CN108265405A - A kind of Static Spinning nanometer multicomponent fibre non-woven material and its preparation method and application - Google Patents
A kind of Static Spinning nanometer multicomponent fibre non-woven material and its preparation method and application Download PDFInfo
- Publication number
- CN108265405A CN108265405A CN201810273255.3A CN201810273255A CN108265405A CN 108265405 A CN108265405 A CN 108265405A CN 201810273255 A CN201810273255 A CN 201810273255A CN 108265405 A CN108265405 A CN 108265405A
- Authority
- CN
- China
- Prior art keywords
- long fibre
- nanometer
- short fiber
- woven material
- static spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of Static Spinning nanometer multicomponent fibre non-woven materials and its preparation method and application,It is related to non-woven material technical field,The Static Spinning multicomponent non-woven material supreme first long fibre layer being cascading under including,Short fiber layers and the second long fibre layer,The first long fibre layer,The short fiber layers and the second long fibre layer are compound successively by hot rolling,The short fiber layers are prepared by melt-blown nano short fiber,The first long fibre layer and the second long fibre layer are prepared by spunbond nanometer long fibre,People can not be met to pro-skin textile techniques problem by alleviating existing viscose non-woven material and melt-blown non-woven material,Static Spinning nanometer multicomponent fibre non-woven material provided by the invention not only has good mechanical strength,And fluffy softness,Good water absorption,It disclosure satisfy that requirement of the people for pro-skin water suction textile.
Description
Technical field
The present invention relates to non-woven material technical fields, non-woven more particularly, to a kind of Static Spinning nanometer multicomponent fibre
Material and its preparation method and application.
Background technology
Non-woven material, also known as non-woven cloth, nonwoven fabric, supatex fabric, adhesive-bonded fabric or non-woven fabrics.Nonwoven techniques
It is a kind of new technology most promising in textile industry, production breaches traditional textile principle, combines weaving, changes
The industrial technologies such as work, plastics and papermaking take full advantage of the knowledge of the subjects such as modern physics, chemistry.Therefore, non-woven material
Development degree be to weigh the one of the important signs that of a national Technical Progress in Textile Industry.
Existing non-woven material is prepared mostly by spun-bond process or meltblown etc., spun-bond process non-woven material intensity
Height, vertically and horizontally performance approaches, but its networking uniformity and fluffy water imbibition are poor, and melt blown nonwoven material fiber diameter is thin,
Porosity is small, fluffy good water absorption, but intensity is low, can not meet requirement of the people for pro-skin water suction textile.
In view of this, it is special to propose the present invention.
Invention content
The purpose of the present invention is to provide a kind of Static Spinning nanometer multicomponent fibre non-woven material, to alleviate existing spinning
The bonded non-woven strength of materials is high, but the networking uniformity and fluffy water imbibition are poor, the fluffy good water absorption of melt-blown non-woven material, but
It is that intensity is low, can not meets the technical issues of people are to pro-skin water suction textile requirement.
Static Spinning nanometer multicomponent fibre non-woven material provided by the invention, including what is be cascading from bottom to up
First long fibre layer, short fiber layers and the second long fibre layer, the first long fibre layer, the short fiber layers and second length
Fibrous layer is compound successively by hot rolling, and the short fiber layers are prepared by melt-blown nano short fiber, the first long fibre layer
It is prepared with the second long fibre layer by spunbond nanometer long fibre.
Further, the spunbond nanometer long fibre is selected from polypropylene, polyethylene, polyamide or poly terephthalic acid second two
At least one of alcohol ester.
Further, the nano short fiber in natural fiber, chemical synthetic fiber or regenerated fiber at least one
Kind;
Preferably, it is described melt-blown nano short fiber in natural fiber, chemical synthetic fiber or regenerated fiber at least
It is a kind of;
Preferably, the melt-blown nano short fiber is chemical synthetic fiber;
Preferably, the chemical synthetic fiber is selected from polypropylene, polyethylene, polyamide or polyethylene terephthalate
At least one of.
Further, the long stapled a diameter of 100-500nm of the spunbond nanometer;
Preferably, a diameter of 100-500nm of the melt-blown nano short fiber.
Further, the thickness of the Static Spinning nanometer multicomponent fibre non-woven material is 0.5-0.55mm;
Preferably, the thickness of the first long fibre layer is 0.17-0.2mm;
Preferably, the thickness of the second long fibre layer is 0.28-0.32mm;
Preferably, the thickness of the short fiber layers is 0.03-0.05mm.
The second object of the present invention is to provide a kind of preparation method of Static Spinning nanometer multicomponent fibre non-woven material,
Include the following steps:
(a) spunbond nanometer long fibre is prepared, and makes its air drawing networking, the first long fibre layer is made;
(b) melt-blown nano short fiber is prepared on the first long fibre layer, and makes its networking that short fiber layers be made;
(c) it prepares spunbond nanometer long fibre again in short fiber layers, and makes its air drawing networking, it is fine that the second length is made
Tie up layer;
(d) by the first long fibre layer, short fiber layers and the second long fibre layer successively method hot rolling, Static Spinning nanometer is obtained
Multicomponent fibre non-woven material.
Further, in step (a), spunbond nanometer long fibre passes through filament die extrusion molding.
Further, in step (b), melt-blown nano short fiber sprays molding of quenching by being meltblown injector.
Further, the preparation method of the Static Spinning nanometer multicomponent fibre non-woven material further includes step (e) work(
It can arrange, including hydrophilic, antibacterial, fluffy, soft or at least one of antistatic finishing technique.
The third object of the present invention is to provide above-mentioned Static Spinning nanometer multicomponent fibre non-woven material in facial mask or wet
Application on towel.
Static Spinning nanometer multicomponent fibre non-woven material provided by the invention, is prepared by spunbond nanometer long fibre
The first long fibre layer, the short fiber layers that are prepared of melt-blown nano short fiber and spunbond nanometer long fibre be prepared second
Long fibre layer intersecting is set, the advantages of having both viscose non-woven material and melt-blown non-woven material, not only with good
Mechanical strength, and fluffy softness, good water absorption disclosure satisfy that requirement of the people for pro-skin water suction textile.
The preparation method of Static Spinning nanometer multicomponent fibre non-woven material provided by the invention, simple for process, operation side
Just, a large amount of man power and material can be saved, effectively improves production efficiency.
Description of the drawings
It, below will be to specific in order to illustrate more clearly of the specific embodiment of the invention or technical solution of the prior art
Embodiment or attached drawing needed to be used in the description of the prior art are briefly described, it should be apparent that, in being described below
Attached drawing is some embodiments of the present invention, for those of ordinary skill in the art, before not making the creative labor
It puts, can also be obtained according to these attached drawings other attached drawings.
Fig. 1 is the structure diagram of Static Spinning nanometer multicomponent fibre non-woven material that the embodiment of the present invention 1 provides.
Icon:10- the first long fibre layers;20- short fiber layers;30- the second long fibre layers.
Specific embodiment
Technical scheme of the present invention will be clearly and completely described below, it is clear that described embodiment is this hair
Bright part of the embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not having
All other embodiments obtained under the premise of creative work are made, shall fall within the protection scope of the present invention.
Embodiment 1
Fig. 1 is the structure diagram of Static Spinning nanometer multicomponent fibre non-woven material that the embodiment of the present invention 1 provides;Such as
Shown in Fig. 1, an embodiment of the present invention provides a kind of Static Spinning nanometer multicomponent fibre non-woven material, including from bottom to up successively
The first long fibre layer 10, the 20 and second long fibre layer 30 of short fiber layers being stacked, the first long fibre layer 10, short fiber layers 20
Compound successively by hot rolling with the second long fibre layer 30, short fiber layers 20 are prepared by melt-blown nano short fiber, and the first length is fine
Dimension 10 and second long fibre layer 30 of layer is prepared by spunbond nanometer long fibre.
Static Spinning nanometer multicomponent fibre non-woven material provided in an embodiment of the present invention, passes through spunbond nanometer long fibre system
It is prepared by the short fiber layers 20 and spunbond nanometer long fibre that standby the first long fibre layer 10 formed, melt-blown nano short fiber are prepared
30 intersecting of the second long fibre layer setting formed, the advantages of having both viscose non-woven material and melt-blown non-woven material, no
Only there is good mechanical strength, and fluffy softness, good water absorption, disclosure satisfy that people want pro-skin water suction textile
It asks.
In a kind of preferred embodiment of the embodiment of the present invention, spunbond nanometer long fibre pass sequentially through polymer chips with
Auxiliary agent mixing, air-flow conveying, screw extruding melting, filtering and spinning are prepared.
Polymer chips includes but not limited to one in polypropylene, polyethylene, polyamide or polyethylene terephthalate
Kind or several compositions.
In a kind of preferred embodiment of the embodiment of the present invention, melt-blown nano short fiber is selected from natural fiber, chemistry closes
Into one or more of fiber or regenerated fiber.
Natural fiber includes but not limited to cotton, hair, fiber crops and silk etc..
Chemical synthetic fiber includes but not limited to polypropylene, polyethylene, polyamide or polyethylene terephthalate.
Regenerated fiber be with natural polymer be raw material, through made of chemical method, with original copolymer in chemical composition
Essentially identical chemical fibre.
Regenerated fiber includes but not limited to viscose rayon, azlon and polynosic etc..
In the further preferred embodiment of the embodiment of the present invention, melt-blown staple fiber is chemical synthetic fiber, by gathering
Polymer beads are prepared successively by air-flow conveying, screw extruding melting, filtering and melt-blown.
In a kind of preferred embodiment of the embodiment of the present invention, the long stapled a diameter of 100-500nm of spunbond nanometer.
In the typical but non-limiting embodiment of the embodiment of the present invention, spunbond nanometer is long stapled a diameter of 100,
150th, 200,250,300,350,400,450 or 500nm.
The first long fibre layer 10 and the second long fibre layer 30 are prepared by using spunbond nanometer long fibre, makes its networking more
It is uniformly fine and closely woven, to further improve the mechanical strength of Static Spinning multicomponent fibre non-woven material.
In a kind of preferred embodiment of the embodiment of the present invention, it is meltblown a diameter of 100-500nm of nano short fiber.
In the typical but non-limiting embodiment of the embodiment of the present invention, spunbond is meltblown a diameter of of nano short fiber
100th, 150,200,250,300,350,400,450 or 500nm.
Short fiber layers 20 are prepared by using melt-blown nano short fiber, are more uniformly distributed its networking fine and closely woven, further to carry
The fluffy water imbibition of high Static Spinning multicomponent fibre non-woven material.
In a kind of preferred embodiment of the embodiment of the present invention, the thickness of Static Spinning nanometer multicomponent fibre non-woven material
It spends for 0.5-0.55mm.
In the typical but non-limiting embodiment of the embodiment of the present invention, Static Spinning nanometer multicomponent fibre is non-woven
The thickness of material is as being 0.5,0.51,0.52,0.53,0.54 or 0.55mm.
By the way that the thickness of Static Spinning nanometer multicomponent fibre non-woven material is set as 0.5-0.55mm, so that electrostatic
Spinning nanometer multicomponent fibre non-woven material not only has good mechanical strength, but also with good fluffy sense and hydrophily.When
When the thickness of Static Spinning nanometer multicomponent fibre non-woven material is less than 0.5mm, Static Spinning nanometer multicomponent fibre is non-woven
The intensity of material is poor, can not meet the requirement of pro-skin textile field, when Static Spinning nanometer multicomponent fibre is non-woven
When the thickness of material is more than 0.55mm, the fluffy sense of obtained Static Spinning nanometer multicomponent fibre non-woven material and hydrophily
It is not good enough, the requirement of pro-skin textile can not be met.
In a kind of preferred embodiment of the embodiment of the present invention, the thickness of the first long fibre layer 10 is 0.17-0.2mm.
In the typical but non-limiting embodiment of the embodiment of the present invention, the thickness of the first long fibre layer 10 is such as
0.17th, 0.18,0.19 or 0.2mm.
In a kind of preferred embodiment of the embodiment of the present invention, the thickness of the second long fibre layer 30 is 0.28-0.32mm.
In the typical but non-limiting embodiment of the embodiment of the present invention, the thickness of the second long fibre layer 30 is such as
0.28th, 0.29,0.3,0.31 or 0.32mm.
In a kind of preferred embodiment of the embodiment of the present invention, the thickness of short fiber layers 20 is 0.03-0.05mm.
In the typical but non-limiting embodiment of the present invention, the thickness of short fiber layers 20 as 0.031,0.032,
0.333、0.3034、0.035、0.036、0.037、0.038、0.039、0.04、0.041、0.042、0.043、0.044、
0.045th, 0.046,0.047,0.048,0.049 or 0.05mm.
By the way that the thickness of the first fibrous layer is set as 0.17-0.2mm respectively, the thickness of the second long fibre layer 30 is set as
0.28-0.32mm, the thickness of short fiber layers 20 are set as 0.03-0.05mm, are knitted so that Static Spinning nanometer multicomponent fibre is non-
The mechanical strength higher of producing material material, more fluffy more soft, water imbibition is more preferable.
In the preferred embodiment of the present embodiment, the grammes per square metre of the compound water ripples non-woven material of Static Spinning nanometer multicomponent
For 40-50g/m2。
It is obtained when the material of the first long fibre layer 10,20 and second long fibre layer 30 of short fiber layers is polypropylene
Static Spinning nanometer multicomponent fibre non-woven material grammes per square metre be 40-50g/m2, mechanical performance, bulkiness and hydrophily are more
Good, result of the test is as shown in table 1 below:
1 Static Spinning nanometer multicomponent fibre non-woven material performance data table of table
As it can be seen from table 1 when the grammes per square metre of Static Spinning nanometer multicomponent fibre non-woven material is 40-50g/m2When,
Tensile strength and elongation at break are larger, and softness is good, fluffy water suction, meet the requirement of pro-skin textile.
Embodiment 2
The present invention applies the preparation side that example provides 1 described Static Spinning nanometer multicomponent fibre non-woven material of embodiment
Method includes the following steps:
(a) spunbond nanometer long fibre is prepared, and makes its air drawing networking, the first long fibre layer 10 is made;
(b) melt-blown nano short fiber is prepared on the first long fibre layer 10, and makes its networking that short fiber layers 20 be made;
(c) it prepares spunbond nanometer long fibre again in short fiber layers 20, and makes its air drawing networking, the second length is made
Fibrous layer 30;
(d) by the first long fibre layer 10,20 and second long fibre layer 30 of short fiber layers successively method hot rolling, electrostatic is obtained
Spin nanometer multicomponent fibre non-woven material.
The preparation method of Static Spinning nanometer multicomponent fibre non-woven material provided in an embodiment of the present invention, passes through spun-bond process
After preparing the first long fibre layer 10, then nano short fiber of quenching is sprayed by meltblown on the first long fibre layer 10, short fiber layers are made
20, then the second long fibre layer 30 is prepared in short fiber layers 20 by anti-bonding, make the first long fibre finally by pressure roller hot rolling
Layer 10,20 and second long fibre layer of short fiber layers, 30 compound one-pass molding not only cause the stabilization that is completely embedded between three layers, and
And technique is simplified, a large amount of man power and material has been saved, has effectively improved production efficiency.
Now by taking the first long fibre layer 10,20 and second long fibre layer 30 of short fiber layers are pp material as an example, to this
The preparation method for the Static Spinning nanometer multicomponent fibre non-woven material that inventive embodiments provide illustrates, the embodiment of the present invention
The process equipment used is the first filament die, the melt-blown injector and the second filament die that set gradually.
The preparation method of Static Spinning nanometer multicomponent fibre non-woven material provided in an embodiment of the present invention is according to following step
Suddenly it is prepared:
(a) polypropylene agglomerate is mixed with other auxiliary agent master batches, and pass through air-flow be delivered to the first screw extruding melting set
Standby to be heated, the first screw extruding fusion apparatus is connected with the first filament die, when polypropylene agglomerate and other auxiliary agents are female
Jet spinning and the networking under air drawing are carried out by the spinneret orifice on the first filament die after grain melting uniformly, are made first
Long fibre layer 10;
(b) the first long fibre layer 10 is delivered to below the nozzle of melt-blown injector, polypropylene agglomerate is defeated by air-flow
It send to the second screw extruding fusion apparatus and is heated, the second screw extruding fusion apparatus is connected with melt-blown injector, and poly- third
It is sprayed to networking on the first long fibre layer 10, is made short by the spinneret orifice being meltblown on injector spray tip after the melting uniformly of alkene master batch
Fibrous layer 20;
(c) the first long fibre layer 10 and short fiber layers 20 that are stacked are delivered to below the second filament die, second
Filament die is connected with third screw extruding fusion apparatus, melts uniform polypropylene and other auxiliary agents and passes through the second long filament mould
Spinneret orifice on head carries out the networking in short fiber layers 20 under jet spinning and air drawing, and the second long fibre layer 30 is made;
(d) by pressure roller to the first long fibre layer 10, the 20 and second long fibre layer 30 of short fiber layers that are cascading
Hot rolling is carried out, makes three layers of method hot rolling, obtains Static Spinning nanometer multicomponent fibre non-woven material.
The preparation method of Static Spinning nanometer multicomponent fibre non-woven material provided in an embodiment of the present invention, combines two kinds
Different net-forming technologies, production technology has many advantages and flexibility, can adjust respectively according to the performance requirement of product
The thickness proportion of one long fibre layer 10, the second long fibre layer 30 and short fiber layers 20 so that product has superior performance, full
Sufficient customer demand.
In the preferred embodiment of the embodiment of the present invention, the preparation side of Static Spinning nanometer multicomponent fibre non-woven material
Method further includes step (e) finishing functions, including at least one of hydrophilic, antibacterial, fluffy, soft, antistatic finishing technique.
By carrying out function to Static Spinning nanometer multicomponent fibre non-woven material provided by the invention, so that its performance is more
It is good excellent, it more disclosure satisfy that the different demands of user.
In addition, it is necessary to explanation, Static Spinning nanometer multicomponent fibre non-woven material provided by the invention is used to manufacture
The pro-skins textile such as facial mask and wet tissue, but above-mentioned field is not limited to, those skilled in the art can be according to the demand of related field
Using.
Finally it should be noted that:The above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations;To the greatest extent
Pipe is described in detail the present invention with reference to foregoing embodiments, it will be understood by those of ordinary skill in the art that:Its according to
Can so modify to the technical solution recorded in foregoing embodiments either to which part or all technical features into
Row equivalent replacement;And these modifications or replacement, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution
The range of scheme.
Claims (10)
1. a kind of Static Spinning nanometer multicomponent fibre non-woven material, which is characterized in that including being cascading from bottom to up
The first long fibre layer, short fiber layers and the second long fibre layer, the first long fibre layer, the short fiber layers and described second
Long fibre layer is compound successively by hot rolling, and the short fiber layers are prepared by melt-blown nano short fiber, first long fibre
Layer and the second long fibre layer are prepared by spunbond nanometer long fibre.
2. Static Spinning nanometer multicomponent fibre non-woven material according to claim 1, which is characterized in that the spunbond is received
Rice long fibre is selected from least one of polypropylene, polyethylene, polyamide or polyethylene terephthalate.
3. Static Spinning nanometer multicomponent fibre non-woven material according to claim 1, which is characterized in that the melt-blown is received
Rice staple fiber is selected from least one of natural fiber, chemical synthetic fiber or regenerated fiber;
Preferably, the melt-blown nano short fiber is chemical synthetic fiber;
Preferably, the chemical synthetic fiber is in polypropylene, polyethylene, polyamide or polyethylene terephthalate
It is at least one.
4. Static Spinning nanometer multicomponent fibre non-woven material according to claim 1, which is characterized in that the spunbond is received
The long stapled a diameter of 100-500nm of rice;
Preferably, a diameter of 100-500nm of the melt-blown nano short fiber.
5. Static Spinning nanometer multicomponent fibre non-woven material according to claim 1, which is characterized in that the Static Spinning
The thickness of nanometer multicomponent fibre non-woven material is 0.5-0.55mm;
Preferably, the thickness of the first long fibre layer is 0.17-0.2mm;
Preferably, the thickness of the second long fibre layer is 0.28-0.32mm;
Preferably, the thickness of the short fiber layers is 0.03-0.05mm.
6. according to the preparation method of claim 1-5 any one of them Static Spinning nanometer multicomponent fibre non-woven materials,
It is characterized in that, includes the following steps:
(a) spunbond nanometer long fibre is prepared, and makes its air drawing networking, the first long fibre layer is made;
(b) melt-blown nano short fiber is prepared on the first long fibre layer, and makes its networking that short fiber layers be made;
(c) it prepares spunbond nanometer long fibre again in short fiber layers, and makes its air drawing networking, the second long fibre is made
Layer;
(d) by the first long fibre layer, short fiber layers and the second long fibre layer successively method hot rolling, it is multigroup to obtain Static Spinning nanometer
Divide fibrous nonwoven material.
7. the preparation method of Static Spinning nanometer multicomponent fibre non-woven material according to claim 6, which is characterized in that
In step (a), spunbond nanometer long fibre passes through filament die extrusion molding.
8. the preparation method of Static Spinning nanometer multicomponent fibre non-woven material according to claim 6, which is characterized in that
In step (b), melt-blown nano short fiber sprays molding of quenching by being meltblown injector.
9. according to the preparation method of claim 6-8 any one of them Static Spinning nanometer multicomponent fibre non-woven materials,
It is characterized in that, further includes step (e) finishing functions, including hydrophilic, antibacterial, fluffy, soft or at least one of antistatic whole
Science and engineering skill.
10. according to claim 1-5 any one of them Static Spinning nanometer multicomponent fibre non-woven materials in facial mask or wet tissue
On application.