CN108441074A - A kind of water-repellent paint of cementitious composite packaging bag - Google Patents
A kind of water-repellent paint of cementitious composite packaging bag Download PDFInfo
- Publication number
- CN108441074A CN108441074A CN201810278187.XA CN201810278187A CN108441074A CN 108441074 A CN108441074 A CN 108441074A CN 201810278187 A CN201810278187 A CN 201810278187A CN 108441074 A CN108441074 A CN 108441074A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- packaging bag
- repellent paint
- cementitious composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of water-repellent paint of cementitious composite packaging bag is related to packaging bag processing technical field, it is characterised in that：Material including following parts by weight is made, 15 20 parts of resin, 15 parts of copper citrate, 7 13 parts of modified micaceous powder, 26 parts of phenyl glycidyl ether, 15 parts of vinyltriethoxysilane, 15 parts of isophorone diamine, 27 parts of dimethylamine propylamine, 5 10 parts of casein sodium, 28 parts of oxalic acid, 7 14 parts of starch paste, 39 parts of nano-titanium dioxide, 27 parts of maleic anhydride inoculated polypropylene, 7 12 parts of anti-aging agent, 9 14 parts of biological assistant, 30 35 parts of deionized water.The method of the present invention is reasonable, easy to operate, waterproof, pressure resistance.
Description
Technical field
The present invention relates to packaging bags to process technical field, and in particular to a kind of waterproof painting of cementitious composite packaging bag
Material.
Background technology
Cement:Powdery hydraulicity inorganic coagulation material.At slurry after adding water to stir, can harden in air or in water
Preferably hardening, and can the materials such as sand, stone are cemented together securely.
The mixture of early stage lime and volcanic ash and modern lime pozzolanic cement are much like, are made of its cementing rubble
Concrete, not only intensity is higher after hardening, and can also resist the erosion of fresh water or brackish water.For a long time, it is as one
The important cementitious material of kind, is widely used in the engineerings such as civil construction, water conservancy, national defence.
Ball-milling technology is applied to two production links in cement industry, and a link is identical as Thermal Power Generation Industry, is applied to mill
Coal dust processed provides fire coal for production；Another link is applied to be sintered blocking clinker and grind powdering, this link
The production efficiency and product quality of cement production enterprise are played a crucial role.
And packaging bag is very important for cement, because installation, transport etc. are required for packaging bag to operate, but
Be since the performance of present many packaging bags is all not particularly good, it is all non-watertight, also not wear-resisting, packaging is transported in this way
Defeated is all very big trouble, can waste a large amount of time to re-operate, and can be caused to damage to cement.
Invention content
Technical problem to be solved by the present invention lies in overcome existing technological deficiency provide a kind of method rationally, operation side
Just, waterproof, pressure resistance a kind of cementitious composite packaging bag water-repellent paint.
The technical problems to be solved by the invention are realized using technical solution below：
A kind of water-repellent paint of cementitious composite packaging bag, it is characterised in that：Material including following parts by weight is made,
15-20 parts of resin, 1-5 parts of copper citrate, powder 7-13 parts modified micaceous, 2-6 parts of phenyl glycidyl ether, vinyl
1-5 parts of triethoxysilane, 1-5 parts of isophorone diamine, 2-7 parts of dimethylamine propylamine, 5-10 parts of casein sodium, oxalic acid 2-
8 parts, it is 7-14 parts of starch paste, 3-9 parts of nano-titanium dioxide, 2-7 parts of maleic anhydride inoculated polypropylene, 7-12 parts of anti-aging agent, raw
9-14 parts of object auxiliary agent, 30-35 parts of deionized water；
The resin includes in E-12 epoxy resin, organic siliconresin, Hydroxylated acrylic resin, long oil alkyd
It is a kind of；
The anti-aging agent includes one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD, antioxidant A W；
The preparation method of the modified micaceous powder is：Mica is ground to and crossed 300-400 mesh sieve, three fourth of methyl is then added
Ketoximinosilanes are stirred 10min at normal temperatures, then heat to 80-85 DEG C of heat preservation grinding 30min, add water stirring and be made
Solid content reaches the solution of 25-35%, and gained mixed liquor is sent into dry in spray dryer, the spheric granules of obtained 20-40 mesh,
And it is dried at 100-110 DEG C；
The mass ratio of the methyl tributanoximo silane and mica powder is 1：4.1；
The biological assistant includes that the material of following parts by weight is made,
1 part of radix cynanchi atrati, 2 parts of curcuma zedoary, 3 parts of trigone, 4 parts of Cynanchum glaucescens, 5 parts of lily, 6 parts of bulbus fritillariae cirrhosae, 7 parts of radish seed, Inula britannica chinensis 1
Part, 2 parts of pappy shell, 3 parts of ginger；
Preparation method is：Above-mentioned material is placed in 90-100 DEG C of drying equipment and is tiled, is then dried 2-3 small
When, it is then placed in milling apparatus and is ground into powder；
A kind of preparation method of the water-repellent paint of cementitious composite packaging bag is,
I by resin, copper citrate, modified micaceous powder, phenyl glycidyl ether, vinyltriethoxysilane, different Fo Er
Ketone diamines, dimethylamine propylamine are placed in reaction kettle and are uniformly mixed, and are warming up to 220-260 DEG C, 1~2h of insulated and stirred is mixed
Close material stand for standby use；
II by casein sodium, oxalic acid, starch paste, nano-titanium dioxide, maleic anhydride inoculated polypropylene, anti-aging agent,
Biological assistant, deionized water are added in I, and cool to 100-120 DEG C, mix to form the preferable slurry of mobility；
III, by the preferable slurry indentation three-roller of above-mentioned mobility, is ground to grain size and is less than 20 μm, tinning.
Beneficial effects of the present invention are：The coating used can apply multilayer, and can be used in mixed way with others japanning etc., this
Nine enhanced convenience of sample, and the water resistant of product, the performance of waterproof are very good, and extra water can effectively be isolated, and ensure
The drying of cement, and the bond properties of product, wear-resisting property are very good, and the biological assistant used can not only play
The effect to neutralize a toxin, additionally it is possible to increase the toughness and pressure resistance, wear-resisting performance of product, product can be used in a variety of matrix materials
In matter, coating is with a wide range of features, and few, at low cost, the nontoxic no side reaction of material consumption, and processability is good, molding is easy.
Specific implementation mode
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention be easy to understand, below into
One step illustrates the present invention.
Embodiment 1
A kind of water-repellent paint of cementitious composite packaging bag, it is characterised in that：Material including following parts by weight is made,
15 parts of resin, 1 part of copper citrate, 7 parts of modified micaceous powder, 2 parts of phenyl glycidyl ether, vinyl triethoxyl silicon
1 part of alkane, 1 part of isophorone diamine, 2 parts of dimethylamine propylamine, 5 parts of casein sodium, 2 parts of oxalic acid, starch paste 7 part, nanometer
3 parts of titanium dioxide, 2 parts of maleic anhydride inoculated polypropylene, 7 parts of anti-aging agent, 9 parts of biological assistant, 30 parts of deionized water；
The resin includes in E-12 epoxy resin, organic siliconresin, Hydroxylated acrylic resin, long oil alkyd
It is a kind of；
The anti-aging agent includes one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD, antioxidant A W；
The preparation method of the modified micaceous powder is：Mica is ground to and crossed 300-400 mesh sieve, three fourth of methyl is then added
Ketoximinosilanes are stirred 10min at normal temperatures, then heat to 80-85 DEG C of heat preservation grinding 30min, add water stirring and be made
Solid content reaches the solution of 25-35%, and gained mixed liquor is sent into dry in spray dryer, the spheric granules of obtained 20-40 mesh,
And it is dried at 100-110 DEG C；
The mass ratio of the methyl tributanoximo silane and mica powder is 1：4.1；
The biological assistant includes that the material of following parts by weight is made,
1 part of radix cynanchi atrati, 2 parts of curcuma zedoary, 3 parts of trigone, 4 parts of Cynanchum glaucescens, 5 parts of lily, 6 parts of bulbus fritillariae cirrhosae, 7 parts of radish seed, Inula britannica chinensis 1
Part, 2 parts of pappy shell, 3 parts of ginger；
Preparation method is：Above-mentioned material is placed in 90-100 DEG C of drying equipment and is tiled, is then dried 2-3 small
When, it is then placed in milling apparatus and is ground into powder；
A kind of preparation method of the water-repellent paint of cementitious composite packaging bag is,
I by resin, copper citrate, modified micaceous powder, phenyl glycidyl ether, vinyltriethoxysilane, different Fo Er
Ketone diamines, dimethylamine propylamine are placed in reaction kettle and are uniformly mixed, and are warming up to 220-260 DEG C, 1~2h of insulated and stirred is mixed
Close material stand for standby use；
II by casein sodium, oxalic acid, starch paste, nano-titanium dioxide, maleic anhydride inoculated polypropylene, anti-aging agent,
Biological assistant, deionized water are added in I, and cool to 100-120 DEG C, mix to form the preferable slurry of mobility；
III, by the preferable slurry indentation three-roller of above-mentioned mobility, is ground to grain size and is less than 20 μm, tinning.
Embodiment 2
A kind of water-repellent paint of cementitious composite packaging bag, it is characterised in that：Material including following parts by weight is made,
20 parts of resin, 5 parts of copper citrate, 13 parts of modified micaceous powder, 6 parts of phenyl glycidyl ether, vinyl triethoxyl
5 parts of silane, 5 parts of isophorone diamine, 7 parts of dimethylamine propylamine, 10 parts of casein sodium, 8 parts of oxalic acid, 14 parts of starch paste,
9 parts of nano-titanium dioxide, 7 parts of maleic anhydride inoculated polypropylene, 12 parts of anti-aging agent, 14 parts of biological assistant, 35 parts of deionized water；
The resin includes in E-12 epoxy resin, organic siliconresin, Hydroxylated acrylic resin, long oil alkyd
It is a kind of；
The anti-aging agent includes one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD, antioxidant A W；
The preparation method of the modified micaceous powder is：Mica is ground to and crossed 300-400 mesh sieve, three fourth of methyl is then added
Ketoximinosilanes are stirred 10min at normal temperatures, then heat to 80-85 DEG C of heat preservation grinding 30min, add water stirring and be made
Solid content reaches the solution of 25-35%, and gained mixed liquor is sent into dry in spray dryer, the spheric granules of obtained 20-40 mesh,
And it is dried at 100-110 DEG C；
The mass ratio of the methyl tributanoximo silane and mica powder is 1：4.1；
The biological assistant includes that the material of following parts by weight is made,
1 part of radix cynanchi atrati, 2 parts of curcuma zedoary, 3 parts of trigone, 4 parts of Cynanchum glaucescens, 5 parts of lily, 6 parts of bulbus fritillariae cirrhosae, 7 parts of radish seed, Inula britannica chinensis 1
Part, 2 parts of pappy shell, 3 parts of ginger；
Preparation method is：Above-mentioned material is placed in 90-100 DEG C of drying equipment and is tiled, is then dried 2-3 small
When, it is then placed in milling apparatus and is ground into powder；
A kind of preparation method of the water-repellent paint of cementitious composite packaging bag is,
I by resin, copper citrate, modified micaceous powder, phenyl glycidyl ether, vinyltriethoxysilane, different Fo Er
Ketone diamines, dimethylamine propylamine are placed in reaction kettle and are uniformly mixed, and are warming up to 220-260 DEG C, 1~2h of insulated and stirred is mixed
Close material stand for standby use；
II by casein sodium, oxalic acid, starch paste, nano-titanium dioxide, maleic anhydride inoculated polypropylene, anti-aging agent,
Biological assistant, deionized water are added in I, and cool to 100-120 DEG C, mix to form the preferable slurry of mobility；
III, by the preferable slurry indentation three-roller of above-mentioned mobility, is ground to grain size and is less than 20 μm, tinning.
Embodiment 3
A kind of water-repellent paint of cementitious composite packaging bag, it is characterised in that：Material including following parts by weight is made,
18 parts of resin, 3 parts of copper citrate, 10 parts of modified micaceous powder, 5 parts of phenyl glycidyl ether, vinyl triethoxyl
3 parts of silane, 5 parts of dimethylamine propylamine, 8 parts of casein sodium, 5 parts of oxalic acid, 11 parts of starch paste, is received 4 parts of isophorone diamine
7 parts of titanium dioxide of rice, 5 parts of maleic anhydride inoculated polypropylene, 9 parts of anti-aging agent, 12 parts of biological assistant, 33 parts of deionized water；
The resin includes in E-12 epoxy resin, organic siliconresin, Hydroxylated acrylic resin, long oil alkyd
It is a kind of；
The anti-aging agent includes one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD, antioxidant A W；
The preparation method of the modified micaceous powder is：Mica is ground to and crossed 300-400 mesh sieve, three fourth of methyl is then added
Ketoximinosilanes are stirred 10min at normal temperatures, then heat to 80-85 DEG C of heat preservation grinding 30min, add water stirring and be made
Solid content reaches the solution of 25-35%, and gained mixed liquor is sent into dry in spray dryer, the spheric granules of obtained 20-40 mesh,
And it is dried at 100-110 DEG C；
The mass ratio of the methyl tributanoximo silane and mica powder is 1：4.1；
The biological assistant includes that the material of following parts by weight is made,
1 part of radix cynanchi atrati, 2 parts of curcuma zedoary, 3 parts of trigone, 4 parts of Cynanchum glaucescens, 5 parts of lily, 6 parts of bulbus fritillariae cirrhosae, 7 parts of radish seed, Inula britannica chinensis 1
Part, 2 parts of pappy shell, 3 parts of ginger；
Preparation method is：Above-mentioned material is placed in 90-100 DEG C of drying equipment and is tiled, is then dried 2-3 small
When, it is then placed in milling apparatus and is ground into powder；
A kind of preparation method of the water-repellent paint of cementitious composite packaging bag is,
I by resin, copper citrate, modified micaceous powder, phenyl glycidyl ether, vinyltriethoxysilane, different Fo Er
Ketone diamines, dimethylamine propylamine are placed in reaction kettle and are uniformly mixed, and are warming up to 220-260 DEG C, 1~2h of insulated and stirred is mixed
Close material stand for standby use；
II by casein sodium, oxalic acid, starch paste, nano-titanium dioxide, maleic anhydride inoculated polypropylene, anti-aging agent,
Biological assistant, deionized water are added in I, and cool to 100-120 DEG C, mix to form the preferable slurry of mobility；
III, by the preferable slurry indentation three-roller of above-mentioned mobility, is ground to grain size and is less than 20 μm, tinning.
Comparative example
A kind of water-repellent paint of packaging bag, including：18 parts of polyvinyl resin, 10 parts of mica powder, phenyl glycidyl ether 5
Part, 5 parts of dimethylamine propylamine, 8 parts of casein sodium, 5 parts of oxalic acid, 33 parts of water；
Preparation method：Above-mentioned material is put into reaction kettle, 40-50 points are stirred in 110-120 DEG C of temperature
Clock is then pressed into three-roller, is ground into powder.
By experiment, the performance and effect of 1-3 of the embodiment of the present invention and comparative example, such as following table are measured：
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of water-repellent paint of cementitious composite packaging bag, it is characterised in that：Material including following parts by weight is made,
15-20 parts of resin, 1-5 parts of copper citrate, powder 7-13 parts modified micaceous, 2-6 parts of phenyl glycidyl ether, three second of vinyl
1-5 parts of oxysilane, 1-5 parts of isophorone diamine, 2-7 parts of dimethylamine propylamine, 5-10 parts of casein sodium, 2-8 parts of oxalic acid,
7-14 parts of starch paste, 3-9 parts of nano-titanium dioxide, 2-7 parts of maleic anhydride inoculated polypropylene, 7-12 parts of anti-aging agent, biology help
9-14 parts of agent, 30-35 parts of deionized water.
2. a kind of water-repellent paint of cementitious composite packaging bag according to claim 1, it is characterised in that：A kind of water
The preparation method of the water-repellent paint of mud combined package bag is,
I by resin, copper citrate, modified micaceous powder, phenyl glycidyl ether, vinyltriethoxysilane, isophorone two
Amine, dimethylamine propylamine are placed in reaction kettle and are uniformly mixed, and are warming up to 220-260 DEG C, 1~2h of insulated and stirred obtains mixture
Stand for standby use；
II by casein sodium, oxalic acid, starch paste, nano-titanium dioxide, maleic anhydride inoculated polypropylene, anti-aging agent, biology
Auxiliary agent, deionized water are added in I, and cool to 100-120 DEG C, mix to form the preferable slurry of mobility；
III, by the preferable slurry indentation three-roller of above-mentioned mobility, is ground to grain size and is less than 20 μm, tinning.