CN108395112A - A kind of hydrophobic method - Google Patents
A kind of hydrophobic method Download PDFInfo
- Publication number
- CN108395112A CN108395112A CN201810163458.7A CN201810163458A CN108395112A CN 108395112 A CN108395112 A CN 108395112A CN 201810163458 A CN201810163458 A CN 201810163458A CN 108395112 A CN108395112 A CN 108395112A
- Authority
- CN
- China
- Prior art keywords
- sheet surface
- glass sheet
- hydrophobic
- glass
- polishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to glass processing field more particularly to a kind of hydrophobic methods；Specifically include following steps：Step 1 is polished glass sheet surface；Step 2 carries out surface acid-washing to the glass obtained by step 1；Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface；Beneficial effects of the present invention are：By forming water-repellent layer in glass sheet surface after hydrophobic method, 90 ° can be more than or equal to water to the contact angle of glass in use；Water-repellent layer has non-adhesive, does not get wet not only, other pollutants of vapour can be easy to remove.
Description
Technical field
The present invention relates to glass processing field more particularly to a kind of hydrophobic methods.
Background technology
The type of glass is various at present is widely used.In some specific areas, on vehicle glass, there is spy for glass
Different requirement, such as sound insulation, mechanical strength it is big, it is broken after do not detach.Simultaneously in vehicle glass and other field using upper, it is therefore desirable to
It enough requires glass to have certain hydrophobicity performance, the adherency of rainwater can be effectively prevent in rainy day or other glass, is kept away
Exempt to influence using effect.
Invention content
The technical problem to be solved by the present invention is to：There is provided one kind can make glass have good hydrophobic effect, simultaneously
The diactinic hydrophobic method of glass is not influenced.
In order to solve the above-mentioned technical problem, the technical solution adopted by the present invention is：A kind of hydrophobic method is provided, is specifically included
Following steps：
Step 1 is polished glass sheet surface；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface.
Further, it in above-mentioned hydrophobic method, states step 1) and at least carries out twice；It is polishing hair used in the polishing
Felt uses polishing fluid on the felt polishing bob, and the dosage of the polishing fluid is every square metre 10-35 milliliters；The time of polishing is
Every square metre 50-200 seconds.
Further, in above-mentioned hydrophobic method, the felt polishing bob needs replacing new polishing after polishing 10 square metres
Felt；The polishing fluid of additional 8-15 milliliters of addition is needed when the felt polishing bob more renewed, when being polished for the first time.
Further, in above-mentioned hydrophobic method, in the step 1), glass sheet surface be polished after using cleaning paper into
Row clean wiping；Glass sheet surface is handled for 5% hydrochloric acid using Solute mass percentage after wiping, the solute matter
Amount percentage is that the dosage of 5% hydrochloric acid is every square metre of 6-18 milliliters；Back glass sheet surface is cleaned to carry out using new cleaning paper
Clean wiping.
Further, in above-mentioned hydrophobic method, in the step 2), using Solute mass percentage be 5% hydrochloric acid to glass
Glass carries out pickling processes at least twice, stands 1-5 minutes；The Solute mass percentage is that the dosage of 5% hydrochloric acid is every square
20-45 milliliters of rice；After standing clean wiping is carried out using cleaning paper；After wiping, using deionized water to glass sheet surface into
Row processing；After processing, clean wiping is carried out using new cleaning paper.
Further, in above-mentioned hydrophobic method, in the step 3), hydrophober used by the first time hydrophobic processing
Dosage be every square metre 6-15 milliliter, the speed of hydrophobic processing is 0.15-0.6 meters per second, wipes number 2-8 times；In hydrophobic
After treatment carries out clean wiping using cleaning paper to glass sheet surface.
Further, in above-mentioned hydrophobic method, in the step 4), hydrophober used by second of hydrophobic processing
Dosage be every square metre 8-15 milliliter, the speed of hydrophobic processing is 0.15-0.6 meters per second, wipes number 6-11 times；In hydrophobic
After treatment carries out clean wiping using cleaning paper to glass sheet surface.
Further, described to specifically include following steps in above-mentioned hydrophobic method：
Step 1 is polished glass sheet surface；
A, sheet glass is positioned；
B, the sheet glass that a has good positioning is polished, is at least carried out twice；It is felt polishing bob used in the polishing,
Polishing fluid is used on the felt polishing bob, the dosage of the polishing fluid is every square metre 10-35 milliliters；The time of polishing is often to put down
Square rice 50-200 seconds；The felt polishing bob needs replacing new felt polishing bob after polishing 10 square metres；The throwing more renewed
The polishing fluid of additional 8-15 milliliters of addition is needed when light felt, when being polished for the first time；
C, the glass sheet surface obtained by b is subjected to clean wiping using cleaning paper；
D, the use of Solute mass percentage is that 5% hydrochloric acid handles glass sheet surface by the glass sheet surface obtained by c,
The Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 6-18 milliliters；
E, the glass sheet surface obtained by d is subjected to clean wiping using new cleaning paper；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
F, the use of Solute mass percentage is that 5% hydrochloric acid carries out acid at least twice to glass by the glass sheet surface obtained by e
Processing is washed, stands 1-5 minutes；The Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 20-45 milliliters；
G, the glass sheet surface obtained by f is subjected to clean wiping using cleaning paper；
H, the glass sheet surface obtained by g is handled glass sheet surface using deionized water；
I, by the glass sheet surface obtained by h, clean wiping is carried out using new cleaning paper；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
J, the glass sheet surface obtained by i is subjected to first time hydrophobic processing, hated used by the first time hydrophobic processing
The dosage of aqua is every square metre 6-15 milliliters, and the speed of hydrophobic processing is 0.15-0.6 meters per second, wiping number 2-8 times；
K, by the glass sheet surface obtained by j, clean wiping is carried out to glass sheet surface using cleaning paper；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface；
L, by the glass sheet surface obtained by k, second of hydrophobic processing is carried out, is hated used by second of hydrophobic processing
The dosage of aqua is every square metre 8-15 milliliters, and the speed of hydrophobic processing is 0.15-0.6 meters per second, wiping number 6-11 times；
M, by the glass sheet surface obtained by l, in hydrophobic after treatment, glass sheet surface is cleaned using cleaning paper
Wiping.
The beneficial effects of the present invention are：By forming water-repellent layer in glass sheet surface after hydrophobic method, can use
Water is more than or equal to 90 ° to the contact angle of glass in the process；Water-repellent layer has non-adhesive, does not get wet not only, other pollutants of vapour
It can be easy to remove, generated frost and ice are easy to remove in winter；By water-repellent layer, it can effectively stop the alkali in glass
The precipitation of ion, prevents glass elegance and talent and goes bad；The hardness of water-repellent layer is big, corrosion resistance is strong, can be effective for glass itself
Glass scratch is prevented, service life is promoted.
Description of the drawings
Fig. 1 is a kind of flow chart of hydrophobic method of the specific embodiment of the invention.
Specific implementation mode
To explain the technical content, the achieved purpose and the effect of the present invention in detail, below in conjunction with embodiment and coordinate attached
Figure is explained.
The design of most critical of the present invention is：By forming water-repellent layer in glass sheet surface after hydrophobic method, can make
90 ° are more than or equal to the contact angle of glass with water in the process；Water-repellent layer has non-adhesive, does not get wet not only, other pollutions of vapour
Object can be easy to remove.
Fig. 1 is please referred to, a kind of hydrophobic method includes the following steps：
Step 1 is polished glass sheet surface；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface.
As can be seen from the above description, the beneficial effects of the present invention are：By hating in glass sheet surface formation after hydrophobic method
Water layer can be more than or equal to 90 ° by water to the contact angle of glass in use；Water-repellent layer has non-adhesive, not only non-sticky
Water, other pollutants of vapour can be easy to remove, and generated frost and ice are easy to remove in winter；Pass through water-repellent layer, Neng Gouyou
The precipitation of basic ion in effect blocking glass, prevents glass elegance and talent and goes bad；The hardness of water-repellent layer is big, corrosion resistance is strong, for
Glass itself can effectively prevent glass scratch, promote service life.
Further, the step 1) at least carries out twice；It is felt polishing bob used in the polishing, the polishing hair
Polishing fluid is used on felt, the dosage of the polishing fluid is every square metre 10-35 milliliters；The time of polishing is every square metre of 50-200
Second.
Further, the felt polishing bob needs replacing new felt polishing bob after polishing 10 square metres；The throwing more renewed
The polishing fluid of additional 8-15 milliliters of addition is needed when light felt, when being polished for the first time.
Further, in the step 1), glass sheet surface uses cleaning paper to carry out clean wiping after being polished；It is wiping
Glass sheet surface is handled for 5% hydrochloric acid using Solute mass percentage after wiping, the Solute mass percentage is 5% salt
The dosage of acid is every square metre 6-18 milliliters；It cleans back glass sheet surface and carries out clean wiping using new cleaning paper.
Further, the use of Solute mass percentage is that 5% hydrochloric acid carries out acid at least twice to glass in the step 2)
Processing is washed, stands 1-5 minutes；The Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 20-45 milliliters；It stands
Cleaning paper is used to carry out clean wiping afterwards；After wiping, glass sheet surface is handled using deionized water；After processing, make
Clean wiping is carried out with new cleaning paper.
Further, in the step 3), hydrophober used by first time hydrophobic processing glass sheet surface into
The processing of row hydrophobic；The dosage of the hydrophober of the first time hydrophobic just is every square metre 6-15 milliliters, the speed of hydrophobic processing
Degree is 0.15-0.6 meters per second, wiping number 2-8 times；In hydrophobic after treatment, glass sheet surface is carried out using cleaning paper
Clean wiping.
Further, in the step 4), hydrophober used by second of hydrophobic processing glass sheet surface into
The processing of row hydrophobic；The dosage of the hydrophober of second of hydrophobic just is every square metre 8-15 milliliters, the speed of hydrophobic processing
Degree is 0.15-0.6 meters per second, wiping number 6-11 times；In hydrophobic after treatment, glass sheet surface is carried out using cleaning paper
Clean wiping.
Further, the hydrophobic method specifically includes following steps：
Step 1 is polished glass sheet surface；
A, sheet glass is positioned；
B, the sheet glass that a has good positioning is polished, is at least carried out twice；It is felt polishing bob used in the polishing,
Polishing fluid is used on the felt polishing bob, the dosage of the polishing fluid is every square metre 10-35 milliliters；The time of polishing is often to put down
Square rice 50-200 seconds；The felt polishing bob needs replacing new felt polishing bob after polishing 10 square metres；The throwing more renewed
The polishing fluid of additional 8-15 milliliters of addition is needed when light felt, when being polished for the first time；
C, the glass sheet surface obtained by b is subjected to clean wiping using cleaning paper；
D, the use of Solute mass percentage is that 5% hydrochloric acid handles glass sheet surface by the glass sheet surface obtained by c,
The Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 6-18 milliliters；
E, the glass sheet surface obtained by d is subjected to clean wiping using new cleaning paper；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
F, the use of Solute mass percentage is that 5% hydrochloric acid carries out acid at least twice to glass by the glass sheet surface obtained by e
Processing is washed, stands 1-5 minutes；The Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 20-45 milliliters；
G, the glass sheet surface obtained by f is subjected to clean wiping using cleaning paper；
H, the glass sheet surface obtained by g is handled glass sheet surface using deionized water；
I, by the glass sheet surface obtained by h, clean wiping is carried out using new cleaning paper；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
J, the glass sheet surface obtained by i is subjected to first time hydrophobic processing, hated used by the first time hydrophobic processing
The dosage of aqua is every square metre 6-15 milliliters, and the speed of hydrophobic processing is 0.15-0.6 meters per second, wiping number 2-8 times；
K, by the glass sheet surface obtained by j, clean wiping is carried out to glass sheet surface using cleaning paper；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface；
L, by the glass sheet surface obtained by k, second of hydrophobic processing is carried out, is hated used by second of hydrophobic processing
The dosage of aqua is every square metre 8-15 milliliters, and the speed of hydrophobic processing is 0.15-0.6 meters per second, wiping number 6-11 times；
M, by the glass sheet surface obtained by l, in hydrophobic after treatment, glass sheet surface is cleaned using cleaning paper
Wiping.
Embodiment one
A kind of hydrophobic method, specifically includes following steps：
Step 1 is polished glass sheet surface；
A, sheet glass is positioned；
B, the sheet glass that a has good positioning is polished, is at least carried out twice；It is felt polishing bob used in the polishing,
Polishing fluid is used on the felt polishing bob, the dosage of the polishing fluid is 25 milliliters every square metre；The time of polishing is every square
Rice 125 seconds；The felt polishing bob needs replacing new felt polishing bob after polishing 10 square metres；The felt polishing bob more renewed
When, the polishing fluid of additional 10 milliliters of addition is needed when being polished for the first time；
C, the glass sheet surface obtained by b is subjected to clean wiping using cleaning paper；
D, the use of Solute mass percentage is that 5% hydrochloric acid handles glass sheet surface by the glass sheet surface obtained by c,
The Solute mass percentage is that the dosage of 5% hydrochloric acid is 12 milliliters every square metre；
E, the glass sheet surface obtained by d is subjected to clean wiping using new cleaning paper；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
F, the use of Solute mass percentage is that 5% hydrochloric acid carries out acid at least twice to glass by the glass sheet surface obtained by e
Processing is washed, stands 2 minutes；The Solute mass percentage is that the dosage of 5% hydrochloric acid is 30 milliliters every square metre；
G, the glass sheet surface obtained by f is subjected to clean wiping using cleaning paper；
H, the glass sheet surface obtained by g is handled glass sheet surface using deionized water；
I, by the glass sheet surface obtained by h, clean wiping is carried out using new cleaning paper；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
J, the glass sheet surface obtained by i is subjected to first time hydrophobic processing, hated used by the first time hydrophobic processing
The dosage of aqua is 10 milliliters every square metre, and the speed of hydrophobic processing is 0.4 meter per second, wiping number 4 times；
K, by the glass sheet surface obtained by j, clean wiping is carried out to glass sheet surface using cleaning paper；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface；
L, by the glass sheet surface obtained by k, second of hydrophobic processing is carried out, is hated used by second of hydrophobic processing
The dosage of aqua is 10 milliliters every square metre, and the speed of hydrophobic processing is 0.25 meter per second, wiping number 9 times；
M, by the glass sheet surface obtained by l, in hydrophobic after treatment, glass sheet surface is cleaned using cleaning paper
Wiping.
Embodiment two
A kind of hydrophobic method, specifically includes following steps：
Step 1 is polished glass sheet surface；
A, sheet glass is positioned；
B, the sheet glass that a has good positioning is polished, is at least carried out twice；It is felt polishing bob used in the polishing,
Polishing fluid is used on the felt polishing bob, the dosage of the polishing fluid is 10 milliliters every square metre；The time of polishing is every square
Rice 200 seconds；The felt polishing bob needs replacing new felt polishing bob after polishing 10 square metres；The felt polishing bob more renewed
When, the polishing fluid of additional 15 milliliters of addition is needed when being polished for the first time；
C, the glass sheet surface obtained by b is subjected to clean wiping using cleaning paper；
D, the use of Solute mass percentage is that 5% hydrochloric acid handles glass sheet surface by the glass sheet surface obtained by c,
The Solute mass percentage is that the dosage of 5% hydrochloric acid is 18 milliliters every square metre；
E, the glass sheet surface obtained by d is subjected to clean wiping using new cleaning paper；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
F, the use of Solute mass percentage is that 5% hydrochloric acid carries out acid at least twice to glass by the glass sheet surface obtained by e
Processing is washed, stands 2 minutes；The Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 20-45 milliliters；
G, the glass sheet surface obtained by f is subjected to clean wiping using cleaning paper；
H, the glass sheet surface obtained by g is handled glass sheet surface using deionized water；
I, by the glass sheet surface obtained by h, clean wiping is carried out using new cleaning paper；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
J, the glass sheet surface obtained by i is subjected to first time hydrophobic processing, the first time hydrophobic handles used hydrophobic
The dosage of agent is 15 milliliters every square metre, and the speed of hydrophobic processing is 0.6 meter per second, wiping number 6 times；
K, by the glass sheet surface obtained by j, clean wiping is carried out to glass sheet surface using cleaning paper；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface；
L, by the glass sheet surface obtained by k, second of hydrophobic processing is carried out, is hated used by second of hydrophobic processing
The dosage of aqua is 12 milliliters every square metre, and the speed of hydrophobic processing is 0.35 meter per second, wiping number 11 times；
M, by the glass sheet surface obtained by l, in hydrophobic after treatment, glass sheet surface is cleaned using cleaning paper
Wiping.
Embodiment three
A kind of hydrophobic method, specifically includes following steps：
Step 1 is polished glass sheet surface；
A, sheet glass is positioned；
B, the sheet glass that a has good positioning is polished, is at least carried out twice；It is felt polishing bob used in the polishing,
Polishing fluid is used on the felt polishing bob, the dosage of the polishing fluid is 35 milliliters every square metre；The time of polishing is every square
Rice 200 seconds；The felt polishing bob needs replacing new felt polishing bob after polishing 10 square metres；The felt polishing bob more renewed
When, the polishing fluid of additional 12 milliliters of addition is needed when being polished for the first time；
C, the glass sheet surface obtained by b is subjected to clean wiping using cleaning paper；
D, the use of Solute mass percentage is that 5% hydrochloric acid handles glass sheet surface by the glass sheet surface obtained by c,
The Solute mass percentage is that the dosage of 5% hydrochloric acid is 13 milliliters every square metre；
E, the glass sheet surface obtained by d is subjected to clean wiping using new cleaning paper；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
F, the use of Solute mass percentage is that 5% hydrochloric acid carries out acid at least twice to glass by the glass sheet surface obtained by e
Processing is washed, stands 3 minutes；The Solute mass percentage is that the dosage of 5% hydrochloric acid is 33 milliliters every square metre；
G, the glass sheet surface obtained by f is subjected to clean wiping using cleaning paper；
H, the glass sheet surface obtained by g is handled glass sheet surface using deionized water；
I, by the glass sheet surface obtained by h, clean wiping is carried out using new cleaning paper；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
J, the glass sheet surface obtained by i is subjected to first time hydrophobic processing, hated used by the first time hydrophobic processing
The dosage of aqua is 15 milliliters every square metre, and the speed of hydrophobic processing is 0.6 meter per second, wiping number 4 times；
K, by the glass sheet surface obtained by j, clean wiping is carried out to glass sheet surface using cleaning paper；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface；
L, by the glass sheet surface obtained by k, second of hydrophobic processing is carried out, is hated used by second of hydrophobic processing
The dosage of aqua is 15 milliliters every square metre, and the speed of hydrophobic processing is 0.6 meter per second, wiping number 7 times；
M, by the glass sheet surface obtained by l, in hydrophobic after treatment, glass sheet surface is cleaned using cleaning paper
Wiping.
In conclusion a kind of hydrophobic method provided by the invention, by forming hydrophobic in glass sheet surface after hydrophobic method
Layer can be more than or equal to 90 ° by water to the contact angle of glass in use；Water-repellent layer has non-adhesive, does not get wet not only,
Other pollutants of vapour can be easy to remove, and generated frost and ice are easy to remove in winter；By water-repellent layer, can effectively hinder
The precipitation for keeping off the basic ion in glass, prevents glass elegance and talent and goes bad；The hardness of water-repellent layer is big, corrosion resistance is strong, for glass
Itself, can effectively prevent glass scratch, promote service life.
Example the above is only the implementation of the present invention is not intended to limit the scope of the invention, every to utilize this hair
Equivalents made by bright specification and accompanying drawing content are applied directly or indirectly in relevant technical field, include similarly
In the scope of patent protection of the present invention.
Claims (8)
1. a kind of hydrophobic method, which is characterized in that specifically include following steps：
Step 1 is polished glass sheet surface；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface.
2. hydrophobic method according to claim 1, which is characterized in that the step 1) at least carries out twice；The polishing
Used is felt polishing bob, polishing fluid is used on the felt polishing bob, the dosage of the polishing fluid is every square metre of 10-35 milli
It rises；The time of polishing be every square metre 50-200 seconds.
3. hydrophobic method according to claim 2, which is characterized in that the felt polishing bob needs after polishing 10 square metres
The felt polishing bob more renewed；The throwing of additional 8-15 milliliters of addition is needed when the felt polishing bob more renewed, when being polished for the first time
Light liquid.
4. hydrophobic method according to claim 1, which is characterized in that in the step 1), glass sheet surface is polished
Cleaning paper is used to carry out clean wiping afterwards；Glass sheet surface is carried out for 5% hydrochloric acid using Solute mass percentage after wiping
Processing, the Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 6-18 milliliters；Back glass sheet surface is cleaned to use
New cleaning paper carries out clean wiping.
5. hydrophobic method according to claim 1, which is characterized in that in the step 2), use Solute mass percentage
Pickling processes at least twice are carried out to glass for 5% hydrochloric acid, stand 1-5 minutes；The Solute mass percentage is 5% hydrochloric acid
Dosage is every square metre 20-45 milliliters；After standing clean wiping is carried out using cleaning paper；After wiping, deionized water pair is used
Glass sheet surface is handled；After processing, clean wiping is carried out using new cleaning paper.
6. hydrophobic method according to claim 1, which is characterized in that in the step 3), the first time hydrophobic processing
The dosage of hydrophober be every square metre 6-15 milliliter, the speed of hydrophobic processing is 0.15-0.6 meters per second, wipes number 2-8
It is secondary；In hydrophobic after treatment, clean wiping is carried out to glass sheet surface using cleaning paper.
7. hydrophobic method according to claim 1, which is characterized in that in the step 4), second of hydrophobic processing
The dosage of hydrophober be every square metre 8-15 milliliter, the speed of hydrophobic processing is 0.15-0.6 meters per second, wipes number 6-11
It is secondary；In hydrophobic after treatment, clean wiping is carried out to glass sheet surface using cleaning paper.
8. hydrophobic method according to claim 1, which is characterized in that described to specifically include following steps：
Step 1 is polished glass sheet surface；
A, sheet glass is positioned；
B, the sheet glass that a has good positioning is polished, is at least carried out twice；It is felt polishing bob used in the polishing, it is described
Polishing fluid is used on felt polishing bob, the dosage of the polishing fluid is every square metre 10-35 milliliters；The time of polishing is every square metre
50-200 seconds；The felt polishing bob needs replacing new felt polishing bob after polishing 10 square metres；The polishing hair more renewed
The polishing fluid of additional 8-15 milliliters of addition is needed when felt, when being polished for the first time；
C, the glass sheet surface obtained by b is subjected to clean wiping using cleaning paper；
D, the use of Solute mass percentage is that 5% hydrochloric acid handles glass sheet surface by the glass sheet surface obtained by c, it is described
Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 6-18 milliliters；
E, the glass sheet surface obtained by d is subjected to clean wiping using new cleaning paper；
Step 2 carries out surface acid-washing to the glass obtained by step 1；
F, the use of Solute mass percentage is that 5% hydrochloric acid carries out at pickling at least twice glass by the glass sheet surface obtained by e
Reason stands 1-5 minutes；The Solute mass percentage is that the dosage of 5% hydrochloric acid is every square metre of 20-45 milliliters；
G, the glass sheet surface obtained by f is subjected to clean wiping using cleaning paper；
H, the glass sheet surface obtained by g is handled glass sheet surface using deionized water；
I, by the glass sheet surface obtained by h, clean wiping is carried out using new cleaning paper；
Step 3 carries out the glass obtained by step 2 processing of surface first time hydrophobic；
J, the glass sheet surface obtained by i is subjected to first time hydrophobic processing, the dosage of the hydrophober of the first time hydrophobic processing
It it is every square metre of 6-15 milliliters, the speed of hydrophobic processing is 0.15-0.6 meters per second, wiping number 2-8 times；
K, by the glass sheet surface obtained by j, clean wiping is carried out to glass sheet surface using cleaning paper；
Step 4 carries out the glass obtained by step 3 second of the hydrophobic processing in surface；
L, by the glass sheet surface obtained by k, second of hydrophobic processing, the dosage of the hydrophober of second of hydrophobic processing are carried out
It it is every square metre of 8-15 milliliters, the speed of hydrophobic processing is 0.15-0.6 meters per second, wiping number 6-11 times；
M, by the glass sheet surface obtained by l, in hydrophobic after treatment, wipe clean is carried out to glass sheet surface using cleaning paper
It wipes.