CN108274195A - A kind of production and processing technology of metal can - Google Patents
A kind of production and processing technology of metal can Download PDFInfo
- Publication number
- CN108274195A CN108274195A CN201810057287.XA CN201810057287A CN108274195A CN 108274195 A CN108274195 A CN 108274195A CN 201810057287 A CN201810057287 A CN 201810057287A CN 108274195 A CN108274195 A CN 108274195A
- Authority
- CN
- China
- Prior art keywords
- production
- degreasing
- crimping
- metal
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production and processing technologies of metal can; cleaning solution processing is carried out after the degreasing; and the proportioning of cleaning solution; rust staining, dirt and other oiliness stains on iron plate can effectively be removed; that improves tank body uses duration; it is put into drying box and is dried after the sealing; it can ensure the stability of tank body after sealing; product inspection is carried out after the spraying of the protective paint; it may insure the satisfactory quality of finished product manufacture; the production technology of the tank body has the advantages that production efficiency height and good seal performance, wide market.
Description
Technical field
The present invention relates to the production field of tank body, more particularly to a kind of production and processing technology of metal can.
Background technology
Iron flask product is widely present in our daily life, and a variety of different moulding, color let us are dazzled.
Iron flask is used according to different performance parameters, and iron flask is by spies such as its outstanding printing performance, metal-like retention properties
Point possesses many effects in various industries.1. incrustation performance is good, there is beautiful metallic luster, then to be equipped with color fresh
Gorgeous picture and text printing and advanced metal working process can form good iron flask image；2. metal iron flask belongs to environment-friendly type packet
Dress, waste treatment performance are good；3. due to metal strength height, during handling, transport, storage etc. are a series of, it is unlikely to deform, protects
Inner packing vial is protected, loss is reduced；4. the secondary purposes of mental package；5. easy-open end and the extensive of other easy opening apparatus make
With not only turning on conveniently, while iron flask body has the function of stronger destructive anti-counterfeit.
CN105689587A discloses a kind of production technology of can, it is ensured that the product of the can of production
Matter adopts this method the can shape rule of processing, when having the advantages that pressure-resistant performance is high, but being used there is tank body
Between to be improved and production efficiency urgently need improve the problem of.
Invention content
Technical problem to be solved by the invention is to provide a kind of production and processing technologies of metal can, to solve existing skill
Caused the above-mentioned defects in art.
To achieve the above object, the present invention provides technical solution below：A kind of production and processing technology of metal can, packet
Include following steps：
(1) degreasing is washed
Iron plate is put into degreaser and carries out dipping degreasing, the temperature of the degreasing is 40-50 DEG C, the dipping degreasing
Time be 10-20min, then the clean iron plate of degreasing is cleaned with water；
(2) shear
Iron plate is cut into oblong tin body and tank bottom plectane, institute with hydraulic plate shears according to the size of drawing requirement first
The exploitation speed for stating guillotine is 60-100m/min；
(3) it is ground
By after shear oblong tin body and tank bottom plectane pass through polishing machine carry out burr removal；
(4) corner cut and notch
Then one end of oblong tin body cuts bottom and top two corners by lath cutter, then passes through in the corresponding position of the other end
Lath cutter cuts two notches；
(5) crimping
Then oblong tin body is positioned in crimping room, it is by crimping machine that oblong tin body long side edges are involute
At circular arc, the temperature of the crimping is 30-50 DEG C, and the humidity of the crimping is 5-15%；
(6) end folding
Then by the oblong tin body after crimping by end edging machine respectively to obverse and reverse flanging, form end folding, institute
The speed for stating end edging machine is 60-80mm/s；
(7) Cheng Yuan
Oblong tin body is sent in roller circular knitting machine, is formed into round can body；
(8) it smashes
To be rolled into it is columnar the mutual hook of row is folded by the end on both sides at round can body, then depressing machine is utilized to flatten,
Form can body；
(9) back cover
Can body and tank bottom plectane are sent into tin seamer, allows can body and tank bottom to realize sealing, forms iron flask ontology；
(10) surface grinding
Iron flask ontology is subjected to smooth grinding processing to whole by grinder, forms iron flask, the speed of the grinder is
The power of 50-60mm/s, grinder are 5000-6000W；
(11) spraying of protective paint
Then it in tank surface sprayed protection paint 1-3 times, and is dried, forms finished product.
Preferably, cleaning solution processing is carried out in the step (1) after degreasing.
Preferably, the proportioning of the cleaning solution is 45 parts of ethyl alcohol, 22 parts of turpentine oil, 23 parts of diesel oil, 0 part of phosphatase 11.
Preferably, the time of the cleaning solution processing is 20-40min.
Preferably, it is put into drying box and is dried after sealing in the step (9), the time of the drying is 5-
The temperature of 9h, the drying are 80-100 DEG C.
Preferably, product inspection is carried out after the spraying of protective paint in the step (11), specially to finished product according to iron flask
Standard is being tested, by the bearing products packaging of passed examination, manufacture.
It is using the advantageous effect of above technical scheme：A kind of production and processing technology of metal can provided by the invention,
The proportioning that cleaning solution processing and cleaning solution are carried out after the degreasing, can effectively remove rust staining on iron plate, dirt and its
His oiliness stain, that improves tank body uses duration, is put into drying box and is dried after the sealing, it is ensured that sealing
The stability of tank body afterwards carries out product inspection after the spraying of the protective paint, it can be ensured that the satisfactory quality of finished product manufacture,
The production technology of the tank body has the advantages that production efficiency height and good seal performance, wide market.
Specific implementation mode
The following detailed description of the preferred embodiment of the present invention.
Embodiment 1：
A kind of production and processing technology of metal can, includes the following steps：
(1) degreasing is washed
Iron plate is put into degreaser and carries out dipping degreasing, the temperature of the degreasing is 40 DEG C, the dipping degreasing
Time is 10min, then cleans the clean iron plate of degreasing with water, and cleaning solution processing is carried out after the degreasing, described clear
The proportioning of washing lotion is 45 parts of ethyl alcohol, 22 parts of turpentine oil, 23 parts of diesel oil, 0 part of phosphatase 11, and the time of cleaning solution processing is
20min；
(2) shear
Iron plate is cut into oblong tin body and tank bottom plectane, institute with hydraulic plate shears according to the size of drawing requirement first
The exploitation speed for stating guillotine is 60m/min；
(3) it is ground
By after shear oblong tin body and tank bottom plectane pass through polishing machine carry out burr removal；
(4) corner cut and notch
Then one end of oblong tin body cuts bottom and top two corners by lath cutter, then passes through in the corresponding position of the other end
Lath cutter cuts two notches；
(5) crimping
Then oblong tin body is positioned in crimping room, it is by crimping machine that oblong tin body long side edges are involute
At circular arc, the temperature of the crimping is 30 DEG C, and the humidity of the crimping is 5%；
(6) end folding
Then by the oblong tin body after crimping by end edging machine respectively to obverse and reverse flanging, form end folding, institute
The speed for stating end edging machine is 60mm/s；
(7) Cheng Yuan
Oblong tin body is sent in roller circular knitting machine, is formed into round can body；
(8) it smashes
To be rolled into it is columnar the mutual hook of row is folded by the end on both sides at round can body, then depressing machine is utilized to flatten,
Form can body；
(9) back cover
Can body and tank bottom plectane are sent into tin seamer, allows can body and tank bottom to realize sealing, forms iron flask ontology, the envelope
It is put into drying box and is dried after closing, the time of the drying is 5h, and the temperature of the drying is 80 DEG C；
(10) surface grinding
Iron flask ontology is subjected to smooth grinding processing to whole by grinder, forms iron flask, the speed of the grinder is
The power of 50mm/s, grinder are 5000W；
(11) spraying of protective paint
Then it in tank surface sprayed protection paint 1 time, and is dried, forms finished product, the spraying of protective paint is laggard
Row product inspection is specially testing to finished product according to iron flask standard, by the bearing products packaging of passed examination, manufacture.
Embodiment 2：
A kind of production and processing technology of metal can, includes the following steps：
(1) degreasing is washed
Iron plate is put into degreaser and carries out dipping degreasing, the temperature of the degreasing is 45 DEG C, the dipping degreasing
Time is 15min, then cleans the clean iron plate of degreasing with water, and cleaning solution processing is carried out after the degreasing, described clear
The proportioning of washing lotion is 45 parts of ethyl alcohol, 22 parts of turpentine oil, 23 parts of diesel oil, 0 part of phosphatase 11, and the time of cleaning solution processing is
30min；
(2) shear
Iron plate is cut into oblong tin body and tank bottom plectane, institute with hydraulic plate shears according to the size of drawing requirement first
The exploitation speed for stating guillotine is 80m/min；
(3) it is ground
By after shear oblong tin body and tank bottom plectane pass through polishing machine carry out burr removal；
(4) corner cut and notch
Then one end of oblong tin body cuts bottom and top two corners by lath cutter, then passes through in the corresponding position of the other end
Lath cutter cuts two notches；
(5) crimping
Then oblong tin body is positioned in crimping room, it is by crimping machine that oblong tin body long side edges are involute
At circular arc, the temperature of the crimping is 40 DEG C, and the humidity of the crimping is 10%；
(6) end folding
Then by the oblong tin body after crimping by end edging machine respectively to obverse and reverse flanging, form end folding, institute
The speed for stating end edging machine is 70mm/s；
(7) Cheng Yuan
Oblong tin body is sent in roller circular knitting machine, is formed into round can body；
(8) it smashes
To be rolled into it is columnar the mutual hook of row is folded by the end on both sides at round can body, then depressing machine is utilized to flatten,
Form can body；
(9) back cover
Can body and tank bottom plectane are sent into tin seamer, allows can body and tank bottom to realize sealing, forms iron flask ontology, the envelope
It is put into drying box and is dried after closing, the time of the drying is 7h, and the temperature of the drying is 90 DEG C；
(10) surface grinding
Iron flask ontology is subjected to smooth grinding processing to whole by grinder, forms iron flask, the speed of the grinder is
The power of 55mm/s, grinder are 5500W；
(11) spraying of protective paint
Then it in tank surface sprayed protection paint 2 times, and is dried, forms finished product, the spraying of protective paint is laggard
Row product inspection is specially testing to finished product according to iron flask standard, by the bearing products packaging of passed examination, manufacture.
Embodiment 3：
A kind of production and processing technology of metal can, includes the following steps：
(1) degreasing is washed
Iron plate is put into degreaser and carries out dipping degreasing, the temperature of the degreasing is 50 DEG C, the dipping degreasing
Time is 20min, then cleans the clean iron plate of degreasing with water, and cleaning solution processing is carried out after the degreasing, described clear
The proportioning of washing lotion is 45 parts of ethyl alcohol, 22 parts of turpentine oil, 23 parts of diesel oil, 0 part of phosphatase 11, and the time of cleaning solution processing is
40min；
(2) shear
Iron plate is cut into oblong tin body and tank bottom plectane, institute with hydraulic plate shears according to the size of drawing requirement first
The exploitation speed for stating guillotine is 100m/min；
(3) it is ground
By after shear oblong tin body and tank bottom plectane pass through polishing machine carry out burr removal；
(4) corner cut and notch
Then one end of oblong tin body cuts bottom and top two corners by lath cutter, then passes through in the corresponding position of the other end
Lath cutter cuts two notches；
(5) crimping
Then oblong tin body is positioned in crimping room, it is by crimping machine that oblong tin body long side edges are involute
At circular arc, the temperature of the crimping is 50 DEG C, and the humidity of the crimping is 15%；
(6) end folding
Then by the oblong tin body after crimping by end edging machine respectively to obverse and reverse flanging, form end folding, institute
The speed for stating end edging machine is 80mm/s；
(7) Cheng Yuan
Oblong tin body is sent in roller circular knitting machine, is formed into round can body；
(8) it smashes
To be rolled into it is columnar the mutual hook of row is folded by the end on both sides at round can body, then depressing machine is utilized to flatten,
Form can body；
(9) back cover
Can body and tank bottom plectane are sent into tin seamer, allows can body and tank bottom to realize sealing, forms iron flask ontology, the envelope
It is put into drying box and is dried after closing, the time of the drying is 9h, and the temperature of the drying is 100 DEG C；
(10) surface grinding
Iron flask ontology is subjected to smooth grinding processing to whole by grinder, forms iron flask, the speed of the grinder is
The power of 60mm/s, grinder are 6000W；
(11) spraying of protective paint
Then it in tank surface sprayed protection paint 3 times, and is dried, forms finished product, the spraying of protective paint is laggard
Row product inspection is specially testing to finished product according to iron flask standard, by the bearing products packaging of passed examination, manufacture.
After above method, sample is taken out respectively, and measurement result is as follows：
| Detection project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Existing index |
| Production efficiency | It is high | It is high | It is high | It is higher |
| Usage time | It is long | It is long | It is long | It is longer |
| Weld seam amount of lap (mm) | 0.03 | 0.02 | 0.9 | 0.15 |
It can be obtained according to above table data, when the parameter of embodiment 2, the can seam amount of lap of production is low, makes
It is long with the time, and production efficiency is high, is more advantageous to the production of tank body at this time.
The present invention provides a kind of production and processing technologies of metal can, and cleaning solution processing is carried out after the degreasing, and
The proportioning of cleaning solution can effectively remove rust staining, dirt and other oiliness stains on iron plate, when improving the use of tank body
It is long, it is put into drying box and is dried after the sealing, it is ensured that the stability of tank body after sealing, the protective paint
Product inspection is carried out after spraying, it can be ensured that there is the production technology of the satisfactory quality of finished product manufacture, the tank body production to imitate
The advantages of rate height and good seal performance, wide market.
What has been described above is only a preferred embodiment of the present invention, it is noted that for those of ordinary skill in the art
For, without departing from the concept of the premise of the invention, various modifications and improvements can be made, these belong to the present invention
Protection domain.
Claims (6)
1. a kind of production and processing technology of metal can, which is characterized in that include the following steps：
(1) degreasing is washed
Iron plate is put into degreaser and carries out dipping degreasing, the temperature of the degreasing is 40-50 DEG C, the dipping degreasing when
Between be 10-20min, then the clean iron plate of degreasing is cleaned with water；
(2) shear
Iron plate is cut into oblong tin body and tank bottom plectane, the sanction with hydraulic plate shears according to the size of drawing requirement first
The exploitation speed for cutting machine is 60-100m/min；
(3) it is ground
By after shear oblong tin body and tank bottom plectane pass through polishing machine carry out burr removal；
(4) corner cut and notch
Then one end of oblong tin body cuts bottom and top two corners by lath cutter, then passes through cutting plate in the corresponding position of the other end
Machine-cut removes two notches；
(5) crimping
Then oblong tin body is positioned in crimping room, circle will be rolled into oblong tin body long side edges by crimping machine
The temperature of arc, the crimping is 30-50 DEG C, and the humidity of the crimping is 5-15%；
(6) end folding
Then by the oblong tin body after crimping by end edging machine respectively to obverse and reverse flanging, form end folding, the end
The speed of folding machine is 60-80mm/s；
(7) Cheng Yuan
Oblong tin body is sent in roller circular knitting machine, is formed into round can body；
(8) it smashes
To be rolled into it is columnar the mutual hook of row is folded by the end on both sides at round can body, then depressing machine is utilized to flatten, is formed
Can body；
(9) back cover
Can body and tank bottom plectane are sent into tin seamer, allows can body and tank bottom to realize sealing, forms iron flask ontology；
(10) surface grinding
Iron flask ontology is subjected to smooth grinding processing to whole by grinder, forms iron flask, the speed of the grinder is 50-
The power of 60mm/s, grinder are 5000-6000W；
(11) spraying of protective paint
Then it in tank surface sprayed protection paint 1-3 times, and is dried, forms finished product.
2. a kind of production and processing technology of metal can according to claim 1, which is characterized in that in the step (1)
Cleaning solution processing is carried out after degreasing.
3. a kind of production and processing technology of metal can according to claim 2, which is characterized in that the cleaning solution is matched
Than for 45 parts of ethyl alcohol, 22 parts of turpentine oil, 23 parts of diesel oil, 0 part of phosphatase 11.
4. a kind of production and processing technology of metal can according to claim 2, which is characterized in that the cleaning solution processing
Time be 20-40min.
5. a kind of production and processing technology of metal can according to claim 1, which is characterized in that in the step (9)
It is put into drying box and is dried after sealing, the time of the drying is 5-9h, and the temperature of the drying is 80-100 DEG C.
6. a kind of production and processing technology of metal can according to claim 51, which is characterized in that the step (11)
Product inspection is carried out after the spraying of middle protective paint, is specially being tested according to iron flask standard to finished product, by passed examination
Bearing products packaging, manufacture.