CN108412113A - A kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction and application - Google Patents
A kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction and application Download PDFInfo
- Publication number
- CN108412113A CN108412113A CN201810392677.2A CN201810392677A CN108412113A CN 108412113 A CN108412113 A CN 108412113A CN 201810392677 A CN201810392677 A CN 201810392677A CN 108412113 A CN108412113 A CN 108412113A
- Authority
- CN
- China
- Prior art keywords
- wall
- gauge cold
- light gauge
- screed
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction, by including that light gauge cold-formed steel shape, steel wire, wall spray are built screed, polymer waterproof anti-crack mortar and anti-corrosion net and formed；The light gauge cold-formed steel shape is fixed by Structural Design Requirement arrangement；The steel wire is mounted on the outside or both sides of cold formed steel structure；The steel wire can be embedded in as needed do not install steel wire side wall spray build in mortar layer Mian Ceng；The wall spray builds screed using layering sprayed construction mode, and the gap of light gauge cold-formed steel shape and steel plate silk screen is tamped, wrap up, is covered and is levelling, forms unified wall spray and builds screed material face layer；The polymer waterproof anti-crack mortar batch scrapes wall spray on the outside and builds on screed and be implanted into anti-corrosion net, forms fish tail and waterproof layer and cracking resistance layer.The light gauge cold-formed steel shape composite gypsum light mortar outer wall body constructs, and systematic entirety can be good, and wall is enriched without hollowing, perfectly solves light steel house " cavity wall " and " metope cracking " two is big " pain spot ".
Description
Technical field
The present invention relates to light gauge cold-formed steel shape building construction technology field, specially a kind of light gauge cold-formed steel shape composite gypsum
Light mortar outer wall body constructs and application.
Background technology
One, the wall structure Shortcomings of modern low layer light gauge cold-formed steel shape building
The wall of modern low layer light gauge cold-formed steel shape building is by light gauge cold-formed steel shape skeleton, wall body structure panel
(cement plate, plasterboard, calcium silicate board with microporous and OSB plates etc.), lumen loading fireproof heat insulating cotton or hard polyurethane foam etc. pass through screw
Connect the complex being composed.
This wall has compared to traditional architecture blockwork in construction, transport, antidetonation, energy saving etc. prodigious excellent
Gesture, but also have many deficiencies, it shows as：
1, it is substantially hollow structure among light gauge cold-formed steel shape retaining wall, it is easy to form " eardrum " effect, hit
Soundproof effect is very poor, and " cavity wall " structural form of formed steel construction retaining wall both sides covering plank allows and gets used to " Qin Zhuanhan
Watt " Chinese of solid wall are beyond affordability.
2, exterior wall plate stitch leads to external wall seepage, paint film bubbling and other issues, influences to decorate because of the easy cracking of difference variation
And using effect.
3, fireproof heat insulating cotton quality differs, and second-rate fireproof heat insulating cotton will disperse out to swim in air for a long time
Tiny, naked eyes almost invisible fiber, after being sucked by human body, gradually deposits and gives rise to diseases in lung；And hard is sent out
Polyurethane fireproof poor performance is steeped, it is sustainable to volatilize harmful substance.
Two, industry by-product gypsum especially ardealite utilization rate is low
The year yield of China's industry by-product gypsum is about 1.84 hundred million tons, wherein newly-increased 70,000,000 tons of ardealite every year；Phosphorus
It is more than 300,000,000 that gypsum, which adds up volume of cargo in storage, and for utilization rate less than 20%, the overwhelming majority is taken as waste to abandon.
Phosphogypsum slag stockpiling occupies a large amount of soils；Its acidity contained and other harmful substances are easy to make surrounding enviroment
At pollution, runed counter to the fundamental state policy of China's environmental protection！If not increasing using disposition, by the hair of extreme influence phosphate fertilizer industry
Exhibition.
Currently, the industry by-product gypsums such as ardealite, are mainly used in cement retarder, Thistle board and gypsum hollow and build
Block, consumption tend to be saturated, it is therefore necessary to extend other application direction.
Invention content
In view of the deficiencies of the prior art, the present invention provides a kind of light gauge cold-formed steel shape composite gypsum light mortar exterior wall walls
Body constructs, and solves the problems mentioned above in the background art.
In order to achieve the above object, the present invention is achieved by the following technical programs：A kind of light gauge cold-formed steel shape composite stone
Cream light mortar outer wall body construct, by include light gauge cold-formed steel shape, steel wire, wall spray build screed, polymer waterproof resists
Split mortar and anti-corrosion net composition；The light gauge cold-formed steel shape is fixed by Structural Design Requirement arrangement；The steel wire is mounted on cold
The outside or both sides of curved thin-walled steel structure；The steel wire can be embedded in the wall spray for not installing steel wire side as needed
It builds in mortar layer Mian Ceng；The wall spray builds screed using layering sprayed construction mode, by light gauge cold-formed steel shape and steel plate silk
The gap of net is tamped, wraps up, is covered and levelling, forms unified wall spray and builds screed material face layer；The polymer waterproof is anti-
It splits mortar and batch scrapes wall spray on the outside and build on screed and be implanted into anti-corrosion net, form fish tail and waterproof layer and cracking resistance layer.
Screen cloth replacement also can be used in the steel wire, and steel wire includes：Fiberglass gridding cloth (common, middle alkali or resistance to
Alkali), gauze etc..
Light gauge cold-formed steel shape is a kind of flexible building system, and this programme is solid by outside steel fabric sheet and light gauge cold-formed steel shape
It is fixed, under the premise of not changing flexible structural system, improve anti-seismic performance and exterior wall anti-cracking performance；Screed is built in wall spray
It is injected in inside wall and is higher by shaped steel, the gap of light gauge cold-formed steel shape and steel wire can be tamped, wrapped up, covered and is levelling,
It forms unified wall spray and builds screed material face layer, the flexibility characteristics of screed are built using wall spray prevents metope cracking, hollowing
Phenomenon generates；Using polymer waterproof anti-crack mortar on the outside of exterior wall and additionally arranging alkaline-resisting steel wire protects spray to build mortar from rainwater leaching
Outside wall anti-cracking performance is attacked and improved, surface brick adherence or coating application can be directly carried out.
The above way is easy to operate, quick construction, cheap, disposably solves cracking resistance, waterproof, energy saving, construction etc. and asks
Topic.Ensure that the fire endurance of light gauge cold-formed steel shape exterior wall sound insulation cracking resistance wall body structure is more than 3 hours, heat transfer coefficient is less than 1.6w/
(m2.k)。
As present invention further optimization scheme, sequence of construction is characterized in that：Light gauge cold-formed steel shape → installation is installed
Have steel wire on the outside of light gauge cold-formed steel shape → from inside to outside layering injection wall spray build screed → installation hot-galvanized steel silk screen
On the inside of light gauge cold-formed steel shape → inside and outside side wall floating screed and be higher by shaped steel → interior lateral surface injection wall spray and build screed and scrape
It is scraped on the outside of flat → exterior wall and smears polymer waterproof anti-crack mortar 3-5mm and be embedded to alkali-resistant glass fiber mesh.
As present invention further optimization scheme, the light gauge cold-formed steel shape be c-type aluminum-zinc alloy steel, width 89mm,
Spacing is calculated according to structural requirement.
As present invention further optimization scheme, described have a steel wire, specification 4.5*15*0.6mm, need to be through anti-corrosion at
Reason；The hot-galvanized steel silk screen, mesh aperture 10*10*0.6mm.
As present invention further optimization scheme, the wall spray builds screed for wall whole, technical indicator
For：
| Project name | Dry density | Compression strength | Thermal coefficient | Burning behavior class |
| Unit | kg/m3 | Mpa | [w/(m.K)] | |
| Technical indicator | ≤900 | ≥3.5 | ≤0.20 | A |
As present invention further optimization scheme, the steel wire is coating medium-alkali glass fibre grid cloth, technology
Index is：
As present invention further optimization scheme, the polymer waterproof anti-crack mortar batch is scraped using trowel on wall,
Then it is laid with after alkaline-resisting steel wire and alkaline-resisting steel wire is pressed into mortar and is struck off with spatula, form fish tail and waterproof layer and resist and open
Parting, technical indicator are：
| Project name | Water penetration | Compression strength | Backfin ratio | Tensile bond strength | Immersion post-tensioning adhesion strength |
| Unit | ml | Mpa | - | Map | Map |
| Technical indicator | ≤2.5 | ≥20.0 | ≤3.0 | ≥0.70 | ≥0.50 |
As present invention further optimization scheme, the anti-corrosion net is alkali-proof glass fiber mesh, technical indicator
For：
As present invention further optimization scheme, screed is built in the wall spray should be layered injection, and thickness is not more than
50mm, wall spray, which is built, could carry out other surface material constructions after screed wall should be completely dried.
Advantageous effect
The present invention provides a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body constructions, have following beneficial
Effect：
Light gauge cold-formed steel shape exterior wall sound insulation cracking resistance wall structure, the wall with existing low layer light gauge cold-formed steel shape building
Body is anti-by light gauge cold-formed steel shape skeleton, wall body structure panel (cement plate, plasterboard, calcium silicate board with microporous and OSB plates etc.), lumen loading
Thermal insulation materials such as fiery heat-preservation cotton or hard polyurethane foam etc. are connected by screw the compound body technique being composed and compare, this hair
Bright advantageous effect is：A kind of light gauge cold-formed steel shape exterior wall sound insulation cracking resistance wall structure of the present invention, systematic entirety can good, wall
It enriches without hollowing, perfectly solves light steel house " cavity wall " and " metope cracking " two is big " pain spot ".
1, become " cavity wall " as " solid wall ", structural form allows the Chinese for getting used to " Qin brick and Han tile " solid wall to be more easy to
Receive, while solving the problems, such as that existing construction safety is poor, sound insulation is poor, oise insulation factor is more than 45dB.
2, cracking resistance and water seepage preventing structure solve prior art exterior wall plate stitch because difference variation is easy cracking, lead to exterior wall
The housing qualities problems such as infiltration, paint film bubbling.
3, fire-proof function is more preferable, and the thin wall shaped steel of clod wash builds screed for wall spray and is filled up completely and wraps up, and fire resistance period can
Up to 3h or more, wall fire protecting performance is made to greatly improve.
4, energy-saving effect is more preferable, and 120 thickness of screed is built in single wall spray can make wall heat transfer coefficient be less than 1.50, can expire
The energy-saving design requirement in the mild area of foot, hot summer and warm winter zone；If middle layer is filled using gypsum insulation mortar, same 120 thickness
Wall heat transfer coefficient is less than 1.00, can meet the cold energy-saving design requirements of Xia Redong.
5, batch production is prefabricated, site machineryization construction, and speed of application quickness and high efficiency, employment are few, scene civilization clean hygiene.
The material that wall structure of the present invention is related to, be entirely prefabricated in the factory it is uniformly mixed it is packed transport scene to, sprayed using special equipment
It builds, when construction only needs to connect electricity, water receiving enters machine, implements dry operation, meets " the assembly producing building " that country advocates
Industrial policy.
6, it is industrial solid waste residue-ardealite or other by-product gypsums that it is raw materials used, which to build screed, for wall of the present invention spray, can
The waste residue that the annual newly-increased waste residue of consumption and consumption were stacked originally completely, turns waste into wealth, solves the by-product gypsums such as phosphate fertilizer plant enterprise at one stroke
Industry produces environmental protection pressure and local government's environmental protection pressure problem.
Description of the drawings
Fig. 1 is the overall structure diagram of the present invention；
Fig. 2 is the side view of the present invention.
In figure：Screed, 4- polymer waterproof anti-crack mortars, 5- are built in 1- light gauge cold-formed steel shapes, 2- steel wires, the spray of 3- walls
Anti-corrosion net.
Specific implementation mode
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation describes, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Please refer to Fig.1-2, the present invention provides a kind of technical solution 1：A kind of light gauge cold-formed steel shape composite gypsum light mortar
Outer wall body constructs, thickness of wall body 125mm, and wall heat transfer coefficient is 1.43 [W/m2.K], by including light gauge cold-formed steel shape 1, having
Screed 3, polymer waterproof anti-crack mortar 4, anti-corrosion net 5 are built in steel wire 2, wall spray；It is described to have steel wire 2 thin mounted on clod wash
The outside of 1 structure of wall-shaped steel；The wall spray builds screed 3 using layering sprayed construction mode, by light gauge cold-formed steel shape 1 and steel
The gap of silk screen 2 is tamped, wraps up, is covered and levelling, forms unified materials for wall, and mortar layer thickness is 120mm and high on the outside
Go out light gauge cold-formed steel shape 20mm, inside is higher by light gauge cold-formed steel shape 10mm；The anti-corrosion net 5 is implanted in wall spray and builds mortar level
On 3 layers；The waterproof polymer mortar 4 batches scrapes wall spray on the outside and builds 3 layers of screed above and be implanted into the floating of anti-corrosion net 5, is formed
5mm thickness fish tail and waterproof layer and cracking resistance layer.
Its sequence of construction is characterized in that：Installation light gauge cold-formed steel shape → be equipped on the outside of light gauge cold-formed steel shape steel wire →
Two layers of injection wall spray is divided to build screed → inside and outside side wall floating screed and be higher by shaped steel (outside 20mm, inside 10mm) from inside to outside
→ interior outside spray respectively wall spray build screed and strike off (implantation coating medium-alkali glass fibre grid cloth when inside strikes off) →
Outside, which is scraped, smears polymer waterproof anti-crack mortar 5mm and is implanted into alkali-resistant glass fiber mesh.
The light gauge cold-formed steel shape is zinc-plated C-type steel, and width 89mm erects spacing 600mm, horizontal spacing 1000mm.
Described to have steel wire, specification 4.5*15*0.6mm need to be through preservative treatment.
Mortar layer thickness 120mm is built in the wall spray and outside is higher by shaped steel 20mm, inside is higher by shaped steel 10mm, wall spray
It builds screed and sprays in four times and build, technical indicator is：
| Project name | Dry density | Compression strength | Thermal coefficient | Burning behavior class |
| Unit | kg/m3 | Mpa | [w/(m.K)] | |
| Technical indicator | ≤900 | ≥3.5 | ≤0.20 | A |
The polymer waterproof anti-crack mortar batch is scraped using 10mm trowels on wall, then with spatula by alkaline-resisting steel wire pressure
Enter in mortar and strike off, the fish tail and waterproof layer and cracking resistance layer, technical indicator for forming 5mm are：
| Project name | Water penetration | Compression strength | Backfin ratio | Tensile bond strength | Immersion post-tensioning adhesion strength |
| Unit | ml | Mpa | - | Map | Map |
| Technical indicator | ≤2.5 | ≥20.0 | ≤3.0 | ≥0.70 | ≥0.50 |
The alkaline-resisting steel wire is layed in polymer waterproof anti-crack mortar layer, and technical indicator is：
The polymer waterproof anti-crack mortar and inside surface material must could construct after the drying of wall mortar, with true
Materials for wall reaches strength grade to guarantor, wall moisture fully escapes.
Please refer to Fig.1-2, the present invention provides a kind of technical solution 2：A kind of light gauge cold-formed steel shape composite gypsum light mortar
Outer wall body constructs, thickness of wall body 143mm, and wall heat transfer coefficient is 1.22 [W/m2.K], by including light gauge cold-formed steel shape, having steel
Screed, waterproof polymer mortar and alkaline-resisting steel wire are built in silk screen, hot-galvanized steel silk screen, wall spray；It is described to have steel wire installation
In the outside of cold formed steel structure；The hot-galvanized steel silk screen is mounted on the inside of cold formed steel structure；The wall
Body spray is built screed and is injected on wall, and light gauge cold-formed steel shape, steel wire are tamped, wrap up, covered and is levelling, forms unified wall
Body material, mortar layer thickness is higher by light gauge cold-formed steel shape 30mm on the outside of outer wall, inside is higher by light gauge cold-formed steel shape 20mm；It is described
Polymer waterproof anti-crack mortar batch scrapes wall spray on the outside and builds on screed and be implanted into alkaline-resisting steel wire floating, and it is anti-to form 3mm thickness
Water conservation layer and cracking resistance layer.
Its sequence of construction is characterized in that：Installation light gauge cold-formed steel shape → be equipped with steel wire on the outside of light gauge cold-formed steel shape →
Divide from inside to outside the spray of two layers injection wall build screed → installation hot-galvanized steel silk screen on the inside of light gauge cold-formed steel shape → interior outside
Metope screed and be higher by shaped steel (outside 30mm, inside 20mm) → interior outside spray respectively wall spray build screed and strike off → it is outer
Side, which is scraped, smears polymer waterproof anti-crack mortar 3mm and is embedded to alkali-resistant glass fiber mesh.
The light gauge cold-formed steel shape is aluminum-zinc alloy C-type steel, and width 89mm erects spacing 600mm, horizontal spacing 1000mm.
It is described to have steel wire specification for 4.5*15*0.6mm；Hot-galvanized steel silk screen mesh hole diameter 10*10*0.6mm.
Mortar layer thickness 140mm is built in the wall spray, and technical indicator is：
| Project name | Dry density | Compression strength | Thermal coefficient | Burning behavior class |
| Unit | kg/m3 | Mpa | [w/(m.K)] | |
| Technical indicator | ≤900 | ≥3.5 | ≤0.20 | A |
The polymer waterproof anti-crack mortar flattens after being scraped with 6mm serrated knives batch, forms the water-proof crack-resistant layer of thickness 3mm,
Technical indicator is：
| Project name | Water penetration | Compression strength | Backfin ratio | Tensile bond strength | Immersion post-tensioning adhesion strength |
| Unit | ml | Mpa | - | Map | Map |
| Technical indicator | ≤2.5 | ≥20.0 | ≤3.0 | ≥0.70 | ≥0.50 |
The alkaline-resisting steel wire is layed in polymer waterproof anti-crack mortar layer, and technical indicator is：
The polymer waterproof anti-crack mortar and inside surface material must could construct after the drying of wall mortar, with true
Materials for wall reaches strength grade to guarantor, wall moisture fully escapes.
Screen cloth replacement also can be used in the steel wire, and the screen cloth includes：Fiberglass gridding cloth (common, middle alkali or resistance to
Alkali), gauze, steel wire.
It should be noted that herein, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also include other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (9)
1. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction, by include light gauge cold-formed steel shape, steel wire,
Screed, polymer waterproof anti-crack mortar and anti-corrosion net composition are built in wall spray；The light gauge cold-formed steel shape presses Structural Design Requirement
Arrangement is fixed；The steel wire is mounted on the outside or both sides of cold formed steel structure；The steel wire can bury as needed
It sprays and is built in mortar layer Mian Ceng set on the wall for not installing steel wire side；The wall spray builds screed using layering sprayed construction
The gap of light gauge cold-formed steel shape and steel plate silk screen is tamped, wrapped up, covered and is levelling by mode, forms unified wall spray and builds mortar
Layer material face layer；The polymer waterproof anti-crack mortar batch scrapes wall spray on the outside and builds on screed and be implanted into anti-corrosion net, is formed
Fish tail and waterproof layer and cracking resistance layer.
2. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction according to claims, construction
Ordinal characteristics are：Light gauge cold-formed steel shape → installation steel wire is installed on the outside of light gauge cold-formed steel shape or wall is sprayed in both sides → layering
Body spray, which builds screed → inside and outside side wall floating screed and is higher by the injection wall spray of shaped steel → outside and builds, screed and strikes off → interior side spray
Penetrate wall spray build screed and strike off → outside scrapes and smears polymer waterproof anti-crack mortar 3-5mm and be embedded to anti-corrosion net.
3. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction according to claim 1, feature
It is：The light gauge cold-formed steel shape refers to the finished steel with steel plate or the strip bending various section configurations under cold state,
Shaped steel need to be set through preservative treatment, size according to structural requirement.
4. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction according to claim 1, feature
It is：The steel wire is to use mild steel wire, bullet wire, high-carbon steel wire, the braiding of the materials such as stainless steel wire or welding networking
The general name of shape material, including expanded metal lath (seine), steel wire (mesh grid) and welded mesh, steel wire need to be through preservative treatment, sizes
It is designed according to structural requirement.
5. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction according to claims, feature
It is：It is by industry by-product gypsums such as ardealites as cementitious material, glass bead (or pearl that screed is built in wall spray
Rock) it is used as aglite, compound a variety of additives to be mixed into single component in factory according to a certain ratio, transport scene to after packed,
Spray is carried out using special equipment and builds construction, scene only needs water source, power supply being communicated to equipment interface, and screed is built in wall spray and is fallen
Enter equipment feed inlet and can spray to build, live neat and tidy without take material, without rubbish, meet fabricated construction requirement；
Described spray builds the technical indicator of mortar and is：
6. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction according to claim 1, feature
It is：The polymer waterproof anti-crack mortar is existed in proportion by cement, quartz sand, waterproofing agent, polymer and a variety of additives
Factory's mixture manufacturing transports scene to and adds water to stir into slurry by ratio of mud requirement at single component, with serrated knife batch scrape on wall i.e.
After being implanted into anti-corrosion net, anti-corrosion net is pressed into mortar and is struck off with spatula, fish tail and waterproof layer is formed and cracking resistance layer, technology refers to
It is designated as：
7. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction according to claim 1, feature
It is：The anti-corrosion net includes：Coat medium-alkali glass fibre grid cloth, alkali-proof glass fiber mesh, galvanizing electrowelding net.
8. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction according to claim 1, feature
It is：Screed is built in the wall spray should be layered injection, and thickness is not more than 50mm；Wall spray is built after screed wall is completely dried
It could carry out surface material construction.
9. a kind of light gauge cold-formed steel shape composite gypsum light mortar outer wall body construction according to claim 1, feature
It is：Screen cloth replacement also can be used in the steel wire.