CN108396428A - A kind of method of high rigidity fragile fibre short route double twisting resultant yarn - Google Patents
A kind of method of high rigidity fragile fibre short route double twisting resultant yarn Download PDFInfo
- Publication number
- CN108396428A CN108396428A CN201810126462.6A CN201810126462A CN108396428A CN 108396428 A CN108396428 A CN 108396428A CN 201810126462 A CN201810126462 A CN 201810126462A CN 108396428 A CN108396428 A CN 108396428A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fiber
- twisting
- high rigidity
- ribbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of methods of high rigidity fragile fibre short route double twisting resultant yarn, belong to textile technology field.The characteristics of nonwoven flexible facestock is easily made using high rigidity fragile fibre in the present invention, it is placed on cutting machine using by nonwoven flexible facestock package made of high rigidity fragile fibre raw material, nonwoven plane materiel cuts into fibrous ribbon, a kind of performed polymer of ribbon high rigidity brittleness fibre is quickly made, then the double twisting disk double twisting of two-for-one twister is used to act on, the performed polymer of ribbon high rigidity fragile fibre is directly continuously transformed into linear cylindric yarn, the resultant yarn method of the present invention has broken high rigidity fragile fibre and has been difficult to tradition combing collection technical bottleneck in stripes, change fibrous ribbon structural form, remove drafting from, the series of processes such as rove, solve the problems, such as that high rigidity fragile fibre is difficult to resultant yarn.The method of the present invention process flow is short, application easy to spread.
Description
Technical field
The present invention relates to a kind of methods of high rigidity fragile fibre short route double twisting resultant yarn, belong to textile technology field.
Background technology
Textile fabric for clothes can be divided into three categories:Woven (tatting), knitting and non-woven fabric.Woven and knitting
Fabric is made by yarn or long filament by weaving process;Non-woven fabric (also known as non-woven fabrics) is by textile fabric through viscous
It closes, fusion or other machinery, chemical method are process.Woven fabric is that warp thread is mutually perpendicular to weave in weft yarn and is formed
Fabric, fabric tissue have plain weave, twill, satin weave and by above-mentioned three kinds of elementary organizations and by its hand over phase change be formed by group
It knits.Knitting fabric is yarn or long filament to be constituted coil, then coil is mutually gone here and there and is covered, since the loop construction of knitted fabric is special
It levies, yarn storage amount is more in unit length, therefore has good elasticity mostly.Woven and knitting belongs to traditional textile processing model
Farmland, traditional textile are using first spinning, rear weaver's sequence, specific woven step:Staple in bulk shredding removal of impurities, mixing, combing, combing, one
Road drafting, rove, spun yarn, winder, warping, sizing, wears tying-in, weft preparing, weaving at two draftings;Specific weft-knitting step
Suddenly it is:Staple in bulk shredding removal of impurities, mixing, combing, combing, one of drafting, two draftings, rove, spun yarn, winder, thermal finalization, latitude
Needle is knitted.In traditional textile processing, there are three big technical problems:Traditional ring spinning is processed into process needed for yarn by staple in bulk first
More, long flow path, recruitment are more, time-consuming more, of high cost, and efficient matter short route spinning is the basis for solving to shorten textile flow;Second,
It spins the weaving preparation after spinning process and weaving process flow is longer, the speed of service is high, to yarn abrasion, intensity, filoplume etc.
Quality requirements are higher, and Yarn filoplume easily causes hosiery yarns around crochet hook broken needle more or woven opening is unclear so that wefting insertion efficiency drops
Low, yarn abrasion and intensity is low leads to that woven warp end break frequency is high, weaving efficiency is low, end product quality is poor;Third, although
Traditional ring spinning yarn resultant yarn cohesive force is high, spun size range is wide, but spins by factors such as fibre length, rigidity, number of fiber
Restriction, especially fibre length is too short (length be less than 20 millimeters), during resultant yarn the inside and outside transfer cohesive force of fiber it is insufficient, at
Yarn strength is low, breakage is frequent, can not continuous spinning.
To solve the problems, such as that traditional ring spinning yarn process flow is grown, various free end high-speed spinning technologies are come into being.Whirlpool
Stream spinning is to utilize fixed vortex spinning spool, and the rotor and Yarn-spinning spindle, wire loop to replace revolution at a high speed carry out
A kind of spinning method of spinning.Due to vortex replace machinery twisting and cohesion without revolution parts,
Thus there are the advantages such as speed is fast, yield is high, technological process is short, row yielding is high.But air-jet eddy-current spinning is pushed by being vortexed
Free end yarn tail is made annular revolution at a high speed and is twisted and resultant yarn, belongs to the non-gripping spinning in free end, causes in spinning process to fiber
Curable grip it is insufficient, metastasis degree is low inside and outside fiber, and fiber obvolvent degree is poor, and spinning strength is relatively low, therefore obvolvent force difference, length
Short, rigidity can not all carry out vortex spun yarn greatly, with the fluffy fiber of bending.Friction spun yarn is that a kind of technological process is short, sets
Standby simple, low speed high yield Yarn spinning method, is combined with air with machinery and carrys out adsorption-condensation fiber, in the same of adsorption-condensation fiber
When, rubbing is carried out to yarn by revolution dust cage friction roller by frictional force and twists resultant yarn.But FRICTION SPINNING yarn is that layer twists looping knot
Yarn is constituted, lacks inside and outside transfer between yarn interior fiber, obvolvent force difference between fiber, yarn strength is low.Therefore, when fiber is curved
When stiffness is big, length is too short, dust cage afterturn can not effectively turn bent, winding and twisting resultant yarn, friction spun yarn resultant yarn difficulty is big, at
Yarn quality is low.Raw materials used rotor spinning is the thick item of fiber, is different from rove used when ring spinning, is not required to thin by multiple tracks
The drawing-off and combing of cause can be fed directly into rotor spinning machine and carry out rotor spinning, and rotor spinning rotor spinning rotor spinning
Twisting separates progress with winding, and spinning speed is not influenced by yarn package, and revolving cup velocity of rotation is high, therefore rotor spinning has
Spinning speed is high, big, at low cost, the advantages such as low to ingredient requirement are wrapped.But rotor spinning mechanism is that fiber is free in sliver
End resultant yarn in such a way that overlapped, easily causes that be overlapped on the control force that the fiber of yarn volume surrounding is subject in spinning process small, causes to turn
It is poor that cup spinning holds forming control ability to fiber, be not suitable for obvolvent force difference, length is short, rigidity is big, with the fluffy fibre of bending
Dimension spinning.In conclusion compared with traditional ring spinning yarn technology, each open-end-spinning greatly improves spinning speed, by taking
Roving Frames disappear to shorten flow;But open-end-spinning can not still be avoided being combed into the conventional processes such as item, combing, drafting, flow
Still longer, and free end Spinning principle determines that resultant yarn cohesive force is insufficient, yarn strength is low, obvolvent force difference, length is short, rigidity
Greatly, with fluffy difficult spinning fiber with cannot the carrying out continuous effective high-quality open-end-spinning of bending.
During solving traditional ring spinning, open-end-spinning, fibre length is too short (length is less than 20 millimeters), resultant yarn mistake
The inside and outside transfer cohesive force of fiber is insufficient in journey, yarn strength is low, breakage is frequent, can not continuous spinning the technical issues of, often
Using long filament, the compound resultant yarn method of staple fiber.China Patent Publication No. CN101492843B, publication date on May 12nd, 2010, invention
Create a kind of entitled positioning spinning method of embedded system, embedded spin is by two root long silks with a determining deviation disclosed in the complicated legal case
Front roller is fed, two root items are symmetrically fed into front roller with a determining deviation respectively, forms long filament and the side of side
Then the first pre- looping of staple fiber yarn carries out converging twisting with the complex yarn yarn after the pre- looping in the other side, forms structure again
More complicated complex yarn;The embedded yarn formation zone spun is the resultant yarn that long filament forms big symmetry acute triangle shape
Area, two root items are fed into the resultant yarn area of the acute triangle of long filament composition so that long filament can have staple fiber yarn
Automatic contact of effect winds with catching type, extends fiber-spinnable type, yarn count range, realizes that difficult spinning fiber strip can
It is smoothed out RING SPINNING resultant yarn.China Patent Publication No. CN103215700B, publication date on 01 06th, 2016, innovation and creation name
Referred to as a kind of vortex compound spinning method producing fancy yarn substantially discloses a kind of carrier long filament and is clamped with staple fiber
Formula air vortex spinning, effectively captures staple fiber so that the fiber of short length can be effectively spun into yarn body, and it is short to realize difficult spinning
Fiber strip can be smoothed out vortex spun yarn.Although it is above-mentioned can solve to a certain degree it is difficult spin fiber can not resultant yarn ask
Topic, but above-mentioned technology does not obtain large area use, key is that above-mentioned technology still uses ribbon or rove as correspondence
Process raw material, exactly superbhort fiber, high rigidity fragile fibre, high spring back that super fluffy fiber, pulverulent material etc. are difficult to spin raw material hardly possible
To produce ribbon or rove.It can be seen that by superbhort fiber, high rigidity fragile fibre, the super fluffy fiber of high rebound, powdery
The cylindric cohesion style linear body that the difficult spinning raw material such as difficult spinning raw material such as material is directly prepared into longitudinal ordered arrangement is extremely difficult, therefore
Short route produces superbhort fiber, high rigidity fragile fibre, the high hardly possible such as super fluffy fiber, pulverulent material that springs back and spins the continuous of raw material
Linear body, the spinning unit for embedded fiber is efficiently clamped use, and are the key that solve the difficult raw material that spins smoothly to spin.
It is non-woven no longer to need spinning, woven fabric process, only fiber or long filament are oriented or random alignment, formation are fine
Then web frame forms non-woven fabrics using the methods of mechanical, hot sticky or chemical reinforce;Yarns interwoven, woollen yarn knitting with one one
The traditional textile processing for forming fabric together is compared, and non-woven cloth is usually that one-step method is completed (as used polypropylene granules
For raw material, batch continuous one-step through high-temperature fusion, spinneret, paving guiding principle, hot pressing and produce polypropylene non-woven fabric), breach biography
System weaving principle, has the advantages such as technological process is short, throughput rate is fast, and yield is high, at low cost, purposes is wide, raw material sources are more.Root
According to non-woven key technology method difference, it is broadly divided into:Spun lacing method, needle point method, meltblown, spun-bond process, calendar bonding process, loop bonding
Method, composite algorithm etc..Spun lacing method is so that fiber is mutually become entangled in one by high pressure fine water flow jet to one or more layers web
It rises, has certain strength to enable fibre web to reinforce, it is different according to the product quality requirement processed, it is divided into two kinds of techniques
Route:A. fibrous raw material → shredding mixing → combing → lapping → drawing-off → prewet (water process cycle) → positive and negative spun lacing is (at water
Reason cycle) → final finishing → drying → winding;B. fibrous raw material → shredding mixes → combs disordered wet forming → prewetting, (water process is followed
Ring) → positive and negative spun lacing (water process cycle) → final finishing → drying → winding.Flow A to fibre web vertically and horizontally strength ratio adjusting compared with
It is good, it is suitable for production spunlaced synthetic leather substrates;Flow B is suitable for production spun lacing and defends material.Needle point method is the one of dry method nonwoven forming
Kind, it is to be acted on using the puncture of pricker, fluffy fibre web is reinforced into cloth.Meltblown is in extruded polymer method nonwovens process
One kind, technique original is that the polymer melt stream squeezed out to die head spinneret orifice using high velocity, hot air carries out drawing-off, thus
It forms superfine fibre and condenses upon on solidifying lace curtaining or roller, and rely on and itself be bonded as non-woven cloth, specific embodiment
For:Polymer is fed, and -- -- fiber is formed, and -- fiber cooling -- networking -- is reinforced into cloth for melting extrusion.Spun-bond process is also that melting is spun
Silk networking method belongs to one-step method into cloth nonwoven techniques, it is the method using chemical fibre spinning, in polymer spinning technique
The melt filament of extrusion is cooled down by the air of quenching in the process, filament is made to be stretched air-flow work in cooling procedure
With, formation continuous filament yarn, the then networking on solidifying lace curtaining, and be laid in on lace curtaining, then formed and spun after consolidation device is handled
Bonding non-woven cloth.To realize multigroup part, various nonwoven fabric composite performances, frequently with composite algorithm nonwoven techniques, such as:SM、
(S represents that spun-bond process is non-woven, M represents melt blown nonwoven, C represents hot calendering bonding to the complex forms such as SMS, SMSMS, CS, CSC
Method is non-woven).As fibrous material is in the continuous development of each field application technology, nano-fiber material becomes research and function is answered
Hot subject.Nanofiber diameter is within the scope of 1nm-100nm, has porosity height, large specific surface area, draw ratio
Greatly, surface energy and the high performance advantage of activity, embody the functions such as excellent enhancing, antibacterial, water repellent, filtering, apply and detaching
Each field such as filtering, biologic medical, energy and material, enhancing by polymer, photoelectric sensing.With the extension of nanofiber application field
And demand, the forming technology of preparing of nanofiber have also obtained further exploitation and innovation;Up to the present, the system of nanofiber
Preparation Method includes mainly chemical method, phase separation method, self-assembly method and spinning processing method etc..And spinning processing method is considered as scale
Change prepares the most promising method of high polymer nano fiber, includes mainly method of electrostatic spinning, two-component composite spinning method, meltblown
With laser pulling method etc..Wherein laser ultrasonic pulling method is to heat fiber using laser irradiation, while in Ultrasonic Conditions
Under it is stretched, generate about 105 times of draw ratio, prepare nanofibers, belong to a kind of conventional filament post-processing
Method;In addition to this, other nanometer spinning process are also all directly related to spinning head, have in common that:It is assisted using spinneret
It is acted on drawing-off so that fibre diameter reaches nanoscale.China Intellectual Property Office's invention disclosed on November 11st, 2016 is special
Sharp " controllable screening electrostatic spinning nano fiber film of multiple response and preparation method thereof ", number of patent application
ZL201611005678.4, this application complicated legal case provide a kind of by Thermo-sensitive and PH responsive polymer solution merging electrostatic spinning
Instrument lays the method for forming nano fibrous membrane through electrostatic spinning machine injection.The critical issue of Static Spinning is that electrostatic spinning belongs to
Non-positive grab tensile spinning, electrostatic jet stream form taylor cone in filamentation process, and jet stream fiber is difficult to carry out effective high power
Drawing-off, drawing-off deficiency cause in nanofiber that macromolecular oriented degree is poor, nanofiber fineness needs further to be refined, strength
Too low and scale needs further to be refined;In addition the filamentation process of taylor cone form causes fiber obtained by Static Spinning that cannot be indulged
It is laid to orderly row, it is difficult to spun fiber linearly be collected and be gathered, mainly for the production of micro/nano fibrous membrane material.China
On 08 29th, 2016 invention disclosed patents of Department of Intellectual Property " a kind of coaxial eccentricity device for spinning and method ", number of patent application
ZL201610753443.7, this application complicated legal case provide a kind of by the way that inside and outside multilayer syringe needle, realization are arranged on coaxial eccentricity pipe
The centrifugal spinning method of high speed rotation coaxial eccentricity pipe progress large-scale production superfine fibre, even nanofiber;Chinese knowledge
" a kind of titanium dioxide/Kynoar is micro-/receives tunica fibrosa and its centrifugation to property right office invention disclosed patent on December 14th, 2016
Electrospinning method for preparing ", number of patent application ZL201611154055.3, this application complicated legal case provide a kind of by homemade Detitanium-ore-type
TiO2 mixes the centrifugal spinning solution produced with Kynoar (PVDF) the two, and centrifugal spinning is carried out on centrifugal box-spinning machine,
The method that micro-nano fiber film is made.The critical issue that centrifugation is spun is that, by high speed rotation centrifugal action spinneret, that is sprayed penetrates
It is in that circular ring type is laid into silk to flow into silk correspondingly, it is difficult to and spun fiber is subjected to longitudinal ordered arrangement, linearly collects and gathers, it is main
It is used to produce micro/nano fibrous membrane material;During centrifugal spinning, non-positive grab tensile spinning is also belonged to, centrifuges jet stream drawing-off
Power is restricted by factors such as rotating speed, air drag, causes the drawing-off of spinning insufficient, and drawing-off deficiency causes macromolecular in nanofiber to arrange
The row degree of orientation is poor, nanofiber fineness needs further to be refined, and strength is too low and scale needs further to be refined.But nanofiber
Diameter is too small, causes nanofiber absolutely strength too low, easy to wear, falls off coated in fabric surface is easy to wear, there is coating and spin
Fabric products function persistence is poor, causes nanofiber that can only carry out lapping on a small quantity and is processed into nano fibrous membrane, and can not carry out often
The drawing-off of rule, twisting resultant yarn, the serious industrial applications for restricting nanofiber.Nanofiber is such as processed into macroscopic view, can be adopted
The products such as medical types of functionality, function clothes, industrial fabric are produced with modern textile means, traditional textile products will be broken through
It can and be worth, have a extensive future.Therefore, drawing-off deficiency causes macromolecular oriented in nanofiber in nanometer spinning production
Poor, the nanofiber fineness of degree needs further to be refined, strength is too low and scale needs further to be refined cause again adherency with it is durable
Property it is poor, coated in fabric surface it is easy to wear fall off, be unable to conventional spinning processing, cause nanofiber textile industry metaplasia produce
In, it can only be processed into non-woven fabrics or nanometer film, high speed short route textile process can not be carried out, the serious weaving for restricting nanofiber
Industrial applications.It can be seen that not only process flow is very short for the non-woven networking of nonwoven or film-forming process, and be particularly easy to by
Various superbhort fibers, high rigidity fragile fibre, the high difficult difficult raw material that spins such as raw material that spins such as super fluffy fiber, pulverulent material that springs back are made
Meet the planar or scale aggregate of intensity needed for postorder processed and applied, assign the higher intensity of product, fluffy degree, flexibility,
Gas permeability and hydrophily.But nano fiber non-woven film, there are following defects for conventional fineness fiber non-woven cloth:1) non-woven fabrics is strong
Degree and durability are poor, can not compare favourably with traditional textile cloth, traditional textile dress-goods cannot be replaced to use;It 2) cannot be as it
He equally cleans cloth, it is difficult to be used for garment material;3) fiber arranges, easily splits from right angle orientation in certain direction.Therefore
By superweak (nanofiber etc.), ultrashort (short flannel), high rigidity brittleness (carbon fiber, glass, quartz fibre etc.), the high super bulkiness of rebound
The hardly possible woven material system such as (down-like fiber), powdery (fibrous crystal palpus, carbon nanotube, graphene, various nanoparticles, nano-particle)
At the planar or scale aggregate of nonwoven film or non-woven cloth, then planar or scale aggregate are quickly converted to and spun with tradition
Fabric increases fabric intensity and durability, while retaining the performances such as fluffy, ventilative, the soft, antibacterial of nonwoven film, non-woven cloth, is
Solve nonwoven film, Nonwovens In Technology disadvantage, the key for expanding non-woven products that application field.
For the key problem in technology, China Patent Publication No. CN202247124U, publication date on May 30th, 2012, invention wound
Make a kind of non-woven fabrics flat bar flame of entitled two-way cladding, the yarn by a non-woven fabrics flat bar as heart yarn, two
The two-way cladding heart yarn of monofilament, wherein non-woven fabrics flat bar do not twist obvolvent, only external sheath long filament, are substantially a kind of fancy
Line, it is totally different with tradition twisting obvolvent yarn texture;China Patent Publication No. CN2670389Y, publication date on 01 12nd, 2005,
Invention and created name is a kind of bulky yarn made from nno-weavon fabrics, which is the flat-shaped pressure of continous way that the hot pressing of non-woven fabrics longitudinal direction is constituted
Item, this presses against item fiber itself and tends to longitudinal arrangement, and hot pressing softening is binded into dense state, and presses against two outside tool of item
There is the fluffy fiber hair not pressed against.Obviously, although the yarn that above two complicated legal case provides has the LINEAR CONTINUOUS of certain strength special
Sign, but yarn shape structure is flat bar state, lacks fiber twisting cohesion style cylindrical structure, it is widely different with conventional textile yarn texture
It is different, it is not suitable with conventional textile equipment and walks yarn and yarn-guiding duct, cannot veritably incorporate conventional batch yarn weaving equipment and life
Production. art does not solve superweak (nanofiber etc.), ultrashort (short flannel), high rigidity brittleness (carbon fiber, glass, quartz fibre
Deng), high spring back that super bulkiness (down-like fiber), powdery (carbon nanotube, graphene, various nanoparticles, receive by fibrous crystal palpus
Rice corpuscles) etc. difficult woven material the technical issues of how being spinned, being weaved, therefore superbhort fiber is generally used for papermaking at present
Industry, the strengthening filler of composite material, flocking products exploitation.
Invention content
To solve the problems, such as that difficult woven material is difficult to resultant yarn, present invention aims at provide a kind of short stream of high rigidity fragile fibre
The method of journey double twisting resultant yarn.To achieve the goals above, technical solution of the invention is:
A kind of method of high rigidity fragile fibre short route double twisting resultant yarn, this method carry out according to the following steps:
A nonwoven flexible facestocks cut into fibrous ribbon
The nonwoven flexible facestock that surface density made of high rigidity fragile fibre raw material is 50-300 grams/m is wrapped,
It is placed on guillotine, nonwoven plane materiel is cut into the fibrous ribbon that line density is 90-600 grams kms, per one ribbon band difference
On mound bobbins, bobbin package is formed;
Fiber B band double twisting resultant yarn
Bobbin package is respectively placed in the yarn storage tank of two-for-one twister, the every one ribbon band unwound from bobbin package
It is each passed through two-for-one twister flier, it is fixed through tensioner, the two-for-one twister in hollow shaft successively into the hollow shaft of two-for-one twister hollow ingot
In the sleeve of position into spool, drawn from the spool outlet that goes out of two-for-one twister twisting plate, be then passed through yarn guiding ring, enter delivery roller pincers
Mouthful place, under delivery roller jaw and tensioner collective effect, positioned at tensioner to delivery roller jaw section fibrous ribbon by
To traction action power, traction action power draws fibrous ribbon internal fiber and is stretched along band length direction, increases fiber-wall-element model,
Under interior magnet steel and fixation magnet steel collective effect on double twisting board, yarn storage tank, stationary disk are stationary, and spindle band drives times
The twisting plate of twister is turned round with 3000-7000 revs/min of rotating speed, to the fibre of the tensioning between flier and twisting plate
It ties up band and implements primary twisting effect, primary active force solid torsioned fibres interior strips fiber of twisting carries out close obvolvent, increasing
Add obvolvent between fiber, the fibrous ribbon of linear sheet is transformed into linear columned yarn, and linear cylindric yarn is from twisting
Disk goes out spool outlet and draws, and before entering delivery roller jaw, is acted on by the secondary twisting of revolution twisting plate, secondary twisting
Active force solid reverses yarn interior fiber, further increases obvolvent between fiber in yarn, and it is 100-620 special to ultimately form fineness
The yarn of gram this yarn, formation passes through twizzle, guide traversing gear, groove drum successively again, is finally wound up on bobbin.
As a result of above technical scheme, compared with prior art, a kind of short stream of high rigidity fragile fibre of the invention
The method of journey double twisting resultant yarn, the advantage is that:The present invention by surface density made of high rigidity fragile fibre raw material be 50-300 grams/
Square metre the package of nonwoven flexible facestock, be placed on guillotine, it is 90-600 grams kms that nonwoven plane materiel, which is cut into line density,
Fibrous ribbon, it is ingenious be utilized high rigidity fragile fibre be easy to random laid, felting formed nonwoven flexible facestock feature, soon
A kind of flexible performed polymer of ribbon high rigidity fragile fibre is made in speed, has broken superbhort fiber and has been difficult to tradition combing collection into item
Technical bottleneck, difficult spinning ribbon directly twists resultant yarn and is ready, eliminate tradition spinning the multiple drawing-off drafting of preceding spinning,
The series of processes such as rove are made in ripe bar draw twisting, fibre rod flow when substantially shortening tradition spinning.Using two-for-one twister
Delivery roller jaw carries out traction action to the fibrous ribbon positioned at tensioner to delivery roller jaw section jointly with tensioner, leads
It draws active force traction fibrous ribbon internal fiber along the stretching, extension of band length direction, increase fiber-wall-element model, change in fibrous ribbon
High rigidity fragile fibre is excessively at random, random distribution form;Using the twisting plate of two-for-one twister to being located at tensioner to drawing leno
The fibrous ribbon of draw vice mouth section carries out primary rotation and applies two times of twisting, twists active force solid torsioned fibres interior strips fiber
It carries out close obvolvent, increase obvolvent between fiber, the fibrous ribbon of linear sheet is transformed into linear columned yarn, changes
Fibrous ribbon middle short fiber is excessively loose, random distribution form, solves high rigidity fragile fibre in non-twist flat bar or flat yarn
Obvolvent tightness is small, non-cylindrical is difficult to adapt to the technical problems such as textile process requirement, and not only efficient double twisting processes yarn, but also
Spun yarn drafting, Yarn twisting that tradition is spinned is omitted and is processed into the processes such as cylinder yarn at coil, again by coil progress winder, into one
Step effectively shortens resultant yarn flow.The nonwoven flexible facestock that fiber is spun present invention employs high rigidity brittleness difficulty cuts into ribbon
Two band, fibrous ribbon double twisting resultant yarn steps, realize the short route resultant yarn of high rigidity fragile fibre, solve high rigidity brittleness
Fiber with the technical barrier of resultant yarn, for high rigidity fragile fibre is made high function high-quality yarn and garment material provide it is quick,
Effective method.The method of the present invention resultant yarn advantage is notable, flow is short, is easy to be widely applied.
Description of the drawings
Fig. 1 is the process flow chart of the short route double twisting resultant yarn of the present invention.
Specific implementation mode
A kind of method of high rigidity fragile fibre short route double twisting resultant yarn of the present invention is made below in conjunction with the accompanying drawings further
Detailed description.
See attached drawing.
A kind of method of high rigidity fragile fibre short route double twisting resultant yarn, this method carry out according to the following steps:
A nonwoven flexible facestocks cut into fibrous ribbon
The nonwoven flexible facestock that surface density made of high rigidity fragile fibre raw material is 50-300 grams/m is wrapped,
It is placed on guillotine, nonwoven plane materiel is cut into the fibrous ribbon that line density is 90-600 grams kms, per one ribbon band difference
On mound bobbins, bobbin package is formed;The step is ingenious to be utilized that high rigidity fragile fibre is easy to random laid, felting is formed
The nonwoven flexible facestock of high rigidity fragile fibre is directly accurately uniformly cut into fibrous ribbon by the feature of nonwoven flexible facestock,
A kind of flexible performed polymer of ribbon high rigidity fragile fibre is quickly made, has broken high rigidity fragile fibre and has been difficult to traditional combing
Technical bottleneck in stripes is collected, difficult spinning ribbon is directly twisted resultant yarn and is ready, and the preceding spinning for eliminating tradition spinning is multiple
The series of processes such as rove are made in drawing-off drafting, ripe bar draw twisting, fibre rod flow when substantially shortening tradition spinning.
Fiber B band double twisting resultant yarn
Bobbin package is respectively placed in the yarn storage tank of two-for-one twister, the every one ribbon band unwound from bobbin package
It is each passed through two-for-one twister flier, it is fixed through tensioner, the two-for-one twister in hollow shaft successively into the hollow shaft of two-for-one twister hollow ingot
In the sleeve of position into spool, drawn from the spool outlet that goes out of two-for-one twister twisting plate, be then passed through yarn guiding ring, enter delivery roller pincers
Mouthful place, under delivery roller jaw and tensioner collective effect, positioned at tensioner to delivery roller jaw section fibrous ribbon by
To traction action power, traction action power is drawn fibrous ribbon internal fiber along the stretching, extension of band length direction, increase fiber-wall-element model, is changed
Become that high rigidity fragile fibre in fibrous ribbon is excessively at random, form of random distribution, in interior magnet steel and has been mounted on double twisting board
On fixation magnet steel collective effect under, yarn storage tank, stationary disk are stationary, spindle band drive two-for-one twister twisting plate with 3000-
7000 revs/min of rotating speed is turned round, and implements primary twisting to the fibrous ribbon of the tensioning between flier and twisting plate
Effect, primary active force solid torsioned fibres interior strips fiber of twisting carry out close obvolvent, increase obvolvent between fiber, linear piece
The fibrous ribbon of shape is transformed into linear columned yarn, solves high rigidity fragile fibre obvolvent in non-twist flat bar or flat yarn
Tightness is small, non-cylindrical is difficult to adapt to the technical problems such as textile process requirement, and linear cylindric yarn goes out spool from twisting plate and goes out
Mouth is drawn, and before entering delivery roller jaw, is acted on by the secondary twisting of revolution twisting plate, secondary twisting active force solid
Yarn interior fiber is reversed, obvolvent between fiber in yarn is further increased, ultimately forms the yarn that fineness is 100-620 Tekes
The yarn of line, formation passes through twizzle, guide traversing gear, groove drum successively again, is finally wound up on bobbin, not only efficient double twisting
Yarn is processed, and the spun yarn drafting of tradition spinning, Yarn twisting is omitted into coil, then coil progress winder is processed into
The processes such as cylinder yarn, further effectively shorten resultant yarn flow.
With reference to the high rigidity fragile fibre short route resultant yarn process of unlike material, to the concrete application of the present invention make into
One step elaborates.
Embodiment 1 carries out short route resultant yarn using high rigidity brittleness carbon fiber
Carbon fiber elastic modulus is big, friction coefficient is big, brittleness is high, this is allowed for, and its surface is more coarse and bending is easy to break
It is disconnected, it is difficult to torsional bending resultant yarn is directly carried out by the way of routinely twisting;Therefore when carbon fiber sectional material forming, carbon fiber avoids
Larger torsional bending is easily processed into the proximate matters such as felt flexible, band, paper.In addition, carbon fiber is removed as adiabatic guarantor in traditional use
It outside adiabator, is not used alone generally, is mostly added in the materials such as resin, metal, ceramics, concrete as reinforcing material, structure
At composite material.The composite material of fibre reinforced can be used as aircraft construction material, electromagnetic shielding except electric material, artificial ligament etc.
Body substitute material and for manufacturing rocket envelope, power ship, industrial robot, leaf springs of car and drive shaft etc..To solve
Carbon fiber is difficult to the technical barrier of direct torsional bending resultant yarn, will be chopped into the carbon fiber of certain length first by doing (wet) method
Carbon fiber mat is made in forming process, has the characteristics that fiber is evenly distributed, surfacing, gas permeability are high, strong adsorption, then
Film felt is wrapped around the nonwoven flexible facestock that surface density is 50 grams/m on paper tube, is made;Then the present invention is used
Short route resultant yarn is carried out, the specific steps are:
A nonwoven flexible facestocks cut into fibrous ribbon
The nonwoven flexible facestock that surface density made of high rigidity fragile fibre raw material is 50 grams/m is wrapped, is placed in
On guillotine, nonwoven plane materiel is cut into the fibrous ribbon that line density is 90 grams kms, distinguishes mound bobbins per one ribbon band
On, form bobbin package;The step is ingenious be utilized carbon fiber be easy to random laid, the nonwoven flexible facestock that felting is formed spy
Sign, directly accurately fibrous ribbon is uniformly cut by carbon-fibre nonwoven flexible facestock, and a kind of ribbon carbon fiber is quickly made
Flexible performed polymer has broken carbon fiber and has been difficult to tradition and combs collect technical bottleneck in stripes, difficult spinning ribbon directly twist at
Yarn is ready, eliminate tradition spinning the multiple drawing-off drafting of preceding spinning, ripe bar draw twisting the series of processes such as rove are made,
Fibre rod flow when substantially shortening tradition spinning.
Fiber B band double twisting resultant yarn
Bobbin package is respectively placed in the yarn storage tank of two-for-one twister, the every one ribbon band unwound from bobbin package
It is each passed through two-for-one twister flier, it is fixed through tensioner, the two-for-one twister in hollow shaft successively into the hollow shaft of two-for-one twister hollow ingot
In the sleeve of position into spool, drawn from the spool outlet that goes out of two-for-one twister twisting plate, be then passed through yarn guiding ring, enter delivery roller pincers
Mouthful place, under delivery roller jaw and tensioner collective effect, positioned at tensioner to delivery roller jaw section fibrous ribbon by
To traction action power, traction action power is drawn fibrous ribbon internal fiber along the stretching, extension of band length direction, increase fiber-wall-element model, is changed
Become that carbon fiber in fibrous ribbon is excessively at random, form of random distribution, in interior magnet steel and the fixation on double twisting board
Under magnet steel collective effect, yarn storage tank, stationary disk are stationary, and spindle band drives the twisting plate of two-for-one twister with 7000 revs/min of turn
Speed is turned round, and implementing primary twisting to the fibrous ribbon of the tensioning between flier and twisting plate acts on, and primary twisting is made
Firmly three-dimensional torsioned fibres interior strips fiber carries out close obvolvent, increases obvolvent between fiber, and the fibrous ribbon of linear sheet turns
It is turned into linear columned yarn, it is small, not rounded solves high rigidity brittleness carbon fiber obvolvent tightness in non-twist flat bar or flat yarn
Column is difficult to adapt to the technical problems such as textile process requirement, and linear cylindric yarn goes out spool outlet from twisting plate and draws, into
It before entering delivery roller jaw, is acted on by the secondary twisting of revolution twisting plate, in secondary twisting active force solid torsion yarn
Portion's fiber further increases obvolvent between fiber in yarn, ultimately forms the yarn that fineness is 100 Tekes, the yarn of formation is again
Pass through twizzle, guide traversing gear, groove drum successively, is finally wound up on bobbin, not only efficient double twisting processes yarn, but also
Spun yarn drafting, Yarn twisting that tradition is spinned is omitted and is processed into the processes such as cylinder yarn at coil, then by coil progress winder, into one
Step effectively shortens resultant yarn flow.
Embodiment 2 carries out short route resultant yarn using high rigidity brittle glass fiber
Glass fibre is a kind of inorganic non-metallic material haveing excellent performance, and type is various, and advantage is good insulating, heat resistance
By force, corrosion resistance is good, high mechanical strength, but the disadvantage is that property is crisp, wearability is poor.Therefore it is brittle directly to twist resultant yarn for glass fibre
It is disconnected, it is generally used to make zero twisted yarn, glass felt.Glass fiber rough yarn is chopped into 50mm, random laid is being previously positioned at conveyer belt
On ground on, then pierced into the hand-manipulating of needle with the needle with barb, needle lunges chopped strand in ground, and crochet hook is by some fibre
It takes up to form three-dimensional structure upwards, forms short glass fiber Nomex.Ground used can be glass fibre or other fibers
Dilute fabric, this Nomex villous sense, main application include as heat-and sound-insulating material, lining hot material, filtering material.
Needle thorn glass mat is wrapped around the nonwoven flexible facestock that surface density is 300 grams/m on paper tube, is made again;So
Short route resultant yarn is carried out using the present invention afterwards, the specific steps are:
A nonwoven flexible facestocks cut into fibrous ribbon
The nonwoven flexible facestock that surface density made of high rigidity fragile fibre raw material is 300 grams/m is wrapped, is placed in
On guillotine, nonwoven plane materiel is cut into the fibrous ribbon that line density is 600 grams kms, distinguishes winch spool per one ribbon band
Guan Shang forms bobbin package;The step is ingenious to be utilized the nonwoven flexible facestock that glass fibre is easy to random laid, felting is formed
Feature, glass fiber non-woven flexible facestock is directly accurately uniformly cut into fibrous ribbon, a kind of ribbon glass is quickly made
The flexible performed polymer of glass fiber has broken glass fibre and has been difficult to tradition combing collection technical bottleneck in stripes, difficult spinning ribbon
Directly twisting resultant yarn is ready, and eliminates the multiple drawing-off drafting of preceding spinning of tradition spinning, rove etc. is made in ripe bar draw twisting
Series of processes, fibre rod flow when substantially shortening tradition spinning.
Fiber B band double twisting resultant yarn
Bobbin package is respectively placed in the yarn storage tank of two-for-one twister, the every one ribbon band unwound from bobbin package
It is each passed through two-for-one twister flier, it is fixed through tensioner, the two-for-one twister in hollow shaft successively into the hollow shaft of two-for-one twister hollow ingot
In the sleeve of position into spool, drawn from the spool outlet that goes out of two-for-one twister twisting plate, be then passed through yarn guiding ring, enter delivery roller pincers
Mouthful place, under delivery roller jaw and tensioner collective effect, positioned at tensioner to delivery roller jaw section fibrous ribbon by
To traction action power, traction action power is drawn fibrous ribbon internal fiber along the stretching, extension of band length direction, increase fiber-wall-element model, is changed
Become that carbon fiber in fibrous ribbon is excessively at random, form of random distribution, in interior magnet steel and the fixation on double twisting board
Under magnet steel collective effect, yarn storage tank, stationary disk are stationary, and spindle band drives the twisting plate of two-for-one twister with 3000 revs/min of turn
Speed is turned round, and implementing primary twisting to the fibrous ribbon of the tensioning between flier and twisting plate acts on, and primary twisting is made
Firmly three-dimensional torsioned fibres interior strips fiber carries out close obvolvent, increases obvolvent between fiber, and the fibrous ribbon of linear sheet turns
It is turned into linear columned yarn, it is small, not rounded solves high rigidity brittleness carbon fiber obvolvent tightness in non-twist flat bar or flat yarn
Column is difficult to adapt to the technical problems such as textile process requirement, and linear cylindric yarn goes out spool outlet from twisting plate and draws, into
It before entering delivery roller jaw, is acted on by the secondary twisting of revolution twisting plate, in secondary twisting active force solid torsion yarn
Portion's fiber further increases obvolvent between fiber in yarn, ultimately forms the yarn that fineness is 620 Tekes, the yarn of formation is again
Pass through twizzle, guide traversing gear, groove drum successively, is finally wound up on bobbin, not only efficient double twisting processes yarn, but also
Spun yarn drafting, Yarn twisting that tradition is spinned is omitted and is processed into the processes such as cylinder yarn at coil, then by coil progress winder, into one
Step effectively shortens resultant yarn flow.
Claims (1)
1. a kind of method of high rigidity fragile fibre short route double twisting resultant yarn, which is characterized in that the method is according to the following steps
It carries out:
A nonwoven flexible facestocks cut into fibrous ribbon
The nonwoven flexible facestock that surface density made of high rigidity fragile fibre raw material is 50-300 grams/m is wrapped, is placed in
On guillotine, nonwoven plane materiel is cut into the fibrous ribbon that line density is 90-600 grams kms, is wound respectively per one ribbon band
On bobbin, bobbin package is formed;
Fiber B band double twisting resultant yarn
Bobbin package is respectively placed in the yarn storage tank of two-for-one twister, the every one ribbon band difference unwound from bobbin package
Across two-for-one twister flier, into the hollow shaft of two-for-one twister hollow ingot, successively through tensioner, the two-for-one twister positioning sleeve in hollow shaft
In cylinder into spool, drawn from the spool outlet that goes out of two-for-one twister twisting plate, be then passed through yarn guiding ring, enter delivery roller jaw
Place, under delivery roller jaw and tensioner collective effect, be located at tensioner to delivery roller jaw section fibrous ribbon by
Traction action power, traction action power draw fibrous ribbon internal fiber along the stretching, extension of band length direction, increase fiber-wall-element model, inside
Under magnet steel and fixation magnet steel collective effect on double twisting board, yarn storage tank, stationary disk are stationary, and spindle band drives double twisting
The twisting plate of machine is turned round with 3000-7000 revs/min of rotating speed, to the fiber of the tensioning between flier and twisting plate
Band implements primary twisting effect, and primary active force solid torsioned fibres interior strips fiber of twisting carries out close obvolvent, increase
Obvolvent between fiber, the fibrous ribbon of linear sheet are transformed into linear columned yarn, and linear cylindric yarn is from twisting plate
Go out spool outlet to draw, before entering delivery roller jaw, be acted on by the secondary twisting of revolution twisting plate, secondary twisting is made
Firmly three-dimensional torsion yarn interior fiber, further increases obvolvent between fiber in yarn, and it is special gram of 100-620 to ultimately form fineness
The yarn of this yarn, formation passes through twizzle, guide traversing gear, groove drum successively again, is finally wound up on bobbin.