CN108264874A - For drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing and preparation method thereof - Google Patents
For drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing and preparation method thereof Download PDFInfo
- Publication number
- CN108264874A CN108264874A CN201711482829.XA CN201711482829A CN108264874A CN 108264874 A CN108264874 A CN 108264874A CN 201711482829 A CN201711482829 A CN 201711482829A CN 108264874 A CN108264874 A CN 108264874A
- Authority
- CN
- China
- Prior art keywords
- packaging machine
- high temperature
- temperature heat
- high speed
- blister package
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention provides one kind for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, include each component of following mass percentage content:Modified polyolefin resin 20 39.9%;Modified epoxy 10 20%;Solvent 50 60%;Auxiliary agent 0.1 0.5%;Preparation method includes the following steps:S1, it will be stirred and evenly mixed in solvent input reaction kettle, sequentially add modified polyolefin resin, modified epoxy under stiring, stir and evenly mix;S2, auxiliary agent is added in the mixed liquor of step S1, after high-speed stirred is mixed, shuts down curing;S3, solid content is measured, and adjusted to theoretical value;It is stirred for, cools down, filters.Compared with prior art, the invention has the advantages that:When medicine-packaging machine high temperature and high speed seals, no leakage envelope, without burnt fine wrinkle mark, free from extraneous odour;Heat seal strength is high, meets product demand;Glue-line stability is good, and it is unchanged that coated film places 1 year intensity;It is applied widely.
Description
Technical field
The present invention relates to high temperature heat-resistant sealing technical fields in drug blister package, and in particular, to one kind is used for drug
Blister package high speed medicine-packaging machine high temperature heat-resistant sealing and preparation method thereof.
Background technology
It grows continuously and fast with the economic situation in China, living standards of the people are continuously improved, and pharmaceuticals industry accordingly develops
Comparatively fast, while modern mechanical develops towards directions such as high-precision, high speed and low costs, these factors have all pushed directly on pharmacy
The fast development of enterprise.In order to make full use of the pharmaceutical equipment of pharmacy corporation, high-speed packet medicine is most directly, efficiently, most easily
Mode, but simultaneously also along with some inevitable problems.
During medicine-packaging machine Fast Packet medicine, when coating internal layer heat sealability is poor, sealing, which will appear, when temperature is too low leaks envelope or insecure,
Temperature is too high, and coating outer layer poor heat resistance, and sealing will appear xanthochromia, the burnt trace to wrinkle, and with peculiar smell.
Disclosed in the patent application of Publication No. CN106221646A a kind of aqueous heat-seal adhesive for drug bubble-cap and
Preparation method, the heat-seal adhesive include following component:Polyester emulsion, modified polyolefin hydrocarbon emulsion, polyaminoester emulsion, auxiliary agent, increasing
Stick, ethylene glycol, glycerine, ethyl alcohol, water;The preparation of the heat-seal adhesive includes the following steps:By polyester emulsion, polyurethane breast
Liquid, modified polyolefin hydrocarbon emulsion after mixing, add in ethyl alcohol, water, ethylene glycol, propylene glycol mixture;Add in auxiliary agent and thickening
Agent is cured after stirring;The solid content of product is detected, and the solid content is adjusted to theoretical value, stirring discharging.It but should
The heat-seal adhesive prepared in patent has:1. hydrolytic resistance is poor;2. the poor adhesive force with aluminium;3. the deficiencies of diluting easily demulsification with alcohol;
4. it is sealed when not having high-speed sealing without leakage, the effect without burnt fine wrinkle mark.
Invention content
For the defects in the prior art, the object of the present invention is to provide one kind to be used for drug blister package high speed medicine-packaging machine
High temperature heat-resistant sealing and preparation method thereof.
The purpose of the present invention is achieved through the following technical solutions:
The present invention provides one kind for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, including following quality percentage
Than each component of content:
For above-mentioned raw materials used mass content range:
If the content of modified polyolefin resin is higher than 39.9%, cost is higher;If less than 20%, glue-line intensity is relatively low;
If the content of modified epoxy can influence strength of coating higher than 20%, and can make the weatherability, ageing-resistant of coating
It is less able;And if less than 10%, the high temperature resistance of glue-line cannot be significantly improved;
If the content of auxiliary agent can reduce the intensity of coating higher than 0.5%;And less than 0.1%, then overfoaming is apparent, and levelling becomes
Difference is unfavorable for producing.
Preferably, the modified polyolefin resin is selected from maleic anhydride modified polyolefin, carboxyl acid modified polyethylene, EVA, gathers
One or more of vinyl alcohol, Carboxy, vinyl chloride-vinyl acetate resin.It is outstanding to metal under the conditions of above-mentioned improved polyalkene low-temperature heat-sealing
It is that aluminium has superior adhesion, also there is excellent adhesion to PVC;During high temperature heat seal, above-mentioned modified polyolefin resin can
Fully softening, it is more preferable with the adhesion of base material, it can be sealed to avoid the leakage occurred when sealing or insecure.
Preferably, the modified epoxy is selected from polyether modified epoxy resin, modifying epoxy resin by organosilicon, acrylic acid
At least one of modified epoxy.The epoxy resin of above-mentioned several modifications is with adhesive force is good, chemicals-resistant is outstanding, corrosion resistant
The features such as corrosion is outstanding.The high temperature resistance of coating can be improved, xanthochromia and coke during high temperature heat seal is avoided to wrinkle.
Preferably, the solvent is selected from one or more of butanone, ethyl acetate, n-propyl acetate, n-butyl acetate.
Preferably, the auxiliary agent includes at least one of levelling agent and antifoaming agent.
Preferably, the levelling agent is organosilicon levelling agent.With heat-resisting quantity, when use, can improve adhesive force, reduce
Or eliminate shrinkage cavity caused by due to base material.
Preferably, the antifoaming agent is polyethers antifoaming agent.Polyethers antifoaming agent is with the suds time is long, effect is good, disappears
Steep the features such as speed is fast, thermal stability is good.
There are certain synergistic effect between above-mentioned modified polyolefin resin, modified epoxy and organosilicon levelling agent,
Heatproof and the attachment with base material aluminium can be improved, so that heat-seal adhesive obtained has nothing when high temperature and high speed seals packet medicine
Leakage envelope, without burnt fine wrinkle mark the advantages that.
The present invention also provides a kind of preparation method for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, including
Following steps:
S1, it will be stirred and evenly mixed in solvent input reaction kettle, sequentially add modified polyolefin resin, modified epoxy under stiring
Resin stirs 1-2 hours, obtains mixed liquor;
S2, auxiliary agent is added in the mixed liquor of step S1, high-speed stirred 0.5-1 hours, after mixing, shuts down curing
10-12 hours;
S3, solid content is measured, and adjusted to theoretical value;It is stirred for 1-2 hours, cooling, filtering.
Present invention the reason of using above-mentioned preparation process for:It, should be first fully molten since modified polyolefin resin is solid-like
After solution is complete, liquid modifying epoxy resin is added, auxiliary agent should after mixing be added in above-mentioned solution, and be improved after having fed intake
Mixing speed makes it be uniformly dispersed.If each component is added in mixing simultaneously, conglomeration and attached wall are generally resulted in.
Compared with prior art, the present invention has following advantageous effect:
1st, when medicine-packaging machine high temperature and high speed seals, no leakage envelope, without burnt fine wrinkle mark, free from extraneous odour.
2nd, heat seal strength is high, meets product demand.
3rd, glue-line stability is good, and it is unchanged that coated film places 1 year intensity.
4th, it is applied widely, matrix resin content can be formulated by change in wider range and adjust heat seal strength, so as to
Suitable for different Al foil substrates.
5th, the adhesive force with aluminium is improved by modified polyolefin resin and part of auxiliary in the present invention, modified epoxy changes
Kind anti-hydrolytic performance and high temperature resistance, and the present invention, based on oiliness heat-seal adhesive, demulsification caused by there is no being diluted with alcohol is asked
Topic.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail.Following embodiment will be helpful to the technology of this field
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill to this field
For personnel, without departing from the inventive concept of the premise, several changes and improvements can also be made.These belong to the present invention
Protection domain.
In following each embodiment and comparative examples:
The optional trade mark of maleic anhydride modified polyolefin is MAG-PP, Du Pont 353D;The optional trade mark of EVA is Du Pont 210,
VE810;The optional trade mark of vinyl chloride-vinyl acetate resin is CP-450, SOLBIN-A, H15/45M, VAM, E22/48A.
The optional trade mark of polyether modified epoxy resin is EPU-73B, EP-4000;The trade mark of modifying epoxy resin by organosilicon
For SF-8413;The optional trade mark of acrylic modified epoxy resin is assists space chemical industry A102, FB9801, still promise 4400.
The trade mark of organosilicon levelling agent is BYK-322.
The trade mark of polyether-type antifoaming agent is DF-830.
Embodiment 1
The present embodiment is related to one kind for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, and specific formula is shown in Table 1,
Preparation method includes the following steps:
(1) first whole solvents are put by proportioning in reaction kettle and stirred;
(2) it is kept stirring and puts into improved polyalkene, modified epoxy in reaction kettle successively, stir 1-2 hours;
(3) it is to be mixed uniformly after auxiliary agent is slowly put into reaction kettle, high-speed stirred 0.5-1 hours;
(4) when after mixing, shutdown cures 10-12 hours;
(5) solid content is measured, and is adjusted to theoretical value;
(6) it slowly stirs 1-2 hours again, cooling, 250 mesh filter screen filtrations, weighing and bagging.
Embodiment 2-5
Embodiment 2-5 relates separately to a kind of for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, preparation side
Method is consistent with embodiment 1, and specific formula is shown in Table 1.
Table 1
Comparative example 1
This comparative example is related to a kind of for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, preparation method and reality
It is basically identical to apply example 1, the difference lies in:Without maleic anhydride modified polyolefin component.
Comparative example 2
This comparative example is related to a kind of for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, preparation method and reality
It is basically identical to apply example 1, the difference lies in:Without polyether modified epoxy resin Composition.
Comparative example 3
This comparative example is to disclose a kind of aqueous heat-seal adhesive for drug bubble-cap in the patent application of CN106221646A.
The present invention is oleaginous system, generally uses ethyl ester, butanone etc. as dicyandiamide solution, and the patent Shen of CN106221646A
Please be water-based system, the equal objectionable intermingling of the two each component partial alternative, the performance of the heat-seal adhesive of acquisition is also poor.
Comparative example 4
This comparative example is related to a kind of for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, preparation method and reality
It is basically identical to apply example 1, the difference lies in:Polyether modified epoxy resin is replaced using polyether-modified polyurethane.
Comparative example 5
This comparative example is related to a kind of for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, preparation method and reality
It is basically identical to apply example 1, the difference lies in:Maleic anhydride modified polyolefin is replaced using Hydroxylated acrylic resin.
Comparative example 6
This comparative example is related to a kind of for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, preparation method and reality
It is basically identical to apply example 2, the difference lies in:Modifying epoxy resin by organosilicon is replaced using polyether-modified polyurethane.
Comparative example 7
This comparative example is related to a kind of for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, preparation method and reality
It is basically identical to apply example 1, the difference lies in:Polyether modified epoxy resin is replaced using bisphenol A-type modified epoxy.
Comparative example 8
This comparative example is related to a kind of for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, preparation method and reality
It is basically identical to apply example 1, the difference lies in:Polyether modified epoxy resin is replaced using unmodified epoxy resin.
Performance test
1. heat sealability, 2. readily oxidizable substance, 3. uncoiling performance etc. use testing standard for:
National Drug Administration national drug packing container (material) standard (tentative) YBB00152002;
Adhesion test method:Cross-cut methods;
Hydrolytic resistance test method:Constant temperature and humidity (double 85 conditions) tests heat seal strength after three days.
High temperature sealing correlated performance test:The small-sized medicine-packaging machine simulation packet medicine in pharmaceutical factory, xanthochromia performance are tested using color difference meter;
B values change before and after comparison sealing, and difference is no more than 1.5 anti-yellowing property ok.
Each embodiment and comparative example is tested for the property, test result is as follows shown in table 2:
Table 2
Note:The national standard of readily oxidizable substance is less than 1.5mL/ ㎡, some are, readily oxidizable substance numbers harmful to drug
Value is bigger, and drug is faster by oxidation deactivation.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make a variety of changes or change within the scope of the claims, this not shadow
Ring the substantive content of the present invention.In the absence of conflict, the feature in embodiments herein and embodiment can arbitrary phase
Mutually combination.
Claims (8)
1. one kind is used for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, which is characterized in that including following quality percentage
Than each component of content:
2. according to claim 1 be used for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, which is characterized in that institute
State modified polyolefin resin be selected from maleic anhydride modified polyolefin, carboxyl acid modified polyethylene, EVA, polyvinyl alcohol, Carboxy,
One or more of vinyl chloride-vinyl acetate resin.
3. according to claim 1 be used for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, which is characterized in that institute
Modified epoxy is stated in polyether modified epoxy resin, modifying epoxy resin by organosilicon, acrylic modified epoxy resin
It is at least one.
4. according to claim 1 be used for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, which is characterized in that institute
It states solvent and is selected from one or more of butanone, ethyl acetate, n-propyl acetate, n-butyl acetate.
5. according to claim 1 be used for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, which is characterized in that institute
It states auxiliary agent and includes at least one of levelling agent and antifoaming agent.
6. according to claim 5 be used for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, which is characterized in that institute
Levelling agent is stated as organosilicon levelling agent.
7. according to claim 5 be used for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing, which is characterized in that institute
Antifoaming agent is stated as polyethers antifoaming agent.
8. a kind of preparation side according to claim 1 for drug blister package high speed medicine-packaging machine high temperature heat-resistant sealing
Method, which is characterized in that include the following steps:
S1, it will be stirred and evenly mixed in solvent input reaction kettle, sequentially add modified polyolefin resin, modified epoxy tree under stiring
Fat stirs 1-2 hours, obtains mixed liquor;
S2, auxiliary agent is added in the mixed liquor of step S1, high-speed stirred 0.5-1 hours, after mixing, shuts down curing 10-12
Hour;
S3, solid content is measured, and adjusted to theoretical value;It is stirred for 1-2 hours, cooling, filtering.