CN108340517B - Preparation method of plastic release agent - Google Patents
Preparation method of plastic release agent Download PDFInfo
- Publication number
- CN108340517B CN108340517B CN201711487868.9A CN201711487868A CN108340517B CN 108340517 B CN108340517 B CN 108340517B CN 201711487868 A CN201711487868 A CN 201711487868A CN 108340517 B CN108340517 B CN 108340517B
- Authority
- CN
- China
- Prior art keywords
- parts
- release agent
- attapulgite
- kaolin
- ethyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active - Reinstated
Abstract
The invention discloses a preparation method of a plastic release agent, which is prepared from the following substances: maleic acid modified rosin resin, kaolin, attapulgite, calcium hydrogen peroxide, epoxidized soybean oil, silicone oil, ethylene glycol, acetyl triethyl citrate, ethyl acetate and water. The mold release agent disclosed by the invention is small in smell and toxicity, the added kaolin, attapulgite and double-flying powder components improve the compactness, smoothness and uniformity of a formed film of the mold release agent, and meanwhile, the heat resistance, corrosion resistance and impact resistance of the mold release agent are enhanced, the quality of a plastic shell is effectively improved, and the mold release agent has great popularization and use values.
Description
Technical Field
The invention belongs to the technical field of plastic processing treatment, and particularly relates to a preparation method of a plastic release agent.
Background
Along with the development of society and the transformation of consumption concept, people pay more and more attention to body health, so that various fitness equipment in cities and homes are continuously increased, and great convenience and help are provided for the health improvement of people. Common fitness equipment includes a walking machine, a body building vehicle, a rowing machine, a running machine, a waist beautifying machine and the like, and a large number of plastic shells are used in the equipment. When the plastic shell is processed, there is a step of demolding, the quality of demolding is closely related to the quality of the shell, and a demolding agent is usually added to improve the surface quality of the plastic shell. Most of the release agents on the market at present have single component and poor using effect, and need to be continuously improved.
Disclosure of Invention
The invention aims to provide a preparation method of a plastic release agent aiming at the existing problems.
The invention is realized by the following technical scheme:
a preparation method of a plastic release agent is prepared from the following substances in parts by weight:
110-120 parts of maleic acid modified rosin resin, 25-30 parts of kaolin, 14-18 parts of attapulgite, 6-10 parts of boomerang, 7-11 parts of epoxidized soybean oil, 5-8 parts of silicone oil, 40-45 parts of ethylene glycol, 4-7 parts of acetyl triethyl citrate, 9-12 parts of ethyl acetate and 320-350 parts of water.
Preferably, the feed is prepared from the following substances in parts by weight:
115-120 parts of maleic acid modified rosin resin, 28-30 parts of kaolin, 16-18 parts of attapulgite, 8-10 parts of boomerang, 9-11 parts of epoxidized soybean oil, 7-8 parts of silicone oil, 43-45 parts of ethylene glycol, 6-7 parts of acetyl triethyl citrate, 11-12 parts of ethyl acetate and 340-350 parts of water.
Preferably, the feed is prepared from the following substances in parts by weight:
115 parts of maleic acid modified rosin resin, 28 parts of kaolin, 16 parts of attapulgite, 8 parts of calcium hydrogen peroxide, 9 parts of epoxidized soybean oil, 7 parts of silicone oil, 43 parts of ethylene glycol, 6 parts of acetyl triethyl citrate, 11 parts of ethyl acetate and 340 parts of water.
A preparation method of a plastic release agent comprises the following steps:
(1) mixing epoxidized soybean oil, silicone oil, ethylene glycol and water together, putting the mixture into a stirring tank, heating the mixture to keep the temperature in the stirring tank between 65 and 70 ℃, and stirring the mixture for 30 to 35 minutes at a rotating speed of between 400 and 500 revolutions per minute for later use;
(2) adding kaolin, attapulgite and double-flying powder into the stirring tank treated in the step (1) together, and stirring at the rotating speed of 1800-2000 rpm for 25-30 min for later use;
(3) and (3) putting the maleic acid modified rosin resin, acetyl triethyl citrate and ethyl acetate into the stirring tank treated in the step (2), performing ultrasonic treatment for 35-40 min, and taking out.
Further, the frequency of the ultrasonic treatment in the step (3) is 88-96 kHz.
Compared with the prior art, the invention has the following advantages:
the mold release agent disclosed by the invention is small in smell and toxicity, the added kaolin, attapulgite and double-flying powder components improve the compactness, smoothness and uniformity of a formed film of the mold release agent, and meanwhile, the heat resistance, corrosion resistance and impact resistance of the mold release agent are enhanced, the quality of a plastic shell is effectively improved, and the mold release agent has great popularization and use values.
Detailed Description
Example 1
A preparation method of a plastic release agent is prepared from the following substances in parts by weight:
110 parts of maleic acid modified rosin resin, 25 parts of kaolin, 14 parts of attapulgite, 6 parts of calcium hydrogen peroxide, 7 parts of epoxidized soybean oil, 5 parts of silicone oil, 40 parts of ethylene glycol, 4 parts of acetyl triethyl citrate, 9 parts of ethyl acetate and 320 parts of water.
A preparation method of a plastic release agent comprises the following steps:
(1) mixing epoxidized soybean oil, silicone oil, ethylene glycol and water together, putting the mixture into a stirring tank, heating the mixture to keep the temperature in the stirring tank at 65 ℃, and stirring the mixture for 30min at the rotating speed of 400 r/min for later use;
(2) adding kaolin, attapulgite and double-flying powder into the stirring tank treated in the step (1) together, and stirring at the rotating speed of 1800 rpm for 25min for later use;
(3) and (3) putting the maleic acid modified rosin resin, acetyl triethyl citrate and ethyl acetate into the stirring tank treated in the step (2), performing ultrasonic treatment for 35min, and taking out.
Further, the frequency of the ultrasonic treatment in the step (3) is 88 kHz.
Example 2
A preparation method of a plastic release agent is prepared from the following substances in parts by weight:
115 parts of maleic acid modified rosin resin, 28 parts of kaolin, 16 parts of attapulgite, 8 parts of calcium hydrogen peroxide, 9 parts of epoxidized soybean oil, 7 parts of silicone oil, 43 parts of ethylene glycol, 6 parts of acetyl triethyl citrate, 11 parts of ethyl acetate and 340 parts of water.
A preparation method of a plastic release agent comprises the following steps:
(1) mixing epoxidized soybean oil, silicone oil, ethylene glycol and water together, putting the mixture into a stirring tank, heating the mixture to keep the temperature in the stirring tank at 68 ℃, and stirring the mixture for 33min at the rotating speed of 450 revolutions per minute for later use;
(2) adding kaolin, attapulgite and double-flying powder into the stirring tank treated in the step (1) together, and stirring at the rotating speed of 1900 rpm for 27min for later use;
(3) and (3) putting the maleic acid modified rosin resin, acetyl triethyl citrate and ethyl acetate into the stirring tank treated in the step (2), performing ultrasonic treatment for 37min, and taking out.
Further, the frequency of the ultrasonic treatment in the step (3) is 92 kHz.
Example 3
A preparation method of a plastic release agent is prepared from the following substances in parts by weight:
120 parts of maleic acid modified rosin resin, 30 parts of kaolin, 18 parts of attapulgite, 10 parts of calcium hydrogen peroxide, 11 parts of epoxidized soybean oil, 8 parts of silicone oil, 45 parts of ethylene glycol, 7 parts of acetyl triethyl citrate, 12 parts of ethyl acetate and 350 parts of water.
A preparation method of a plastic release agent comprises the following steps:
(1) mixing epoxidized soybean oil, silicone oil, ethylene glycol and water together, putting the mixture into a stirring tank, heating the mixture to keep the temperature in the stirring tank at 70 ℃, and stirring the mixture for 35min at the rotating speed of 500 revolutions per minute for later use;
(2) adding kaolin, attapulgite and double-flying powder into the stirring tank treated in the step (1) together, and stirring at the rotating speed of 2000 rpm for 30min for later use;
(3) and (3) putting the maleic acid modified rosin resin, acetyl triethyl citrate and ethyl acetate into the stirring tank treated in the step (2), performing ultrasonic treatment for 40min, and taking out.
Further, the frequency of the ultrasonic treatment in the step (3) is 96 kHz.
The release agent has good use quality, the release yield reaches more than 98%, the repeated use performance is good, the quality is stable, and the release agent has great popularization and application values.
Claims (4)
1. The preparation method of the plastic release agent is characterized by being prepared from the following substances in parts by weight:
110-120 parts of maleic acid modified rosin resin, 25-30 parts of kaolin, 14-18 parts of attapulgite, 6-10 parts of boomerang, 7-11 parts of epoxidized soybean oil, 5-8 parts of silicone oil, 40-45 parts of ethylene glycol, 4-7 parts of acetyl triethyl citrate, 9-12 parts of ethyl acetate and 320-350 parts of water;
the preparation method comprises the following steps:
(1) mixing epoxidized soybean oil, silicone oil, ethylene glycol and water together, putting the mixture into a stirring tank, heating the mixture to keep the temperature in the stirring tank between 65 and 70 ℃, and stirring the mixture for 30 to 35 minutes at a rotating speed of between 400 and 500 revolutions per minute for later use;
(2) adding kaolin, attapulgite and double-flying powder into the stirring tank treated in the step (1) together, and stirring at the rotating speed of 1800-2000 rpm for 25-30 min for later use;
(3) and (3) putting the maleic acid modified rosin resin, acetyl triethyl citrate and ethyl acetate into the stirring tank treated in the step (2), performing ultrasonic treatment for 35-40 min, and taking out.
2. The method for preparing the plastic release agent according to claim 1, which is characterized by being prepared from the following substances in parts by weight:
115-120 parts of maleic acid modified rosin resin, 28-30 parts of kaolin, 16-18 parts of attapulgite, 8-10 parts of boomerang, 9-11 parts of epoxidized soybean oil, 7-8 parts of silicone oil, 43-45 parts of ethylene glycol, 6-7 parts of acetyl triethyl citrate, 11-12 parts of ethyl acetate and 340-350 parts of water.
3. The method for preparing the plastic release agent according to claim 1, which is characterized by being prepared from the following substances in parts by weight:
115 parts of maleic acid modified rosin resin, 28 parts of kaolin, 16 parts of attapulgite, 8 parts of calcium hydrogen peroxide, 9 parts of epoxidized soybean oil, 7 parts of silicone oil, 43 parts of ethylene glycol, 6 parts of acetyl triethyl citrate, 11 parts of ethyl acetate and 340 parts of water.
4. The method for preparing the plastic release agent according to claim 1, wherein the ultrasonic treatment in the step (3) has a frequency of 88 to 96 kHz.