CN108411537A - The manufacturing method of high-elasticity pressure socks - Google Patents
The manufacturing method of high-elasticity pressure socks Download PDFInfo
- Publication number
- CN108411537A CN108411537A CN201810342058.2A CN201810342058A CN108411537A CN 108411537 A CN108411537 A CN 108411537A CN 201810342058 A CN201810342058 A CN 201810342058A CN 108411537 A CN108411537 A CN 108411537A
- Authority
- CN
- China
- Prior art keywords
- decatize
- warming
- manufacturing
- temperature
- socks
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the manufacturing method of high-elasticity pressure socks, successively by weaving, cutting out, piece, decatize, dyeing, setting；Decatize is first carried out before dyeing, and the good product of piece is put into the steaming box of band vacuum extractor, it is evacuated down to certain negative pressure, 80 DEG C is warming up to the rate of 2 DEG C/min, keeps the temperature 10min, it vacuumizes again, decatize, is warming up to 95 105 DEG C, 20min is kept the temperature, then exhaust decompression, product is taken out after cooling, it is put into dye vat, 95 98 DEG C is warming up to the rate of 1 DEG C/min, keeps the temperature 50min, 60 DEG C are cooled to again, drain；The present invention has the characteristics that elastomeric using polyamide fibre and spandex, is carried out shaping using steam method, is then dyed again, changes the internal stress of product, and when wearing, socks recycle naturally, but wears simultaneously comfortable, achievees the effect that thin leg.
Description
Technical field
The present invention relates to the manufactures of a kind of manufacturing method of socks more particularly to the high-elasticity pressure socks of polyamide fibre and spandex
Method.
Background technology
Socks are a kind of haberdasheries being through on foot, play a part of protecting foot and beautify foot.Modern socks are in addition to right
Foot plays outside warming and protective effect, is more a kind of decoration, a kind of fashion.The advantages of polyamide fibre：Wearability, moisture absorption
Property, elastic force it is very good, it is yielding under small external force, the disadvantage is that yielding under small external force, therefore the easy crumple during wearing of its fabric
Folding；Its heat resistance and light resistance inequality.Spandex also known as polyurethanes fiber, because it is with excellent elastic force, it is also known as elasticity
Fiber has obtained a large amount of application on garment fabric, has the characteristics that elasticity is high.
Invention content
The present invention utilizes the characteristic of polyamide fibre and spandex, in conjunction with the market demand, manufactures a kind of socks of high-elasticity pressure, can be right
Leg generates pressure, and dress is comfortable, does not have constraint sense, generates the effect of thin leg, the technical solution adopted in the present invention is such as
Under：
The manufacturing method of high-elasticity pressure socks, it is raw material to select polyamide fibre and spandex, successively by weaving, cutting out, piece, vapour
It steams, dyeing, shape；Decatize is first carried out before dyeing, by the good product of piece, is put into the steaming box of band vacuum extractor
In, it is evacuated down to certain negative pressure, 80 DEG C is warming up to the rate of 2 DEG C/min, keeps the temperature 10min, vacuumize again, decatize, rise
Temperature arrives 95-105 DEG C, keeps the temperature 20min, then exhaust decompression, takes out product after cooling, dye vat is put into, with the rate liter of 1 DEG C/min
Temperature keeps the temperature 50min, then cool to 60 DEG C, drain to 95-98 DEG C.
It is evacuated down to certain negative pressure, negative pressure value 20kPa.
When decatize, bath raio 1:15-1:20, wetting softener dosage is 1%-3%.
It is raw material that the present invention, which selects polyamide fibre and spandex, and decatize is first carried out before dyeing processing, allow coil certain temperature with
Released stress under certain process stage, contracting receive it is certain it is in stable condition get off, while using wetting softener in dyeing, increase
Bath raio reduces the frictional force between fabric.Since fiber has plasticity more under hygrometric state, using steam method, make socks product in hygrometric state
Under be heated evenly, moulding effect is good, and does not influence uniform dyeing property, that is, improves the flatness of socks product, also socks is made to have more
Moulding effect.
Specific implementation mode
Technical scheme of the present invention described in detail below.The embodiment of the present invention is only for illustrating concrete structure, the rule of the structure
Mould should not be limited by the examples.
The manufacturing method of high-elasticity pressure socks, it is raw material to select polyamide fibre and spandex, successively by weaving, cutting out, piece, vapour
It steams, dyeing, shape；Decatize is first carried out before dyeing, by the good product of piece, is put into the steaming box of band vacuum extractor
In, it is evacuated down to certain negative pressure, negative pressure value 20kPa is warming up to 80 DEG C with the rate of 2 DEG C/min, keeps the temperature 10min, again
It vacuumizes, decatize, is warming up to 95-105 DEG C, keep the temperature 20min, when decatize, bath raio 1:15-1:20, wetting softener dosage is
1%-3%, then exhaust decompression, takes out product after cooling, is put into dye vat, is warming up to 95-98 DEG C with the rate of 1 DEG C/min, protects
Warm 50min, then 60 DEG C are cooled to, drain.
Claims (3)
1. the manufacturing method of high-elasticity pressure socks, it is raw material to select polyamide fibre and spandex, successively by weaving, cutting out, piece, vapour
It steams, dyeing, shape；It is characterized in that, first carrying out decatize before dyeing, by the good product of piece, it is put into band vacuum means
In the steaming box set, it is evacuated down to certain negative pressure, 80 DEG C is warming up to the rate of 2 DEG C/min, keeps the temperature 10min, is taken out again true
Sky, decatize are warming up to 95-105 DEG C, keep the temperature 20min, then exhaust decompression, take out product after cooling, are put into dye vat, with 1 DEG C/
The rate of min is warming up to 95-98 DEG C, keeps the temperature 50min, then cool to 60 DEG C, drain.
2. the manufacturing method of high-elasticity pressure socks according to claim 1, it is characterised in that described being evacuated down to is certain
Negative pressure, negative pressure value 20kPa.
3. the manufacturing method of high-elasticity pressure socks according to claim 1, it is characterised in that when the decatize, bath raio 1:
15-1:20, wetting softener dosage is 1%-3%.