CN108329829A - Interior wall coating and its preparation method and application - Google Patents
Interior wall coating and its preparation method and application Download PDFInfo
- Publication number
- CN108329829A CN108329829A CN201711045351.4A CN201711045351A CN108329829A CN 108329829 A CN108329829 A CN 108329829A CN 201711045351 A CN201711045351 A CN 201711045351A CN 108329829 A CN108329829 A CN 108329829A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- interior wall
- wall coating
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of interior wall coatings and its preparation method and application, including：The water of 14 25 parts by weight；The wetting dispersing agent of 0.5 0.8 parts by weight；The cellulose of 0.2 0.25 parts by weight；The antifoaming agent of 0.1 0.2 parts by weight；The antifreezing agent of 0.8 1.2 parts by weight；The scratching resistant of 0.3 0.6 parts by weight；The titanium dioxide of 0 10 parts by weight；The calcite in powder of 20 30 parts by weight；The pH adjusting agent of 0.1 0.2 parts by weight；The lotion of 40 50 parts by weight；The coalescents of 2 2.5 parts by weight；The preservative of 0.2 0.3 parts by weight；The hydrophobing agent of 0.2 0.4 parts by weight；And 0.2 0.3 anti-graffiti dose of parts by weight.The interior wall coating can prevent liquid stain from penetrating into inside coating, and have stronger hydrophobicity, anti-stain characteristic, chemical resistance and scrub resistance.
Description
Technical field
The invention belongs to paint fields, specifically, the present invention relates to interior wall coatings and its preparation method and application.
Background technology
The quality of interior wall coating contaminated resistance has been largely fixed the decorative effect of coating in use, kitchen
Room oil smoke, dust, various writings, liquid stain are indoor most common metope pollution, the coating with excellent contaminated resistance
It not only can guarantee the lasting beautiful of coating decorative effect, and extend the time interval of coating application again, greatly save
Manpower and materials cost reduces resource waste and alleviates environmental pressure.Spot-resistant interior wall coating is particularly suitable for family, doctor
The decoration of the inner wall surfaces such as institute, school.However existing interior wall coating on the market has the following disadvantages：(1) common interior wall coating
Spot-resistant effect is poor, is not easy to get rid of after being stained with spot；(2) some liquid stains can also penetrate into inside coating, to complete
Spot is dispelled entirely, need to there will be spot part coatings complete liquidation to fall, it is serious to lose powder；(3) time interval of coating application again
It is short, wasting manpower and material resources' cost.
Therefore, need to be developed the better interior wall coating of quality.
Invention content
The present invention is directed to solve at least some of the technical problems in related technologies.For this purpose, the present invention
One purpose is to propose a kind of interior wall coating and its preparation method and application.The lacquer painting that the interior wall coating is formed can prevent liquid
Body spot is penetrated into inside coating, and the lacquer painting has stronger hydrophobicity, anti-stain characteristic, chemical resistance and scrubbing resistance
Property.
In one aspect of the invention, the present invention proposes a kind of interior wall coating, according to an embodiment of the invention, the interior wall
Coating includes：
The water of 14-25 parts by weight；
The wetting dispersing agent of 0.5-0.8 parts by weight；
The cellulose of 0.2-0.25 parts by weight；
The antifoaming agent of 0.1-0.2 parts by weight；
The antifreezing agent of 0.8-1.2 parts by weight；
The scratching resistant of 0.3-0.6 parts by weight；
The titanium dioxide of 0-10 parts by weight；
The calcite in powder of 20-30 parts by weight；
The pH adjusting agent of 0.1-0.2 parts by weight；
The lotion of 40-50 parts by weight；
2-2.5 the coalescents of parts by weight；
The preservative of 0.2-0.3 parts by weight；
The hydrophobing agent of 0.2-0.4 parts by weight；And
Anti-graffiti dose of 0.2-0.3 parts by weight.
The lacquer painting that interior wall coating according to the ... of the embodiment of the present invention is formed have higher anti-stain characteristic, chemical resistance,
Scrub resistance and water resistance, and can prevent liquid stain from penetrating into inside lacquer painting, and enhance the stain resistance of lacquer painting, simultaneously
The greasy dirt easy cleaning on lacquer painting surface.The interior wall coating can guarantee that lacquer painting decorative effect is persistently beautiful as a result, extend coating again
The time interval of application has greatly saved manpower and materials cost, reduces resource waste and alleviates environmental pressure.
In addition, interior wall coating according to the above embodiment of the present invention can also have following additional technical characteristic：
In some embodiments of the invention, the wetting dispersing agent is BYK-154.Be conducive to improve interior wall painting as a result,
The quality of material.
In some embodiments of the invention, the cellulose is Bermocoll E 351FQ.It can further carry as a result,
The quality of high interior wall coating.
In some embodiments of the invention, the antifoaming agent is BYK-094.It can further improve interior wall coating as a result,
Quality.
In some embodiments of the invention, the antifreezing agent is propylene glycol.It can further improve interior wall coating as a result,
Quality.
In some embodiments of the invention, the scratching resistant is VK-S01W nano silicon dioxide water slurrys.As a result, may be used
Further increase the quality of interior wall coating.
In some embodiments of the invention, the pH adjusting agent is AMP-95.It can further improve interior wall coating as a result,
Quality.
In some embodiments of the invention, the lotion is at least one of silane emulsion and silicone emulsion.By
This, can further improve the quality of interior wall coating.
In some embodiments of the invention, the coalescents are alcohol ester-12.It can further improve interior wall painting as a result,
The quality of material.
In some embodiments of the invention, the preservative is ECOCIDE BNI.It can further improve interior wall as a result,
The quality of coating.
In some embodiments of the invention, the hydrophobing agent is Phobe 1500N.It can further improve interior wall as a result,
The quality of coating.
In some embodiments of the invention, described anti-graffiti dose is BYK-SILCLEAN 3720.It as a result, can be further
Improve the quality of interior wall coating.
In another aspect of the invention, the present invention proposes a kind of method preparing above-mentioned interior wall coating, according to this hair
Bright embodiment, this method include：
(1) under the stir speed (S.S.) of 200~400r/min, water, wetting dispersing agent and cellulose are mixed according to predetermined ratio
1~3min of stirring is closed, to obtain the first mixed liquor；
(2) the first mixed liquor is mixed with antifoaming agent and antifreezing agent according to predetermined ratio, and obtained mixed liquor is existed
2~7min is stirred under the stir speed (S.S.) of 300~700r/min, to obtain the second mixed liquor；
(3) the second mixed liquor is mixed with scratching resistant, titanium dioxide, calcite in powder and pH adjusting agent according to predetermined ratio,
And obtained mixed liquor is stirred into 20~40min to obtain third mixed liquor under the stir speed (S.S.) of 1300~1700r/min；
(4) it under the stir speed (S.S.) of 600~1000r/min, by third mixed liquor and lotion, coalescents, preservative, dredges
Aqua and anti-graffiti dose are mixed according to predetermined ratio, to obtain interior wall coating.
The lacquer painting that the interior wall coating that the method according to the ... of the embodiment of the present invention for preparing interior wall coating obtains is formed has higher
Anti-stain characteristic, chemical resistance, scrub resistance and water resistance, and can prevent liquid stain penetrate into lacquer painting inside, and
Enhance the stain resistance of lacquer painting, while the greasy dirt easy cleaning on lacquer painting surface.The interior wall coating can guarantee lacquer painting decoration effect as a result,
Fruit is persistently beautiful, extends the time interval of coating application again, has greatly saved manpower and materials cost, reduces resource wave
Take and alleviates environmental pressure.
In an additional aspect of the present invention, the present invention proposes a kind of building.According to an embodiment of the invention, the building
Object includes：Wall；And lacquer painting, the lacquer painting pass through by above-mentioned interior wall coating or using the above-mentioned method for preparing interior wall coating
The interior wall coating being prepared is applied to the wall-body energy saving and is formed.The time of lacquer painting application again can significantly be extended as a result,
Interval, has greatly saved manpower and materials cost, has saved energy consumption.
The additional aspect and advantage of the present invention will be set forth in part in the description, and will partly become from the following description
Obviously, or practice through the invention is recognized.
Description of the drawings
The above-mentioned and/or additional aspect and advantage of the present invention will become in the description from combination following accompanying drawings to embodiment
Obviously and it is readily appreciated that, wherein：
Fig. 1 is the method schematic diagram according to an embodiment of the invention for preparing interior wall coating.
Specific implementation mode
The embodiment of the present invention is described below in detail, examples of the embodiments are shown in the accompanying drawings, wherein from beginning to end
Same or similar label indicates same or similar element or element with the same or similar functions.Below with reference to
The embodiment of attached drawing description is exemplary, it is intended to for explaining the present invention, and is not considered as limiting the invention.
In addition, term " first ", " second " are used for description purposes only, it is not understood to indicate or imply relative importance
Or implicitly indicate the quantity of indicated technical characteristic.Define " first " as a result, the feature of " second " can be expressed or
Person implicitly includes at least one this feature.In the description of the present invention, the meaning of " plurality " is at least two, such as two,
Three etc., unless otherwise specifically defined.
In one aspect of the invention, the present invention proposes a kind of interior wall coating, according to an embodiment of the invention, the interior wall
Coating includes：The water of 14-25 parts by weight；The wetting dispersing agent of 0.5-0.8 parts by weight；The cellulose of 0.2-0.25 parts by weight；
The antifoaming agent of 0.1-0.2 parts by weight；The antifreezing agent of 0.8-1.2 parts by weight；The scratching resistant of 0.3-0.6 parts by weight；0-10 weight
The titanium dioxide of part；The calcite in powder of 20-30 parts by weight；The pH adjusting agent of 0.1-0.2 parts by weight；The lotion of 40-50 parts by weight；
2-2.5 the coalescents of parts by weight；The preservative of 0.2-0.3 parts by weight；The hydrophobing agent of 0.2-0.4 parts by weight；And 0.2-
Anti-graffiti dose of 0.3 parts by weight.
Inventor find, by by water, wetting dispersing agent, cellulose, antifoaming agent, antifreezing agent, scratching resistant, titanium dioxide,
Calcite in powder, pH adjusting agent, lotion, coalescents, preservative, hydrophobing agent and anti-graffiti dose of mixing, wherein wetting and dispersing
Agent can make the dispersion stability of each component in coating；Scratching resistant is remarkably improved the hardness of interior wall coating coating, wearability
And durability, improve the adhesive force of coating, greatly improves the anti-stain characteristic of coating, chemical resistance, scrub resistance and water-fast
Property；Hydrophobing agent is used cooperatively with anti-graffiti dose, can significantly reduce the surface tension of interior wall coating coating so that coating surface
Hydrophobicity enhances, and generates " lotus leaf effect ", prevents liquid stain from penetrating into inside coating, and enhance the stain resistance of paint film, simultaneously
The greasy dirt easy cleaning of coating surface.As a result, use the component interior wall coating formed lacquer painting have higher anti-stain characteristic,
Chemical resistance, scrub resistance and water resistance, and can prevent liquid stain from penetrating into inside lacquer painting, and enhance lacquer painting
Stain resistance, while the greasy dirt easy cleaning on lacquer painting surface.The interior wall coating can guarantee that lacquer painting decorative effect is persistently beautiful as a result,
The time interval for extending coating application again, has greatly saved manpower and materials cost, has reduced resource waste and alleviate ring
Border pressure.
According to one embodiment of present invention, the concrete type of wetting dispersing agent is not particularly restricted, the skill of this field
Art personnel can select according to actual needs, a specific embodiment according to the present invention, and wetting dispersing agent can be
BYK-154.Inventor has found that BYK-154 wetting dispersing agents can make the dispersion stability of each component in coating, improve coating
Gloss and levelling.It can further improve the quality of interior wall coating as a result,.
According to still a further embodiment, the concrete type of cellulose is not particularly restricted, the technology of this field
Personnel can select according to actual needs, a specific embodiment according to the present invention, and cellulose can be
Bermocoll E 351 FQ.Specifically, cellulose can be the Bermocoll E 351FQ of Akzo Nobel companies.Invention
People has found that Bermocoll E 351FQ can improve levelability, covering power and the anti-splashing ability of coating.It as a result, can be further
Improve the quality of interior wall coating.
According to still another embodiment of the invention, the concrete type of antifoaming agent is not particularly restricted, the technology of this field
Personnel can select according to actual needs, a specific embodiment according to the present invention, and antifoaming agent can be BYK-094.
Inventor has found that BYK-094 has very high shear stability, and can prevent coating from producing and bubble in work progress.By
This, can further improve the quality of interior wall coating.
According to still another embodiment of the invention, the concrete type of antifreezing agent is not particularly restricted, the technology of this field
Personnel can select according to actual needs, a specific embodiment according to the present invention, and antifreezing agent can be propylene glycol.
It can further improve the quality of interior wall coating as a result,.
According to still another embodiment of the invention, the concrete type of scratching resistant is not particularly restricted, the skill of this field
Art personnel can select according to actual needs, a specific embodiment according to the present invention, and scratching resistant can be VK-
S01W nano silicon dioxide water slurrys.Specifically, can be the VK-S01W nanometers two of Hangzhou Wanjing New Material Co., Ltd.'s production
Silica water slurry.Inventor find, VK-S01W nano silicon dioxide water slurrys have it is non-toxic and tasteless, pollution-free, stability is good,
Grain size is small, has good intersolubility with system, has good dispersibility, suspension, high solids content, and can be directly added into system
In, reduce the technical process of dispersion, significantly improves the hardness, wearability and durability of coating, improve the attachment of coating
Power greatly improves anti-stain characteristic, chemical resistance, scrub resistance and the water resistance of coating.
According to still another embodiment of the invention, titanium dioxide can be the R996 of Sichuan dragon boa, and calcite in powder can be wide
Fujian material (Jiangling) is refined the CC-700 of Co., Ltd.
According to still another embodiment of the invention, the concrete type of pH adjusting agent is not particularly restricted, the skill of this field
Art personnel can select according to actual needs, a specific embodiment according to the present invention, and pH adjusting agent can be AMP-
95.Inventor has found that the resistance to wiping and water resistance of coating can be improved in AMP-95, and can reduce many commonly-used coating and add
Add the dosage of agent so that the increase of volatile organic matter (VOC) is minimum in coating, effectively reduces coating smell, i.e. AMP-95
The cost of raw material can be efficiently reduced, while improving the performance of coating.
According to still another embodiment of the invention, the concrete type of lotion is not particularly restricted, those skilled in the art
Member can be selected according to actual needs, and a specific embodiment according to the present invention, lotion can be silane emulsion and silicon
At least one of oxygen alkane lotion, preferably silane/siloxane lotion.Specifically, lotion can be DOW CORNING IE6683 silane/
Silicone emulsion.Inventor has found, selects silane/siloxane lotion, can be by the reactivity of silane and permeability and siloxanes
Mobility and water droplet effect are combined so that coating molecular volume is minimum, and coating can depth infiltration base after being coated in substrate surface
Material, and its can with base material and itself react, to realize durability.After solidification, coating allows vapor to penetrate into, but
It can prevent that dissolved chlorion may be contained or the liquid water of acid penetrates into base material.It also occur that polycondensation reaction, is constituted between silane
Si-O-Si polymer, the alkyl towards outside can be effectively hydrophobic, can provide, infiltration impaired for freeze thawing, permeability and mould
Protection.It can further improve the quality of interior wall coating as a result,.
According to still another embodiment of the invention, the concrete type of coalescents is not particularly restricted, the skill of this field
Art personnel can select according to actual needs, a specific embodiment according to the present invention, and coalescents can be alcohol
Ester -12.Specifically, the alcohol ester-12 of coalescents Ke Yi Wei Yi Shiman.Inventor find, alcohol ester-12 contribute to coating at
Film, and the minimum film formation temperature of coating can be reduced.It can further improve the quality of interior wall coating as a result,.
According to still another embodiment of the invention, the concrete type of preservative is not particularly restricted, the technology of this field
Personnel can select according to actual needs, a specific embodiment according to the present invention, and preservative can be ECOCIDE
BNI.Specifically, preservative can be the ECOCIDE BNI of Pu Laijiwen companies.It can further improve interior wall coating as a result,
Quality.
According to still another embodiment of the invention, the concrete type of hydrophobing agent is not particularly restricted, the technology of this field
Personnel can select according to actual needs, a specific embodiment according to the present invention, and hydrophobing agent can be Phobe
1500N.Specifically, hydrophobing agent can be the Phobe 1500N of Tego.Inventor has found that hydrophobing agent can make coating reach good
Good lotus leaf effect, helps to improve the hydrophobicity of coating.It can further improve the quality of interior wall coating as a result,.
According to still another embodiment of the invention, anti-graffiti dose of concrete type is not particularly restricted, the skill of this field
Art personnel can select according to actual needs, and a specific embodiment according to the present invention, anti-graffiti dose can be
BYK-SILCLEAN 3720.Inventor has found, is added to the greasy dirt easy-clear that coating can be dramatically increased after anti-graffiti dose.By
This, can further improve the quality of interior wall coating.
In another aspect of the invention, the present invention proposes a kind of method preparing above-mentioned interior wall coating, according to this hair
Bright embodiment, with reference to figure 1, this method includes：
S100：Water, wetting dispersing agent and cellulose are mixed
In the step, under the stir speed (S.S.) of 200~400r/min, by water, wetting dispersing agent and cellulose according to predetermined
1~3min is mixed in ratio, to obtain the first mixed liquor.
S200：First mixed liquor is mixed with antifoaming agent and antifreezing agent
In the step, mixing that the first mixed liquor is mixed according to predetermined ratio with antifoaming agent and antifreezing agent, and will obtained
Liquid stirs 2~7min under the stir speed (S.S.) of 300~700r/min, to obtain the second mixed liquor.
S300：Second mixed liquor is mixed with scratching resistant, titanium dioxide, calcite in powder and pH adjusting agent
In the step, by the second mixed liquor and scratching resistant, titanium dioxide, calcite in powder and pH adjusting agent according to predetermined ratio
Mixing, and obtained mixed liquor is stirred into 20~40min under the stir speed (S.S.) of 1300~1700r/min, to obtain third
Mixed liquor.It should be noted that titanium dioxide can be the R996 of Sichuan dragon boa, calcite in powder can be wide Fujian material (Jiangling)
Refine the CC-700 of Co., Ltd.
S400：Third mixed liquor is mixed with lotion, coalescents, preservative, hydrophobing agent and anti-graffiti dose
In the step, under the stir speed (S.S.) of 600~1000r/min, by third mixed liquor and lotion, coalescents, prevent
Rotten agent, hydrophobing agent and anti-graffiti dose are mixed according to predetermined ratio, to obtain interior wall coating.
The lacquer painting that the interior wall coating that the method according to the ... of the embodiment of the present invention for preparing interior wall coating obtains is formed has higher
Anti-stain characteristic, chemical resistance, scrub resistance and water resistance, and can prevent liquid stain penetrate into lacquer painting inside, and
Enhance the stain resistance of lacquer painting, while the greasy dirt easy cleaning on lacquer painting surface.The interior wall coating can guarantee lacquer painting decoration effect as a result,
Fruit is persistently beautiful, extends the time interval of coating application again, has greatly saved manpower and materials cost, reduces resource wave
Take and alleviates environmental pressure.
It should be noted that above-mentioned term " predetermined ratio " refers to each component in interior wall coating described in preceding embodiment
Proportioning, specifically, in S100~S400, predetermined ratio refers to the water of 14-25 parts by weight；The wetting of 0.5-0.8 parts by weight
Dispersant；The cellulose of 0.2-0.25 parts by weight；The antifoaming agent of 0.1-0.2 parts by weight；The antifreezing agent of 0.8-1.2 parts by weight；
The scratching resistant of 0.3-0.6 parts by weight；The titanium dioxide of 0-10 parts by weight；The calcite in powder of 20-30 parts by weight；0.1-0.2 weight
The pH conditioning agents of part；The lotion of 40-50 parts by weight；2-2.5 the coalescents of parts by weight；The preservative of 0.2-0.3 parts by weight；
The hydrophobing agent of 0.2-0.4 parts by weight；And anti-graffiti dose of 0.2-0.3 parts by weight.
Meanwhile it will be appreciated to those of skill in the art that above for feature and advantage described in interior wall coating, together
Sample is suitable for the method for preparing interior wall coating, and details are not described herein.
In an additional aspect of the present invention, the present invention proposes a kind of building, according to an embodiment of the invention, the building
Object includes：Wall and lacquer painting, wherein lacquer painting is by by above-mentioned interior wall coating or using the above-mentioned method for preparing interior wall coating
The interior wall coating being prepared is applied to wall-body energy saving and is formed.As a result, by the way that above-mentioned interior wall coating to be applied in cavity
On surface, the lacquer painting which forms has higher anti-stain characteristic, chemical resistance, scrub resistance and water resistance,
And it can prevent liquid stain from penetrating into inside lacquer painting, and enhance the stain resistance of lacquer painting, while the greasy dirt on lacquer painting surface is easily clear
It washes.Thus, it is possible to ensure that wall-body energy saving lacquer painting decorative effect is persistently beautiful, extend the time interval of coating application again, pole
Big has saved manpower and materials cost, reduces resource waste and alleviates environmental pressure.It should be noted that above-mentioned be directed to
It interior wall coating and prepares feature and advantage described in the method for interior wall coating and is equally applicable to the building, it is no longer superfluous herein
It states.
Below with reference to specific embodiment, present invention is described, it should be noted that these embodiments are only to describe
Property, without limiting the invention in any way.
Preparation method:
(1) under the stir speed (S.S.) of 200~400r/min, water, wetting dispersing agent and cellulose are mixed according to predetermined ratio
1~3min of stirring is closed, to obtain the first mixed liquor；
(2) the first mixed liquor is mixed with antifoaming agent and antifreezing agent according to predetermined ratio, and by obtained mixed liquor 300
2~7min is stirred under the stir speed (S.S.) of~700 r/min, to obtain the second mixed liquor；
(3) the second mixed liquor is mixed with scratching resistant, titanium dioxide, calcite in powder and pH adjusting agent according to predetermined ratio,
And obtained mixed liquor is stirred into 20~40min to obtain third mixed liquor under the stir speed (S.S.) of 1300~1700r/min；
(4) it under the stir speed (S.S.) of 600~1000r/min, by third mixed liquor and lotion, coalescents, preservative, dredges
Aqua and anti-graffiti dose are mixed according to predetermined ratio, to obtain interior wall coating.
Embodiment 1,2, comparative example 1,2 formulation contents it is as shown in table 1, and the following institute of each component concrete type in table 1
Show：
Water is deionized water；
Wetting dispersing agent is BYK-154；
Cellulose is the Bermocoll E 351FQ of Akzo Nobel companies；
Antifoaming agent is BYK-094；
Antifreezing agent is propylene glycol；
Scratching resistant is the VK-S01W nano silicon dioxide water slurrys of Hangzhou Wanjing New Material Co., Ltd.'s production；
Titanium dioxide is the R996 of Sichuan dragon boa；
Calcite in powder is the CC-700 of Guangfu Building Materials (Jiaoling) Fine Chemicals Industry Co., Ltd.；
PH adjusting agent AMP-95；
Lotion is DOW CORNING IE6683 silane/siloxane lotions；
Coalescents are the alcohol ester-12 of Yi Shiman；
Preservative is ECOCIDE BNI；
Hydrophobing agent is the Phobe 1500N of Tego；And
Anti-graffiti dose is BYK-SILCLEAN 3720.
1 Examples 1 and 2 of table, comparative example 1 and 2 formula compositions
| Raw material (kg) | Embodiment 1 | Embodiment 2 | Comparative example 1 | Comparative example 2 |
| Water | 15 | 20 | 15 | 20 |
| Wetting dispersing agent | 0.5 | 0.8 | 0.5 | 0.8 |
| Cellulose | 0.2 | 0.25 | 0.2 | 0.25 |
| Antifoaming agent | 0.1 | 0.2 | 0.1 | 0.2 |
| Antifreezing agent | 1.0 | 0.8 | 1.0 | 0.8 |
| Scratching resistant | 0.4 | 0.5 | 0.4 | 0.5 |
| Titanium dioxide | 5 | 9 | 5 | 9 |
| Calcite in powder | 25 | 30 | 25 | 30 |
| PH adjusting agent | 0.1 | 0.15 | 0.1 | 0.15 |
| Lotion | 45 | 50 | 45 | 50 |
| Coalescents | 2 | 2 | 2 | 2 |
| Preservative | 0.3 | 0.2 | / | / |
| Anti-graffiti dose | 0.3 | 0.2 | / | / |
| Hydrophobing agent | 0.3 | 0.2 | 0.3 | 0.2 |
Evaluation：
1, Examples 1 and 2, the obtained interior wall coatings of comparative example 1-2 are coated in building concrete wall respectively
Inner surface, and the hydrophobicity to the lacquer painting of formation, anti-stain characteristic, chemical resistance and scrub performance are tested.
2, evaluation index and test method：
Hydrophobicity test method：The paint made is brushed on plank, is conserved 7 days, its paint film is made to dry, toward dry paint
Drop of water on film estimates hydrophobic situation, judge hydrophobicity it is good with it is bad；
Anti-stain characteristic test method (see row table HG/T 4756-2014)：
Chemical resistance test method (see national standard GB/T 31588.1-2015)：
Scrub performance test method (see national standard GBT 9266-2009)：
Anti-doodling and anti-affixing (see national standard JG/T 304-2011)
Test result
In the description of this specification, reference term " one embodiment ", " some embodiments ", " example ", " specifically show
The description of example " or " some examples " etc. means specific features, structure, material or spy described in conjunction with this embodiment or example
Point is included at least one embodiment or example of the invention.In the present specification, schematic expression of the above terms are not
It must be directed to identical embodiment or example.Moreover, particular features, structures, materials, or characteristics described can be in office
It can be combined in any suitable manner in one or more embodiments or example.In addition, without conflicting with each other, this field
Technical staff can carry out the feature of different embodiments or examples described in this specification and different embodiments or examples
In conjunction with and combination.
Although the embodiments of the present invention has been shown and described above, it is to be understood that above-described embodiment is example
Property, it is not considered as limiting the invention, those skilled in the art within the scope of the invention can be to above-mentioned
Embodiment is changed, changes, replacing and modification.
Claims (10)
1. a kind of interior wall coating, which is characterized in that including：
The water of 14-25 parts by weight；
The wetting dispersing agent of 0.5-0.8 parts by weight；
The cellulose of 0.2-0.25 parts by weight；
The antifoaming agent of 0.1-0.2 parts by weight；
The antifreezing agent of 0.8-1.2 parts by weight；
The scratching resistant of 0.3-0.6 parts by weight；
The titanium dioxide of 0-10 parts by weight；
The calcite in powder of 20-30 parts by weight；
The pH adjusting agent of 0.1-0.2 parts by weight；
The lotion of 40-50 parts by weight；
2-2.5 the coalescents of parts by weight；
The preservative of 0.2-0.3 parts by weight；
The hydrophobing agent of 0.2-0.4 parts by weight；And
Anti-graffiti dose of 0.2-0.3 parts by weight.
2. interior wall coating according to claim 1, which is characterized in that the wetting dispersing agent is BYK-154；
Optional, the cellulose is Bermocoll E 351FQ.
3. interior wall coating according to claim 1 or 2, which is characterized in that the antifoaming agent is BYK-094；
Optional, the antifreezing agent is propylene glycol.
4. interior wall coating according to claim 1, which is characterized in that the scratching resistant is VK-S01W nanometer titanium dioxides
Silicon water slurry；
Optional, the pH adjusting agent is AMP-95.
5. interior wall coating according to claim 1, which is characterized in that the lotion is in silane emulsion and silicone emulsion
At least one.
6. interior wall coating according to claim 1, which is characterized in that the coalescents are alcohol ester-12；
Optional, the preservative is ECOCIDE BNI.
7. interior wall coating according to claim 1, which is characterized in that the hydrophobing agent is Phobe 1500N.
8. interior wall coating according to claim 1, which is characterized in that described anti-graffiti dose is BYK-SILCLEAN3720.
9. a kind of method preparing the interior wall coating described in any one of claim 1-8, which is characterized in that including：
(1) under the stir speed (S.S.) of 200~400r/min, water, wetting dispersing agent and cellulose is mixed according to predetermined ratio and stirred
1~3min is mixed, to obtain the first mixed liquor；
(2) the first mixed liquor is mixed with antifoaming agent and antifreezing agent according to predetermined ratio, and by obtained mixed liquor 300~
2~7min is stirred under the stir speed (S.S.) of 700r/min, to obtain the second mixed liquor；
(3) the second mixed liquor is mixed with scratching resistant, titanium dioxide, calcite in powder and pH adjusting agent according to predetermined ratio, and will
Obtained mixed liquor stirs 20~40min to obtain third mixed liquor under the stir speed (S.S.) of 1300~1700r/min；
(4) under the stir speed (S.S.) of 600~1000r/min, by third mixed liquor and lotion, coalescents, preservative, hydrophobing agent
It is mixed according to predetermined ratio with anti-graffiti dose, to obtain interior wall coating.
10. a kind of building, which is characterized in that including：
Wall；And
Lacquer painting, the lacquer painting pass through by interior wall coating according to any one of claims 1 to 8 or using described in claim 9
The interior wall coating that is prepared of method be applied to the wall-body energy saving and formed.