CN108285999A - A kind of preparation method for the pack alloy part that can improve thermal conductivity - Google Patents

A kind of preparation method for the pack alloy part that can improve thermal conductivity Download PDF

Info

Publication number
CN108285999A
CN108285999A CN201711461163.XA CN201711461163A CN108285999A CN 108285999 A CN108285999 A CN 108285999A CN 201711461163 A CN201711461163 A CN 201711461163A CN 108285999 A CN108285999 A CN 108285999A
Authority
CN
China
Prior art keywords
thermal conductivity
aluminum alloy
alloy materials
preparation
shaped article
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201711461163.XA
Other languages
Chinese (zh)
Other versions
CN108285999B (en
Inventor
徐国祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU CHUNXING PRECISION MECHANICAL CO Ltd
Original Assignee
SUZHOU CHUNXING PRECISION MECHANICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU CHUNXING PRECISION MECHANICAL CO Ltd filed Critical SUZHOU CHUNXING PRECISION MECHANICAL CO Ltd
Priority to CN201711461163.XA priority Critical patent/CN108285999B/en
Publication of CN108285999A publication Critical patent/CN108285999A/en
Application granted granted Critical
Publication of CN108285999B publication Critical patent/CN108285999B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The present invention relates to a kind of preparation methods for the pack alloy part that can improve thermal conductivity, including following step:Aluminum alloy materials are configured, the component of aluminum alloy materials contains the element of following mass percent:Si=2.5 3.5;Fe≤0.45‑0.6;Cu≤0.05‑0.09;Mn≤0.01;Mg=0.8 1.2;Zn < 0.01;Ni < 0.01;Pb < 0.01;Ca < 0.01;Sn < 0.01;Ti < 0.01;Cr < 0.01;Its surplus is Al;Above-mentioned aluminum alloy materials are subjected to melting, are then die cast as shaped article;Above-mentioned shaped article is put into 180 ° 240 ° of baking line heating 40min 120min;Shaped article after heating in step 3) is removed, then cooling can finish.The present invention is increased to 180W/mk or more on the basis of not reducing aluminum alloy materials mechanical property, by the thermal conductivity of aluminum alloy materials, meets component radiating requirements.

Description

A kind of preparation method for the pack alloy part that can improve thermal conductivity
Technical field
The invention belongs to aluminum alloy materials fields, are related to a kind of preparation method of pack alloy part, more particularly to a kind of The preparation method of the pack alloy part of thermal conductivity can be improved.
Background technology
In today that science and technology is constantly progressive, communications industry rapid development develops to 4G extensive uses from 2G, 3G, then arrives 5G The technical research of network is that Die Casting Industry brings wider market, but higher requirements are also raised.
Since communication base station internal structure integration degree is higher and higher, the heat for the generation that works is also higher and higher, to understand Certainly heat influences component, also just higher and higher for the shell cooling requirements of all installation electronic components.Improve product Heat dissipation area and thermal conductivity are the effective ways for the heat dissipation performance for improving product.And the fin height of high radiator shutter is Continuous challenge new high degree, improves 80mm or so till now, what is brought is that formed product is bad, cold by past 10mm or so Every serious the defects of, also increase the weight of product, cost increase.And the heat conductivility of aluminum material can be from another side Face solves the high-cooling property requirement of product, and existing aluminum alloy materials thermal conductivity can only achieve 130W/mk or so, and thermal conductivity reaches Less than 180W/mk or so, it cannot meet component radiating requirements.
Invention content
In order to solve the above technical problems, the object of the present invention is to provide a kind of pack alloys that can improve thermal conductivity The preparation method of part, the preparation method that can improve the pack alloy part of thermal conductivity are not reducing aluminum alloy materials mechanics On the basis of performance, the thermal conductivity of aluminum alloy materials is increased to 180W/mk or more, meets component radiating requirements.
To achieve the above object, the present invention adopts the following technical scheme that:
A kind of preparation method for the pack alloy part that can improve thermal conductivity, including following step:
1) aluminum alloy materials are configured, the component of the aluminum alloy materials contains the element of following mass percent:Si= 2.5-3.5;Fe≤0.45-0.6;Cu≤0.05-0.09;Mn≤0.01;Mg=0.8-1.2;Zn < 0.01;Ni < 0.01;Pb < 0.01;Ca < 0.01;Sn < 0.01;Ti < 0.01;Cr < 0.01;Its surplus is Al;
2) above-mentioned aluminum alloy materials are subjected to melting, are then die cast as shaped article;
3) the baking line that above-mentioned shaped article is put into 180 ° -240 ° heats 40min-120min;
4) shaped article after heating in step 3) is removed, then cooling can finish.
Further, the component of the aluminum alloy materials contains the element of following mass percent:Si=2.5;Fe= 0.45;Cu=0.05;Mn=0.002;Mg=0.8;Zn=0.002;Ni=0.002;Pb=0.002;Ca=0.002;Sn= 0.002;Ti=0.002;Cr=0.002;Its surplus is Al.Using the technical solution, conductivity testing mean reaches 27.23MS/m, thermal conductivity average value have reached 180.7W/mK, and thermal conductivity improves 39%.
Further, the component of the aluminum alloy materials contains the element of following mass percent:Si=3.5;Fe =0.6;Cu=0.09;Mn=0.01;Mg=1.2;Zn=0.009;Ni=0.009;Pb=0.09;Ca=0.002;Sn= 0.002;Ti=0.001;Cr=0.009;Its surplus is Al.Using the technical solution, conductivity testing mean reaches 27.89MS/m, thermal conductivity average value have reached 184.6W/mK, and thermal conductivity improves 42%.
Further, the Si=3;Fe=0.5;Cu=0.06;Mn=0.005;Mg=1;Zn=0.005; Ni =0.005;Pb=0.005;Ca=0.005;Sn=0.005;Ti=0.005;Cr=0.005;Its surplus is Al.Using this Technical solution, conductivity testing mean have reached 28.21MS/m, and thermal conductivity average value has reached 187.8W/mK, thermal conductivity Rate improves 44.46%.
Further, the baking line for the shaped article described in the step 3) being put into 200 ° heats 80min.
Inventor has carried out 3 groups of tests to the conductivity and thermal conductivity of the aluminium alloy finished parts of the present invention, and test result is such as Table 1-1
Table 1-1:
By said program it is found that the present invention has at least the following advantages:
The thermal conductivity of pack alloy part improves 20% or more, while mechanical property will not reduce.
Above description is only the general introduction of technical solution of the present invention, in order to better understand the technical means of the present invention, And can be implemented in accordance with the contents of the specification, it is described in detail as after with presently preferred embodiments of the present invention below.
Specific implementation mode
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for Illustrate the present invention, but is not limited to the scope of the present invention.
In order to enable those skilled in the art to better understand the solution of the present invention, to the technical side in the embodiment of the present invention Case is clearly and completely described, it is clear that and described embodiments are only a part of the embodiments of the present invention, rather than all Embodiment.Based on the embodiment of the present invention, those skilled in the art are obtained without making creative work Every other embodiment, shall fall within the protection scope of the present invention.
Embodiment
A kind of preparation method for the pack alloy part that can improve thermal conductivity, including following step:
1) aluminum alloy materials are configured, the component of the aluminum alloy materials contains the element of following mass percent:Si= 2.5-3.5;Fe≤0.45-0.6;Cu≤0.05-0.09;Mn≤0.01;Mg=0.8-1.2;Zn < 0.01;Ni < 0.01;Pb < 0.01;Ca < 0.01;Sn < 0.01;Ti < 0.01;Cr < 0.01;Its surplus is Al;
2) above-mentioned aluminum alloy materials are subjected to melting, are then die cast as shaped article;
3) the baking line that above-mentioned shaped article is put into 180 ° -240 ° heats 40min-120min;
4) shaped article after heating in step 3) is removed, then cooling can finish.
In the present invention, the component of the aluminum alloy materials contains the element of following mass percent:Si=2.5;Fe= 0.45;Cu=0.05;Mn=0.002;Mg=0.8;Zn=0.002;Ni=0.002;Pb=0.002;Ca=0.002;Sn= 0.002;Ti=0.002;Cr=0.002;Its surplus is Al.
In the present invention, the component of the aluminum alloy materials contains the element of following mass percent:Si=3.5;Fe= 0.6;Cu=0.09;Mn=0.01;Mg=1.2;Zn=0.009;Ni=0.009;Pb=0.09;Ca=0.002;Sn= 0.002;Ti=0.001;Cr=0.009;Its surplus is Al.
In the present invention, the Si=3;Fe=0.5;Cu=0.06;Mn=0.005;Mg=1;Zn=0.005;Ni= 0.005;Pb=0.005;Ca=0.005;Sn=0.005;Ti=0.005;Cr=0.005;Its surplus is Al.
The present invention has at least the following advantages:
The thermal conductivity of pack alloy part improves 20% or more, while mechanical property will not reduce.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this For the those of ordinary skill of technical field, without departing from the technical principles of the invention, several improvement can also be made And modification, these improvements and modifications also should be regarded as protection scope of the present invention.

Claims (5)

1. a kind of preparation method for the pack alloy part that can improve thermal conductivity, which is characterized in that including following step:
1) aluminum alloy materials are configured, the component of the aluminum alloy materials contains the element of following mass percent:Si=2.5- 3.5;Fe≤0.45-0.6;Cu≤0.05-0.09;Mn≤0.01;Mg=0.8-1.2;Zn < 0.01;Ni < 0.01;Pb < 0.01;Ca < 0.01;Sn < 0.01;Ti < 0.01;Cr < 0.01;Its surplus is Al;
2) above-mentioned aluminum alloy materials are subjected to melting, are then die cast as shaped article;
3) the baking line that above-mentioned shaped article is put into 180 ° -240 ° heats 40min-120min;
4) shaped article after heating in step 3) is removed, then cooling can finish.
2. a kind of preparation method of pack alloy part that can improve thermal conductivity according to claim 1, feature exist In:The component of the aluminum alloy materials contains the element of following mass percent:Si=2.5;Fe=0.45;Cu=0.05; Mn=0.002;Mg=0.8;Zn=0.002;Ni=0.002;Pb=0.002;Ca=0.002;Sn=0.002;Ti= 0.002;Cr=0.002;Its surplus is Al.
3. a kind of preparation method of pack alloy part that can improve thermal conductivity according to claim 1, feature exist In:The component of the aluminum alloy materials contains the element of following mass percent:Si=3.5;Fe=0.6;Cu=0.09;Mn =0.01;Mg=1.2;Zn=0.009;Ni=0.009;Pb=0.09;Ca=0.002;Sn=0.002;Ti=0.001;Cr =0.009;Its surplus is Al.
4. a kind of preparation method of pack alloy part that can improve thermal conductivity according to claim 1, feature exist In:The Si=3;Fe=0.5;Cu=0.06;Mn=0.005;Mg=1;Zn=0.005;Ni=0.005;Pb= 0.005;Ca=0.005;Sn=0.005;Ti=0.005;Cr=0.005;Its surplus is Al.
5. according to a kind of preparation method for the pack alloy part that can improve thermal conductivity of claim 1-4 any one of them, It is characterized in that:Shaped article described in the step 3) is put into 200 ° of baking line and heats 80min.
CN201711461163.XA 2017-12-28 2017-12-28 A kind of preparation method for the pack alloy part can be improved thermal conductivity Active CN108285999B (en)