CN108327443B - 一种释放负离子的掐丝珐琅画及其制作方法 - Google Patents
一种释放负离子的掐丝珐琅画及其制作方法 Download PDFInfo
- Publication number
- CN108327443B CN108327443B CN201711478688.4A CN201711478688A CN108327443B CN 108327443 B CN108327443 B CN 108327443B CN 201711478688 A CN201711478688 A CN 201711478688A CN 108327443 B CN108327443 B CN 108327443B
- Authority
- CN
- China
- Prior art keywords
- enamel
- glaze
- negative ions
- releasing negative
- painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种释放负离子的掐丝珐琅画及其制作方法，该方法包括以下步骤：1)将珐琅釉料磨碎，调配成珐琅色釉；2)将白色负离子粉按3‑15wt％的比例混入调好的珐琅色釉；3)在胎体上绘制工笔线稿；4)步骤3)处理后的胎体上粘金属丝进行掐丝掰花；5)将珐琅色釉填充到金属丝以外的部分，进行点蓝施釉；6)喷胶定型，干燥，得到释放负离子的掐丝珐琅画。该释放负离子的掐丝珐琅画色泽佳，不会对释放负离子的掐丝珐琅画的色泽造成影响，同时能永久性释放负离子，有效去除甲醛，净化空气，用于室内装饰具有较高的实用性。
Description
技术领域
本发明涉及空气净化产品技术领域，尤其涉及一种释放负离子的掐丝珐琅画及其制作方法。
背景技术
随着城市的发展，人们对空气质量的关注度越来越高。室内装修装潢、家具配置、日用化工品等带来了大量甲醛，对人类身体健康有极大的危害。
甲醛又称蚁醛，是无色有强烈刺激性气味的气体。甲醛易聚合成多聚甲醛，其受热易发生解聚作用，并在室温下可缓慢释放单体甲醛。甲醛主要用于生产各种装修建材，人造板、塑料、皮革、造纸、人造纤维、玻璃纤维、橡胶、涂料、药品、油漆、肥皂等产品。因此，在日常生活当中不可避免的存在着甲醛的危害。
2004年6月15日，世界卫生组织发布了第153号“甲醛致癌”公报，正式确定甲醛对人体有致癌作用：已有充分证据可以证明甲醛会导致人类患鼻咽癌和鼻窦癌；另外，甲醛很可能导致白血病。这是世界卫生组织(WHO)的国际癌症研究机构(IARC)汇集了10个国家26位科学家针对甲醛致癌评议的结果。
甲醛浓度在每立方米空气中达到0.06-0.07mg/m3时，儿童就会发生轻微气喘。当室内空气中甲醛含量为0.1mg/m3时，就有异味和不适感；达到0.5mg/m3时，可刺激眼睛，引起流泪；达到0.6mg/m3，可引起咽喉不适或疼痛。浓度更高时，可引起恶心呕吐，咳嗽胸闷，气喘甚至肺水肿；达到30mg/m3时，会立即致人死亡。在一定条件下，居室环境内空气中甲醛浓度可聚集到标准允许水平以上，而且释放期比较长，一般情况下，是3-15年。而目前，市面上去除甲醛危害的途径以及方法又各有缺点，效果不大理想。
以下是目前市面上5种主要的去除甲醛净化空气方法：
1)用活性炭吸附除醛。由于活性炭内部蜂窝状特殊结构的原因，具有强力的吸附能力，但是活性炭吸附饱和期只有20天左右，超过20天就不再具备吸附能力，无法有效对甲醛进行长期吸附，大量有害物体被吸附并且积聚在活性炭上，具有二次释放的危险。有公开号为CN201534452U中国专利多孔炭基景泰蓝空气净化工艺画，其多孔结构只是延长了活性炭吸附有效期，本质还是不能解决活性炭吸附作用周期短，具有二次释放的弊端。
2)用空气净化器吸附甲醛。空气净化器有一层滤网是用活性炭做的，可以吸附一定的甲醛，但是和单纯使用活性炭存在一样的问题，短时间内就迅速达到饱和。
3)用光触媒分解甲醛。光触媒是一种催化剂，能够和紫外线产生化学反应，将甲醛(HCHO)分解为二氧化碳和水，但是由于对紫外线依赖极高，尤其是室内，紫外线不足，效果难以发挥，实际使用起来非常不方便，还不是永久性的起作用。
4)用负离子磁砖来去除甲醛。负离子磁砖是高温烧制的产品，在高温烧制的过程中，在高温高压的作用下，负离子粉矿物成分大多已经被破坏。如果用量多，则影响釉面光滑度。而且瓷砖只能在装修时才能使用，所以使用频率低，成本高，不能灵活购买使用。
5)用植物来吸收甲醛。芦荟、吊兰、虎尾兰，一叶兰、龟背竹等植物虽然可以吸收甲醛，但研究表明植物吸收甲醛都是很微量的，不能长期有效的去除大量的甲醛。
面对甲醛的严重危害，目前市面上的治理方法均有所不足。比如：吸附饱和期短，具有二次释放危险，过于依赖紫外线，作用不持久，吸附量过少等痛点，而且这些除甲醛设备仅仅是一种短期性的专用于除甲醛，不具备其他实用性作用。
释放负离子的掐丝珐琅画是一种装饰性很强的宫廷艺术门类，是家居艺术装饰的极佳选择。但由于市面上大多为作坊式生产，没有专门研发团队以及技术人员，制作水平相对比较落后，导致产品质量不高，效率低下，制作成本高，材料不环保，耐候性差等通病。
发明内容
为了克服现有技术的不足，本发明的目的之一在于提供一种释放负离子的掐丝珐琅画的制作方法。
本发明的目的之二在于提供上述制作方法得到的释放负离子的掐丝珐琅画。
本发明的目的之二采用如下技术方案实现：
一种释放负离子的掐丝珐琅画的制作方法，包括以下步骤：
1)将珐琅釉料磨碎，调配成珐琅色釉；
2)将白色负离子粉按3-15wt％的比例混入调好的珐琅色釉；所述白色负离子粉的含有以质量百分比计的以下组分：Ce 22.98％、La 15.56％、Ca 17.01％、Na 9.05％、Mg6.95％、Si 3.29％和P 2.78％；
3)在胎体上绘制工笔线稿；
4)步骤3)处理后的胎体上粘金属丝进行掐丝掰花；
5)步骤4)处理后的胎体上，将步骤2)处理后的在珐琅色釉填充到金属丝以外的部分，进行点蓝施釉；
6)在步骤5)处理的釉面喷洒水溶性聚氨酯胶水定型，干燥，得到释放负离子的掐丝珐琅画。
进一步地，步骤1)中，珐琅釉料磨成80-100目。
进一步地，步骤1)中，珐琅釉料磨成400-1000目。
进一步地，步骤2)中，白色负离子粉的粒径为2000目以上。
进一步地，步骤2)中，白色负离子粉的加入量为8-10wt％。
进一步地，步骤3)中，绘制方法包括手工描绘、丝印、雕刻或喷绘中的一种或两种以上。
进一步地，步骤4)中，粘金属丝使用的粘剂为UV光固化树脂粘合剂。
进一步地，步骤5)中，珐琅色釉的填充高度为金属丝高度的60-80％。
进一步地，步骤6中，晾干釉面当釉面水份蒸发60-80％时，喷洒水溶性聚氨酯胶水定型，重复晾干釉面和喷洒水溶性聚氨酯胶水定型，至水份含量低于5％。
本发明的目的之一采用如下技术方案实现：
上述方法得到的释放负离子的掐丝珐琅画。
相比现有技术，本发明的有益效果在于：
本发明提供了一种具有较高艺术鉴赏价值和释放负离子净化空气功能的掐丝珐琅画的制作方法，该方法采用白色负离子粉作为色釉添加剂，不会对掐丝珐琅画的色泽造成影响，同时能永久性释放负离子，有效去除甲醛，净化空气，用于室内装饰具有较高的实用性。
具体实施方式
下面，结合具体实施方式，对本发明做进一步描述，需要说明的是，在不相冲突的前提下，以下描述的各实施例之间或各技术特征之间可以任意组合形成新的实施例。
本发明提供一种释放负离子的掐丝珐琅画的制作方法，包括以下步骤：
1)将珐琅釉料磨碎，调配成珐琅色釉；
2)将白色负离子粉按3-15wt％的比例混入调好的珐琅色釉；所述白色负离子粉的含有以质量百分比计的以下组分：Ce 22.98％、La 15.56％、Ca 17.01％、Na 9.05％、Mg6.95％、Si 3.29％和P 2.78％；白色负离子粉的粒径为2000-2200目；
本步骤中，采用的白色负离子粉相对于黄色负离子粉，能有效地减少负离子粉掺入对色调的影响，该步骤中，应该注意不能采用水溶性的负离子粉，因为水溶性的负离子粉是经过酸液深加工而成，呈酸性，对金属等材料有腐蚀作用；
3)在胎体上绘制工笔线稿；
4)步骤3)处理后的胎体上粘金属丝进行掐丝掰花；
5)步骤4)处理后的胎体上，将步骤2)处理后的在珐琅色釉填充到金属丝以外的部分，进行点蓝施釉；
6)在步骤5)处理的釉面喷洒水溶性聚氨酯胶水定型，干燥，得到释放负离子的掐丝珐琅画。
该释放负离子的掐丝珐琅画的制作方法，是迎合人们越来越高的艺术审美和对家居装饰画的更高追求的。该释放负离子的掐丝珐琅画既能永久性的释放负氧离子，高效去除甲醛危害，净化空气，又能满足艺术装饰需求，还能避免放置除甲醛设备占用的宝贵空间资源。
实施例1：
一种释放负离子的掐丝珐琅画的制作方法，包括以下步骤：
1)将珐琅釉料磨碎至80-100目，调配成珐琅色釉，该珐琅色釉调配过程中，需要调配主色和过渡色；
2)将白色负离子粉按10wt％的比例混入调好的珐琅色釉；所述白色负离子粉的含有以质量百分比计的以下组分：Ce 22.98％、La 15.56％、Ca 17.01％、Na9.05％、Mg6.95％、Si 3.29％和P 2.78％；白色负离子粉的粒径为2000-2200目；
3)在胎体上采用手工绘制工笔线稿；
4)步骤3)处理后的胎体上使用UV光固化树脂粘合剂粘金属丝进行掐丝掰花；该UV光固化树脂粘合剂具有高透明、高粘结力、耐高温和防水性，极大地提高了掐丝的可操作时间和灵活性；
5)步骤4)处理后的胎体上，将步骤2)处理后的在珐琅色釉填充到金属丝以外的部分，进行点蓝施釉；釉料的厚度控制在金属丝高度的三分之二左右，既可以避免串色，突出金属丝，又能增强立体感；
6)在步骤5)处理的釉面喷洒水溶性聚氨酯胶水定型，干燥，得到释放负离子的掐丝珐琅画。该步骤中，采用减量称量法，当釉面的水份蒸发至一半后，喷胶定型，再晾干蒸发至一半后，喷胶定型，如此反复喷胶4次至釉面水份含量小于5％，再采用晒干或烤干的方式干燥至衡重。
实施例2：
1)将珐琅釉料磨碎至800-1000目，调配成珐琅色釉，该珐琅色釉调配过程中，需要调配主色和过渡色；
2)将白色负离子粉按13wt％的比例混入调好的珐琅色釉；所述白色负离子粉的含有以质量百分比计的以下组分：Ce 22.98％、La 15.56％、Ca 17.01％、Na9.05％、Mg6.95％、Si 3.29％和P 2.78％；白色负离子粉的粒径为2000-2200目；
3)在胎体上采用喷绘的方式绘制工笔线稿；
4)步骤3)处理后的胎体上使用UV光固化树脂粘合剂粘金属丝进行掐丝掰花；该UV光固化树脂粘合剂具有高透明、高粘结力、耐高温和防水性，极大地提高了掐丝的可操作时间和灵活性；
5)步骤4)处理后的胎体上，将步骤2)处理后的在珐琅色釉填充到金属丝以外的部分，进行点蓝施釉；釉料的厚度控制在金属丝高度的三分之二左右，既可以避免串色，突出金属丝，又能增强立体感；
6)在步骤5)处理的釉面喷洒水溶性聚氨酯胶水定型，干燥，得到释放负离子的掐丝珐琅画。该步骤中，采用减量称量法，当釉面的水份蒸发至一半后，喷胶定型，再晾干蒸发至一半后，喷胶定型，如此反复喷胶5次至釉面水份含量小于5％，再采用晒干或烤干的方式干燥至衡重。
实施例3：
1)将珐琅釉料磨碎至1000-1200目，调配成珐琅色釉，该珐琅色釉调配过程中，需要调配主色和过渡色；
2)将白色负离子粉按3wt％的比例混入调好的珐琅色釉；所述白色负离子粉的含有以质量百分比计的以下组分：Ce 22.98％、La 15.56％、Ca 17.01％、Na9.05％、Mg6.95％、Si 3.29％和P 2.78％；白色负离子粉的粒径为2000-2200目；
3)在胎体上采用丝印的方式绘制工笔线稿；
4)步骤3)处理后的胎体上使用UV光固化树脂粘合剂粘金属丝进行掐丝掰花；该UV光固化树脂粘合剂具有高透明、高粘结力、耐高温和防水性，极大地提高了掐丝的可操作时间和灵活性；
5)步骤4)处理后的胎体上，将步骤2)处理后的在珐琅色釉填充到金属丝以外的部分，进行点蓝施釉；釉料的厚度控制在金属丝高度的三分之二左右，既可以避免串色，突出金属丝，又能增强立体感；
6)在步骤5)处理的釉面喷洒水溶性聚氨酯胶水定型，干燥，得到释放负离子的掐丝珐琅画。该步骤中，采用减量称量法，当釉面的水份蒸发至一半后，喷胶定型，再晾干蒸发至一半后，喷胶定型，如此反复喷胶5次至釉面水份含量小于5％，再采用晒干或烤干的方式干燥至衡重。
性能检测与效果评价：
采用COM-3010PRO的日本进口负离子检测仪来检测尺寸为30cm×30cm的实施例1-3得到的释放负离子的掐丝珐琅画的负离子释放浓度。结果如下表所示：
表1负离子释放浓度
| 实施例1 | 实施例2 | 实施例3 |
| 1862个/cm<sup>3</sup> | 1891/cm<sup>3</sup> | 1538/cm<sup>3</sup> |
根据联合国卫生组织的标准，空气中负离子含量达到每立方厘米1500个时是空气清新的标准。达到每立方厘米2万个以上则具有医疗保健的功效。即，本申请得到的释放负离子的掐丝珐琅画的负离子释放量超过了空气清新的标准。
上述实施方式仅为本发明的优选实施方式，不能以此来限定本发明保护的范围，本领域的技术人员在本发明的基础上所做的任何非实质性的变化及替换均属于本发明所要求保护的范围。
Claims (7)
1.一种释放负离子的掐丝珐琅画的制作方法，其特征在于，包括以下步骤：
1）将珐琅釉料磨碎，调配成珐琅色釉；
2）将白色负离子粉按8-10wt%的比例混入调好的珐琅色釉；所述白色负离子粉的含有以质量百分比计的以下组分：Ce 22.98%、La 15.56%、Ca 17.01%、Na 9.05%、Mg 6.95%、Si3.29%和P 2.78%；白色负离子粉的粒径为2000目以上；所述白色负离子粉为非水溶性白色负离子粉；
3）在胎体上绘制工笔线稿；
4）步骤3）处理后的胎体上粘金属丝进行掐丝掰花；
5）步骤4）处理后的胎体上，将步骤2）处理后的在珐琅色釉填充到金属丝以外的部分，进行点蓝施釉；
6）在步骤5）处理的釉面喷洒水溶性聚氨酯胶水定型，晾干釉面当釉面水份蒸发60-80%时，喷洒水溶性聚氨酯胶水定型，重复晾干釉面和喷洒水溶性聚氨酯胶水定型，至水份含量低于5%，再采用晒干或烤干的方式干燥，得到释放负离子的掐丝珐琅画。
2.如权利要求1所述的释放负离子的掐丝珐琅画的制作方法，其特征在于，步骤1）中，珐琅釉料磨成80-100目。
3.如权利要求1所述的释放负离子的掐丝珐琅画的制作方法，其特征在于，步骤1）中，珐琅釉料磨成400-1000目。
4.如权利要求1所述的释放负离子的掐丝珐琅画的制作方法，其特征在于，步骤3）中，绘制方法包括手工描绘、丝印、雕刻或喷绘中的一种或两种以上。
5.如权利要求1所述的释放负离子的掐丝珐琅画的制作方法，其特征在于，步骤4）中，粘金属丝使用的粘剂为UV光固化树脂粘合剂。
6.如权利要求1所述的释放负离子的掐丝珐琅画的制作方法，其特征在于，步骤5）中，珐琅色釉的填充高度为金属丝高度的60-80%。
7.如权利要求1-6任一项所述的释放负离子的掐丝珐琅画的制作方法得到的释放负离子的掐丝珐琅画。