CN108374302A - A kind of discontinuous construction method of chromogen bonded polymer Lamina - Google Patents
A kind of discontinuous construction method of chromogen bonded polymer Lamina Download PDFInfo
- Publication number
- CN108374302A CN108374302A CN201810195468.9A CN201810195468A CN108374302A CN 108374302 A CN108374302 A CN 108374302A CN 201810195468 A CN201810195468 A CN 201810195468A CN 108374302 A CN108374302 A CN 108374302A
- Authority
- CN
- China
- Prior art keywords
- bonded polymer
- chromogen bonded
- parts
- component
- polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention proposes a kind of discontinuous construction method of chromogen bonded polymer Lamina, including 1) chromogen bonded polymer prepares;2) priming coat is constructed:Levelling on former base layer, former base layer is one or more in bituminous concrete, cement concrete pavement or steel bridge deck;3) plate is put:The region that will have the template for hollowing out pattern to be placed on pre- construction sprays the chromogen bonded polymer to area of knockout;4) construction of different colours:It takes model off, the color polymer object area that coats done is enclosed with paper matrix and to carry out construction of the pattern with exterior domain with the chromogen bonded polymer of different colours;5) finishing coat is constructed.Chromogen bonded polymer Lamina made from construction technology of the present invention, construction technology is simple, fast, while bringing bright color and pattern to road surface, can play antiskid, wear-resisting, warning function.
Description
Technical field
The invention belongs to technical field of road construction, and in particular to a kind of construction method of chromogen bonded polymer Lamina.
Background technology
Colored road surface is gradually paid attention to by people in recent years, as a kind of novel pavement material, changes conventional pav
Non- black i.e. white dull color acts not only as mark graticule and plays a warning role, can also beautify the environment, road is made to become
City with during the journey together with beautiful scenery.The various patterns made of colored road surface material have just had both mark and decoration is made
With.
But the material of existing colored road surface pattern often uses the mixed of color asphalt or pigment and high molecular polymer
It closes object to construct, such as 102120916 A of patent CN propose a kind of macromolecular colored road surface anti-skid coating, by star-shaped sbs are changed
Property agent, KOH, color pigment, titanium dioxide, color aggregate, accelerating agent, stabilizer, light colour emulsified asphalt, water composition;Such group
Conjunction object color is not bright-coloured enough and does not have water permeability.
Invention content
Place for overcome the deficiencies in the prior art, the object of the present invention is to provide a kind of chromogen bonded polymer Lamina is non-
Continuous construction method, it is simple and fast, it is easy to operate, and round point shape or cotton-shaped paint are provided while enriching pattern, it can be more preferable
Offer it is anti-skidding, wear-resisting, the function of warning, not road surface whole three-dimensional moulding is presented, keep its more attractive.
Realize that the technical solution of the object of the invention is:
A kind of discontinuous construction method of chromogen bonded polymer Lamina, includes the following steps:
1) chromogen bonded polymer prepares:Chromogen bonded polymer is made of component A, B component, component C, the component A contain resin,
Anti- precipitation aid, pigment, filler, ultra-violet stabilizer, accelerating agent and polymerization inhibitor;The B component contains resin, anti-precipitation helps
Agent, 5~15 portions of pigment, filler, ultra-violet stabilizers;The component C is curing agent;
2) priming coat is constructed:Levelling on former base layer, former base layer is bituminous concrete, cement concrete pavement or Steel Bridge Deck
It is one or more in layer;
3) plate is put:The region that will have the template for hollowing out pattern to be placed on pre- construction sprays the color polymer to area of knockout
Object;
4) construction of different colours:It takes model off, the color polymer object area that coats done is enclosed with paper matrix come use
The chromogen bonded polymer of different colours carries out pattern with the construction of exterior domain;
5) finishing coat is constructed:After the chromogen bonded polymer sprayed twice cures, then in whole face layers cover is carried out, it is described
The material of finishing coat contains resin, anti-precipitation aid, filler, ultra-violet stabilizer, accelerating agent and polymerization inhibitor;The component C is
Curing agent.
Further, in step 1), the component A contains the ingredient of following mass parts:40~60 parts of resins, 1~3 part anti-
Precipitation aid, 5~15 parts of pigment, 40~70 parts of fillers, 0.4~1 portion of ultra-violet stabilizer, 0.5~1.5 part of accelerating agent, 0.005
~0.007 part of polymerization inhibitor;The B component contains the ingredient of following mass parts:40~60 parts of resins, 1~3 part of anti-precipitation aid, 5
~15 parts of pigment, 40~100 parts of fillers, 0.5~1 portion of ultra-violet stabilizer.
Wherein, the curing agent is dibenzoyl peroxide, and the component A, B component, the proportioning of component C are 100:95~
100:1~3.
Wherein, the ultra-violet stabilizer is Benzotriazole Ultraviolet Stabilizer and hindered amine light stabilizer, the two
Mass ratio is 1:0.6~1.5, the accelerant N, N- dimethyl-p-toluidines;To be modified fumed silica as anti-precipitation
Auxiliary agent;The polymerization inhibitor is ZJ701.
Wherein, the resin is one kind in methacrylic resin, epoxylite, waterborne polyurethane resin.
Wherein, the pigment is inorganic pigment, in oxide, plumbite, cadmate, aluminate, ultramarine, molybdate red
It is one or more.
Preferably, the chromogen bonded polymer thickness of thin layer of the priming coat spraying is 1~2mm.
It is highly preferred that in step 3), with spraying equipment, the chromogen bonded polymer is sprayed into continuous or discontinuous circle
Spot or cotton-shaped polymer fiber.
Wherein, in step 5), the material of the finishing coat contains the ingredient of following mass parts:40~60 parts of resins, 1~3
The anti-precipitation aid of part, 40~100 parts of fillers, 0.4~1 portion of ultra-violet stabilizer, 0.5~1.5 part of accelerating agent, 0.005~0.007
Part polymerization inhibitor.
The beneficial effects of the present invention are:
Construction method proposed by the present invention is basic polymer, the painting after solidification with heat cured methacrylic resin
Layer has excellent mechanical strength and toughness, and with the adhesive force of pitch or cement pavement height, wearability is good, and surface permanent is constant
Color.
Chromogen bonded polymer Lamina made from construction technology of the present invention is being sent out based on the coating composition formula optimized
Construction is simple is quick while waving bright color function, easy to operate, and the diversification of pattern model may be implemented complex pattern and apply
Work;And round point shape or cotton-shaped paint are provided while enriching pattern, can preferably provide anti-skidding, wear-resisting, the function of warning.
Specific implementation mode
The content that following embodiment further illustrates the present invention, but should not be construed as limiting the invention.
The Optimum Experiment of 1 pigment of embodiment
The adding proportion of pigment influences the appearance of pavement construction in component A, need to compare and optimize by experiment.It is existing
Some color asphalts, including decoloration pitch (no bleaching is black) or polymer two major classes, this technology be with fluoropolymer resin
The basic ingredient of color asphalt, pigment additive amount should suitably, and specific experiment is as follows.
It is basic formulation selection pigment with component A:
By 50 parts of commercially available waterborne polyurethane resins and 2 parts of modified fumed silica antisettling agents, high speed dispersion is extremely
It is sticky, 50 parts of filler blanc fixes (6000 mesh), 0.3 part of UV327,0.3 part of GW508 (benzotriazole purple are added into system
Ultraviolet absorbers and hindered amine light stabilizer), 1.2 parts of accelerant Ns, N- dimethyl-p-toluidines and 0.006 part of polymerization inhibitor
ZJ701, high speed dispersion are uniform.
It pours into horizontal sand mill and is ground to 100 microns of fineness hereinafter, discharging after filtering.Color is set as yellow, compares oxidation
The price of iron oxide yellow and chrome yellow, 11000 yuan/ton or so of iron oxide yellow average price, chrome yellow exist according to its purity difference average price in the market
26000 yuan/ton or so.Selective oxidation iron oxide yellow is constructed.It is 100 by basic components material gross weight, is separately added into 0,3,5,10,15
The pigment of part, and in high-speed shearing machine down cut 5min, the chromogen bonded polymer slurry being allocated as under five kinds of pigment volumes, same
The picture for acquiring five kinds of colored rubber cements under illumination with digital camera, opens in Adobe Photoshop softwares, utilizes image work
Mode setting is Lab color modes by tool, reads L, a, b value (table 1) of picture, by analyze colored rubber cement Lab values and
The aberration of the colored rubber cement of adjacent pigment volume, to obtain best amount of pigment.
Table 1:Influence of the pigment volume to color under Lab patterns
Volume (part) | L | a | b | Aberration △ E |
0 | 25 | 0 | 17 | -- |
3 | 22 | 7 | 59 | 3.14 |
5 | 20.5 | 8 | 61 | 5.01 |
10 | 19.1 | 15 | 66 | 4.66 |
15 | 17.25 | 14 | 68 | 4.14 |
With the increase of iron oxide yellow volume, the color of colored rubber cement is gradually deepened, i.e. L values are gradually reduced, and a and b values by
Cumulative big, i.e., saturation degree increases.But with the gradual increase of volume, the aberration Δ E values between neighboring samples are gradually reduced, i.e. color
Change it is smaller and smaller, accordingly, it is considered to arrive the various reasons of economic dispatch, basic components and pigment 100:5~10 is suitable for admixtures
Ratio.
Embodiment 2
1) chromogen bonded polymer is prepared
Component A:By 55 parts of methacrylic resins and 2 parts of modified fumed silica antisettling agent high speed dispersions to viscous
It is thick, 5 parts of iron oxide yellows, 40 parts of ultra-fine barium sulfate powder (6000 mesh), 0.3 part of UV327,0.2 part of GW508,1.2 are added into system
Part N, N- dimethyl-p-toluidines and 0.006 part of ZJ701, high speed dispersion are uniform.Pouring into horizontal sand mill, to be ground to fineness 100 micro-
Rice after filtering hereinafter, discharge.
B component:By 55 parts of methacrylic resins and 2 parts of modified fumed silica antisettling agent high speed dispersions to viscous
It is thick;6 parts of iron oxide yellows, 40 parts of ultra-fine barium sulfate powder (6000 mesh), 0.2 part of UV327,0.3 part of GW508 are added into system, it is high
Speed is uniformly dispersed;It pours into horizontal sand mill and is ground to 100 microns of fineness hereinafter, discharging after filtering.
Component C direct packaging crosses the dibenzoyl peroxide (Perkadox CH-50X) after dilution.
Pigment is changed to iron oxide red, red chromogen bonded polymer is made in same method.
2) priming coat is constructed:Levelling in base based on former road surface, former road surface is bituminous concrete;
3) plate is put:The region that will have the template for hollowing out pattern of bicycle shape to be placed on pre- construction is sprayed to area of knockout
The chromogen bonded polymer of yellow carries out the construction of coloured coating;The nozzle of the equipment of spraying is round hole, sprays on ground and is formed
The garden spot of discontinuous one by one, diameter about 1cm, thickness are 1~2mm, this layer pattern layer has water permeability.
4) construction of different colours:It takes model off, the color polymer object area that coats done is enclosed with paper matrix come use
Red chromogen bonded polymer carries out pattern with the construction of exterior domain;
5) finishing coat is constructed:After the chromogen bonded polymer sprayed twice cures, then in whole face layers cover is carried out,
It is transparent material, keeps it vivider, it is more smooth.The material of the finishing coat contains the ingredient of following mass parts:50 parts of methyl
Acrylic resin, 3 parts of anti-precipitation aids, 50 parts of fillers, 0.6 portion of ultra-violet stabilizer, 1 part of accelerating agent, 0.006 part of polymerization inhibitor;
The component C is curing agent.The thickness of finishing coat is 1~2mm.
Embodiment 3
1) chromogen bonded polymer is prepared
Component A:Waterborne polyurethane resin prepared by 55 parts of embodiments 1 and 2 parts of anti-precipitations of modified fumed silica
Agent high speed dispersion to sticky, be added into system 5 parts of iron oxide yellows, 40 parts of ultra-fine barium sulfate powder (6000 mesh), 0.3 part of UV327,
0.2 part of GW508,1.2 parts of N, N- dimethyl-p-toluidines and 0.006 part of ZJ701, high speed dispersion are uniform.Pour into horizontal sand mill
100 microns of fineness is ground to hereinafter, discharging after filtering.
B component:Extremely by 55 parts of aqueous polyurethane tree resins and 2 parts of modified fumed silica antisettling agent high speed dispersions
It is sticky;6 parts of iron oxide yellows, 40 parts of ultra-fine barium sulfate powder (6000 mesh), 0.2 part of UV327,0.3 part of GW508 are added into system,
High speed dispersion is uniform;It pours into horizontal sand mill and is ground to 100 microns of fineness hereinafter, discharging after filtering.
Component C direct packaging crosses the dibenzoyl peroxide (Perkadox CH-50X) after dilution.
2) priming coat is constructed:Levelling in base based on former road surface, former road surface is cement concrete pavement;
In step 3), the nozzle of the equipment of spraying is multiple micropores, sprays to one fleece of upper formation after ground, paint solidification
Shape fibrous layer has porous structure, can keep water permeability.
5) finishing coat is constructed:After the chromogen bonded polymer sprayed twice cures, then in whole face layers cover is carried out,
It is transparent material, keeps it vivider, it is more smooth.The material of the finishing coat contains the ingredient of following mass parts:60 parts aqueous
Polyurethane resin, 2 parts of anti-precipitation aids, 40 parts of fillers, 0.6 portion of ultra-violet stabilizer, 1 part of accelerating agent, 0.005 part of polymerization inhibitor;
The component C is curing agent.The thickness of finishing coat is 1~2mm.
Other operations are the same as embodiment 2.
Obtained chromogen bonded polymer Lamina is connected smooth-going with other structures, pollution-free;Surfacing, closely knit, nothing
Bellding, loose, crack and apparent segregation phenomenon;Multicolour pattern appearance luster uniformity, without apparent aberration;Construction Joint is tight
Close, smooth-going.
Embodiment 4
1) chromogen bonded polymer is prepared
Component A:Epoxy resin prepared by 55 parts of embodiments 1 and 2 parts of modified fumed silica antisettling agent high speeds
Be dispersed to it is sticky, into system be added 10 parts of titanium dioxide, 40 parts of ultra-fine barium sulfate powder (6000 mesh), 0.3 part of UV327,0.2 part
GW508,1.2 parts of N, N- dimethyl-p-toluidines and 0.006 part of ZJ701, high speed dispersion are uniform.Horizontal sand mill is poured into be ground to
100 microns of fineness after filtering hereinafter, discharge.
B component:By 55 parts of epoxy resin and 2 parts of modified fumed silica antisettling agent high speed dispersions to sticky;To
10 parts of titanium dioxide, 40 parts of ultra-fine barium sulfate powder (6000 mesh), 0.2 part of UV327,0.3 part of GW508, high speed point are added in system
It dissipates uniform;It pours into horizontal sand mill and is ground to 100 microns of fineness hereinafter, discharging after filtering.
Component C direct packaging crosses the dibenzoyl peroxide (Perkadox CH-50X) after dilution.
Pigment is changed to 5 parts of iron oxide yellow, the chromogen bonded polymer of yellow is made in same method.
2) priming coat is constructed:It is levelling in base based on raw steel bridge floor, as priming coat;
3) plate is put:The region that will there is the template for hollowing out pattern of word and numerical switch to be placed on pre- construction, to area of knockout
The chromogen bonded polymer of spraying white carries out the construction of coloured coating;The nozzle of the equipment of spraying is multiple micropores, sprays to ground
Upper to form cotton-shaped polymer fibres layers, macro-effect is the word or number of white, and coloured coating thickness is 1~2mm, and color
Color coating has pervious function.
4) construction of different colours:It takes model off, the color polymer object area that coats done is enclosed with paper matrix come use
The chromogen bonded polymer of yellow carries out pattern with the construction of exterior domain;
5) finishing coat is constructed:After the chromogen bonded polymer sprayed twice cures, then in whole face layers cover is carried out,
It is transparent material, keeps it vivider, it is more smooth.The material of the finishing coat contains the ingredient of following mass parts:50 parts of epoxies
Resin, 3 parts of anti-precipitation aids, 50 parts of fillers, 0.6 portion of ultra-violet stabilizer, 1 part of accelerating agent, 0.006 part of polymerization inhibitor;The C groups
It is divided into curing agent.The thickness of finishing coat is 1~2mm.
Although above having used general explanation, specific implementation mode and example, the present invention is made to retouch in detail
It states, but on the basis of the present invention, certain supplement and optimization can be made to the discrimination model of this method.Therefore, without departing from
These modifications or improvements on the basis of spirit of that invention, belong to the scope of protection of present invention.
Claims (9)
1. a kind of discontinuous construction method of chromogen bonded polymer Lamina, which is characterized in that include the following steps:
1) chromogen bonded polymer prepares:Chromogen bonded polymer is made of component A, B component, component C, and the component A contains resin, anti-settling
Shallow lake auxiliary agent, pigment, filler, ultra-violet stabilizer, accelerating agent and polymerization inhibitor;The B component contain resin, anti-precipitation aid, 5~
15 portions of pigment, filler, ultra-violet stabilizers;The component C is curing agent;
2) priming coat is constructed:Levelling on former base layer, former base layer is in bituminous concrete, cement concrete pavement or Steel Bridge Deck layer
It is one or more;
3) plate is put:The region that will have the template for hollowing out pattern to be placed on pre- construction sprays the chromogen bonded polymer to area of knockout;
4) construction of different colours:It takes model off, the color polymer object area that coats done is enclosed with paper matrix come with difference
The chromogen bonded polymer of color carries out pattern with the construction of exterior domain;
5) finishing coat is constructed:After the chromogen bonded polymer sprayed twice cures, then in whole face layer progress covers, the cover
The material of layer contains resin, anti-precipitation aid, filler, ultra-violet stabilizer, accelerating agent and polymerization inhibitor;The component C is solidification
Agent.
2. the discontinuous construction method of chromogen bonded polymer Lamina according to claim 1, which is characterized in that step 1)
In, the component A contains the ingredient of following mass parts:40~60 parts of resins, 1~3 part of anti-precipitation aid, 5~15 parts of pigment, 40
~70 parts of fillers, 0.4~1 portion of ultra-violet stabilizer, 0.5~1.5 part of accelerating agent, 0.005~0.007 part of polymerization inhibitor;The B groups
Divide the ingredient containing following mass parts:40~60 parts of resins, 1~3 part of anti-precipitation aid, 5~15 parts of pigment, 40~100 parts fill out
Material, 0.5~1 portion of ultra-violet stabilizer.
3. the discontinuous construction method of chromogen bonded polymer Lamina according to claim 1, which is characterized in that the solidification
Agent is dibenzoyl peroxide, and the component A, B component, the proportioning of component C are 100:95~100:1~3.
4. the discontinuous construction method of chromogen bonded polymer Lamina according to claim 1, which is characterized in that described ultraviolet
Line stabilizer is Benzotriazole Ultraviolet Stabilizer and hindered amine light stabilizer, and the two mass ratio is 1:0.6~1.5, institute
State accelerant N, N- dimethyl-p-toluidines;To be modified fumed silica as anti-precipitation aid;The polymerization inhibitor is
ZJ701。
5. the discontinuous construction method of chromogen bonded polymer Lamina according to claim 1, which is characterized in that the resin
For one kind in methacrylic resin, epoxylite, waterborne polyurethane resin.
6. the discontinuous construction method of chromogen bonded polymer Lamina according to claim 1, which is characterized in that the pigment
It is one or more in oxide, plumbite, cadmate, aluminate, ultramarine, molybdate red for inorganic pigment.
7. according to the discontinuous construction method of Claims 1 to 5 any one of them chromogen bonded polymer Lamina, feature exists
In the chromogen bonded polymer thickness of thin layer of the priming coat spraying is 1~2mm.
8. colour road surface structure according to claim 1, which is characterized in that in step 3), with spraying equipment, by the coloured silk
Color polymer is sprayed into continuous or discontinuous round spot or cotton-shaped polymer fiber.
9. colour road surface structure according to claim 1, which is characterized in that in step 5), the material of the finishing coat contains
There is the ingredient of following mass parts:40~60 parts of resins, 1~3 part of anti-precipitation aid, 40~100 parts of fillers, 0.4~1 part of ultraviolet light
Stabilizer, 0.5~1.5 part of accelerating agent, 0.005~0.007 part of polymerization inhibitor.