CN108300414B - 一种防滑纳米材料及其制备方法 - Google Patents
一种防滑纳米材料及其制备方法 Download PDFInfo
- Publication number
- CN108300414B CN108300414B CN201810131410.8A CN201810131410A CN108300414B CN 108300414 B CN108300414 B CN 108300414B CN 201810131410 A CN201810131410 A CN 201810131410A CN 108300414 B CN108300414 B CN 108300414B
- Authority
- CN
- China
- Prior art keywords
- acid
- skid
- slip
- nanomaterial
- fullerol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及防滑材料领域，更具体的本发明提供一种防滑纳米材料及其制备方法。所述防滑纳米材料，以重量份计，至少包括以下组分：有机酸1～5份；分散保湿剂1～8份；碱性材料0.5～2份；纳米粒子0.1～3份；溶剂50～90份。所述防滑纳米材料的制备方法，至少包括以下步骤：将各组分进行均匀混合后，得到防滑纳米材料。
Description
技术领域
本发明涉及防滑材料领域，更具体的本发明提供一种防滑纳米材料及其制备方法。
背景技术
防滑材料又称为防滑剂，是一种可以防滑的液体，可用于天然石材或硬瓷砖表面，如瓷砖、地砖、水磨石、石板、花岗石、大理石、陶瓷及陶瓷浴缸、沐浴间地面及其他石材或无机材料表面。
现在市面上的防滑剂普遍存在渗透力不强，且处理后需要进行亚光处理，因此需要配套使用抛光机，尤其是大理石材质的地板亮度需下降30％以上，但是在处理时由于抛光机、抛光液、人力等成本，造成国内防滑处理造价偏高。
目前，防滑机理主要有以下两种：(1)在成品表面涂抹防滑剂，利用附着在成品表面的防滑剂提高摩擦系数。(2)将成品表面制成具有宏观或微观的凹凸起伏不平的结构，利用这种结构和鞋底在压力下产生的机械咬合作用来提高摩擦系数，防止打滑摔倒。但是现有方法的不足之处也很明显：虽然在成品表面涂抹防滑剂的方法虽然实用，而且防滑效果也比较理想，但是涂抹的防滑层会随着使用时间的延长而逐渐被磨损，从而失去防滑效果；通过在成品表面制造一些宏观的凹凸或纹路虽然可以实现防滑，但是却破坏了板石的装饰效果；采用具有腐蚀性的液体处理成品板表面，虽然可以增强防滑效果，但是同样破坏了成品表面的美观，而且工艺过程复杂、处理周期太长，对环境的影响较大，造成环境的污染，不适合现有的大生产技术。
因此，非常需要通过技术改进，提供一种新型防滑纳米材料。
发明内容
为了解决上述问题，本发明第一个方面提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
作为本发明一种优选的技术方案，所述防滑纳米材料，以重量份计，至少包括以下组分：
作为本发明一种优选的技术方案，所述防滑纳米材料，以重量份计，至少包括以下组分：
作为本发明一种优选的技术方案，所述有机酸选自：柠檬酸、酒石酸、苹果酸、草酸、马来酸、硬脂酸、枸椽酸、癸酸、己酸、壬酸、辛酸、丙酸、戊酸、牛磺酸中任意一种或几种的混合。
作为本发明一种优选的技术方案，所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物。
作为本发明一种优选的技术方案，所述碱性材料选自：硫酸铵、二乙醇胺、三乙醇胺、异丙醇胺、N,N-二甲基乙醇胺、N-叔丁基二乙醇胺、N-丁基二乙醇胺、N-甲基二乙醇胺、N-乙基二乙醇胺、N-异丁基二乙醇胺、N-甲基二异丙醇胺、N-甲基-N-乙基乙醇胺、三异丙醇胺中的任意一种或几种的混合。
作为本发明一种优选的技术方案，所述纳米粒子为富勒醇纳米粒子。
作为本发明一种优选的技术方案，所述富勒醇纳米粒子为羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物。
作为本发明一种优选的技术方案，所述防滑纳米材料还包括表面活性剂、消泡剂、渗透剂、光稳定剂、杀菌剂中的任意一种或几种的混合。
本发明的第二个方面提供了防滑纳米材料的制备方法，至少包括以下步骤：
将各组分进行均匀混合后，得到防滑纳米材料。
参考以下详细说明更易于理解本申请的上述以及其他特征、方面和优点。
具体实施方式
参选以下本发明的优选实施方法的详述以及包括的实施例可更容易地理解本发明的内容。除非另有限定，本文使用的所有技术以及科学术语具有与本发明所属领域普通技术人员通常理解的相同的含义。当存在矛盾时，以本说明书中的定义为准。
如本文所用术语“由…制备”与“包含”同义。本文中所用的术语“包含”、“包括”、“具有”、“含有”或其任何其它变形，意在覆盖非排它性的包括。例如，包含所列要素的组合物、步骤、方法、制品或装置不必仅限于那些要素，而是可以包括未明确列出的其它要素或此种组合物、步骤、方法、制品或装置所固有的要素。
连接词“由…组成”排除任何未指出的要素、步骤或组分。如果用于权利要求中，此短语将使权利要求为封闭式，使其不包含除那些描述的材料以外的材料，但与其相关的常规杂质除外。当短语“由…组成”出现在权利要求主体的子句中而不是紧接在主题之后时，其仅限定在该子句中描述的要素；其它要素并不被排除在作为整体的所述权利要求之外。
当量、浓度、或者其它值或参数以范围、优选范围、或一系列上限优选值和下限优选值限定的范围表示时，这应当被理解为具体公开了由任何范围上限或优选值与任何范围下限或优选值的任一配对所形成的所有范围，而不论该范围是否单独公开了。例如，当公开了范围“1至5”时，所描述的范围应被解释为包括范围“1至4”、“1至3”、“1至2”、“1至2和4至5”、“1至3和5”等。当数值范围在本文中被描述时，除非另外说明，否则该范围意图包括其端值和在该范围内的所有整数和分数。
单数形式包括复数讨论对象，除非上下文中另外清楚地指明。“任选的”或者“任意一种”是指其后描述的事项或事件可以发生或不发生，而且该描述包括事件发生的情形和事件不发生的情形。
说明书和权利要求书中的近似用语用来修饰数量，表示本发明并不限定于该具体数量，还包括与该数量接近的可接受的而不会导致相关基本功能的改变的修正的部分。相应的，用“大约”、“约”等修饰一个数值，意为本发明不限于该精确数值。在某些例子中，近似用语可能对应于测量数值的仪器的精度。在本申请说明书和权利要求书中，范围限定可以组合和/或互换，如果没有另外说明这些范围包括其间所含有的所有子范围。
此外，本发明要素或组分前的不定冠词“一种”和“一个”对要素或组分的数量要求(即出现次数)无限制性。因此“一个”或“一种”应被解读为包括一个或至少一个，并且单数形式的要素或组分也包括复数形式，除非所述数量明显旨指单数形式。
“聚合物”意指通过聚合相同或不同类型的单体所制备的聚合化合物。通用术语“聚合物”包含术语“均聚物”、“共聚物”、“三元共聚物”与“共聚体”。“共聚体”意指通过聚合至少两种不同单体制备的聚合物。通用术语“共聚体”包括术语“共聚物”(其一般用以指由两种不同单体制备的聚合物)与术语“三元共聚物”(其一般用以指由三种不同单体制备的聚合物)。其亦包含通过聚合更多种单体而制造的聚合物。“共混物”意指两种或两种以上聚合物通过物理的或化学的方法共同混合而形成的聚合物。
为了解决上述问题，本发明第一个方面提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
在一种优选的实施方式中，所述防滑纳米材料，以重量份计，至少包括以下组分：
在一种优选的实施方式中，所述防滑纳米材料，以重量份计，至少包括以下组分：
有机酸
本申请中，所述有机酸并没有特别的限定，可以为市售的任一品种，任一牌号的有机酸。
在一种优选的实施方式中，所述有机酸选自：柠檬酸、酒石酸、苹果酸、草酸、马来酸、硬脂酸、枸椽酸、癸酸、己酸、壬酸、辛酸、丙酸、戊酸、牛磺酸中任意一种或几种的混合。
在一种优选的实施方式中，所述有机酸为柠檬酸、牛磺酸的混合酸。
在一种优选的实施方式中，所述柠檬酸、牛磺酸的混合酸中，柠檬酸、牛磺酸的重量比为100：1。
分散保湿剂
本申请中，所述分散保湿剂并没有特别的限定，在体系中，能够稳定分散纳米粒子，同时还能够对防滑表面进行保湿。
在一种优选的实施方式中，所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物。
在一种优选的实施方式中，所述乙二醇单丁醚、异丙醇的重量比为1：(1～5)；最优选为：所述乙二醇单丁醚、异丙醇的重量比为1：3。
碱性材料
本申请中，所述碱性材料为铵类化合物或者有机胺中的任意一种。
在一种优选的实施方式中，所述碱性材料选自：硫酸铵、二乙醇胺、三乙醇胺、异丙醇胺、N,N-二甲基乙醇胺、N-叔丁基二乙醇胺、N-丁基二乙醇胺、N-甲基二乙醇胺、N-乙基二乙醇胺、N-异丁基二乙醇胺、N-甲基二异丙醇胺、N-甲基-N-乙基乙醇胺、三异丙醇胺中的任意一种或几种的混合。
纳米粒子
本申请中的纳米粒子在体系的作用下，会与基材发生反应，有效的改进了基材表面的微观结构，进一步增加了基材表面的摩擦力与吸盘力。
在一种优选的实施方式中，所述纳米粒子为富勒醇纳米粒子。
在一种优选的实施方式中，所述富勒醇纳米粒子为羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物。
在一种优选的实施方式中，所述羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇纳米粒子复合物中，羧化壳聚糖、七(6-氨基-6-去氧)-β-环糊精、富勒醇的重量比为1：2：1。
在一种优选的实施方式中，所述羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物的制备方法，至少包括以下步骤：
向10mL富勒醇水溶液中，加入1g的羧化壳聚糖，将反应温度升高至40℃，搅拌反应2h后，再向体系中加入2g的七(6-氨基-6-去氧)-β-环糊精，将反应温度升高至50℃，搅拌反应4h后，得到羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物。
所述羧化壳聚糖购于南京都莱生物技术有限公司；
所述七(6-氨基-6-去氧)-β-环糊精购于山东滨州智源生物科技有限公司；
所述富勒醇纳米粒子购于苏州恒球石墨烯有限公司。
溶剂
本申请中，所述溶剂并没有特别的限制，可以为水或者醇类中的任意一种或几种的混合。从环保的角度上考虑，优选为水。
在一种优选的实施方式中，所述防滑纳米材料还包括表面活性剂、消泡剂、渗透剂、光稳定剂、杀菌剂中的任意一种或几种的混合。
所述表面活性剂可以列举的有：十二烷基醇聚氧乙烯醚硫酸钠、十二烷基硫酸铵、十二烷基磷酸酯钾盐、十二烷基磷酸酯三乙醇胺、十二烷基苯磺酸钠、十二烷基甘油醚羧酸盐、月桂基硫酸三乙醇胺、仲烷基磺酸钠、脂肪醇羟乙基磺酸钠、N-月桂酰肌氨酸钠、酰胺基聚氧乙烯醚硫酸镁、十二醇聚氧乙烯醚磺基琥珀酸酯二钠、α-烯基磺酸钠、脂肪醇醚硫酸钠、乙氧基化脂肪酸甲酯的磺酸盐、醇醚羧酸盐、硬脂酸甲酯聚氧乙烯醚磺酸钠、异辛醇磷酸酯等。
所述消泡剂可以列举的有：聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚、聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷等。
所述渗透剂可以列举的有：辛基醇聚氧乙烯醚、壬基醇聚氧乙烯醚、癸基醇聚氧乙烯醚、十一烷基醇聚氧乙烯醚、月桂醇聚氧乙烯醚、十三烷基醇聚氧乙烯醚、肉豆蔻醇聚氧乙烯醚、十五烷基醇聚氧乙烯醚、棕榈醇聚氧乙烯醚、十七烷基醇聚氧乙烯醚、硬脂醇聚氧乙烯醚、辛基醇聚氧乙烯聚氧丙烯醚、壬基醇聚氧乙烯聚氧丙烯醚、癸基醇聚氧乙烯聚氧丙烯醚、十一烷基醇聚氧乙烯聚氧丙烯醚、月桂醇聚氧乙烯聚氧丙烯醚、十三烷基醇聚氧乙烯聚氧丙烯醚、肉豆蔻醇聚氧乙烯聚氧丙烯醚、十五烷基醇聚氧乙烯聚氧丙烯醚、棕榈醇聚氧乙烯聚氧丙烯醚、十七烷基醇聚氧乙烯聚氧丙烯醚、硬脂醇聚氧乙烯聚氧丙烯醚、辛基胺聚氧乙烯聚氧丙烯醚、壬基胺聚氧乙烯聚氧丙烯醚、癸基胺聚氧乙烯聚氧丙烯醚、十一烷基胺聚氧乙烯聚氧丙烯醚、月桂胺聚氧乙烯聚氧丙烯醚、十三烷基胺聚氧乙烯聚氧丙烯醚、肉豆蔻胺聚氧乙烯聚氧丙烯醚、十五烷基胺聚氧乙烯聚氧丙烯醚、棕榈胺聚氧乙烯聚氧丙烯醚、十七烷基胺聚氧乙烯聚氧丙烯醚、硬脂胺聚氧乙烯聚氧丙烯醚等。
所述紫外线吸收剂可以列举的有：2-(2-羟基-5-甲基苯基)苯并三唑、2-(2-羟基-5-丁基苯基)苯并三唑、2-(2-羟基-5-辛基苯基)苯并三唑、2-(3-叔丁基-2-羟基-5-甲基苯基)-5-氯苯并三唑、2-(3，5-二叔戊基-2-羟基苯基)苯并三唑等苯并三唑系紫外线吸收剂；2-羟基-4-甲氧基二苯甲酮、2-羟基-4-正辛基氧基二苯甲酮等二苯甲酮系紫外线吸收剂；2-[4，6-双(2，4-二甲基苯基)-1，3，5-三嗪-2-基]-5-(辛基氧基)苯酚、2-(4，6-二苯基-1，3，5-三嗪-2-基)-5-(己基氧基)苯酚等三嗪系紫外线吸收剂；水杨酸对叔丁基苯酯、水杨酸苯酯等水杨酸酯系紫外线吸收剂等。
所述抗菌剂可以列举的有：银离子类抗菌剂、氧化锌、氧化铜、磷酸二氢铵、碳酸锂、酰基苯胺类、咪唑类、噻唑类、异噻唑酮衍生物、季铵盐类、双胍类、酚类甲酸、山梨酸、有机碘、硫氰、铜剂、三卤化烯丙基化合物、有机氮硫化合物、甲壳素、芥末、蓖麻油、山葵等。
本发明的第二个方面提供了防滑纳米材料的制备方法，至少包括以下步骤：
将各组分进行均匀混合后，得到防滑纳米材料。
下面通过实施例对本发明进行具体描述。有必要在此指出的是，以下实施例只用于对本发明作进一步说明，不能理解为对本发明保护范围的限制，该领域的专业技术人员根据上述本发明的内容做出的一些非本质的改进和调整，仍属于本发明的保护范围。
另外，如果没有其它说明，所用原料都是市售的，购于国药化学试剂。
实施例1：
本发明的实施例1提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸；
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例2：
本发明的实施例2提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸；
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例3：
本发明的实施例3提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸；
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例4：
本发明的实施例4提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸；
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例5：
本发明的实施例5提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸；
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例6：
本发明的实施例6提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为牛磺酸；
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例7：
本发明的实施例7提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸、牛磺酸的混合酸；所述柠檬酸、牛磺酸的混合酸中，柠檬酸、牛磺酸的重量比为1：1。
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例8：
本发明的实施例8提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸、牛磺酸的混合酸；所述柠檬酸、牛磺酸的混合酸中，柠檬酸、牛磺酸的重量比为50：1。
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例9：
本发明的实施例9提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸、牛磺酸的混合酸；所述柠檬酸、牛磺酸的混合酸中，柠檬酸、牛磺酸的重量比为100：1。
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；所述富勒醇纳米粒子为富勒醇水溶液；购于苏州恒球石墨烯有限公司；
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
实施例10：
本发明的实施例10提供了一种防滑纳米材料，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述有机酸为柠檬酸、牛磺酸的混合酸；所述柠檬酸、牛磺酸的混合酸中，柠檬酸、牛磺酸的重量比为100：1。
所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物；所述乙二醇单丁醚、异丙醇的重量比为1：6；
所述碱性材料为硫酸铵；
所述纳米粒子为富勒醇纳米粒子；
所述富勒醇纳米粒子为羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物；
所述羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇纳米粒子复合物中，羧化壳聚糖、七(6-氨基-6-去氧)-β-环糊精、富勒醇的重量比为1：2：1；
所述羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物的制备方法，至少包括以下步骤：
向10mL富勒醇水溶液中，加入1g的羧化壳聚糖，将反应温度升高至40℃，搅拌反应2h后，再向体系中加入2g的七(6-氨基-6-去氧)-β-环糊精，将反应温度升高至50℃，搅拌反应4h后，得到羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物。
所述羧化壳聚糖购于南京都莱生物技术有限公司；
所述七(6-氨基-6-去氧)-β-环糊精购于山东滨州智源生物科技有限公司；
所述富勒醇纳米粒子购于苏州恒球石墨烯有限公司。
所述溶剂为水；
所述防滑纳米材料的制备方法，至少包括以下步骤：
将上述各组分进行均匀混合后，得到防滑纳米材料。
对比例1：
本申请的对比例1同实施例10，不同点在于，将富勒醇纳米粒子修改为羧化壳聚糖。
对比例2：
本申请的对比例2同实施例10，不同点在于，将富勒醇纳米粒子修改为七(6-氨基-6-去氧)-β-环糊精。
对比例3：
本申请的对比例3同实施例10，不同点在于，将富勒醇纳米粒子修改为将羧化壳聚糖、七(6-氨基-6-去氧)-β-环糊精、富勒醇进行简单的混合。
对比例4：
本申请的对比例4同实施例10，不同点在于，将富勒醇纳米粒子修改为羧化壳聚糖/富勒醇复合物。
对比例5：
本申请的对比例5同实施例10，不同点在于，将富勒醇纳米粒子修改为七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物。
对比例6：
本申请的对比例6同实施例10，不同点在于，将七(6-氨基-6-去氧)-β-环糊精更换为β-环糊精。
对比例7：
本申请的对比例7同实施例10，不同点在于，将七(6-氨基-6-去氧)-β-环糊精更换为α-环糊精。
对比例8：
本申请的对比例8同实施例10，不同点在于，将七(6-氨基-6-去氧)-β-环糊精更换为γ-环糊精。
对比例9：
本申请的对比例9同实施例10，不同点在于，将纳米粒子更换为纳米二氧化硅。
对比例10：
本申请的对比例10同实施例10，不同点在于，将纳米粒子更换为将纳米粒子更换为石墨烯。
性能测试：
将实施例1～10以及对比例1～10得到的防滑纳米材料，分别喷涂在陶瓷表面，使用量为10g/m2，设置两组实验，一组进行测试湿静摩擦系数，另一组测试干静摩擦系数，所述干静摩擦系数是指将喷涂了防滑纳米材料的陶瓷进行烘干，静摩擦系数的测试采用美国滑移计公司生产的ASM825A静摩擦系数仪来测试。将这两组实验的陶瓷，在100℃的环境下放置2年后，再次进行测试摩擦系数。结果如表1所示。
表1性能测试结果
本申请中的防滑纳米材料具有非常好的防滑性能，即使是在干燥的环境下仍然具有较好的防滑性能。经过高温以及长时间处理后，湿静摩擦系数和干静摩擦系数有较小的变化。同时，这些成品的表面的光泽度没有发生任何的变化，并没有出现光泽度下降的现象。
上述的实例仅是说明性的，用于解释本发明的特征的一些特征。所附的权利要求旨在要求可以设想的尽可能广的范围，且本文所呈现的实施例仅是根据所有可能的实施例的组合的选择的实施方式的说明。因此，申请人的用意是所附的权利要求不被说明本发明的特征的示例的选择限制，而且在科技上的进步将形成由于语言表达的不准确的原因而未被目前考虑的可能的等同物或子替换，且这些变化也应在可能的情况下被解释为被所附的权利要求覆盖。
Claims (6)
1.一种防滑纳米材料，其特征在于，所述防滑纳米材料，以重量份计，至少包括以下组分：
所述碱性材料选自：硫酸铵、二乙醇胺、三乙醇胺、异丙醇胺、N,N-二甲基乙醇胺、N-叔丁基二乙醇胺、N-丁基二乙醇胺、N-甲基二乙醇胺、N-乙基二乙醇胺、N-异丁基二乙醇胺、N-甲基二异丙醇胺、N-甲基-N-乙基乙醇胺、三异丙醇胺中的任意一种或几种的混合；
所述纳米粒子为富勒醇纳米粒子；
所述富勒醇纳米粒子为羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物；
所述羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物的制备方法，至少包括以下步骤：
向10mL富勒醇水溶液中，加入1g的羧化壳聚糖，将反应温度升高至40℃，搅拌反应2h后，再向体系中加入2g的七(6-氨基-6-去氧)-β-环糊精，将反应温度升高至50℃，搅拌反应4h后，得到羧化壳聚糖/七(6-氨基-6-去氧)-β-环糊精/富勒醇复合物。
2.如权利要求1所述的防滑纳米材料，其特征在于，所述防滑纳米材料，以重量份计，至少包括以下组分：
3.如权利要求1所述的防滑纳米材料，其特征在于，所述有机酸选自：柠檬酸、酒石酸、苹果酸、草酸、马来酸、硬脂酸、枸椽酸、癸酸、己酸、壬酸、辛酸、丙酸、戊酸、牛磺酸中任意一种或几种的混合。
4.如权利要求1所述的防滑纳米材料，其特征在于，所述分散保湿剂为乙二醇单丁醚、异丙醇的混合物。
5.如权利要求1所述的防滑纳米材料，其特征在于，所述防滑纳米材料还包括表面活性剂、消泡剂、渗透剂、光稳定剂、杀菌剂中的任意一种或几种的混合。
6.如权利要求1～5任意一项所述的防滑纳米材料的制备方法，其特征在于，至少包括以下步骤：
将各组分进行均匀混合后，得到防滑纳米材料。