CN108359356A - A kind of diatom art paint coating containing inorganic salts - Google Patents
A kind of diatom art paint coating containing inorganic salts Download PDFInfo
- Publication number
- CN108359356A CN108359356A CN201810245729.3A CN201810245729A CN108359356A CN 108359356 A CN108359356 A CN 108359356A CN 201810245729 A CN201810245729 A CN 201810245729A CN 108359356 A CN108359356 A CN 108359356A
- Authority
- CN
- China
- Prior art keywords
- diatom
- water
- agent
- paint coating
- art paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of diatom art paint coating containing inorganic salts, is made of the raw material of following weight proportion：Soluble epoxide is acrylic resin modified 75 85%, pearl powder 2 6%, water-soluble fibre 0.3 0.6%, dispersant 0.2 0.5%, moisturizer 1 3%, anti-microbial inoculum 0.2 0.4%, fungicide 2 6%, antifoaming agent 1 3%, PH conditioning agents 0.4 0.7%, thickener 2 4%, silica 0.6 1.2%, silicate 10 15%, silane coupling agent 0.3 0.6%, diatomite 4 8%, nano-calcium carbonate calcium powder 2 8%, inorganic pigment 2 4%, eliminating smell agent 2 9%, appropriate amount of water.It is prepared simply, and natural environmental-protective, color are soft, capable of purifying air, water suction is fire-retardant.
Description
Technical field
The present invention relates to art coatings field more particularly to a kind of diatom art paint coating containing inorganic salts.
Background technology
Originating from Europe, advanced technique is also come by Europe sprawling art coatings, new with it into after domestic market
The decorated style of grain husk, unusual decorative effect, welcomed by the people again and high praise.Art coatings are a kind of novel metopes
Decorative art paint adds the treatment process of modern high technology, keeps product nontoxic, environmental protection, while being also equipped with waterproof and dustproof and resistance
Functions, the high-quality art coatings such as combustion can criticize brush, and strong adsorption, color sustains its quality through age.
Currently, the main component of art coatings is acrylic resin, color stuffing, additive and water.Art coatings are in
The rise of state only has more than ten years, but most of is texture or illusion-colour art coatings, and moulding hardening has a single function or without what
Functionality, formula is simple, and application property is complicated, and transreplication, this art coatings will be eliminated gradually by consumer.In view of market pair
The demand of art coatings is more and more, and therefore, the art coatings for developing novel type have important economic value and wide
Wealthy market prospects.
Diatomite, nano-calcium carbonate calcium powder are nontoxic, tasteless, free of contamination inorganic non-metallic materials.Since it has heatproof
Property the excellent performance such as good, acid-alkali-corrosive-resisting, poor thermal conductivity, high insulation, low bulk, stable chemical performance, hardness is big, it is extensive
For chemical industry, electronics, integrated circuit（IC）, electric appliance, plastics, the fields such as rubber or national defence.
Invention content
For above-mentioned deficiency in the prior art, the present invention provides a kind of diatom art paint coating containing inorganic salts,
It is prepared simply, and natural environmental-protective, color are soft, capable of purifying air, water suction is fire-retardant.
In order to reach foregoing invention purpose, the concrete scheme that the present invention uses for：
A kind of diatom art paint coating containing inorganic salts, is made of the raw material of following weight proportion：Soluble epoxide changes
Property acrylic resin 75-85%, pearl powder 2-6%, water-soluble fibre 0.3-0.6%, dispersant 0.2-0.5%, moisturizer 1-
3%, anti-microbial inoculum 0.2-0.4%, fungicide 2-6%, antifoaming agent 1-3%, PH conditioning agent 0.4-0.7%, thickener 2-
4%, silica 0.6-1.2%, silicate 10-15%, silane coupling agent 0.3-0.6%, diatomite 4-8%, nano-calcium carbonate
Calcium powder 2-8%, inorganic pigment 2-4%, eliminating smell agent 2-9%, appropriate amount of water.
Preferably, it is made of the raw material of following weight proportion：Soluble epoxide is acrylic resin modified 80%, pearly-lustre
Powder 4%, water-soluble fibre 0.5%, dispersant 0.4%, moisturizer 2%, anti-microbial inoculum 0.3%, fungicide 4%, antifoaming agent
2%, PH conditioning agents 0.6%, thickener 3%, silica 0.8%, silicate 13%, silane coupling agent 0.4%, diatom
Soil 6%, nano-calcium carbonate calcium powder 6%, inorganic pigment 3%, eliminating smell agent 6%, appropriate amount of water.
Preferably, the preparation method of the diatom art paint coating includes the following steps：
（1）By the formula feeding by with；
（2）Suitable quantity of water is added in mixing machine, sequentially adds dispersant, moisturizer, anti-microbial inoculum, fungicide, eliminating smell agent, with
500 turns of one minute rotating speed mixing disperse 5 minutes；
（3）To the step（2）Dispersion liquid in be added soluble epoxide is acrylic resin modified, pearl powder, water-soluble fibre,
Silica, silicate, silane coupling agent, diatomite, nano-calcium carbonate calcium powder, inorganic pigment, with 1600 turns of one minute rotating speeds
Mixing dispersion 12 minutes；
（4）To the step（3）Dispersion liquid in be added antifoaming agent, PH conditioning agents, thickener, with 1000 turns of one minute rotating speeds
Mixing dispersion 6 minutes adjusts mixed liquor PH to neutral or alkalescent, the diatom art paint coating is made.
Beneficial effects of the present invention are：
Acrylic resin modified soluble epoxide is to introduce acrylic unsaturated double-bond at the both ends of epoxy molecule chain, then
It is copolymerized with other monomers so that the various excellent performances of epoxy resin, adhesion strength is strong, molding shrinkage is low, chemical stability is good,
Electrical insulating property and thermal stability are good etc..
Moisturizer uses nonionic moisturizer, mainly contains simple function group, oleoyl alkylene oxide block copolymer, right
Color stuffing peptizaiton, and improve color developing.
Antifoaming agent is nonionic antifoaming agent, one kind in molecular antifoaming agent, has good compatibility and can principal characteristic.
The diatom art paint coating of the present invention has that natural environmental-protective, color are soft, capable of purifying air, water suction is fire-retardant, are not easy
It is stained with the features such as grey, service life is long.
Specific implementation mode
The present invention is further described below by way of specific embodiment, but the present invention is not limited only to following embodiment.At this
In the range of invention or present disclosure is not being departed from, in spirit and scope, the change that is carried out to the present invention is combined or replaced
It changes, will be apparent to the person skilled in the art, and be included within the scope of the present invention.
A kind of diatom art paint coating containing inorganic salts, is made of the raw material of following weight proportion：Water-soluble ring
The acrylic resin modified 75-85% of oxygen, pearl powder 2-6%, water-soluble fibre 0.3-0.6%, dispersant 0.2-0.5%, moisturizing
Agent 1-3%, anti-microbial inoculum 0.2-0.4%, fungicide 2-6%, antifoaming agent 1-3%, PH conditioning agent 0.4-0.7%, thickener
2-4%, silica 0.6-1.2%, silicate 10-15%, silane coupling agent 0.3-0.6%, diatomite 4-8%, nano-sized carbon
Sour calcium powder 2-8%, inorganic pigment 2-4%, eliminating smell agent 2-9%, appropriate amount of water.
It is made of the raw material of following weight proportion：Soluble epoxide is acrylic resin modified 80%, pearl powder 4%,
Water-soluble fibre 0.5%, dispersant 0.4%, moisturizer 2%, anti-microbial inoculum 0.3%, fungicide 4%, antifoaming agent 2%, PH tune
Section agent 0.6%, silica 0.8%, silicate 13%, silane coupling agent 0.4%, diatomite 6%, is received thickener 3%
Rice Paris white 6%, inorganic pigment 3%, eliminating smell agent 6%, appropriate amount of water.
The preparation method of the diatom art paint coating includes the following steps：
（1）By the formula feeding by with；
（2）Suitable quantity of water is added in mixing machine, sequentially adds dispersant, moisturizer, anti-microbial inoculum, fungicide, eliminating smell agent, with
500 turns of one minute rotating speed mixing disperse 5 minutes；
（3）To the step（2）Dispersion liquid in be added soluble epoxide is acrylic resin modified, pearl powder, water-soluble fibre,
Silica, silicate, silane coupling agent, diatomite, nano-calcium carbonate calcium powder, inorganic pigment, with 1600 turns of one minute rotating speeds
Mixing dispersion 12 minutes；
（4）To the step（3）Dispersion liquid in be added antifoaming agent, PH conditioning agents, thickener, with 1000 turns of one minute rotating speeds
Mixing dispersion 6 minutes adjusts mixed liquor PH to neutral or alkalescent, the diatom art paint coating is made.
The foregoing is merely the preferred embodiments of patent of the present invention, are not intended to limit the invention patent, all at this
All any modification, equivalent and improvement etc., should be included in patent of the present invention made by within the spirit and principle of patent of invention
Protection domain within.
Claims (3)
1. a kind of diatom art paint coating containing inorganic salts, which is characterized in that be made of the raw material of following weight proportion：
The acrylic resin modified 75-85% of soluble epoxide, pearl powder 2-6%, water-soluble fibre 0.3-0.6%, dispersant 0.2-
0.5%, moisturizer 1-3%, anti-microbial inoculum 0.2-0.4%, fungicide 2-6%, antifoaming agent 1-3%, PH conditioning agent 0.4-
0.7%, thickener 2-4%, silica 0.6-1.2%, silicate 10-15%, silane coupling agent 0.3-0.6%, diatom
Native 4-8%, nano-calcium carbonate calcium powder 2-8%, inorganic pigment 2-4%, eliminating smell agent 2-9%, appropriate amount of water.
2. a kind of diatom art paint coating containing inorganic salts according to claim 1, which is characterized in that by following weight
The raw material of proportioning is made：Soluble epoxide is acrylic resin modified 80%, pearl powder 4%, water-soluble fibre 0.5%, point
Powder 0.4%, moisturizer 2%, anti-microbial inoculum 0.3%, fungicide 4%, antifoaming agent 2%, PH conditioning agents 0.6%, thickener
3%, silica 0.8%, silicate 13%, silane coupling agent 0.4%, diatomite 6%, nano-calcium carbonate calcium powder 6%, inorganic
Pigment 3%, eliminating smell agent 6%, appropriate amount of water.
3. a kind of diatom art paint coating containing inorganic salts according to claim 1, it is characterised in that：The diatom skill
The preparation method of art paint coating includes the following steps：
（1）By the formula feeding by with；
（2）Suitable quantity of water is added in mixing machine, sequentially adds dispersant, moisturizer, anti-microbial inoculum, fungicide, eliminating smell agent, with
500 turns of one minute rotating speed mixing disperse 5 minutes；
（3）To the step（2）Dispersion liquid in be added soluble epoxide is acrylic resin modified, pearl powder, water-soluble fibre,
Silica, silicate, silane coupling agent, diatomite, nano-calcium carbonate calcium powder, inorganic pigment, with 1600 turns of one minute rotating speeds
Mixing dispersion 12 minutes；
（4）To the step（3）Dispersion liquid in be added antifoaming agent, PH conditioning agents, thickener, with 1000 turns of one minute rotating speeds
Mixing dispersion 6 minutes adjusts mixed liquor PH to neutral or alkalescent, the diatom art paint coating is made.