CN108373606A - Dry powder imitation porcelain coating - Google Patents
Dry powder imitation porcelain coating Download PDFInfo
- Publication number
- CN108373606A CN108373606A CN201610953852.1A CN201610953852A CN108373606A CN 108373606 A CN108373606 A CN 108373606A CN 201610953852 A CN201610953852 A CN 201610953852A CN 108373606 A CN108373606 A CN 108373606A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- dry powder
- mesh
- imitation porcelain
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of dry powder imitation porcelain coatings, are made of 50 parts of chalk powder, 40 parts of fine particle calcium carbonate, 5 parts of titanium dioxide, 3 parts of polymer glue powder, 2 parts of urea, grey 5 parts of calcium, 0.3 part of cellulose, 0.8 part of thickener, 0.5 part of pigment；The advantage of the invention is that：It avoids and leads to the problem of formaldehyde air pollution, and To Be Protected from Heat, is not afraid of jelly, is not perishable, the resting period is long, and production cost is low, and simplicity easy to use improves work efficiency.
Description
Technical field
The present invention relates to a kind of coating, specifically a kind of dry powder imitation porcelain coating belongs to paint field.
Background technology
Coating, the coating for being especially used for exterior wall and exterior wall product have prodigious developing market in China.It is called " city
For the hard surface-veneer material of city's time bomb " due to cost height, there are some potential safety problemss, are closed by domestic and international project circle
Note, and limit its use.Some provinces and cities of China have put into effect the regulation for limiting the use of hard surface-veneer material at present.How coating is improved resistance to
Long property, especially weather-proof colour retention, stain resistance, while reducing cost, that is, coating high performance-price ratio is assigned, is to influence paint development
One of principal element.
Current coating use 107 glue containing formaldehyde, it is easy to fall off on ground in construction, improve air pollution,
Face is polluted, and formaldehyde air pollution is generated.
Invention content
To solve the above-mentioned problems, the present invention devises a kind of dry powder imitation porcelain coating, does not use containing 107 glue of formaldehyde,
It is not easily to fall off on ground in construction, and much lower air pollution, ground pollution avoid and generate asking for formaldehyde air pollution
Topic, and it is at low cost, and product quality is high.
The technical scheme is that：
Dry powder imitation porcelain coating is made of the raw material of following parts by weight：
50 parts of chalk powder, 40 parts of fine particle calcium carbonate, 5 parts of titanium dioxide, 3 parts of polymer glue powder, 2 parts of urea, grey 5 parts of calcium, 0.3 part of cellulose,
0.8 part of thickener, 0.5 part of pigment.
Wherein, the chalk powder is 600 mesh, and the fine particle calcium carbonate is 1200 mesh, the titanium dioxide is 400 mesh.
When production, raw material is subjected to addition blender, 600 mesh of chalk powder, 1200 mesh of fine particle calcium carbonate, 400 mesh of titanium dioxide, methyl are fine
Dimension element, industrial urea, part material such as fine particle calcium carbonate, pigment are shown in that wind easily ties pomphus, need to individually be ground and be stirred；Industry
Urea need to be subject into powder in advance, and blender can be added together, at the uniform velocity be stirred in blender within about two hours.
In use, can voluntarily add clear water about 150%, the cream for hand mixer stir about being used in bucket 3 minutes into homogeneous soft
Shape can be used, and will be molded paste coating, and painting is scraped in inner wall putty surface, thickness about 3mm, until all covering putty, waits for table
It when face is dried, is firmly criticized and is scraped repeatedly for three times with iron scraper plate, until burnishing, solid colour, feel exquisiteness are charming.
The advantage of the invention is that：107 glue containing formaldehyde is not used, it is not easily to fall off in ground, much lower in construction
Air pollution, ground pollution avoid and lead to the problem of formaldehyde air pollution, and To Be Protected from Heat, is not afraid of jelly, is not perishable, deposit
Put that the time is long, and production cost is low, simplicity easy to use improves work efficiency.
The present invention is further explained in the light of specific embodiments.
Specific implementation mode
Hereinafter, preferred embodiments of the present invention will be described, it should be understood that preferred embodiment described herein is only used
In the description and interpretation present invention, it is not intended to limit the present invention.
The percentage sign " % " arrived involved in the present invention refers to mass percent if not specified；But the percentage of solution,
Unless otherwise specified, refer to containing several grams of solute in solution 100ml；Percentage between liquid, capacity when referring to 20 DEG C
Ratio.
Embodiment 1
Dry powder imitation porcelain coating is made of the raw material of following parts by weight：
50 parts of chalk powder, 40 parts of fine particle calcium carbonate, 5 parts of titanium dioxide, 3 parts of polymer glue powder, 2 parts of urea, grey 5 parts of calcium, 0.3 part of cellulose,
0.8 part of thickener, 0.5 part of pigment.
Wherein, the chalk powder is 600 mesh, and the fine particle calcium carbonate is 1200 mesh, the titanium dioxide is 400 mesh.
When production, raw material is subjected to addition blender, 600 mesh of chalk powder, 1200 mesh of fine particle calcium carbonate, 400 mesh of titanium dioxide, methyl are fine
Dimension element, industrial urea, are at the uniform velocity stirred for about two hours in blender.
In use, can voluntarily add clear water about 150%, the cream for hand mixer stir about being used in bucket 3 minutes into homogeneous soft
Shape can be used, and will be molded paste coating, and painting is scraped in inner wall putty surface, thickness about 3mm, until all covering putty, waits for table
It when face is dried, is firmly criticized and is scraped repeatedly for three times with iron scraper plate, until burnishing, solid colour, feel exquisiteness are charming.
Cost accounting
1, be stored in shady and cool dry place, storable 1-2, be far longer than 5 DEG C or less can also one week of shelf-life old-fashioned cream
Shape imitation porcelain coating；
2,150% freight charges can be saved, he has the characteristics that To Be Protected from Heat, is not afraid of jelly, is indefectible simultaneously in transit；
3,100 ㎡ of equivalents needs 70kg coating, 105 yuan of cost, every 100 ㎡ of product of the present invention only need 30kg dry powder, 60 yuan
Cost；
Can voluntarily plus clear water about 150% when 4, using, the paste of stir about 3 minutes at homogeneous soft can be used in bucket, often
People increases by 10% working efficiency daily.
Raw materials used in the present invention is to commonly use raw material in the production of this field, can be obtained from market, and for production
As a result it will not have an impact；Various equipment employed in the present invention are the conventional equipment used in the production technology of this field,
And operation, the parameter etc. of each equipment are carried out according to routine operation, have no special feature.
Claims (2)
1. dry powder imitation porcelain coating, it is characterised in that：It is made of the raw material of following parts by weight：
50 parts of chalk powder, 40 parts of fine particle calcium carbonate, 5 parts of titanium dioxide, 3 parts of polymer glue powder, 2 parts of urea, grey 5 parts of calcium, 0.3 part of cellulose,
0.8 part of thickener, 0.5 part of pigment.
2. dry powder imitation porcelain coating according to claim 1, it is characterised in that：The chalk powder is 600 mesh, and the fine particle calcium carbonate is
1200 mesh, the titanium dioxide are 400 mesh.