CN108466472A - A kind of lamination process of foaming surfboard - Google Patents

A kind of lamination process of foaming surfboard Download PDF

Info

Publication number
CN108466472A
CN108466472A CN201810315964.3A CN201810315964A CN108466472A CN 108466472 A CN108466472 A CN 108466472A CN 201810315964 A CN201810315964 A CN 201810315964A CN 108466472 A CN108466472 A CN 108466472A
Authority
CN
China
Prior art keywords
surfboard
fiber
glass
foaming
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810315964.3A
Other languages
Chinese (zh)
Inventor
杨林
吕兆轩
刘统磊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anqing Yongda Sports Culture Co Ltd
Original Assignee
Anqing Yongda Sports Culture Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anqing Yongda Sports Culture Co Ltd filed Critical Anqing Yongda Sports Culture Co Ltd
Priority to CN201810315964.3A priority Critical patent/CN108466472A/en
Publication of CN108466472A publication Critical patent/CN108466472A/en
Pending legal-status Critical Current

Abstract

Include raw material the invention discloses a kind of lamination process of foaming surfboard, cut cloth, gluing, do cloth, dry glue processing, polishing step.The present invention sticks glass-fiber-fabric using asphalt mixtures modified by epoxy resin gluing, environmental protection, it is pollution-free, human body will not be damaged, the lamination that this technique carries out expansion type surfboard using glass-fiber-fabric and fiber cloth clad type is handled, can make surfboard there is higher toughness, the surfboard produced to be hardly damaged, good water-proof effect.

Description

A kind of lamination process of foaming surfboard
Technical field：
The present invention relates to the field of production of surfboard, a kind of particularly lamination process of foaming surfboard.
Background technology：
Surfboard is the sports equipment that people are used for that surfing to be moved.Initially use surfboard grows 5 meters or so, weighs 50~60 Kilogram.After World War II, there is plastic foamboard, the shape of plate also has improvement.Surfboard length 1.5 now~ 2.7 meters, about 60 centimetres wide, 7~10 centimetres of thickness, plate is light and puts down, and rear and front end is slightly narrow, and there is the tail of stabilization together in the back lower place Fin.In order to increase frictional force, a kind of outer membrane of wax is also coated in plate face.
With being constantly progressive with people to the higher and higher of product requirement for production technology, produces the technique of surfboard and make Material also becomes increasingly complex and has higher technology requirement, when how to make surfboard more environmentally-friendly and having more longer Wait the service life with meet using and the requirements such as sense organ be a problem to be solved, and it is relatively early before there are production technologies existing Production technology under without practical significance.
Invention content：
The object of the present invention is to provide a kind of lamination process of foaming surfboard.
The technical solution adopted by the present invention is：
A kind of lamination process of foaming surfboard, it is characterised in that：Include the following steps：
1) raw material：It is 21.5-22 ㎏/m to select qualified semi-finished product foaming surfboard, density3, check its size, surface Smoothness and corner angle radian；
2) cloth is cut：The bottom margin of selection order requirements or suitable glass-fiber-fabric, the surfboard that foams according to semi-finished product It cuts, cut size, which is subject to be more than, cuts marginal dimension 2-2.5cm, determines that each semi-finished product foaming surfboard needs glass-fiber-fabric The number of plies；
3) gluing：It is uniformly smeared in semi-finished product foaming surfboard surfaces using the mixture glue of epoxy resin and curing agent, Eye and skin protection are carried out when gluing；
4) cloth is made：The glass-fiber-fabric cut in step 2) is laid with, is coated to the semi-finished product foaming after gluing in step 3) The edge of surfboard surfaces, glass-fiber-fabric is located at semi-finished product foaming surfboard bottom surface；
Then scraping glass-fiber-fabric surface using scraper plate makes that mixture glue permeates glass-fiber-fabric completely, extra mixture glue is gone It removes, ensures glass-fiber-fabric edge unfolded when scraping mixture glue, without nose and bubble, air hole；
In the tail portion of semi-finished product foaming surfboard bottom surface, 0-65cm ranges are laid with fiber cloth bonding securely forward again, fiber cloth Edges cover glass-fiber-fabric edge, spontaneously dry 1.3-1.7 hours；
Finally the whole of entire semi-finished product foaming surfboard outer wall is covered in glass-fiber-fabric and fiber cloth external sheath, one layer of bonding Fiber cloth need to ensure the EDGE CONTACT of the whole fiber cloth or overlap joint, must not have gapless, brush one layer of mixture glue, do Cloth is completed；
5) dry glue is handled：The semi-finished product foaming surfboard for doing after the completion of cloth is placed in 25-28 DEG C of dustfree environment and is stood It is dried to mixture glue；
6) it polishes：It is using tool that foam surfboard surfaces, the height at edge of the semi-finished product obtained in step 5) is convex uneven Glass-fiber-fabric, fiber cloth, mixture glue polishing, be polished to it is smooth, smooth, eliminate air hole to get.
Preferably, the weight of the epoxy resin and curing agent in the mixture glue of the step 3) epoxy resin and curing agent Amount is than being 2: 1.
Preferably, the smearing thickness of the step 3) epoxy resin and the mixture glue of curing agent is：1.6-1.8 ㎏/㎡。
Preferably, the edges cover glass-fiber-fabric edge 5mm wide of the fiber cloth in the step 4).
Preferably, the mixture glue in the step 5) needs to dry 2.5-3 hours.
Compared with prior art, the beneficial effects of the present invention are：
The present invention sticks glass-fiber-fabric using asphalt mixtures modified by epoxy resin gluing, and environmental protection is pollution-free, will not be damaged to human body, this technique is adopted The lamination for carrying out clad type to expansion type surfboard with glass-fiber-fabric and fiber cloth is handled, and having for surfboard can be made higher tough Property, the surfboard produced are hardly damaged, good water-proof effect.
Specific implementation mode：
Below by embodiment, invention is further described in detail：
A kind of lamination process of foaming surfboard, includes the following steps：
1) raw material：It is 21.8 ㎏/m to select qualified semi-finished product foaming surfboard, density3, check that its size, surface are smooth Degree and corner angle radian；
2) cloth is cut：The bottom margin of selection order requirements or suitable glass-fiber-fabric, the surfboard that foams according to semi-finished product It cuts, cut size, which is subject to be more than, cuts marginal dimension 2-2.5cm, determines that each semi-finished product foaming surfboard needs glass-fiber-fabric The number of plies；
3) gluing：Using the mixture glue of epoxy resin and curing agent semi-finished product foaming surfboard surfaces uniformly smear, 1.7 ㎏/㎡ of smearing thickness, epoxy resin and curing agent weight ratio in mixture glue are 2: 1, and when gluing carries out eye and skin Protection；
4) cloth is made：The glass-fiber-fabric cut in step 2) is laid with, is coated to the semi-finished product foaming after gluing in step 3) The edge of surfboard surfaces, glass-fiber-fabric is located at semi-finished product foaming surfboard bottom surface；
Then scraping glass-fiber-fabric surface using scraper plate makes that mixture glue permeates glass-fiber-fabric completely, extra mixture glue is gone It removes, ensures glass-fiber-fabric edge unfolded when scraping mixture glue, without nose and bubble, air hole；
In the tail portion of semi-finished product foaming surfboard bottom surface, 0-65cm ranges are laid with fiber cloth bonding securely forward again, fiber cloth Edges cover glass-fiber-fabric edge 5mm wide, spontaneously dry 1.5 hours；
Finally the whole of entire semi-finished product foaming surfboard outer wall is covered in glass-fiber-fabric and fiber cloth external sheath, one layer of bonding Fiber cloth need to ensure the EDGE CONTACT of the whole fiber cloth or overlap joint, must not have gapless, brush one layer of mixture glue, do Cloth is completed；
5) dry glue is handled：The semi-finished product foaming surfboard for doing after the completion of cloth is placed in 25-28 DEG C of dustfree environment and is stood 2.2 hours to mixture glue dry；
6) it polishes：It is using tool that foam surfboard surfaces, the height at edge of the semi-finished product obtained in step 5) is convex uneven Glass-fiber-fabric, fiber cloth, mixture glue polishing, be polished to it is smooth, smooth, eliminate air hole to get.
The above is only the preferable embodiment of the present invention, and in addition to this, the present invention can also have other realization sides Formula.It should be noted that under the premise of no disengaging present inventive concept, any obvious improvements and modifications should all be fallen into Within protection scope of the present invention.

Claims (5)

1. a kind of lamination process of foaming surfboard, it is characterised in that：Include the following steps：
1) raw material：It is 21.5-22 ㎏/m to select qualified semi-finished product foaming surfboard, density3, check its size, surface flatness With corner angle radian；
2) cloth is cut：The bottom margin cutting of selection order requirements or suitable glass-fiber-fabric, the surfboard that foams according to semi-finished product, Cut size, which is subject to be more than, cuts marginal dimension 2-2.5cm, determines that each semi-finished product foaming surfboard needs the glass-fiber-fabric number of plies；
3) gluing：It is uniformly smeared in semi-finished product foaming surfboard surfaces using the mixture glue of epoxy resin and curing agent, gluing When carry out eye and skin protection；
4) cloth is made：The glass-fiber-fabric cut in step 2) is laid with, is coated to the semi-finished product foaming surfing after gluing in step 3) The edge of plate surface, glass-fiber-fabric is located at semi-finished product foaming surfboard bottom surface；
Then scraping glass-fiber-fabric surface using scraper plate makes mixture glue permeate glass-fiber-fabric, the removal of extra mixture glue completely, scrapes Ensure glass-fiber-fabric edge unfolded when pressing mixture glue, without nose and bubble, air hole；
In the tail portion of semi-finished product foaming surfboard bottom surface, 0-65cm ranges are laid with fiber cloth bonding securely forward again, the side of fiber cloth Edge covers glass-fiber-fabric edge, spontaneously dries 1.3-1.7 hours；
Finally in whole fibre of glass-fiber-fabric and fiber cloth external sheath, the entire semi-finished product foaming surfboard outer wall of one layer of covering of bonding Wei Bu need to ensure the EDGE CONTACT of the whole fiber cloth or overlap joint, must not have a gapless, brush one layer of mixture glue, it is complete to make cloth At；
5) dry glue is handled：The semi-finished product foaming surfboard for doing after the completion of cloth is placed in 25-28 DEG C of dustfree environment and is stood to mixed Close glue dries；
6) it polishes：The glass for surfboard surfaces, the convex injustice of height at edge that the semi-finished product obtained in step 5) are foamed using tool Cloth, fiber cloth, mixture glue polishing, be polished to it is smooth, smooth, eliminate air hole to get.
2. a kind of lamination process of foaming surfboard according to claim 1, it is characterised in that：
The weight ratio of epoxy resin and curing agent in the mixture glue of the step 3) epoxy resin and curing agent is 2: 1.
3. a kind of lamination process of foaming surfboard according to claim 1, it is characterised in that：
The smearing thickness of the step 3) epoxy resin and the mixture glue of curing agent is：1.6-1.8㎏/㎡.
4. a kind of lamination process of foaming surfboard according to claim 1, it is characterised in that：
The edges cover glass-fiber-fabric edge 5mm wide of fiber cloth in the step 4).
5. a kind of lamination process of foaming surfboard according to claim 1, it is characterised in that：
Mixture glue in the step 5) needs 2.5-3 hours dry.
CN201810315964.3A 2018-04-10 2018-04-10 A kind of lamination process of foaming surfboard Pending CN108466472A (en)