CN108611632A - A method of promoting metal surface rustless property - Google Patents
A method of promoting metal surface rustless property Download PDFInfo
- Publication number
- CN108611632A CN108611632A CN201810364038.5A CN201810364038A CN108611632A CN 108611632 A CN108611632 A CN 108611632A CN 201810364038 A CN201810364038 A CN 201810364038A CN 108611632 A CN108611632 A CN 108611632A
- Authority
- CN
- China
- Prior art keywords
- product
- processing
- metal surface
- rustless property
- rinsing bowl
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method of metal surface rustless property being promoted, including after product is placed on product hanger, is put into degreasing tank and carries out oil removing, then product is put into rinsing bowl and is washed;Product is put into after being passivated processing in deactivation slot, places into and carry out washing process in rinsing bowl;Product is put into after carrying out coordination processing in coordination slot, places into and carry out washing process in rinsing bowl;Product is put into after being neutralized in neutralization chamber, places into and carry out washing process in rinsing bowl;Product is put into after carrying out Seal treatment in enclosed slot, places into and carry out washing process in rinsing bowl;Product is put into after carrying out drying and processing in oven, then product is packed.Method treated the product of the promotions metal surface rustless property of the present invention, product ability of resistance salt air corrosion after the processing of soda acid formula greatly improve, can accomplish within certain testing time corrosion-free;The integrated artistic and easy to operate of the present invention simultaneously, equipment investment is low.
Description
Technical field
The present invention relates to a kind of metal surface treating method, especially a kind of promotions by ph balancing process
The method of metal surface rustless property.
Background technology
Currently, in product on the market, especially metal product influences product itself use because of burn into problem of rustiness,
The problem of even resulting in product rejection is countless, caused by loss be also inestimable, the main original of product corrosion
Because be hardware after cutting or processing and forming element exposure in air inevitably by oxygen, aqueous vapor or
Chemistry or electrochemical action occur for the erosion of all kinds of corrosive substances, to cause the corrosion to hardware.This phenomenon goes out
It is typically now caused by metal is influenced by media such as atmosphere moisture, oxygen or other corrosive gas.Therefore, to product
The work of the antirust of antirust, especially metal product is extremely urgent.Current metal rust preventing primarily directed to Treatment of Metal Surface,
Main processing mode can be divided into following several types;1- surface mechanical enhancements, the surfaces 2- conversion film, 3- surface sprayings,
In industrial more commonly used predominantly first two, surface mechanical enhancement and surface convert film, and wherein surface mechanical enhancement is main
Including;Shot-peening/sand processing, rolling and processing, inner hole extruding, wire drawing, polishing and polishing etc., surface conversion film include mainly;Oxidation
Processing, phosphorating treatment, plating, chemical plating, electroforming (a kind of special applications of plating), electrophoresis and electropolishing etc., but it is above-mentioned several
Kind processing method is but haveed the shortcomings that many.The shortcomings that surface mechanical enhancement:
1, product surface compacted zone and its limited, easily wears, scratches;
2, certain equipment and auxiliary clamp class are needed, is handled, investment is larger, and processing time is also longer;
3, the processing means such as sandblasting, polishing have personnel certain harm, easily form occupational disease.
Convert the shortcomings that film in surface:
1, product surface is susceptible to the defects of spot, striped, uneven, heterochromatic processing;
2, conversion film in surface is mainly to be handled in chemical or electrochemistry mode, and Long Term Contact chemical classes medicament is to people
Body is harmful.
3, it is had a certain impact to environment using the sewage generated after chemistry or electrochemical means processing, needs ability after processing
It can discharge;
In addition, film is converted on surface, it includes mainly;Oil spout (solvent based coating), dust (powdery paints), but oil spout pair
It is more demanding to facility environment for appearance member product, it is necessary to reach dustfree environment requirement, equipment investment is larger, to personnel
Technology requires also higher;And the environment that dusts must be noted that " dust " endangers, there are some potential safety problemss.
Invention content
The technical problem to be solved by the present invention is to provide a kind of methods promoting metal surface rustless property, promote the anti-salt of product
Mist corrosive power.
Technical solution of the invention is:
A method of promoting metal surface rustless property, wherein this method includes the following steps the processing of product:
After product is placed on product hanger, it is put into degreasing tank and carries out oil removing, then product is put into rinsing bowl
It is washed;
Product is put into after being passivated processing in deactivation slot, places into and carry out washing process in rinsing bowl;
Product is put into after carrying out coordination processing in coordination slot, places into and carry out washing process in rinsing bowl;
Product is put into after being neutralized in neutralization chamber, places into and carry out washing process in rinsing bowl;
Product is put into after carrying out Seal treatment in enclosed slot, places into and carry out washing process in rinsing bowl;
Product is put into after carrying out drying and processing in oven, then product is packed.
It is learnt by described above, the present invention has the following advantages really:
Method treated the product of the promotions metal surface rustless property of the present invention, the product is by the processing of soda acid formula
The ability for resisting salt air corrosion afterwards greatly improves, and can accomplish within certain testing time corrosion-free;The present invention's is whole simultaneously
Body technology and easy to operate, equipment investment is low.
Description of the drawings
Fig. 1 is the implementation steps schematic process flow diagram of the method for the promotion metal surface rustless property of the present invention.
Specific implementation mode
For a clearer understanding of the technical characteristics, objects and effects of the present invention, now control illustrates this hair
Bright specific implementation mode.
The present invention is for the bad situation of the existing antirust treatment to resultant metal surface, by using ph balancing
The mode of property, carries out product surface to handle a variety of processing, the surface of metal product is made to obtain stronger antirust ability, especially
It is the ability of anti salt spray corrosion.
In its preferred embodiment of the method for promotion metal surface rustless property of the present invention, refering to Figure 1, it is special
Sign is that this method includes the following steps the processing of product:
It after product is placed on product hanger by S101, is put into degreasing tank and carries out oil removing, product is then put into washing
It is washed in slot;
Product is put by S102 be passivated processing in deactivation slot after, place into and carry out washing process in rinsing bowl;
S103 by product be put into coordination slot in carry out coordination processing after, place into and carry out washing process in rinsing bowl;
Product is put by S104 be neutralized in neutralization chamber after, place into and carry out washing process in rinsing bowl;
Product is put into enclosed slot after progress Seal treatment by S105, is placed into and is carried out washing process in rinsing bowl;
Product is put into oven after progress drying and processing, then product is packed by S106.
Treated that metal surface can have is brighter for the method for the promotion metal surface rustless property by the present invention
Aobvious rust-proof effect, under the conditions of identical salt mist environment, the processed metal product surface appearance of the present invention without yellow rust staining, and
The metal product surface of general machining antirust treatment will appear yellow rust staining.
The method of promotion metal surface rustless property present invention as described above is described blunt in preferred embodiment
Change the activating agent that processing uses and contains 10%~25% citric acid and 1%~4% inorganic quaternary ammonium salts activating agent, treatment temperature
It it is 50~65 DEG C, pH value is 3~5, and processing time is 25~35 minutes.
The method of promotion metal surface rustless property present invention as described above, it is described to match in preferred embodiment
Position processing use complexant contain 6~10% potassium bichromate, 1~4% sodium carbonate and 3~10% triethanolamine, PH
Value is 2~4, and treatment temperature is 60~70 DEG C, and processing time is 10~20 minutes.
The method of promotion metal surface rustless property present invention as described above, in preferred embodiment, the envelope
Close processing use sealer contain 6~10% fatty alcohol ether, 5~9% barium mahogany sulfonate, 5~15% N- oleoyls
Sarcosine octadecylamine salt, pH value are 9~11, and treatment temperature is 40~50 DEG C, and processing time is 5~10 minutes.
The method of promotion metal surface rustless property present invention as described above, it is described to remove in preferred embodiment
Oil processing is using that will sleep a concentration of 5%~10%, and treatment temperature is 60~70 DEG C, and processing time is 5~10 minutes;The washing
Processing uses pure water or deionized water, water at normal temperature to wash 5~10 minutes;The temperature of the drying and processing is 100~120 DEG C, when
Between be 5~8 minutes.
As described above, the metal product of the method processing of the promotion metal surface rustless property of the present invention and general machining
Metal product surface salt spray test it is as follows:
1, stainless steel 304 product surface:
2, Stainless steel 316 product surface:
The method that can be seen that promotion metal surface rustless property through the invention from multiple test result above
The antirust ability of treated metal product surface greatly enhances.
The method of promotion metal surface rustless property present invention as described above is described blunt in preferred embodiment
Change the activating agent that processing uses and contains 15% citric acid and 4% inorganic quaternary ammonium salts activating agent.
The method of promotion metal surface rustless property present invention as described above, it is described to match in preferred embodiment
Position processing use complexant contain 8% potassium bichromate, 3% sodium carbonate and 4% triethanolamine.
The method of promotion metal surface rustless property present invention as described above, in preferred embodiment, the envelope
Close processing use sealer contain 8% fatty alcohol ether, 7% barium mahogany sulfonate, 10% N- oleoylsarcosines 18
Amine salt.
In the effect of the processing of the method for the promotion metal surface rustless property of antirust ability and the present invention by product
Fruit is assessed, and obtains following preferably real-time mode:
The method of promotion metal surface rustless property present invention as described above, in preferred embodiment, the envelope
Washing process twice is carried out after closing processing.
The method of promotion metal surface rustless property present invention as described above, the implementation process of better embodiment
It is as follows:
Corresponding hanger is designed according to the design feature of product, product is then put into degreasing tank (equipment:Degreasing tank,
Chemical concentration 5%~10%, 5~10min of time, 60~70 DEG C of temperature) product is put into rinsing bowl (equipment after oil removing:Washing
Slot, concentration;Pure water, 5~10min of time, temperature, room temperature), the product after washing needs to be put into deactivation slot (equipment:Deactivation slot,
Concentration, stoste use, title;Activating agent, main component;Citric acid 15%, inorganic quaternary ammonium salts activating agent 4%, deionized water
45%, 25~35min of time, 50~65 DEG C of temperature, pH value 3~5), (equipment is put into rinsing bowl after passivation:Rinsing bowl is dense
Degree;Pure water, 5~10min of time, temperature, room temperature), the product after washing need to carry out coordination processing (equipment:Coordination slot, concentration,
Stoste uses, title;Complexant, main component;Potassium bichromate (K2Cr2O7) 8%, sodium carbonate 3%, triethanolamine 4%, time
10~20min, 60~70 DEG C of temperature, pH value 2~4), product is put into rinsing bowl (equipment after coordination processing;Rinsing bowl, concentration;It is pure
Water, 5~10min of time, temperature, room temperature), the product after washing needs further neutralisation treatment (equipment:Neutralization chamber, concentration 5%
~10%, 5~10min of time, temperature;Room temperature), it needs further to be washed (equipment after neutralization:Rinsing bowl, concentration;Pure water,
5~10min of time, temperature, room temperature), then carry out Seal treatment (equipment:Enclosed slot, concentration, stoste use, title;Closing
Agent, main component;Fatty alcohol ether 8%, barium mahogany sulfonate 7%, N- oleoylsarcosine octadecylamines salt 10%, the time 5~
10min, 40~50 DEG C of temperature, pH value 9~11), it needs after Seal treatment to carry out washing (equipment twice:Rinsing bowl, concentration;It is pure
Water, 5~10min of time, temperature, room temperature), (equipment is dried later:Oven, 5~8min of time, temperature, 100~120
℃)。
The method of the promotion metal surface rustless property of the present invention waits for that antirust product by upper hanger manually, then passes through first
Oil removing is conducive to Passivation Treatment and the coordination processing of subsequent product, product after oil removing to remove product surface greasy dirt cleaning products
By washing, washing can remove the oil removing medicament of product surface, eliminate the influence to Passivation Treatment, Passivation Treatment using
The processing mode of stoste, the stoste pH value 3~5 belong to acidic materials, can be blunt in one layer of product surface formation after product is passivated
Change film, is remained through washing removal surface passivation medicament after passivation, then product handles the complexant stoste by complexant and uses
PH value 2~4 belongs to acidic materials, and complexant can further consolidate passivating film, improves the anti-corrosion salt fog ability of passivating film, and product is matched
To pass through washing after the processing of position, neutralize the process that wash again, be in order to remove medicament residual and neutralize acid medicine and
Removal neutralizes medicament, and then processing sealer stoste of the product through parlkaline sealer belongs to alkaline matter using pH value 9~11,
The anti-corrosion salt fog ability of product is further promoted, the ability that product resists salt air corrosion after the processing of soda acid formula carries significantly
It is high.
Method treated the product of the promotions metal surface rustless property of the present invention, the product is by the processing of soda acid formula
The ability for resisting salt air corrosion afterwards greatly improves, and can accomplish within certain testing time corrosion-free;The present invention's is whole simultaneously
Body technology and easy to operate, equipment investment is low.
The foregoing is merely the schematical specific implementation modes of the present invention, are not limited to the scope of the present invention.It is any
Those skilled in the art, made equivalent variations and modification under the premise of not departing from design and the principle of the present invention,
The scope of protection of the invention should be belonged to.
Claims (9)
1. a kind of method promoting metal surface rustless property, which is characterized in that this method includes following step to the processing of product
Suddenly:
It after product is placed on product hanger, is put into degreasing tank and carries out oil removing, then product is put into rinsing bowl and is carried out
Washing;
Product is put into after being passivated processing in deactivation slot, places into and carry out washing process in rinsing bowl;
Product is put into after carrying out coordination processing in coordination slot, places into and carry out washing process in rinsing bowl;
Product is put into after being neutralized in neutralization chamber, places into and carry out washing process in rinsing bowl;
Product is put into after carrying out Seal treatment in enclosed slot, places into and carry out washing process in rinsing bowl;
Product is put into after carrying out drying and processing in oven, then product is packed.
2. the method for promoting metal surface rustless property as described in claim 1, which is characterized in that the Passivation Treatment uses
Activating agent contain 10%~25% citric acid and 1%~4% inorganic quaternary ammonium salts activating agent, treatment temperature is 50~65
DEG C, pH value is 3~5, and processing time is 25~35 minutes.
3. the method for promoting metal surface rustless property as claimed in claim 1 or 2, which is characterized in that the coordination processing
The complexant of use contain 6~10% potassium bichromate, 1~4% sodium carbonate and 3~10% triethanolamine, pH value be 2~
4, treatment temperature is 60~70 DEG C, and processing time is 10~20 minutes.
4. the method for promoting metal surface rustless property as claimed in claim 3, which is characterized in that the Seal treatment uses
Sealer contain 6~10% fatty alcohol ether, 5~9% barium mahogany sulfonate, 5~15% N- oleoylsarcosines 18
Amine salt, pH value are 9~11, and treatment temperature is 40~50 DEG C, and processing time is 5~10 minutes.
5. the method for promoting metal surface rustless property as claimed in claim 4, which is characterized in that the oil removal treatment uses
A concentration of 5%~10% is slept, treatment temperature is 60~70 DEG C, and processing time is 5~10 minutes;The washing process is using pure
Water or deionized water, water at normal temperature are washed 5~10 minutes;The temperature of the drying and processing is 100~120 DEG C, and the time is 5~8 points
Clock.
6. the method for promoting metal surface rustless property as claimed in claim 5, which is characterized in that the Passivation Treatment uses
Activating agent contain 15% citric acid and 4% inorganic quaternary ammonium salts activating agent.
7. the method for promoting metal surface rustless property as claimed in claim 6, which is characterized in that the coordination processing uses
Complexant contain 8% potassium bichromate, 3% sodium carbonate and 4% triethanolamine.
8. the method for promoting metal surface rustless property as claimed in claim 7, which is characterized in that the Seal treatment uses
Sealer contain 8% fatty alcohol ether, 7% barium mahogany sulfonate, 10% N- oleoylsarcosine octadecylamine salt.
9. the method for promoting metal surface rustless property as claimed in claim 8, which is characterized in that the Seal treatment is laggard
Capable washing process twice.