CN108410278A - 一种户外负氧离子涂料 - Google Patents

一种户外负氧离子涂料 Download PDF

Info

Publication number
CN108410278A
CN108410278A CN201810296116.2A CN201810296116A CN108410278A CN 108410278 A CN108410278 A CN 108410278A CN 201810296116 A CN201810296116 A CN 201810296116A CN 108410278 A CN108410278 A CN 108410278A
Authority
CN
China
Prior art keywords
oxygen ion
negative oxygen
powder
parts
ion coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810296116.2A
Other languages
English (en)
Inventor
任细川
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hebei Kuo Run Technology Co Ltd
Original Assignee
Hebei Kuo Run Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hebei Kuo Run Technology Co Ltd filed Critical Hebei Kuo Run Technology Co Ltd
Priority to CN201810296116.2A priority Critical patent/CN108410278A/zh
Publication of CN108410278A publication Critical patent/CN108410278A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种户外负氧离子涂料，其特征在于：其原料由以下组分构成：聚合物乳液38～39份，电气石粉末2～3份，铈化合物3～5份，钛酸酯偶联剂3～5份，可再分散性乳胶粉0.55％‑1.5％，轻钙粉1.2％‑1.8％，立德粉0.15％‑0.50％，醇类有机溶剂1～5份，湿润分散剂0.1～0.3份，消泡剂0.2～0.4份，水50～60份。本发明的负氧离子内墙涂料对涂料基材的选择并无特殊要求，且具有耐水洗、黏结强度高的优异性能，本发明的负氧离子内墙涂料不但可以迅速吸除异味、还能长期吸除烟味，刷涂后产生的空气负离子浓度高，功效持久。

Description

一种户外负氧离子涂料
技术领域
本发明属于涂料技术领域，尤其涉及一种户外负氧离子涂料。
背景技术
众所周知，人们70％的时间在室内渡过，因此室内空气的清洁度将直接影响到人们的健康。近几年，随着人民生活水平不断提高，居住环境不断改善，室内装饰装修日趋豪华、美观的同时，因装修引起的室内污染影响人体健康的问题越来越多，调查表明：68％的疾病起因与室内空气的污染有关，80％的癌症与居住环境有关。因此，高效持久地净化室内有害气体，保持清新健康的生活、工作环境成了人们越来越迫切追求的目标。负离子涂料的问世给人类带来了福音，可以让人们在居室内真正享受到清新健康的空气。这种系列涂料不仅具有装饰保护作用，而且可持续释放负离子，从而增加空气中负离子的浓度，达到改善环境的目的。
然而，现有的含负离子添加剂的涂料中，虽然也添加有一定量的负离子添加剂，但是其产品产生的空气负离子浓度并不高，功效不持久。
发明内容
本发明的目的在于克服现有技术的不足，提供一种负氧离子涂料，本发明的负氧离子内墙涂料对涂料基材的选择并无特殊要求，且具有耐水洗、黏结强度高的优异性能，本发明的负氧离子内墙涂料不但可以迅速吸除异味、还能长期吸除烟味，刷涂后产生的空气负离子浓度高，功效持久。
本发明解决其技术问题是采取以下技术方案实现的：
一种户外负氧离子涂料，其特征在于：其原料由以下组分构成：聚合物乳液38～39份，电气石粉末2～3份，铈化合物3～5份，钛酸酯偶联剂3～5份，可再分散性乳胶粉0.55％-1.5％，轻钙粉1.2％-1.8％，立德粉0.15％-0.50％，醇类有机溶剂1～5份，湿润分散剂0.1～0.3份，消泡剂0.2～0.4份，水50～60份。
进一步的，所述可再分散性乳胶粉选自丙烯酸胶粉、丁苯胶粉、乙烯-醋酸乙烯共聚物胶粉、苯乙烯-丁二烯共聚物胶粉、醋酸乙烯酯-乙烯-甲基丙烯酸甲酯共聚物胶粉、乙烯-氯乙烯-月桂酸乙烯酯三元共聚物胶粉中的至少一种。
进一步的，所述的聚合物乳液为苯丙乳液。
进一步的，所述的铈化合物为铈氧化物，较佳的为三氧化二铈和/或二氧化铈。
进一步的，所述的钛酸酯偶联剂为异丙基三(二辛基焦磷酸酰氧基)钛酸酯、异丙基三(二辛基磷酸酰氧基)钛酸酯和异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯中的一种或多种。
进一步的，所述的消泡剂为消泡剂CF-16。
进一步的，所述的湿润分散剂为分散剂SN-5040。
进一步的，所述的醇类有机溶剂为乙醇和/或甲醇。
本发明的优点和积极效果是：
本发明的负氧离子涂料是一种具有优异耐水性能、耐洗刷性能的环保涂料，长期暴露在空气中不开裂、不脱落，黏结强度高，且涂料成膜后可以持续长久产生负离子，负离子释放数量较高。
具体实施方式
首先，需要说明的是，以下将以示例方式来具体说明本发明的具体结构、特点和优点等，然而所有的描述仅是用来进行说明的，而不应将其理解为对本发明形成任何限制。此外，在本文所提及各实施例中予以描述或隐含的任意单个技术特征，仍然可在这些技术特征(或其等同物)之间继续进行任意组合或删减，从而获得可能未在本文中直接提及的本发明的更多其他实施例。
需要注意的是，这里所使用的术语仅是为了描述具体实施方式，而非意图限制根据本申请的示例性实施方式。如在这里所使用的，除非上下文另外明确指出，否则单数形式也意图包括复数形式，此外，术语“包括”和“具有”以及他们的任何变形，意图在于覆盖不排他的包含，例如，包含了一系列步骤或单元的过程、方法、系统、产品或设备不必限于清楚地列出的那些步骤或单元，而是可包括没有清楚地列出的或对于这些过程、方法、产品或设备固有的其它步骤或单元。
在本发明的描述中，需要说明的是，术语“中心”、“上”、“下”、“左”、“右”、“竖直”、“水平”、“内”、“外”等指示的方位或位置关系为该发明产品使用时惯常摆放的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。此外，术语“第一”、“第二”、“第三”等仅用于区分描述，而不能理解为指示或暗示相对重要性。
需要说明的是，在不冲突的情况下，本申请中的实施例及实施例中的特征可以相互组合。
本实施例提供的一种户外负氧离子涂料，其原料由以下组分构成：聚合物乳液38份，电气石粉末2份，铈化合物3份，钛酸酯偶联剂3份，可再分散性乳胶粉0.55％，轻钙粉1.2％，立德粉0.15％，醇类有机溶剂1份，湿润分散剂0.1份，消泡剂0.2份，水50份。
其中：所述可再分散性乳胶粉为丙烯酸胶粉、丁苯胶粉、乙烯-醋酸乙烯共聚物胶粉的混合物；所述的聚合物乳液为苯丙乳液；所述的铈化合物为三氧化二铈；所述的钛酸酯偶联剂为异丙基三(二辛基焦磷酸酰氧基)钛酸酯和异丙基三(二辛基磷酸酰氧基)钛酸酯的混合物；所述的消泡剂为消泡剂CF-16；所述的湿润分散剂为分散剂SN-5040；所述的醇类有机溶剂为乙醇和甲醇。
本发明的负离子内墙涂料不但可以迅速吸除异味、还能长期吸除烟味，检测数据表明刷涂后产生的空气负离子浓度高，功效持久。
实施例2
一种户外负氧离子涂料，其原料由以下组分构成：聚合物乳液39份，电气石粉末3份，铈化合物5份，钛酸酯偶联剂5份，可再分散性乳胶粉1.5％，轻钙粉1.8％，立德粉0.50％，醇类有机溶剂5份，湿润分散剂0.3份，消泡剂0.4份，水60份。
其中：所述可再分散性乳胶粉为丙烯酸胶粉、丁苯胶粉、乙烯-醋酸乙烯共聚物胶粉的混合物；所述的聚合物乳液为苯丙乳液；所述的铈化合物为三氧化二铈；所述的钛酸酯偶联剂为异丙基三(二辛基焦磷酸酰氧基)钛酸酯和异丙基三(二辛基磷酸酰氧基)钛酸酯的混合物；所述的消泡剂为消泡剂CF-16；所述的湿润分散剂为分散剂SN-5040；所述的醇类有机溶剂为乙醇和甲醇。
本发明的负离子内墙涂料不但可以迅速吸除异味、还能长期吸除烟味，检测数据表明刷涂后产生的空气负离子浓度高，功效持久。
实施例3
一种户外负氧离子涂料，其原料由以下组分构成：聚合物乳液38.5份，电气石粉末2.5份，铈化合物4份，钛酸酯偶联剂4份，可再分散性乳胶粉1％，轻钙粉1.5％，立德粉0.45％，醇类有机溶剂3份，湿润分散剂0.2份，消泡剂0.3份，水55份。
其中：所述可再分散性乳胶粉为丙烯酸胶粉、丁苯胶粉、乙烯-醋酸乙烯共聚物胶粉的混合物；所述的聚合物乳液为苯丙乳液；所述的铈化合物为三氧化二铈；所述的钛酸酯偶联剂为异丙基三(二辛基焦磷酸酰氧基)钛酸酯和异丙基三(二辛基磷酸酰氧基)钛酸酯的混合物；所述的消泡剂为消泡剂CF-16；所述的湿润分散剂为分散剂SN-5040；所述的醇类有机溶剂为乙醇和甲醇。
本发明的负离子内墙涂料不但可以迅速吸除异味、还能长期吸除烟味，检测数据表明刷涂后产生的空气负离子浓度高，功效持久。
以上实施例对本发明进行了详细说明，但所述内容仅为本发明的较佳实施例，不能被认为用于限定本发明的实施范围。凡依本发明申请范围所作的均等变化与改进等，均应仍归属于本发明的专利涵盖范围之内。

Claims (8)

1.一种户外负氧离子涂料，其特征在于：其原料由以下组分构成：聚合物乳液38～39份，电气石粉末2～3份，铈化合物3～5份，钛酸酯偶联剂3～5份，可再分散性乳胶粉0.55％-1.5％，轻钙粉1.2％-1.8％，立德粉0.15％-0.50％，醇类有机溶剂1～5份，湿润分散剂0.1～0.3份，消泡剂0.2～0.4份，水50～60份。
2.根据权利要求1所述的一种户外负氧离子涂料，其特征在于：所述可再分散性乳胶粉选自丙烯酸胶粉、丁苯胶粉、乙烯-醋酸乙烯共聚物胶粉、苯乙烯-丁二烯共聚物胶粉、醋酸乙烯酯-乙烯-甲基丙烯酸甲酯共聚物胶粉、乙烯-氯乙烯-月桂酸乙烯酯三元共聚物胶粉中的至少一种。
3.根据权利要求1所述的一种户外负氧离子涂料，其特征在于：所述的聚合物乳液为苯丙乳液。
4.根据权利要求1所述的一种户外负氧离子涂料，其特征在于：所述的铈化合物为铈氧化物，较佳的为三氧化二铈和/或二氧化铈。
5.根据权利要求1所述的一种户外负氧离子涂料，其特征在于：所述的钛酸酯偶联剂为异丙基三(二辛基焦磷酸酰氧基)钛酸酯、异丙基三(二辛基磷酸酰氧基)钛酸酯和异丙基二油酸酰氧基(二辛基磷酸酰氧基)钛酸酯中的一种或多种。
6.根据权利要求1所述的一种户外负氧离子涂料，其特征在于：所述的消泡剂为消泡剂CF-16。
7.根据权利要求1所述的一种户外负氧离子涂料，其特征在于：所述的湿润分散剂为分散剂SN-5040。
8.根据权利要求1所述的一种户外负氧离子涂料，其特征在于：所述的醇类有机溶剂为乙醇和/或甲醇。
CN201810296116.2A 2018-03-30 2018-03-30 一种户外负氧离子涂料 Pending CN108410278A (zh)