CN1084147A - 高效能新型混凝土防冻剂 - Google Patents
高效能新型混凝土防冻剂 Download PDFInfo
- Publication number
- CN1084147A CN1084147A CN 92110542 CN92110542A CN1084147A CN 1084147 A CN1084147 A CN 1084147A CN 92110542 CN92110542 CN 92110542 CN 92110542 A CN92110542 A CN 92110542A CN 1084147 A CN1084147 A CN 1084147A
- Authority
- CN
- China
- Prior art keywords
- sodium
- component
- volume
- chlor
- concrete antifreezer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种掺量少、适用范围大,配方合理
的新型高效能混凝土防冻剂,该防冻剂具有副作用
小,使用方便,价格低廉的优点。
Description
本发明属于化学建筑材料技术领域。
九十年代混凝土防冻剂发展到以复合配方为主,单一组份为副的局面。世界范围内的此类产品都是由防冻组份、早强组份、减水组份、引气组份、催化组份、阻锈组份、载体组份等组成,有二元配方,三元配方及多元配方。
这些防冻剂存在以下问题:(1)药效低、掺量大、波动掺量、适用范围小,掺入量占水泥重量的5-15%,给运输、使用等带来诸多不便;(2)负作用大,引起钢筋锈蚀、强度严重损失、影响混凝土耐久性等,降低混凝土的使用功能;(3)价格高,材料机理认识不足,材料配方不够合理,没有充分发挥各组分的各已所长,没有充分地利用起各组分间的干涉、叠加、产生共济的潜在效能,从而引起材料的浪费。
本发明的目的就是研制一种高效能低掺量、负作用小,使用方便的新型防冻剂。
为达到上述目的,本发明采用下列措施,先对早强组份、引气组份等单项材料进行专题试验发现诸多种早强剂中硫酸钠的早强效果最好,负作用最少,而且它的最佳掺量范围是占水泥重量的1.2-1.5%;发现氯化钠在诸多防冻组份中防冻效果最佳,价格最低,货源最广,掺量也较低,但它严重引起钢筋锈蚀。为了充分的利用氯化钠,在诸多的阻锈组份中选择了阻锈效果显著的亚硝酸钠,另外它具有显著的降低冰点性能,但它货源缺、价格昂贵。通过大量试验把氯化钠和亚硝酸钠合理的匹配,充分发挥各自的长处,达到扬长避短的效能。并确定出氯化钠和亚硝酸钠的最佳搭配比例,及各自的最佳掺量,即氯化钠占水泥重量0.6-1.3%,亚硝酸钠占水泥重量0.9-1.5%。从多种引气剂、减水剂中选择了木质素磺酸钙和萘系高效减水剂的复合剂,通过对比试验,市场调查发现木质素磺酸钙价格低、既减水、又引气,但它缓凝对冬施不利,通过二者复合,利用发挥各自所长,解决了减水、引气、不缓凝、不降低后期强度、经济等问题。确定出木质素磺酸钙的掺量占水泥重量0.15-0.210%,萘系高效减水剂的掺量占水泥重量0.3-0.7%。后对各组份进行复合试验,以“以掺量、技术性能、经济、负作用”四参量通过大量试验得到最佳配方。其配比按重量计为:
硫酸钠1.2-1.5%
氯化钠0.6-1.3%
亚硝酸钠0.9-1.5%
木质磺酸钙0.15-0.210%
萘系高效减水剂0.3-0.7%
即先进行各组份的优选,确定一下各组份的最佳品种、最佳掺量,弄清各组份的单体材性。后进行各最佳组份的配合比较,达到最佳优化组合。
本发明防冻剂用于低温-10℃混凝土,占水泥重量3.5%,用于最低温度-15℃混凝土,占水泥重量4.5%。
Claims (2)
1、一种混凝土防冻剂,由硫酸钠,氯化钠,亚硝酸钠,木质磺酸钙和萘系高效减水剂组成,其特征在于,所述的防冻剂成分配比按重量计为:
硫酸钠 1.2-1.5%
氯化钠 0.6-1.3%
亚硝酸钠 0.9-1.5%
木质磺酸钙 0.15-0.210%
萘系高效减水剂 0.3-0.7%
2、根据权利要求1所述的防冻剂,其特征在于,掺量为水泥重量3.5%,适用于低温-10℃,掺量为水泥重量4.5%,适用于-15℃。