CN108299924A - 一种增白的白色漆及其制作方法 - Google Patents
一种增白的白色漆及其制作方法 Download PDFInfo
- Publication number
- CN108299924A CN108299924A CN201710689037.3A CN201710689037A CN108299924A CN 108299924 A CN108299924 A CN 108299924A CN 201710689037 A CN201710689037 A CN 201710689037A CN 108299924 A CN108299924 A CN 108299924A
- Authority
- CN
- China
- Prior art keywords
- white paint
- brightened
- additive
- fluorescent whitening
- whitening agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种增白的白色漆及其制作方法。主要组成成分及重量配比为UV聚氨酯丙烯酸脂40%‑50%,溶剂20%‑30%,添加剂1%‑2%;钛白粉15%‑20%;荧光增白剂0.5%‑1%。本发明的有益效果为:其添加的荧光增白剂可以吸收不可见的紫外光转换为波长较长的蓝光或紫色的可见光,因而可以补偿基质中不想要的微黄色,同时反射出比原来入射的波长在400‑600nm范围的更多的可见光,从而使白色漆显的更白,更鲜艳,有效提高白色漆的白度,方法简单、有效,且涂料成本增加极小可忽略。
Description
技术领域
本发明涉及涂料技术领域,具体为一种增白的白色漆及其制作方法。
背景技术
油漆是一种能牢固覆盖在物体表面起保护、装饰、标志的产品,其根据需要有不同种颜色,白色漆作为其中最常见的一种颜色,对于白色漆的白度一般有一定的要求,现有技术若想调整白色漆的白度,不外乎两种方法:一是增加钛白粉的含量;二是更换更白的钛白粉,这两种方法都不能从根本上提高白色漆的白度,反而会增加涂料的成本。
发明内容
本发明的目的在于提供一种增白的白色漆及其制作方法,其添加的荧光增白剂可以吸收不可见的紫外光转换为波长较长的蓝光或紫色的可见光,因而可以补偿基质中不想要的微黄色,同时反射出比原来入射的波长在400-600nm范围的更多的可见光,从而使白色漆显的更白,更鲜艳。
本发明所要解决的技术问题采用以下技术方案来实现:
一种增白的白色漆,其主要组成成分及重量配比为:UV聚氨酯丙烯酸脂40%-50%,溶剂20%-30%,添加剂1%-2%;钛白粉15%-20%;荧光增白剂0.5%-1%。
优选的,所述溶剂为丙二醇甲醚醋酸酯。
优选的,所述添加剂为有机改性硅氧烷或氟改性聚丙烯酸。
一种增白的白色漆的制作方法,其主要包括以下步骤:
(1)备料:将UV聚氨酯丙烯酸脂、溶剂、添加剂、钛白粉、荧光增白剂
按照上述重量配比进行称重备料;
(2)混料制料:在容器内加入溶剂,再缓慢加入添加剂,搅拌均匀后,缓慢加入UV聚氨酯丙烯酸脂,在容器中搅拌均匀,搅拌时间不低于30分钟,再缓慢加入钛白粉和荧光增白剂,搅拌时间不低于1小时,将最终混合物进行研磨至指定细度要求的涂料;
(3)试涂膜:在实验产品上涂膜上述制成的涂料,静置至完全干燥;
(4)性能测试:试验产品涂膜完全干燥后,涂膜完全干燥后性能:耐99.5%无水乙醇500g力来回500次,涂膜无露底;耐RCA纸带175g力耐磨测试:500次不漏底;百格法附着力测试100%,0级:水煮80-100℃无变化;
(5)成品包装:将通过步骤(4)性能测试的涂料进行成品包装。
本发明的有益效果是:其添加的荧光增白剂可以吸收不可见的紫外光转换为波长较长的蓝光或紫色的可见光,因而可以补偿基质中不想要的微黄色,同时反射出比原来入射的波长在400-600nm范围的更多的可见光,从而使白色漆显的更白,更鲜艳,有效提高白色漆的白度,方法简单、有效,且涂料成本增加极小可忽略。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
一种增白的白色漆,其主要组成成分及重量配比为:UV聚氨酯丙烯酸脂40%-50%,溶剂20%-30%,添加剂1%-2%;钛白粉15%-20%;荧光增白剂0.5%-1%。
优选的,所述溶剂为丙二醇甲醚醋酸酯。
优选的,所述添加剂为有机改性硅氧烷或氟改性聚丙烯酸。
一种增白的白色漆的制作方法,其主要包括以下步骤:
(1)备料:将UV聚氨酯丙烯酸脂、溶剂、添加剂、钛白粉、荧光增白剂
按照上述重量配比进行称重备料;
(2)混料制料:在容器内加入溶剂,再缓慢加入添加剂,搅拌均匀后,缓慢加入UV聚氨酯丙烯酸脂,在容器中搅拌均匀,搅拌时间不低于30分钟,再缓慢加入钛白粉和荧光增白剂,搅拌时间不低于1小时,将最终混合物进行研磨至指定细度要求的涂料;
(3)试涂膜:在实验产品上涂膜上述制成的涂料,静置至完全干燥;
(4)性能测试:试验产品涂膜完全干燥后,涂膜完全干燥后性能:耐99.5%无水乙醇500g力来回500次,涂膜无露底;耐RCA纸带175g力耐磨测试:500次不漏底;百格法附着力测试100%,0级:水煮80-100℃无变化;
(5)成品包装:将通过步骤(4)性能测试的涂料进行成品包装。
实施例1:
UV聚氨酯丙烯酸脂50%,溶剂30%,添加剂2%;钛白粉17%;荧光增白剂1%。
实施例2:
UV聚氨酯丙烯酸脂48%,溶剂30%,添加剂1.5%,钛白粉20%;荧光增白剂0.5%。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换,凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (4)
1.一种增白的白色漆,其主要组成成分及重量配比为:UV聚氨酯丙烯酸脂40%-50%,溶剂20%-30%,添加剂1%-2%;钛白粉15%-20%;荧光增白剂0.5%-1%。
2.根据权利要求1所述的一种增白的白色漆,其特征在于,所述溶剂为丙二醇甲醚醋酸酯。
3.根据权利要求1所述的一种增白的白色漆,其特征在于,所述添加剂为有机改性硅氧烷或氟改性聚丙烯酸。
4.一种增白的白色漆的制作方法,其特征在于,其主要包括以下步骤:
(1)备料:将UV聚氨酯丙烯酸脂、溶剂、添加剂、钛白粉、荧光增白剂
按照上述重量配比进行称重备料;
(2)混料制料:在容器内加入溶剂,再缓慢加入添加剂,搅拌均匀后,缓慢加入UV聚氨酯丙烯酸脂,在容器中搅拌均匀,搅拌时间不低于30分钟,再缓慢加入钛白粉和荧光增白剂,搅拌时间不低于1小时,将最终混合物进行研磨至指定细度要求的涂料;
(3)试涂膜:在实验产品上涂膜上述制成的涂料,静置至完全干燥;
(4)性能测试:试验产品涂膜完全干燥后,涂膜完全干燥后性能:耐99.5%无水乙醇500g力来回500次,涂膜无露底;耐RCA纸带175g力耐磨测试:500次不漏底;百格法附着力测试100%,0级:水煮80-100℃无变化;
(5)成品包装:将通过步骤(4)性能测试的涂料进行成品包装。