CN108390327A - A kind of FRPVC co-extrusions electric power protecting pipe - Google Patents
A kind of FRPVC co-extrusions electric power protecting pipe Download PDFInfo
- Publication number
- CN108390327A CN108390327A CN201810195663.1A CN201810195663A CN108390327A CN 108390327 A CN108390327 A CN 108390327A CN 201810195663 A CN201810195663 A CN 201810195663A CN 108390327 A CN108390327 A CN 108390327A
- Authority
- CN
- China
- Prior art keywords
- electric power
- stabilizer
- protecting pipe
- power protecting
- frpvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of FRPVC co-extrusions electric power protecting pipes, the electric power protecting pipe is using the first mixed raw material as inside and outside two layers, using made of prilling, contain the second mixing granulation of glass fibre as the interlayer between inside and outside two layers, be made through coextrusion mold.The interlayer of second mixing granulation is clipped in inside and outside two interlayer of the first mixed raw material by the present invention by way of coextrusion mold, avoids the second mixing granulation and its glass fibre is exposed outside, to improve pipe bonding ability.
Description
Technical field
The present invention relates to electric power protecting pipe field, specifically a kind of FRPVC co-extrusions electric power protecting pipe.
Background technology
Conventional electric power protecting pipe is mostly fiberglass, CPVC, MPP material electric power protecting pipe, although this fiberglass, CPVC
Electric power protecting pipe has preferable flame retardant property, and fiberglass electric power protecting pipe has good ring stiffness, still, first, glass
Fiberglass on steel electric power protecting pipe is unfavorable for recycling, and pollutes environment, and the production cost of CPVC, MPP electric power protecting pipe is high;Its
Two, the fiberglass open ground of traditional fiberglass electric power protecting pipe is arranged on the periphery of entire protecting pipe, influences fiberglass electricity
The bonding of power protecting pipe.
Invention content
It is an object of the invention to:In view of the above shortcomings of the prior art, a kind of general by way of coextrusion mold is provided
The interlayer of second mixing granulation is clipped in inside and outside two interlayer of the first mixed raw material, avoids the second mixing granulation and its glass fibers
Tie up it is exposed outside, to improve the FRPVC co-extrusion electric power protecting pipes of pipe bonding ability.It not only increases protecting pipe
Ring stiffness is high, has flame retardant property, product cost low, but also can recycle, environmental protection.
The technical solution adopted by the present invention is a kind of FRPVC co-extrusions electric power protecting pipe, and the electric power protecting pipe is mixed with first
Close raw material as inside and outside two layers, using made of prilling, contain the second mixing granulation of glass fibre as inside and outside two
Interlayer between layer is made through coextrusion mold.
Described inside and outside two layers and it is two layers inside and outside between interlayer pass through the common extrusion molding of extruder, wherein one squeeze
Go out machine to squeeze out inside and outside two layers using the first mixed raw material, another extruder squeezes out interlayer using the second mixing granulation.
Preferably, the extruder is cone double screw extruder.
First mixed raw material is made of dual-screw pelletizer.
Second mixing granulation of the prilling manufacture is made of dual-screw pelletizer.
First mixed raw material is made of following materials in percentage by mass:
Preferably, the stabilizer of first mixed raw material selects lead salt stabilizer, metal soap stabilizer, organotin steady
Determine at least one of agent, organic antimony stabilizer, rare-earth stabilizer, phosphite, epoxy type stabilizers.
Second mixing granulation is made of following materials in percentage by mass:
Preferably, the stabilizer of second mixing granulation selects lead salt stabilizer, metal soap stabilizer, organotin steady
Determine at least one of agent, organic antimony stabilizer, rare-earth stabilizer, phosphite, epoxy type stabilizers.
The beneficial effects of the invention are as follows:
1. the interlayer of the second mixing granulation is clipped in the inside and outside of the first mixed raw material by the present invention by way of coextrusion mold
Two interlayers, avoid the second mixing granulation and its glass fibre is exposed outside, to improve pipe bonding ability.
2. in the present invention, by adding the interlayer of the second mixing granulation, not only increasing the ring stiffness of protecting pipe, there is resistance
It is low to fire performance, product cost, but also can recycle, environmental protection.
Description of the drawings
The present invention will be further described below with reference to the drawings.
Fig. 1 is the sectional view of the present invention.
Code name meaning in figure:1-internal layer;2-outer layers;3-interlayers.
Specific implementation mode
It is shown in Figure 1:The present invention is a kind of FRPVC co-extrusions electric power protecting pipe, and the electric power protecting pipe is with the first mixing
Raw material is as inside and outside two layers (referring to internal layer 1 and outer layer 2, similarly hereinafter), using second made of prilling, containing glass fibre
Mixing granulation is made as the interlayer 3 between inside and outside two layers through coextrusion mold.
Now the content of present invention is described further in conjunction with multiple embodiments in the form of a list.
The first mixed raw material formula of the present invention is shown in Table 1.
Proportioning result (the unit of eight preferred embodiments of the invention of table 1:Mass percent)
The second mixing granulation formula of the present invention is shown in Table 2.
Proportioning result (the unit of eight preferred embodiments of the invention of table 2:Mass percent)
Above-mentioned inside and outside two layers and it is two layers inside and outside between interlayer 3 pass through the common extrusion molding of extruder, wherein one squeeze
Go out machine to squeeze out inside and outside two layers using the first mixed raw material, another extruder squeezes out interlayer 3 using the second mixing granulation.Wherein,
Preferably, extruder is cone double screw extruder.
In addition, first mixed raw material is made of dual-screw pelletizer;Second mixing of the prilling manufacture is made
Grain is made of dual-screw pelletizer.
In table 1 above, the stabilizer of first mixed raw material is selected lead salt stabilizer, metal soap stabilizer, is had
At least one of machine tin stabilizer, organic antimony stabilizer, rare-earth stabilizer, phosphite, epoxy type stabilizers.
In above-mentioned table 2, the stabilizer of second mixing granulation is selected lead salt stabilizer, metal soap stabilizer, is had
At least one of machine tin stabilizer, organic antimony stabilizer, rare-earth stabilizer, phosphite, epoxy type stabilizers.
Above-mentioned pigment is organic and/or inorganic pigment, requires to adjust according to the color of practical electric power protecting pipe.
The preparation method of the FRPVC co-extrusion electric power protecting pipes of the various embodiments described above, by following steps:
Step 1) is respectively configured by dual-screw pelletizer according to the formula ratio in Tables 1 and 2, squeezes out the first mixing original
Material and the second mixing granulation, and second mixing granulation meets prilling;
Step 2) is according to construction requirement, and for the first mixed raw material that step 1) is configured as inside and outside two layers, second is mixed
It closes and is granulated as the interlayer 3 between inside and outside two layers, the interlayer 3 between this inside and outside two layers and this inside and outside two layers passes through two
The common extrusion molding of double screw extruder is bored, electric power protecting pipe is obtained.
With 2 times of the ring stiffness of the about general pvc pipe of the ring stiffness of this obtained electric power protecting pipe.
The present invention replaces fiberglass, CPVC, MPP electric power protecting pipe by FRPVC co-extrusion electric power protecting pipes, not only has glass
The anti-flammability of glass steel and CPVC electric power protecting pipes, the ring stiffness with higher fiberglass electric power protecting pipe, and solve glass
Pollution problem of the glass steel electric power protecting pipe to environment makes the present invention not only with very high ring stiffness, with flame retardant property, product
It is at low cost, but also can recycle, environmental protection.The present invention squeezes out the first mixed raw material and the by dual-screw pelletizer
Two mixing granulations avoid traditional glass steel electric power protecting pipe and pass through the remaining waste silk process problem of fiberglass woven cloth.It is this
It is added to glass fibre in protecting pipe, increases the ability for bearing pressure in tube body, the row's of can also be used as water supply is effective.
The technical solution of the above various embodiments is only to illustrate the present invention, rather than its limitations.Although with reference to aforementioned each reality
Applying the technical solution of example, invention is explained in detail, it will be understood by those of ordinary skill in the art that:It still may be used
To modify to preceding solution or equivalent replacement of some of the technical features;And these are changed or replace
It changes, the spirit and scope of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (9)
1. a kind of FRPVC co-extrusions electric power protecting pipe, it is characterised in that:The electric power protecting pipe using the first mixed raw material as in,
Outer two layers, using made of prilling, contain the second mixing granulation of glass fibre as the interlayer between inside and outside two layers,
It is made through coextrusion mold.
2. FRPVC co-extrusions electric power protecting pipe according to claim 1, it is characterised in that:Described inside and outside two layers and inside and outside two
Interlayer between layer passes through the common extrusion molding of extruder, wherein an extruder squeezes out inside and outside two using the first mixed raw material
Layer, another extruder squeeze out interlayer using the second mixing granulation.
3. FRPVC co-extrusions electric power protecting pipe according to claim 2, it is characterised in that:The extruder is that cone twin-screw squeezes
Go out machine.
4. FRPVC co-extrusions electric power protecting pipe according to claim 1, it is characterised in that:First mixed raw material is by double spiral shells
Bar comminutor is made.
5. FRPVC co-extrusions electric power protecting pipe according to claim 1, it is characterised in that:The second of the prilling manufacture
Mixing granulation is made of dual-screw pelletizer.
6. FRPVC co-extrusions electric power protecting pipe according to claim 1, it is characterised in that:First mixed raw material is by as follows
Materials in percentage by mass forms:
Polyvinyl chloride resin 60~90%,
Dibutyl ester 3~6%,
Stabilizer 2~3%,
Stearic acid 0.1~1%,
Paraffin 0.5~1%,
MBS 1.5~4.5%,
Calcium carbonate 0~30%,
Pigment 0.5~1.5%.
7. FRPVC co-extrusions electric power protecting pipe according to claim 6, it is characterised in that:The stabilization of first mixed raw material
Lead salt stabilizer, metal soap stabilizer, organic tin stabilizer, organic antimony stabilizer, rare-earth stabilizer, phosphorous acid are selected in agent
At least one of salt, epoxy type stabilizers.
8. FRPVC co-extrusions electric power protecting pipe according to claim 1, it is characterised in that:Second mixing granulation is by as follows
Materials in percentage by mass forms:
Polyvinyl chloride resin 60~80%,
Dibutyl ester 3~6%,
Stabilizer 2~3%,
Stearic acid 0.1~1%,
Paraffin 0.5~1%,
MBS 1.5~4.5%,
Calcium carbonate 0~20%,
Glass fibre 10~30%,
Pigment 0.5~1.5%.
9. FRPVC co-extrusions electric power protecting pipe according to claim 8, it is characterised in that:The stabilization of second mixing granulation
Lead salt stabilizer, metal soap stabilizer, organic tin stabilizer, organic antimony stabilizer, rare-earth stabilizer, phosphorous acid are selected in agent
At least one of salt, epoxy type stabilizers.