CN108316023A - 一种阻燃环保型双喷油画布及其生产方法 - Google Patents

一种阻燃环保型双喷油画布及其生产方法 Download PDF

Info

Publication number
CN108316023A
CN108316023A CN201810278347.0A CN201810278347A CN108316023A CN 108316023 A CN108316023 A CN 108316023A CN 201810278347 A CN201810278347 A CN 201810278347A CN 108316023 A CN108316023 A CN 108316023A
Authority
CN
China
Prior art keywords
blotting
layer
parts
base material
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810278347.0A
Other languages
English (en)
Inventor
张洪彪
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU AOLI ADVERTISEMENT MATERIAL CO Ltd
Original Assignee
JIANGSU AOLI ADVERTISEMENT MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU AOLI ADVERTISEMENT MATERIAL CO Ltd filed Critical JIANGSU AOLI ADVERTISEMENT MATERIAL CO Ltd
Priority to CN201810278347.0A priority Critical patent/CN108316023A/zh
Publication of CN108316023A publication Critical patent/CN108316023A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种阻燃环保型双喷油画布，其能解决现有的双喷油画布环保性差、阻燃性差、喷绘效果差，绘画后制作容易起皱纹，淋水易褪色的技术问题。一种阻燃环保型双喷油画布，其特征在于：其包括基材，基材的正面自上而下设置有第一吸墨图层、第二吸墨图层、第三吸墨图层和第四吸墨图层，基材的反面自下而上设置有第一吸墨图层、第二吸墨图层和第三吸墨图层；第二吸墨图层包括按重量份计的以下原料，丙烯酸乳液26份，天然石粉14份，粉状二氧化硅8份、氯化石蜡5份；第三吸墨图层包括按重量份计的以下原料，丙烯酸乳液26份，天然石粉16份，粉状二氧化硅5份、氯化石蜡4.5份、三氧化二锑1.8份。

Description

一种阻燃环保型双喷油画布及其生产方法
技术领域
本发明涉及油画布，具体涉及一种阻燃环保型双喷油画布及其生产方法。
背景技术
现有的双喷油画布包括基材和涂布于基材正反两面的吸墨图层，基材是以纤维素和蛋白质等天然高分子化合物为原料，经化学加工制成高分子浓缩液，然后经纺丝和后处理而制成纺织纤维，再编制成的基布；吸墨图层是将包含甲醇、乙酯的有机物混合搅拌成的浆料于基布正反两面涂布形成。然而该种双喷油画布，不仅环保性差、阻燃性差，而且喷绘效果差，绘画后制作容易起皱纹，淋水易褪色。
发明内容
针对上述问题，本发明提供了一种阻燃环保型双喷油画布，其能解决现有的双喷油画布环保性差、阻燃性差、喷绘效果差，绘画后制作容易起皱纹，淋水易褪色的技术问题。
其技术方案是这样的，一种阻燃环保型双喷油画布，其特征在于：其包括基材，所述基材的正面自上而下设置有第一吸墨图层、第二吸墨图层、第三吸墨图层和第四吸墨图层，所述基材的反面自下而上设置有第一吸墨图层、第二吸墨图层和第三吸墨图层；
所述第一吸墨图层包括按重量份计的以下原料，水性丙烯酸乳液26份，天然石粉14份；
所述第二吸墨图层包括按重量份计的以下原料，丙烯酸乳液26份，天然石粉14份，粉状二氧化硅8份、氯化石蜡5份；
所述第三吸墨图层包括按重量份计的以下原料，丙烯酸乳液26份，天然石粉16份，粉状二氧化硅5份、氯化石蜡4.5份、三氧化二锑1.8份；
所述第四吸墨图层包括按重量份计的以下原料，水性丙烯酸乳液26份，天然石粉14份，水性黑色浆5份。
进一步的，所述基材为化纤编织布。
本发明还提供了上述阻燃环保型双喷油画布的生产方法，包括以下步骤：
S1、将所述第四吸墨图层的各原料按照配比混匀后升温至65℃搅拌5分钟，形成的浆料以25 g/m2-50 g/m2的干胶克重均匀的涂布在基材正面，形成第四吸墨图层，并进行烘干处理；
S2、将第三吸墨图层的各原料按照配比混匀后升温至85℃并搅拌5分钟，形成的浆料以25 g/m2-30 g/m2的干胶克重均匀的涂布在步骤S1处理后的基材的正反两面，形成第三吸墨图层，并进行烘干处理；
S3、将第二吸墨图层的各原料按照配比混匀后升温至85℃搅拌3分钟，形成的浆料以25g/m2-30 g/m2的干胶克重均匀的涂布在步骤S2处理后的基材的正反两面，形成第二吸墨涂层，并进行烘干处理；
S4、将第一吸墨图层的各原料按照配比混匀后升温至65℃搅拌3分钟，形成的浆料以25g/m2-30 g/m2的干胶克重均匀的涂布在步骤S3处理后的基材的正反两面，形成第一吸墨涂层，并进行烘干处理，得到成品。
进一步的，步骤S1、S2和S3中，烘干处理的具体操作为，以25m/min-30m/min的速度通过温度为80℃-110℃的烘箱。
本发明通过水性丙烯酸乳液的选择，提高了产品的环保性，通过在第二吸墨图层、第三吸墨图层添加氯化石蜡，提高产品的阻燃性，通过在第三吸墨涂层添加三氧化二锑、第四吸墨图层添加黑色浆，提高产品的遮光性，同时，通过对各吸墨图层的组分选择和配比调整，使得画面平整、防水性能提升，并且产品喷绘后，色泽靓丽，饱和度高。
附图说明
图1为本发明的结构示意图。
具体实施方式
如图1所示，一种阻燃环保型双喷油画布,其包括基材5，基材5的正面自上而下设置有第一吸墨图层1、第二吸墨图层2、第三吸墨图层3和第四吸墨图层4，基材5的反面自下而上设置有第一吸墨图层1、第二吸墨图层2和第三吸墨图层3；
基材5为化纤编织布；
第一吸墨图层1包括按重量份计的以下原料，水性丙烯酸乳液26份，天然石粉14份；
第二吸墨图层2包括按重量份计的以下原料，丙烯酸乳液26份，天然石粉14份，粉状二氧化硅8份、氯化石蜡5份；
第三吸墨图层3包括按重量份计的以下原料，丙烯酸乳液26份，天然石粉16份，粉状二氧化硅5份、氯化石蜡4.5份、三氧化二锑1.8份；
第四吸墨图层4包括按重量份计的以下原料，水性丙烯酸乳液26份，天然石粉14份，水性黑色浆5份。
上述阻燃环保型双喷油画布的生产方法，包括以下步骤：
S1、将第四吸墨图层的各原料按照配比混匀后升温至65℃搅拌5分钟，形成的浆料以30g/m2的干胶克重均匀的涂布在基材正面，形成第四吸墨图层，并以30m/min的速度通过温度为80℃的烘箱进行烘干处理；
S2、将第三吸墨图层的各原料按照配比混匀后升温至85℃并搅拌5分钟，形成的浆料以25 g/m2的干胶克重均匀的涂布在步骤S1处理后的基材的正反两面，形成第三吸墨图层，并以25m/min的速度通过温度为100℃的烘箱进行烘干处理；
S3、将第二吸墨图层的各原料按照配比混匀后升温至85℃搅拌3分钟，形成的浆料以25g/m2的干胶克重均匀的涂布在步骤S2处理后的基材的正反两面，形成第二吸墨涂层，并以5m/min的速度通过温度为100℃的烘箱进行烘干处理；
S4、将第一吸墨图层的各原料按照配比混匀后升温至65℃搅拌3分钟，形成的浆料以25g/m2的干胶克重均匀的涂布在步骤S3处理后的基材的正反两面，形成第一吸墨涂层，并以30m/min的速度通过温度为80℃的烘箱进行烘干处理，得到成品。
其中，各吸墨图层的原料混合时，可根据需求添加5份~20份的去离子水。
本发明制备的双喷油画布，环保性、阻燃性、防水性能，画面平整，喷绘后色泽靓丽，饱和度高，不易起皱纹，喷绘效果好，并且淋水不褪色。

Claims (4)

1.一种阻燃环保型双喷油画布，其特征在于：其包括基材，所述基材的正面自上而下设置有第一吸墨图层、第二吸墨图层、第三吸墨图层和第四吸墨图层，所述基材的反面自下而上设置有第一吸墨图层、第二吸墨图层和第三吸墨图层；
所述第一吸墨图层包括按重量份计的以下原料，水性丙烯酸乳液26份，天然石粉14份；
所述第二吸墨图层包括按重量份计的以下原料，丙烯酸乳液26份，天然石粉14份，粉状二氧化硅8份、氯化石蜡5份；
所述第三吸墨图层包括按重量份计的以下原料，丙烯酸乳液26份，天然石粉16份，粉状二氧化硅5份、氯化石蜡4.5份、三氧化二锑1.8份；
所述第四吸墨图层包括按重量份计的以下原料，水性丙烯酸乳液26份，天然石粉14份，水性黑色浆5份。
2.根据权利要求1所述的一种阻燃环保型双喷油画布，其特征在于：所述基材为化纤编织布。
3.如权利要求1所述的阻燃环保型双喷油画布的生产方法，包括以下步骤：
S1、将所述第四吸墨图层的各原料按照配比混匀后升温至65℃搅拌5分钟，形成的浆料以25 g/m2-50 g/m2的干胶克重均匀的涂布在基材正面，形成第四吸墨图层，并进行烘干处理；
S2、将第三吸墨图层的各原料按照配比混匀后升温至85℃并搅拌5分钟，形成的浆料以25 g/m2-30 g/m2的干胶克重均匀的涂布在步骤S1处理后的基材的正反两面，形成第三吸墨图层，并进行烘干处理；
S3、将第二吸墨图层的各原料按照配比混匀后升温至85℃搅拌3分钟，形成的浆料以25g/m2-30 g/m2的干胶克重均匀的涂布在步骤S2处理后的基材的正反两面，形成第二吸墨涂层，并进行烘干处理；
S4、将第一吸墨图层的各原料按照配比混匀后升温至65℃搅拌3分钟，形成的浆料以25g/m2-30 g/m2的干胶克重均匀的涂布在步骤S3处理后的基材的正反两面，形成第一吸墨涂层，并进行烘干处理，得到成品。
4.根据权利要求3所述的生产方法，其特征在于：步骤S1、S2和S3中，烘干处理的具体操作为，以25m/min-30m/min的速度通过温度为80℃-110℃的烘箱。
CN201810278347.0A 2018-03-31 2018-03-31 一种阻燃环保型双喷油画布及其生产方法 Pending CN108316023A (zh)