CN108373710A - A kind of preparation method substituting overlay film water-based gloss oil - Google Patents
A kind of preparation method substituting overlay film water-based gloss oil Download PDFInfo
- Publication number
- CN108373710A CN108373710A CN201611027504.8A CN201611027504A CN108373710A CN 108373710 A CN108373710 A CN 108373710A CN 201611027504 A CN201611027504 A CN 201611027504A CN 108373710 A CN108373710 A CN 108373710A
- Authority
- CN
- China
- Prior art keywords
- water
- liquid
- overlay film
- gloss oil
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods substituting overlay film water-based gloss oil; raw material stirring is added; material is warming up under nitrogen protection all to melt as liquid; slowly heating up; insulation reaction is completed to water outlet is preliminary; material all melts to be completed to be to slowly warm up to reaction to water outlet after liquid, and stirring keeps the various stock dispersions of system uniform.Beneficial effects of the present invention：It makes simply, it is convenient, it is coated on paper packaging box surface, the waterproof layer that a scratch-resistant can be formed makes paper packaging box have water-proof function, instead of plastic film used in traditional technology, production cost is reduced, glazing is preprinted suitable for packing cases such as various beer, fruits and vegetables.
Description
Technical field
The present invention relates to a kind of water-based gloss oil, more particularly to a kind of preparation method substituting overlay film water-based gloss oil.
Background technology
Since the 1980s, with opening and commodity economy fast development, printing product it is increasingly superior,
Colorization and diversification, various glazing technologies obtain rapid development, and glazing processing becomes increasingly popular, at present on country's printed matter
The year application amount of optical coating (oil polish) alreadys exceed ten thousand tons, it has also become prints a key areas of post-processing.Early stage it is upper
Optical coating less varieties, technique are simple and crude.Nowadays glazing paint has formed diversified, multi items series of products, is broadly divided into molten
Dosage form oil polish, oiliness oil polish, UV oil polishes and deionization water lustering oil.
Invention content
It is an object of the invention to overcome the above-mentioned deficiency in the presence of the prior art, provide a kind of replacement overlay film aqueous light
The preparation method of oil.
In order to achieve the above-mentioned object of the invention, the present invention provides following technical schemes：
A kind of preparation method substituting overlay film water-based gloss oil, first by acrylate copolymer, titanium dioxide, huge sum of money mountain flour, heavy carbon
Suitable quantity of water is added after sour calcium, kaolin and water soluble acrylic resin's mixing, then slowly sequentially adds wax breast while stirring
Liquid, neutralizer be, wetting dispersing agent, thickener, biocide mildewcide and remaining water, and 60-80 °C of guarantor is warming up under nitrogen protection
Temperature is all melted to material as liquid, is being to slowly warm up to 80-100 DEG C or so, insulation reaction to be discharged it is preliminary complete, material is whole
Melt and completed to be to slowly warm up to 110-150 DEG C or so reaction to water outlet after liquid, in the state that rotating speed is 800-1200 revs/min
Stirring 10-20 minutes, keeps the various stock dispersions of system uniform.
Compared with prior art, beneficial effects of the present invention：It makes simply, it is convenient, it is coated on paper packaging box surface, it can
The waterproof layer for forming a scratch-resistant makes paper packaging box have water-proof function, instead of plastic film used in traditional technology,
Production cost is reduced, glazing is preprinted suitable for packing cases such as various beer, fruits and vegetables.
Specific implementation mode
With reference to test example and specific implementation mode, the present invention is described in further detail.But this should not be understood
It is only limitted to embodiment below for the range of the above-mentioned theme of the present invention, it is all that this is belonged to based on the technology that the content of present invention is realized
The range of invention.
Embodiment 1：A kind of preparation method substituting overlay film water-based gloss oil, first by acrylate copolymer, titanium dioxide, a huge sum of money
Mountain flour, powdered whiting, kaolin and water soluble acrylic resin mixing after suitable quantity of water is added, then while stirring slowly according to
Secondary addition wax emulsion, neutralizer be, wetting dispersing agent, thickener, biocide mildewcide and remaining water, is warming up under nitrogen protection
60 DEG C of heat preservations are all melted to material as liquid, are being to slowly warm up to 80 DEG C or so, insulation reaction to be discharged it is preliminary complete, material is complete
Portion melts to complete to be to slowly warm up to 110 DEG C or so reactions to water outlet after liquid, and 10 are stirred in the state that rotating speed is 800 revs/min
Minute, keep the various stock dispersions of system uniform.
Embodiment 2：A kind of preparation method substituting overlay film water-based gloss oil, first by acrylate copolymer, titanium dioxide, a huge sum of money
Mountain flour, powdered whiting, kaolin and water soluble acrylic resin mixing after suitable quantity of water is added, then while stirring slowly according to
Secondary addition wax emulsion, neutralizer be, wetting dispersing agent, thickener, biocide mildewcide and remaining water, is warming up under nitrogen protection
70 °C of heat preservations are all melted to material as liquid, are being to slowly warm up to 90 DEG C or so, insulation reaction to be discharged it is preliminary complete, material is complete
Portion melts to complete to be to slowly warm up to 130 DEG C or so reactions to water outlet after liquid, and 15 are stirred in the state that rotating speed is 1000 revs/min
Minute, keep the various stock dispersions of system uniform.
Embodiment 3：A kind of preparation method substituting overlay film water-based gloss oil, first by acrylate copolymer, titanium dioxide, a huge sum of money
Mountain flour, powdered whiting, kaolin and water soluble acrylic resin mixing after suitable quantity of water is added, then while stirring slowly according to
Secondary addition wax emulsion, neutralizer be, wetting dispersing agent, thickener, biocide mildewcide and remaining water, is warming up under nitrogen protection
80 °C of heat preservations are all melted to material as liquid, are being to slowly warm up to 100 DEG C or so, insulation reaction to be discharged it is preliminary complete, material
All melt and completed to be to slowly warm up to 150 DEG C or so reactions to water outlet after liquid, is stirred in the state that rotating speed is 1200 revs/min
20 minutes, keep the various stock dispersions of system uniform.
Claims (1)
1. a kind of preparation method substituting overlay film water-based gloss oil, which is characterized in that first by acrylate copolymer, titanium dioxide, again
Suitable quantity of water is added after metal and stone powder, powdered whiting, kaolin and water soluble acrylic resin's mixing, then while stirring slowly
Sequentially add wax emulsion, neutralizer is, wetting dispersing agent, thickener, biocide mildewcide and remaining water, heat up under nitrogen protection
All melt to material as liquid to 60-80 °C of heat preservation, is being to slowly warm up to 80-100 DEG C or so, insulation reaction is preliminary complete to being discharged
At material all melts to be completed to be to slowly warm up to 110-150 DEG C or so reaction to water outlet after liquid, is 800-1200 in rotating speed
It is stirred 10-20 minutes in the state of rev/min, keeps the various stock dispersions of system uniform.