CN108273248A - A kind of golf club head - Google Patents
A kind of golf club head Download PDFInfo
- Publication number
- CN108273248A CN108273248A CN201810374440.1A CN201810374440A CN108273248A CN 108273248 A CN108273248 A CN 108273248A CN 201810374440 A CN201810374440 A CN 201810374440A CN 108273248 A CN108273248 A CN 108273248A
- Authority
- CN
- China
- Prior art keywords
- golf club
- club head
- golf
- striking surface
- amorphous metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of golf club heads, the golf club head is non-crystaline amorphous metal golf club head, non-crystaline amorphous metal golf club head has higher elastic limit and preferable tensile strength and hardness, can meet requirement of the golf club head to elastic limit, tensile strength, hardness and toughness.In conjunction with the material property of non-crystaline amorphous metal, on the basis of golf club head is non-crystaline amorphous metal golf club head, golf club head is Openworks shape, and Openworks shape golf club head further increases the elastic property of golf club head.The design of golf ball-batting face enables non-crystaline amorphous metal golf club head to limit deformation extent of the bulb on beating position, and scope of attack material is enable to spring back in a short time, fast implements the transmission of energy, and can generate frictional force in square stance prevents golf from skidding.The combination of the structure design of non-billon golf club head and golf makes the elastic limit of golf club head, tensile strength obtain the improvement of bigger, further improves the capability and performance of golf club head.
Description
Technical field
The invention belongs to the technical field of golf club, more particularly to a kind of golf club head.
Background technology
The movement that golf sports are integrated as a kind of enjoyment the Nature enjoyment, physical training and game, originating from Soviet Union
Glan is increasingly liked by countries in the world after 19th century spread.Golf club head it is important as golf club one
Part generates certain deformation when hitting golf.Golf club head and golf are non-rigid, in the moment of batting
Adaptability to changes in golf club head is extremely complex, it is necessary to consider that anelastic influence, anelasticity are to generate in-fighting and shock-absorbing
The main reason for.The material manufactures golf club head such as generally use stainless steel, titanium alloy or aluminium alloy in the prior art
Striking surface.To make ball speed greatly and flying distance is remote, the material and design of striking surface should be with higher elastic limits and low
Energy consumption, should also have preferable tensile strength, hardness and toughness.The batting that stainless steel, titanium alloy and aluminum alloy materials make
Face has their own advantages, but can not meet wanting for golf club in elastic limit, tensile strength, hardness and toughness etc. simultaneously
It asks.
In the prior art, the structure design of golf club head is varied, in order to can be realized most in square stance
Excellent balling effect, wherein the momentum for reducing vibration and increase golf that square stance striking surface is brought is golf club head skill
The problem of art.
Application No. is 201310339140.7 patents of invention《A kind of glof club head》It describes and is inserted using impact surface
Enter the shock sucking function that part, the structure design of rear insert and material selection improve glof club head, improves the matter of club head
Measure feature.Striking face insert material is stainless steel, titanium, aluminium, copper, metal alloy, polymer and fibre-reinforced polymerization
Object, wherein stainless steel, titanium and aluminium and its common used material that alloy is glof club head in the prior art, these three materials all have
There is preferable metallicity.Stainless steel has preferable elastic limit, tensile strength and hardness, but stainless steel and titanium alloy
Or aluminium alloy is compared, in-fighting is high.Titanium alloy and aluminium alloy in-fighting are relatively low, but its elastic limit, tensile strength and hard
Performance in terms of degree is but not as good as stainless steel.In above-mentioned patent of invention, using striking face insert and rear insert and
The vibration of the reduction glof club head of absorption of vibrations plate or the like is equipped in club head rear.Its design effectiveness in vibration suppression be
Preferably, but its component is more, and assembling procedure is complicated, and club quality is easy to be influenced by human factor.
Invention content
In order to solve the deficiencies in the prior art, the present invention provides a kind of golf club head, the golf club head
Striking surface for non-crystaline amorphous metal golf club head, golf club head is made of non-crystaline amorphous metal.The golf club head of non-crystaline amorphous metal has
There are higher elastic limit and preferable tensile strength, hardness and toughness.Golf club head is engraved structure, can be into one
Step improves the performance of golf club head, and can save manufacture raw material.The stress rib of striking surface can reduce the biography of vibration in square stance
It leads, reduces the interference that the vibration that square stance generates brings golf player, golf player is made to play preferable batting water
It is flat;Stress rib can generate preferable elasticity, and can convert elasticity to kinetic energy in the moment of batting passes to golf, makes golf
The instantaneous ball speed of ball is big, and flight is remote;Stress rib makes striking surface is coarse can prevent in square stance, and golf slides.It utilizes
The material property that non-crystaline amorphous metal has high-strength height hard, sets in conjunction with the hollow design of golf club head and the stress rib structure of striking surface
Meter, on the one hand makes characteristic of the bulb in the moment contacted with ball due to material, can realize that blow energy can pass to the greatest extent
It leads.On the other hand deformation extent of the bulb on beating position can be limited after there is above-mentioned stress rib due to surface design,
So that scope of attack material is sprung back in a short time, fast implements the transmission of energy.
Institute of the invention technique effect to be achieved is realized by following scheme:
Golf club head made of a kind of non-crystaline amorphous metal.
Further, the striking surface of the golf club head is made of non-crystaline amorphous metal.
The striking surface of non-crystaline amorphous metal material has higher elastic limit and preferable hardness, tensile strength and toughness,
Preferable effect can be played in square stance.
Further, the non-crystaline amorphous metal be zirconium-base amorphous alloy, it is magnesium base amorphous alloy, cu-based amorphous alloys, Ni-based non-
It is peritectic alloy, al based amorphous alloy, rare-earth-base amorphous alloy, Fe-based amorphous alloy, cobalt base amorphous alloy, titanium-based amorphous alloy, more
The combination of one or more of entropy non-crystaline amorphous metal.
Further, the hardness of the golf club head is 700-900HV, elasticity modulus 80-100GPa, tensile strength
For 1170-1800MPa.
Further, the golf club head is Openworks shape.
Non-crystaline amorphous metal is utilized with the hard material property of high-strength height, golf club head is designed as Openworks shape.It can improve
The elastic property of golf club head enables golf club head to realize that batting energy conducts to the greatest extent.Openworks shape makes Gao Er
Husband's bulb thickness is uniform, can guarantee that contraction is consistent during non-crystaline amorphous metal is molded golf club head.
Further, the striking surface of the golf club head is equipped with recessed portion, and it is in cambered surface to make striking surface.
Further, the striking surface of the golf club head is equipped with cavity and stress rib.
Further, the stress rib is in dentation or arcuation, makes the cross section of golf club head in comb teeth-shaped or bow word
Connect shape.
Further, the stress rib is the shape being closed in striking surface.
The vibration generated on square stance, striking surface turns half-turn by being closed the conduction of stress rib, vibration along stress rib both sides
Become the vibration of different directions, then meets and offset most vibrational energy.The vibration of striking surface is supported on being closed stress rib
Disappeared most vibration, reduces vibration and is transmitted at golf grip by golf club, to reduce vibration pair
The interference of golf player.
Further, the stress rib striking surface it is close-shaped include annular, it is ellipse, triangle, rectangular, polygon
Shape and irregular annular.
The present invention has the following advantages:
1, the material of golf club head is non-crystaline amorphous metal, has high elastic limit and preferable hardness, tensile strength and toughness, makes
Preferable balling effect is realized in square stance.
2, in conjunction with the material property of non-crystaline amorphous metal, golf club head is designed as Openworks shape, can further increase golf
The elastic property of head enables golf club head to realize that batting energy conducts to the greatest extent.Openworks shape keeps golf club head thick
Degree is uniform, can guarantee that contraction is consistent during non-crystaline amorphous metal is molded golf club head.
3, stress rib improves the elastic property of striking surface, increases the instantaneous kinetic energy of square stance golf club head.It is close-shaped
Stress rib can reduce the conduct vibrations of striking surface, the hand of golf club is transmitted to reduce vibration by golf club
On handle, interference of the vibration to golf player is reduced.The design of cavity and stress rib enables non-crystaline amorphous metal golf club head
Deformation extent of the bulb on beating position is limited, so that scope of attack material is sprung back in a short time, fast implements energy
It transmits.
4, stress rib increases the roughness of striking surface, and frictional force can be generated in square stance, prevents golf from skidding and sending out
Raw direction offset.
Description of the drawings
Fig. 1 is golf club head structure schematic diagram in the present invention;
Fig. 2 is the another structural schematic diagram of golf club head in the present invention;
Fig. 3 is striking face structure schematic diagram in the present invention;
Fig. 4 is the sectional view at A-A in Fig. 3;
Fig. 5 is another sectional view at A-A in Fig. 3;
Fig. 6 is another sectional view at A-A in Fig. 3;
Fig. 7 is another sectional view at A-A in Fig. 3;
Fig. 8 is another sectional view at A-A in Fig. 3;
Fig. 9 is another sectional view at A-A in Fig. 3;
Accompanying drawings symbol description:1, golf club head;2, striking surface;21, stress rib;22, cavity.
Specific implementation mode
The present invention will be described in detail for 1-9 and embodiment below in conjunction with the accompanying drawings, in the present embodiment, shown in attached drawing
Same or analogous drawing reference numeral to beginning to indicating that identical structure or similar structure, the present embodiment are intended to preferably eventually
Explain the present invention, not limitation of the present invention.
Material for golf club head should have higher elastic limit and preferable tensile strength and hardness, high bullet
Property the limit can guarantee that golf club head deflection is small;Good tensile strength can avoid square stance with hardness and be broken.Using interior
Small material is consumed, then ensures that the energy of golf club head itself anelastic absorption is small.With high elastic limit and low interior consumptive material
Glof club head batting made of material can make ball speed greatly and flying distance is remote under the same conditions.
In the prior art, the common used material of golf club head has stainless steel, titanium, aluminium and metal alloy, in nowadays city
On face, the more commonly used material of golf club is stainless steel, titanium alloy and aluminium alloy.Wherein stainless steel is most common material
Material.Stainless steel is with respect to titanium alloy and aluminium alloy, the better performances of elastic limit and tensile strength, but its in-fighting is opposite
It is higher, and hardness is not as good as aluminium alloy and titanium alloy.The in-fighting of titanium alloy and aluminium alloy is relatively low, but elastic limit and tension
The performance of intensity is relatively poor.The density of titanium alloy is smaller, and the golf club head of manufacture is lighter, and feel is preferable in use,
But the market price of titanium alloy is more high than stainless steel, this is also that golf club head manufacturer uses stainless steel as possible
The one of the major reasons of material manufacture golf club head.Existing experimental data shows strong with the golf club head tension of stainless steel making
Degree is 430-600MPa, hardness 543-610HV;The golf club head tensile strength of titanium alloy manufacture is 390-416MPa, firmly
Degree is 671-773HV;The golf club head tensile strength of aluminium alloy manufacture is 402-427MPa, hardness 628-723HV.To sum up
The golf club head that is described, being manufactured using above-mentioned material cannot always reach ideal requirement in the various aspects of performance.
Likewise, the striking surface of golf club head is made of non-crystaline amorphous metal, it is the high resiliency pole based on amorphous alloy material
Limit and preferable tensile strength and hardness.
Above-mentioned non-crystaline amorphous metal is zirconium-base amorphous alloy, magnesium base amorphous alloy, cu-based amorphous alloys, ni-based amorphous alloy, aluminium
Base noncrystal alloy, rare-earth-base amorphous alloy, Fe-based amorphous alloy, cobalt base amorphous alloy, titanium-based amorphous alloy, more entropy non-crystaline amorphous metals
One or more of combination.
Non-crystaline amorphous metal includes the non-crystaline amorphous metal kind that sill is Zr, Ni, Fe, Cu, Al, Mg, Co, Ti, V and rare earth etc.
Class.In the present invention, not to being defined as the shaping raw material of golf club head using which kind of non-crystaline amorphous metal, but in reality
The type of non-crystaline amorphous metal can be selected in situation according to the required performance of golf club head.Non-crystaline amorphous metal generally all has higher
Tensile strength, higher elastic limit, outstanding anti-fatigue performance, larger elastic limit and good corrosion resistance, but
It is the non-crystaline amorphous metal of different substrate materials material in performance or difference, golf club head can selects amorphous according to actual needs
The type of alloy.
In the present invention, golf club head is non-crystaline amorphous metal golf club head, and amorphous alloy material has higher elasticity
The limit and preferable tensile strength and hardness, and its in-fighting is small.Non-crystaline amorphous metal is the manufacture for being highly suitable as golf club head
Material.The elastic limit of the golf club head manufactured with non-crystaline amorphous metal is preferably 80-100GPa, and tensile strength is preferably 1170-
1800MPa, hardness are preferably 700-900HV., it is clear that elastic limit, the tension of the golf club head of non-billon manufacture
Performance in terms of intensity and hardness is better than stainless steel, titanium alloy and aluminium alloy.For example, when golf club head is Ni-based amorphous
When alloy, hardness 780-850HV, tensile strength 1230-1670MPa, in terms of hardness and tensile strength better than not
Become rusty steel, titanium alloy and aluminium alloy.
As shown in attached drawing 1-9, golf club head 1 is Openworks shape.The Openworks shape of golf club head mainly leads in the present invention
It crosses striking surface to embody, in conjunction with the material property that the high-strength height of amorphous alloy material is hard, golf club head is designed as Openworks shape,
On the one hand the elastic property of golf club head can be improved, another aspect Openworks shape keeps golf club head thickness uniform, is closed in amorphous
During gold molding golf club head, the contraction of golf club head is consistent.The thickness of golf club head is uniform, in forming process
In each position cooling velocity and shrink consistent, molding golf club head can increase in terms of mechanical property.
As shown in attached drawing 4-9, golf head batting surface 2 is equipped with recessed portion in plane or on striking surface.In this hair
In bright, preferably the striking surface of golf club head is equipped with recessed portion(It is not identified in figure), it is in cambered surface to make striking surface.Striking surface is arc
Face increases the contact area of striking surface and golf, can increase ball speed in the case where hitting power is constant so that golf
The kinetic energy of bigger, flight stroke bigger are obtained in the moment hit.When striking surface is arc, the power collection of golf declines
The center of arc, opposite, the power of golf club concentrates on the position at arc center and is conducted to golf when swinging,
Golf fortune is contributed to play more preferable batting horizontal.Striking surface also can effectively prevent golf when being arc and hit
Moment occur direction offset.
Referring again to attached drawing 4-9, the striking surface of golf club head is equipped with cavity 22 and stress rib 21.Preferably, stress rib
Cross section be in dentation or arcuation so that the cross section of golf club head in comb teeth-shaped or bow word connect shape.
The cross section of stress rib 21 is in dentation, and square stance stress rib surface is by the extruding force of golf, stress rib hair
Raw deformation, is become from extruding force to the drawing force of both sides deformation.The cross section of stress rib is in dentation, is had time between adjacent stress rib
Chamber 22, when elastic deformation occurs for stress rib, the dynamics for not contacting or contacting between adjacent stress rib is little, adjacent stress rib
Between opposite force would not cancel out each other, or offset power it is smaller.In this way, stress rib can be by more elastically-deformable energy
It is again converted to the momentum of golf.
21 cross section of stress rib is arcuation, and in addition to the cavity 21 between stress rib, the inside same design of stress rib is sky
Chamber, and cavity is open-type so that stress rib cross section is arcuation.Cavity is open-type, is conducive to the molding of golf club head,
Reduce the difficulty of striking surface at the time of molding.Stress rib cross section is arcuation, in the upper surface of square stance stress rib by golf
The extruding of ball, elastic deformation, which occurs, makes stress rib bottom surface by certain drawing force, when elastic deformation occurs, stress rib
The power that middle section is subject to is smaller, so when stress rib is too thick, it is extra that stress rib middle section, which is most of,.It will
Stress rib interior design is cavity, on the one hand can save the material of striking surface, reduces manufacturing cost, on the other hand makes striking surface
Each position thickness it is uniform, be conducive to striking surface molding, avoid causing to make because in uneven thickness each position of striking surface
Mechanical property is different.Striking surface can be integrally formed with the main body of golf club head, also can separately as a parts-moulding,
In the present embodiment, striking surface is an individual parts.It is cavity inside stress rib, square stance golf is to stress rib
Extruding become elastic deformation, due to being cavity inside stress rib, stress rib will not be contacted with other places and by elastic deformation
Energy expenditure fall, therefore the in-fighting of striking surface energy can be reduced, increase the instantaneous kinetic energy of square stance golf, flight is more
Far.
In the present invention, stress rib is preferably and is formed and be closed in striking surface for the annular being closed, stress rib on striking surface
Stress rib, the vibration generated on square stance, striking surface by be closed stress rib conduct, vibration along stress rib both ends around half-turn
Become the vibration of different directions, then meets and offset most vibrational energy.The vibration of striking surface is supported on being closed stress rib
Disappeared most vibration, reduces vibration and is transmitted at handle by golf club, to reduce vibration to golf sports
The interference of member.
Stress rib striking surface it is close-shaped include annular, ellipse, triangle, rectangular, polygon and irregularly
Annular.In the present embodiment, stress rib is in the close-shaped for annular of striking surface.
Stress rib thickness be 1-15mm, be highly 0.5-15mm, the distance between adjacent two stress rib is equal, two it is adjacent by
Power rib distance is 1-7mm.The selection of above-mentioned data is that the experiment based on technical staff obtains, the batting in this data area
Face makes more excellent in square stance balling effect.Specific more excellent aspect is to be embodied in square stance, the elastic limit of golf club head
Higher, the elastic kinetic energy ratio that can be converted to golf of square stance is larger, and golf acquisition instantaneous kinetic energy is larger, flight
Farther out, in addition to this, striking surface within the above range can generate frictional force, and the size of its frictional force can prevent square stance
Slipping phenomenon occurs for golf, and can in-fighting of the relatively low golf club head to kinetic energy to greatest extent.The weight of golf club head
Amount can also be adjusted by the thickness of stress rib and height, according to different golf weight requirements, produce different-thickness or
The stress rib striking surface of height is arranged in pairs or groups with golf club head, can save the program of additional adjustment counterweight.The distance between stress rib
Equal, the friction coefficient of generation is equal, can prevent golf from skidding.
It is what non-crystaline amorphous metal golf club head was made that the structure design of above-mentioned striking surface, which is all based on golf club head, but
The structure design of striking surface is not intended to limit in the present invention to be made in non-crystaline amorphous metal golf club head, equally can be stainless
It is made on the golf club head of the other materials such as steel, titanium alloy, aluminium alloy.Non-crystaline amorphous metal has preferable mouldability and injection molding
Property, it can preferably realize the striking face structure design of the present invention.The structure and size and spacing distance of stress rib on striking surface are all
There is certain requirement, although the striking face structure of the present invention can also make on the golf club head of other materials, this hair
Bright striking face structure design is implemented to have the effect of vibration damping on the golf club head of non-crystaline amorphous metal, and elastic limit resists
The performance of tensile strength is also preferably improved.The mouldability and injection molding property of the materials such as stainless steel, titanium alloy and aluminium alloy
Can be poor, with the processing of these materials or molding stress rib, striking surface elastic limit, tensile strength and hardness are closed not as good as amorphous
Golf club head made of gold.According to stainless steel, titanium alloy and aluminum alloy materials characteristic, stainless steel, titanium alloy and aluminium alloy
Than stress rib more difficult to process, the effect that can be run counter to desire in the case where processing technology is undesirable.Non-crystaline amorphous metal is preferable
Mouldability and injection molding property, can be molded stress rib in die molding process, can also be processed on blocky non-billon striking surface
Stress rib.Be integrally formed also or mach stress rib with non-crystaline amorphous metal golf club head, can reach improve elastic limit,
The effect of tensile strength and hardness performance.
In order to preferably illustrating the present invention, golf club head of the present invention is enable preferably to show, citing below compared with
Good embodiment, Gao Er ball head structures for explaining the present invention, but the golf club head of the present invention is not limited in following reality
Apply example.
Based on the structural representation of 3 golf head batting surface of the present invention of attached drawing, according to golf club head knot of the present invention
Structure describes, and there are many different structural schematic diagrams in section at A-A in attached drawing 3.
Embodiment one, as shown in Fig. 4, golf club head are engraved structure, and striking surface is concordant shape, stress rib cross section
For dentation 21, the cross section of golf club head is comb teeth-shaped at this time.
Embodiment two, as shown in Fig. 5, golf club head are engraved structure, and striking surface is concordant shape, stress rib cross section
For arcuation, the cross section of golf club head is that bow word connects shape at this time.
Embodiment three, as shown in Fig. 6, golf club head are Openworks shape, and striking surface is concordant shape, 21 cross section of stress rib
For arcuation, and the edge rounded corner of stress rib, the cross section of golf club head is that bow word connects shape at this time.
Example IV, as shown in Fig. 7, golf club head are Openworks shape, and striking surface is equipped with recessed portion, and striking surface is in arc
Face, 21 cross section of stress rib are dentation, and the cross section of golf club head is comb teeth-shaped at this time, and stress rib height is from striking surface both sides
Gradually successively decrease to centre on edge.
Embodiment five, as shown in Fig. 8, golf club head are Openworks shape, and striking surface is equipped with recessed portion, and striking surface is in arc
Face, 21 transversal arcuation of stress rib, the cross section of golf club head is that bow word connects shape at this time, and stress rib height is from striking surface both sides
Gradually successively decrease to centre on edge.
Embodiment six, as shown in Fig. 9, golf club head are Openworks shape, and striking surface is equipped with recessed portion, and striking surface is in arc
Face, 21 transversal arcuation of stress rib, and the edge rounded corner of stress rib, the cross section of golf club head is that bow word connects shape at this time,
Stress rib height is gradually successively decreased to centre from two edge of striking surface.
In the present embodiment use thermoplastic molding's technology and foundry engieering in it is a kind of using mold to non-crystaline amorphous metal
Golf club head is molded, and method is as follows:
S01:The melting storehouse of golf club head mold is poured into using non-crystaline amorphous metal as raw material;
S02:Non-crystaline amorphous metal in heating melting storehouse makes it become molten completely;
S03:The non-crystaline amorphous metal of molten is molded, the non-crystaline amorphous metal of molten is shaped to golf club head or golf
Any parts of head;
S04:Take out the molded part in mold.
Deburring, polishing, machining or polishing are carried out to molded part.
Non-crystaline amorphous metal golf club head is manufactured in aforementioned manners, and production efficiency is high, and the golf area of bed essence produced
Degree is high.
Finally, it should be noted that above example be only to illustrate the embodiment of the present invention technical solution rather than to its into
Row limitation, although the embodiment of the present invention is described in detail with reference to preferred embodiment, those skilled in the art
It should be understood that the technical solution of the embodiment of the present invention can be still modified or replaced equivalently, and these are changed or wait
The range of modified technical solution disengaging technical solution of the embodiment of the present invention cannot also be made with replacement.
Claims (10)
1. golf club head made of a kind of non-crystaline amorphous metal.
2. golf club head as described in claim 1, it is characterised in that:The striking surface of the golf club head is by non-crystaline amorphous metal
It is made.
3. golf club head as described in any as described in claim 1-2, it is characterised in that:The non-crystaline amorphous metal is zirconium-base amorphous conjunction
Gold, magnesium base amorphous alloy, cu-based amorphous alloys, ni-based amorphous alloy, al based amorphous alloy, rare-earth-base amorphous alloy, iron-based are non-
The combination of one or more of peritectic alloy, cobalt base amorphous alloy, titanium-based amorphous alloy, more entropy non-crystaline amorphous metals.
4. any golf club head as described in claim 1-2, it is characterised in that:The hardness of the golf club head is 700-
900HV, elasticity modulus 80-100GPa, tensile strength 1170-1800MPa.
5. the golf club head as described in claim 1-2 is any, it is characterised in that:The golf club head is Openworks shape.
6. golf club head as claimed in claim 2, it is characterised in that:The striking surface of the golf club head is equipped with recessed portion,
It is in cambered surface to make striking surface.
7. golf club head as claimed in claim 2, it is characterised in that:The striking surface of the golf club head be equipped with cavity and by
Power rib.
8. golf club head as claimed in claim 7, it is characterised in that:The stress rib is in dentation or arcuation, makes golf
The cross section of head connects shape in comb teeth-shaped or bow word.
9. golf club head as claimed in claim 7, which is characterized in that the stress rib is the shape being closed in striking surface.
10. golf club head as claimed in claim 9, which is characterized in that the stress rib includes in the close-shaped of striking surface
Annular, ellipse, triangle, rectangular, polygon and irregular annular.