CN108405290A - A kind of technique of bone ash storage frame baking vanish - Google Patents
A kind of technique of bone ash storage frame baking vanish Download PDFInfo
- Publication number
- CN108405290A CN108405290A CN201810325189.XA CN201810325189A CN108405290A CN 108405290 A CN108405290 A CN 108405290A CN 201810325189 A CN201810325189 A CN 201810325189A CN 108405290 A CN108405290 A CN 108405290A
- Authority
- CN
- China
- Prior art keywords
- supporting plate
- technique
- baking
- baking vanish
- bone ash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of technique of bone ash storage frame baking vanish, the bone ash storage frame includes frame, door leaf, supporting plate, head cover and pedestal, the door leaf and supporting plate are using stamping forming technique after first baking vanish, the baking finish process of the door leaf and supporting plate includes oxidation pre-treatment and preheating, using three times priming paint and twice of finishing coat technique.After baking vanish, ensure lacquer painting non-scale, not blistering, not depainting, not grey, current similar product 10 years or so lacquer painting peelings, blistering, depainting, intensely dark phenomenons can be changed with the gloss of permanent retention lacquer painting, smooth；Meanwhile ensure that storage rack baking vanish is uniform, thin portion structure can be looked after, each details position can same process, to realize beautiful exquisite and details in place.
Description
Technical field
The present invention relates to a kind of cinerary casket frame fields, more particularly to bone ash storage frame process of surface treatment.
Background technology
In short supply due to land resource, if must tie up a large amount of soil using burial in the ground when people, country also emphasizes to carry a coffin to the burial place
Reform is buried, cremation is advocated, people after death directly cremates and is packed into cinerary casket.But for the storage of cinerary casket, someone can also be embedded to underground,
The final waste for still causing soil.Relatively effective method is to leave cinerary casket concentratedly, such as can be put into cinerary casket
Bone ash storage frame, storing compartment etc..Bone ash storage frame generally uses tower structure, each gridiron that large space is separated into one
A small space can be arranged door leaf, portrait or glass can be arranged on door leaf for storing single cinerary casket on gridiron, can be with
Cinerary casket is had an X-rayed, sees that cinerary casket indicates the feelings of grief when being looked at reverence so as to relatives.
Existing bone ash storage frame often only plays storage function, but people have also entrusted to the care of bone ash storage frame more people
Literary emotion generally requires the more beautiful exquisiteness of storage rack, more durable, permanent to keep gloss etc..Existing storage rack, often
Using metal former material, or simple spray painting processing is carried out, just will produce dull after a period of time or even is got rusty, spray painting face is risen
Skin, blistering, depainting, grey, glossiness are greatly reduced；In the prior art, Spray Painter often is carried out to molding storage rack
Skill, and storage rack is often due to the labyrinth of some thin portions causes to paint uneven, or polishing is difficult, final to cause
Product often seem very coarse in detail, it is not exquisite.
Invention content
For prior art defect, the purpose of the present invention is to provide a kind of techniques of bone ash storage frame baking vanish, by roasting
After paint, ensure lacquer painting non-scale, not blistering, not depainting, not grey, can be changed current with the gloss of permanent retention lacquer painting, smooth
Similar product 10 years or so lacquer painting peelings, blistering, depainting, intensely dark phenomenons；Meanwhile ensureing that storage rack baking vanish is uniform, carefully
Portion's structure can be looked after, each details position can same process, to realize beautiful exquisite and details in place.
Specific technical solution is as follows：
A kind of technique of bone ash storage frame baking vanish, the bone ash storage frame include frame, door leaf, supporting plate, head cover and pedestal,
It is characterized in that：The door leaf and supporting plate are using stamping forming technique after first baking vanish, the baking finish process of the door leaf and supporting plate
Include the following steps：
1) leveling pretreatment is carried out to plate；
2) surface fine sand is handled, surface cleaning processing；
3) panel surface, using chemical oxidation treatment：Natrium carbonicum calcinatum 3%, anhydrous sodium chromate 1.5%.Work temperature
90~100 DEG C of degree, 3~5 minutes processing times；
4) low-temperature bake is carried out to the plate, baking temperature is at 40 DEG C -60 DEG C, and baking time was at 1-3 minutes；
5) by paint spraying apparatus, spray-applied primer and finishing coat, the basecoat paint three times, first time priming paint is seal coat,
It is toasted in 140 DEG C -190 DEG C of oven after spray, baking time is 15-20 minutes, and room temperature cooling is carried out after baking；Second of bottom
Paint is that PE is painted, and is toasted in 190 DEG C -240 DEG C of oven after spray, and baking time is 25-40 minutes, and it is cold that room temperature is carried out after baking
But；Third uses air drying primer all over priming paint, and airdrying time is more than 60 minutes under room temperature；
The finishing coat sprays twice, carries out low-temperature bake after spraying every time, toasts 4-6 hours at a temperature of 40-60 DEG C, so
It is dried under room temperature again afterwards.
6) it polishes, the silicon carbide paper that different meshes are respectively adopted carries out classification polishing, then using envelope glaze grinding and polishing table
Face.
Further, there are four-sided openings in the middle part of the door leaf, the plate at the opening position by punching press flanging at
Upper and lower two W-shaped structures, and on the inside of the door leaf；The supporting plate is mutually fastened by two supporting plate disks and is formed, the supporting plate
Disk is square, and the front and back of the supporting plate disk are two folded edges, and the left side and the right of the supporting plate disk do not set folding
Side, the supporting plate disk centre has at least one bending ribs, described to bend plate of the ribs by the making supporting plate disk
Bending is integrally formed, and has buckling groove on the bending ribs.
Further, the thickness control of the spray painting of the door leaf and supporting plate is in 5mm-10mm.
Further, the technique that the frame, head cover and pedestal use baking vanish after first punch forming.
Further, in the baking finish process of the frame, head cover and pedestal, the thickness control of spray painting is in 15-30mm.
Further, the priming paint is pure polyester resin powder thermosetting.
Further, diluent or high boiling solvent is added in the priming paint and finishing coat.
Advantages of the present invention and the advantageous effect of generation are：
Using the technique of punching press after first baking vanish, it is ensured that can be at same technique at each details of storage rack finished product
Reason, avoids the partial structurtes caused by complicated that from cannot painting or polish, and ensures the technique at product details, in conjunction with supporting plate and
The structure of door leaf, since its structure simplifies, supporting plate disk only needs flanging in one direction, substantially reduces technology difficulty, promotes quality,
Punch forming can't cause poly-injury to baking vanish face；By oxidation processes and low temperature prebake conditions, attachment can be submitted significantly
Power；And glossiness, durability and the toughness and ductility of lacquer painting can be greatly improved by painting process, after baking vanish,
Ensure lacquer painting non-scale, not blistering, not depainting, not grey, can be changed similar at present with the gloss of permanent retention lacquer painting, smooth
Product 10 years or so lacquer painting peelings, blistering, depainting, intensely dark phenomenons.
Description of the drawings
Fig. 1：The bone ash storage frame overall structure figure of the present invention；
Fig. 2：The bone ash storage frame support board structure figure of the present invention；
Fig. 3：The bone ash storage frame door leaf structure schematic diagram of the present invention.
Specific implementation mode
Below according to attached drawing, the present invention will be described in detail, is a kind of preferred reality in numerous embodiments of the present invention
Apply example.
A kind of technique of bone ash storage frame baking vanish, the bone ash storage frame include frame 1, door leaf 2, supporting plate, head cover 3 and bottom
Seat 4, it is characterised in that：Stamping forming technique after the door leaf 2 and the first baking vanish of supporting plate use, the door leaf 2 and supporting plate are baked
Lacquer craftwork includes the following steps：
1) leveling pretreatment is carried out to plate；
2) surface fine sand is handled, surface cleaning processing；
3) panel surface, using chemical oxidation treatment：Natrium carbonicum calcinatum 3%, anhydrous sodium chromate 1.5%.Work temperature
90~100 DEG C of degree, 3~5 minutes processing times；
4) low-temperature bake is carried out to the plate, baking temperature is at 40 DEG C -60 DEG C, and baking time was at 1-3 minutes；
5) by paint spraying apparatus, spray-applied primer and finishing coat, the basecoat paint three times, first time priming paint is seal coat,
It is toasted in 140 DEG C -190 DEG C of oven after spray, baking time is 15-20 minutes, and room temperature cooling is carried out after baking；Second of bottom
Paint is that PE is painted, and is toasted in 190 DEG C -240 DEG C of oven after spray, and baking time is 25-40 minutes, and it is cold that room temperature is carried out after baking
But；Third uses air drying primer all over priming paint, and airdrying time is more than 60 minutes under room temperature；
The finishing coat sprays twice, carries out low-temperature bake after spraying every time, toasts 4-6 hours at a temperature of 40-60 DEG C, so
It is dried under room temperature again afterwards.
6) it polishes, the silicon carbide paper that different meshes are respectively adopted carries out classification polishing, then using envelope glaze grinding and polishing table
Face.
Further, the middle part of the door leaf 2 has a four-sided openings, the plate at the opening position by punching press flanging at
Upper and lower two W-shaped structures 10, and on the inside of the door leaf；The supporting plate is mutually fastened by two supporting plate disks 5 and is formed, the support
Plate disc is square, and the front and back of the supporting plate disk are two folded edges, and the left side and the right of the supporting plate disk are not set
Flanging, the supporting plate disk centre has at least one bending ribs 6, described to bend plate of the ribs by the making supporting plate disk
Material bending is integrally formed, and has buckling groove 7 on the bending ribs.
Further, the thickness control of the spray painting of the door leaf and supporting plate is in 5mm-10mm.
Further, the technique that the frame, head cover and pedestal use baking vanish after first punch forming.
Further, in the baking finish process of the frame, head cover and pedestal, the thickness control of spray painting is in 15-30mm.
Further, the priming paint is pure polyester resin powder thermosetting.
Further, diluent or high boiling solvent is added in the priming paint and finishing coat.
Further, the punching course of the door leaf and supporting plate carries out in the environment of temperature is at 40 DEG C -60 DEG C.
Further, the silicon carbide paper of the different meshes is respectively 800 mesh, 1200 mesh, 1500 mesh.
The present invention is exemplarily described above in conjunction with attached drawing, it is clear that the present invention implements not by aforesaid way
Limitation, as long as using the various improvement of inventive concept and technical scheme of the present invention progress, or not improved direct application
In other occasions, within protection scope of the present invention.
Claims (9)
1. a kind of technique of bone ash storage frame baking vanish, the bone ash storage frame includes frame, door leaf, supporting plate, head cover and pedestal,
It is characterized in that：The door leaf and supporting plate are using stamping forming technique after first baking vanish, the baking finish process packet of the door leaf and supporting plate
Include following steps：
1) leveling pretreatment is carried out to plate；
2) surface fine sand is handled, surface cleaning processing；
3) panel surface, using chemical oxidation treatment：Natrium carbonicum calcinatum 3%, anhydrous sodium chromate 1.5%.Operating temperature 90
~100 DEG C, 3~5 minutes processing times；
4) low-temperature bake is carried out to the plate, baking temperature is at 40 DEG C -60 DEG C, and baking time was at 1-3 minutes；
5) by paint spraying apparatus, spray-applied primer and finishing coat, the basecoat paint three times, first time priming paint is seal coat, after spray
It is toasted in 140 DEG C -190 DEG C of oven, baking time is 15-20 minutes, and room temperature cooling is carried out after baking；Second of priming paint is
PE is painted, and is toasted in 190 DEG C -240 DEG C of oven after spray, and baking time is 25-40 minutes, and room temperature cooling is carried out after baking；The
Three times priming paint use air drying primer, and airdrying time is more than 60 minutes under room temperature；
The finishing coat sprays twice, carries out low-temperature bake after spraying every time, toasts 4-6 hours at a temperature of 40-60 DEG C, then again
It is dried under room temperature.
6) it polishes, the silicon carbide paper that different meshes are respectively adopted carries out classification polishing, then using envelope glaze grinding and polishing surface.
2. the technique of bone ash storage frame baking vanish as described in claim 1, it is characterised in that：There is quadrangle in the middle part of the door leaf
Opening, the plate at the opening position by punching press flanging at upper and lower two W-shaped structures, and on the inside of the door leaf；It is described
Supporting plate is mutually fastened by two supporting plate disks and is formed, and the supporting plate disk is square, and the front and back of the supporting plate disk are two
Folded edges, the left side and the right of the supporting plate disk do not set flanging, have at least one bending ribs among the supporting plate disk,
The bending ribs is bent by the plate for making the supporting plate disk and is integrally formed, and has buckling groove on the bending ribs.
3. the technique of bone ash storage frame baking vanish as described in claim 1, it is characterised in that：The spray painting of the door leaf and supporting plate
Thickness control is in 5mm-10mm.
4. the technique of bone ash storage frame baking vanish as described in claim 1, it is characterised in that：The frame, head cover and pedestal are adopted
With the technique of baking vanish after first punch forming.
5. the technique of bone ash storage frame baking vanish as claimed in claim 4, it is characterised in that：The frame, head cover and pedestal
In baking finish process, the thickness control of spray painting is in 15-30mm.
6. the technique of bone ash storage frame baking vanish as described in claim 1, it is characterised in that：The priming paint is pure polyester resin heat
Solidity powder.
7. the technique of bone ash storage frame baking vanish as described in claim 1, it is characterised in that：It is added in the priming paint and finishing coat dilute
Release agent or high boiling solvent.
8. the technique of bone ash storage frame baking vanish as described in claim 1, it is characterised in that：The punching press of the door leaf and supporting plate
Journey carries out in the environment of temperature is at 40 DEG C -60 DEG C.
9. the technique of bone ash storage frame baking vanish as described in claim 1, it is characterised in that：The silicon carbide paper of the different meshes
Respectively 800 mesh, 1200 mesh, 1500 mesh.