CN108264791A - A kind of general color masterbatch of coating - Google Patents
A kind of general color masterbatch of coating Download PDFInfo
- Publication number
- CN108264791A CN108264791A CN201810096340.7A CN201810096340A CN108264791A CN 108264791 A CN108264791 A CN 108264791A CN 201810096340 A CN201810096340 A CN 201810096340A CN 108264791 A CN108264791 A CN 108264791A
- Authority
- CN
- China
- Prior art keywords
- color masterbatch
- general color
- organic
- toner
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of general color masterbatch of coating, including consisting of composition and mass percent：Organic-inorganic amphoteric dispersant 40 95%, cosolvent 0 40%, toner 5 20%.The present invention is a kind of novel general color masterbatch, regardless of single two-component, realizes general purpose, makes production management easy, will not be chaotic, so as to improve production efficiency.This general color masterbatch is suitable for aqueous or oil paint, and can cross the target to low VOC.Product is suitable for a variety of systems such as acrylic resin, alkyd resin, polyester resin, water-base resin, is worth recommending.
Description
Technical field
The invention belongs to aqueous/oil paint fields, and in particular to a kind of general color masterbatch of coating.
Background technology
At present, pigment printing paste or color masterbatch all divide single two-component used in many companies at present, can not be general, cause in life
It is easier to situation of the material using mistake occur in production management, is unfavorable for production management and warehousing management.
Invention content
Present invention aims at a kind of general color masterbatch of coating is provided, its applicability is wide, applicable organic or inorganic toner, and
It is suitble to different form and aspect, various demands can be met, with overcome the deficiencies in the prior art.
The technical scheme is that：A kind of general color masterbatch of coating, including consisting of composition and mass percent：
Organic-inorganic amphoteric dispersant 40-95%,
Cosolvent 0-40%,
Toner 5-20%.
The general color masterbatch of above-mentioned coating, which is characterized in that the organic-inorganic amphoteric dispersant, cosolvent, toner are mixing
After being uniformly dispersed with below 10 microns of laboratory grinder fineness of grind (according to normal abrasive fineness is used to can adjust, to be suitble to
Various criterion).
The organic-inorganic amphoteric dispersant is 4310 dispersants of BASF.
The cosolvent is PMA cosolvents.
The general color masterbatch of above-mentioned coating, when the content of cosolvent is 0, organic-inorganic amphoteric dispersant, the quality of toner hundred
Ratio is divided to be：Organic-inorganic amphoteric dispersant 80-95%, toner 5-20%.When toner selects black powder, organic-inorganic both sexes point
Powder, toner mass percent be：Organic-inorganic amphoteric dispersant 90-95%, toner 5-10%.
The general color masterbatch of above-mentioned coating, when toner selects black powder, each composition and mass percent are：Organic-inorganic
Amphoteric dispersant 60-95%, cosolvent 0-30%, black powder 5-10%.When the content of cosolvent is 0, organic-inorganic both sexes
Dispersant, toner mass percent be：Organic-inorganic amphoteric dispersant 90-95%, black powder 5-10%.
The beneficial effects of the invention are as follows：The present invention is a kind of novel general color masterbatch, regardless of single two-component, is realized general
Purpose makes production management easy, will not be chaotic, so as to improve production efficiency.
The general color masterbatch of the present invention is suitable for aqueous or oil paint, and can cross the target to low VOC.Product is suitable for third
A variety of systems such as olefin(e) acid resin, alkyd resin, polyester resin, water-base resin, facilitate production, improve the unification of form and aspect, give
Library tape preferably controls, and is worth recommending.
Specific embodiment
Embodiment 1：
The formula of the general color masterbatch of coating is as follows：Organic-inorganic amphoteric dispersant 40%, cosolvent 40%, toner 20%.
Embodiment 2：
The formula of the general color masterbatch of coating is as follows：Organic-inorganic amphoteric dispersant 60%, cosolvent 30%, toner 10%.
Embodiment 3：
The formula of the general color masterbatch of coating is as follows：Organic-inorganic amphoteric dispersant 55%, cosolvent 40%, toner 5%.
Embodiment 4：
The formula of the general color masterbatch of coating is as follows：Organic-inorganic amphoteric dispersant 80%, cosolvent 0, toner 20%.
Embodiment 5：
The formula of the general color masterbatch of coating is as follows：Organic-inorganic amphoteric dispersant 93%, cosolvent 0, toner 7%.
In above-described embodiment, organic-inorganic amphoteric dispersant selects 4310 dispersant (models of such as BASF：EFKA-
E4310), cosolvent selection PMA amphiprotic solvents.Toner can be used it is organic or inorganic, be suitble to different form and aspect, Ke Yiman
The various demands of foot.More than material is mixed after being uniformly dispersed with 10 microns of laboratory grinder fineness of grind hereinafter, to reach work
Industry requirement.Cosolvent selection PMA amphiprotic solvents (propylene glycol methyl ether acetate) are because of existing ehter bond in its molecule, and have carbonyl
Base, carbonyl form the structure of ester again, while contain alkyl again.The existing nonpolar moiety in same molecule, and polarized portion
Point, this two-part functional group, which not only mutually restricted, to be repelled, but also respectively play its intrinsic effect.Therefore, it can be to non-polar material
Matter and polar substances have solvability.With versatility.
The general color masterbatch of coating that embodiment 1-5 is produced, carrying out compatibility test, (aqueous system uses aqueous color
Powder), it is as a result as follows：
Claims (8)
1. a kind of general color masterbatch of coating, which is characterized in that including consisting of composition and mass percent：
Organic-inorganic amphoteric dispersant 40-95%,
Cosolvent 0-40%,
Toner 5-20%.
2. the general color masterbatch of coating according to claim 1, which is characterized in that the organic-inorganic amphoteric dispersant, cosolvent,
Toner after mixing is uniformly dispersed with 10 microns of laboratory grinder fineness of grind below.
3. the general color masterbatch of coating according to claim 1, which is characterized in that the organic-inorganic amphoteric dispersant is BASF
4310 dispersants.
4. the general color masterbatch of coating according to claim 1, which is characterized in that the cosolvent is PMA cosolvents.
5. according to any general color masterbatch of coating of Claims 1-4, which is characterized in that when the content of cosolvent is 0, have
The inorganic amphoteric dispersant of machine, the mass percent of toner are：Organic-inorganic amphoteric dispersant 80-95%, toner 5-20%.
6. the general color masterbatch of coating according to claim 5, which is characterized in that when toner selects black powder, organic-inorganic two
Property dispersant, toner mass percent be：Organic-inorganic amphoteric dispersant 90-95%, toner 5-10%.
7. according to any general color masterbatch of coating of Claims 1-4, which is characterized in that when toner selects black powder, each group
It is into composition and mass percent：Organic-inorganic amphoteric dispersant 60-95%, cosolvent 0-30%, black powder 5-10%.
8. the general color masterbatch of coating according to claim 7, which is characterized in that when the content of cosolvent is 0, organic-inorganic two
Property dispersant, toner mass percent be：Organic-inorganic amphoteric dispersant 90-95%, black powder 5-10%.