Dry processing obtains silica aerogel resin mass;
C, the silica aerogel resin crushing grinding of gained in step b is crossed into 250 mesh sieve to get silica aerogel toner at powder.
Wherein, the impregnating agent is impregnating with silane agent, and the silica aerogel powder is 1 with epoxy resin mass ratio:60, institute
Epoxy resin is stated as aqueous epoxy resins, coating used in face coat described in step 6 is in phenolic resin.
Embodiment three
A kind of silica aerogel insulation quilt of environment-friendly and green, which is characterized in that preparation method, including step in detail below:
1, using soft felt as substrate, specified specification is cut into;
2, impregnating agent is added in dipping tank, and the silica aerogel toner used is added, be heated to 40 DEG C and stir evenly;
3, the soft felt cut is put into dipping tank, is impregnated, dipping duration 10 minutes, repeated impregnations are three times;
4, after the completion of impregnating, processing is dried to soft felt;
5, after the completion of dry, multiple soft felts is bonded by bonding agent and are superimposed;
6, the soft felt of heap poststack carries out face coat processing to get a kind of silica aerogel insulation quilt of environment-friendly and green;
Wherein, the silica aerogel toner is made by silica aerogel and epoxy resin, and specific preparation method is as follows:
A, it takes silica aerogel crushing grinding at powder, crosses 250 mesh sieve, obtain silica aerogel powder,
B, the silica aerogel powder of gained in step a is added in epoxy resin, is uniformly mixed at 35 DEG C, it is then dry
Dry processing obtains silica aerogel resin mass;
C, the silica aerogel resin crushing grinding of gained in step b is crossed into 250 mesh sieve to get silica aerogel toner at powder.
Wherein, the impregnating agent is impregnating with silane agent, and the silica aerogel powder is 1 with epoxy resin mass ratio:70,
The epoxy resin is aqueous epoxy resins, and coating used in face coat described in step 6 is water-soluble resin glue, phenolic aldehyde tree
The mixture of both fat, mixed proportion 1:1.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, the change or replacement that can be readily occurred in,
Should all it cover within the scope of the present invention.Therefore, protection scope of the present invention should be with the protection domain of claims
Subject to.
Claims (5)
1. a kind of silica aerogel insulation quilt of environment-friendly and green, which is characterized in that preparation method, including step in detail below:
(1), using soft felt as substrate, cut into specified specification;
(2), impregnating agent is added in dipping tank, and the silica aerogel toner used is added, it is equal to be heated to 40 DEG C of stirrings
It is even;
(3), the soft felt cut is put into dipping tank, impregnated, dipping duration 10 minutes, repeated impregnations are three times;
(4), after the completion of dipping, processing is dried to soft felt;
(5), after the completion of drying, multiple soft felts are passed through into bonding agent bonding superposition;
(6), heap poststack soft felt, carry out face coat processing to get a kind of environment-friendly and green silica aerogel insulation quilt;
Wherein, the silica aerogel toner is made by silica aerogel and epoxy resin, and specific preparation method is as follows:
A, it takes silica aerogel crushing grinding at powder, crosses 250 mesh sieve, obtain silica aerogel powder,
B, the silica aerogel powder of gained in step a is added in epoxy resin, is uniformly mixed at 35 DEG C, it is then dry
Dry processing obtains silica aerogel resin mass;
C, the silica aerogel resin crushing grinding of gained in step b is crossed into 250 mesh sieve to get silica aerogel toner at powder.
2. a kind of silica aerogel insulation quilt of environment-friendly and green as described in claim 1, which is characterized in that the impregnating agent is silicon
Alkane impregnating agent.
3. a kind of silica aerogel insulation quilt of environment-friendly and green as described in claim 1, which is characterized in that the silica aerogel powder
Body is 1 with epoxy resin mass ratio:50~70.
4. a kind of silica aerogel insulation quilt of environment-friendly and green as described in claim 1, which is characterized in that the epoxy resin is
Aqueous epoxy resins.
5. a kind of silica aerogel insulation quilt of environment-friendly and green as described in claim 1, which is characterized in that step(6)Described in
Coating used in face coat is water-soluble resin glue, a kind of or both mixture in phenolic resin.