CN108251945A - A kind of healthcare face fabric of far infrared - Google Patents
A kind of healthcare face fabric of far infrared Download PDFInfo
- Publication number
- CN108251945A CN108251945A CN201810272306.0A CN201810272306A CN108251945A CN 108251945 A CN108251945 A CN 108251945A CN 201810272306 A CN201810272306 A CN 201810272306A CN 108251945 A CN108251945 A CN 108251945A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- micron
- silk
- grain size
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of healthcare face fabric of far infrared, and the healthcare face fabric is formed by following parts by weight material is blended：Special 20 ~ 30 parts of spandex thread, 45 ~ 55 parts of silk, 35 ~ 45 parts of soybean fiber silk；Contain following parts by weight of component in the special spandex thread：40 ~ 50 parts of polyurethanes, 2 ~ 3 parts of tourmaline powder, 1 ~ 2 part of glass microballoon, 1 ~ 3 part of magnetic iron powder, 2 ~ 4 parts of magnesia, 1 ~ 2 part of zinc oxide, 1 ~ 2 part of ramulus et uncus uncariae, 1 ~ 3 part of mistletoe, 1 ~ 2 part of Fructus meliae toosendan, 1 ~ 3 part of ox rattan, 1 ~ 3 part of moutan bark, 1 ~ 2 part of madder, 1 ~ 2 part of Radix Astragali；Advantageous effect：The warm fabric of the present invention is organically combined using natural fiber silk and artificial silk, by carrying out deep processing to artificial silk, with it is submissive, crease-resistant, wear-resisting, nontoxic, durable, anti-infrared, have effects that magnetic field can with dysmenorrhoea active, clearing damp and promoting diuresis, qi-restoratives, dampness elimination, it is calming the liver to stop the wind, there is anion and drug ingedient to promote blood circulation.
Description
Technical field
The present invention relates to textile material field, more particularly to a kind of healthcare face fabric of far infrared.
Background technology
With social progress and improvement of living standard, requirement of the people to clothes is higher and higher, especially to underwear
Soft comfortable is not only focused in selection, more focuses on health, healthcare function.Traditional farinfrared health-care material is generally mostly wool, wood
Cotton fiber etc., and generally use thickeies design, although warmth retention property is good, there are clothing is excessively thick and heavy, comfort and gas permeability
The problems such as poor.Existing farinfrared health-care material durability is poor, and repeatedly warming effect weakens significantly after washing.Therefore, one is developed
The healthcare face fabric planted i.e. non-toxic and safe and have both healthcare function simultaneously with excellent durability is actually necessary.
Invention content
The purpose of the present invention is to provide a kind of healthcare face fabrics of far infrared, to solve the deficiencies in the prior art, make health care
Fabric with it is nontoxic, durable, anti-infrared, with magnetic field can it is active with dysmenorrhoea, promote blood with anion and drug ingedient
Many effects such as cycle.
Technical scheme of the present invention:
A kind of healthcare face fabric of far infrared, the healthcare face fabric are formed by following parts by weight material is blended：Special spandex thread 20 ~ 30
Part, 45 ~ 55 parts of silk, 35 ~ 45 parts of soybean fiber silk；Contain following parts by weight of component in the special spandex thread：Poly- amino first
40 ~ 50 parts of acid esters, 2 ~ 3 parts of tourmaline powder, 1 ~ 2 part of glass microballoon, 1 ~ 3 part of magnetic iron powder, 2 ~ 4 parts of magnesia, 1 ~ 2 part of zinc oxide,
1 ~ 2 part of ramulus et uncus uncariae, 1 ~ 3 part of mistletoe, 1 ~ 2 part of Fructus meliae toosendan, 1 ~ 3 part of ox rattan, 1 ~ 3 part of moutan bark, 1 ~ 2 part of madder, 1 ~ 2 part of Radix Astragali.
As the preferred embodiment of the present invention, healthcare face fabric of the present invention is formed by following parts by weight material is blended：
Special 25 parts of spandex thread, 50 parts of silk, 40 parts of soybean fiber silk；Contain following parts by weight of component in the special spandex thread：It is poly-
45 parts of carbamate, 3 parts of tourmaline powder, 2 parts of glass microballoon, 2 parts of magnetic iron powder, 3 parts of magnesia, 2 parts of zinc oxide, 2 parts of ramulus et uncus uncariae,
2 parts of mistletoe, 2 parts of Fructus meliae toosendan, 2 parts of ox rattan, 2 parts of moutan bark, 2 parts of madder, 2 parts of Radix Astragali.
The special spandex thread is prepared using following methods：S1. macro is milled：By tourmaline powder, glass microballoon, magnet
It is 0.01 ~ 0.02 micron of the first mixed-powder that powder, magnesia, zinc oxide wear into grain size with precision lapping machine, then by ramulus et uncus uncariae, Mongolian oak
Parasitism, Fructus meliae toosendan, Niu Teng, moutan bark, madder and Radix Astragali with precision lapping machine wear into that grain size is 0.02 ~ 0.03 micron it is second mixed
Close powder；S2. melting mixing：Under vacuum, the first mixed-powder is heated to 1600 ~ 1800 DEG C, becomes molten condition,
The second mixed-powder is added in after being cooled to 230 ~ 260 DEG C, adds polyurethanes, forms molten mixture；It S3. will melting
Mixture is squeezed out with extruser, is granulated and then special spandex thread is made after spinning, stretching.
As the preferred embodiment of the present invention, special spandex thread of the present invention is prepared using following methods：S1. macro
Milling：It is 0.01 ~ 0.02 that tourmaline powder, glass microballoon, magnetic iron powder, magnesia, zinc oxide are worn into grain size with precision lapping machine
First mixed-powder of micron, then by ramulus et uncus uncariae, mistletoe, Fructus meliae toosendan, Niu Teng, moutan bark, madder and Radix Astragali precision lapping machine
Wear into the second mixed-powder that grain size is 0.02 ~ 0.03 micron；S2. melting mixing：Under vacuum, by the first mixed-powder
1700 DEG C are heated to, becomes molten condition, the second mixed-powder is added in after being cooled to 245 DEG C, adds polyurethanes, shape
Into molten mixture；S3. molten mixture with extruser squeezed out, be granulated and then special ammonia is made after spinning, stretching
Synthetic fibre silk.
As the preferred embodiment of the present invention, the grain size of special spandex thread of the present invention is 0.06 ~ 0.08 micron, silkworm
The grain size of silk is 0.02 ~ 0.04 micron, and the grain size of soybean fiber silk is 0.05 ~ 0.07 micron.
Advantageous effect：The warm fabric of the present invention is organically combined using natural fiber silk and artificial silk, by being carried out to artificial silk
Deep processing, with it is submissive, crease-resistant, wear-resisting, nontoxic, durable, anti-infrared, can be lived with dysmenorrhoea with magnetic field
Network, clearing damp and promoting diuresis, qi-restoratives, dampness elimination, it is calming the liver to stop the wind, have effects that anion and drug ingedient promote blood circulation.
Specific embodiment
The following content is a further detailed description of the present invention in conjunction with specific preferred embodiments, it is impossible to assert
The specific implementation of the present invention is confined to these explanations, it should be noted that in the absence of conflict, the reality in the application
Applying the feature in example and embodiment can be combined with each other.
Embodiment 1：
A kind of healthcare face fabric of far infrared of the present embodiment, which is characterized in that the healthcare face fabric is blended by following parts by weight material
It forms：Special 20 parts of spandex thread, 45 parts of silk, 35 parts of soybean fiber silk；Contain following parts by weight group in the special spandex thread
Point：40 parts of polyurethanes, 1 part of glass microballoon, 1 part of magnetic iron powder, 2 parts of magnesia, 1 part of zinc oxide, hooks 2 parts of tourmaline powder
1 part of rattan, 1 part of mistletoe, 1 part of Fructus meliae toosendan, 1 part of ox rattan, 1 part of moutan bark, 1 part of madder, 1 part of Radix Astragali.
The special spandex thread is prepared using following methods：S1. macro is milled：By tourmaline powder, glass microballoon, magnet
It is 0.01 micron of the first mixed-powder that powder, magnesia, zinc oxide wear into grain size with precision lapping machine, then by ramulus et uncus uncariae, mistletoe,
Fructus meliae toosendan, Niu Teng, moutan bark, madder and Radix Astragali wear into the second mixed-powder that grain size is 0.02 micron with precision lapping machine；S2.
Melting mixing：Under vacuum, the first mixed-powder is heated to 1600 DEG C, becomes molten condition, added after being cooled to 230 DEG C
Enter the second mixed-powder, add polyurethanes, form molten mixture；S3. by molten mixture extruser
It squeezes out, be granulated and then special spandex thread is made after spinning, stretching.
The grain size of the special spandex thread is 0.06 micron, and the grain size of silk is 0.02 micron, the grain size of soybean fiber silk
It is 0.05 micron.
Embodiment 2：
A kind of healthcare face fabric of far infrared, the healthcare face fabric are formed by following parts by weight material is blended：Special 25 parts of spandex thread,
50 parts of silk, 40 parts of soybean fiber silk；Contain following parts by weight of component in the special spandex thread：45 parts of polyurethanes,
3 parts of tourmaline powder, 2 parts of glass microballoon, 2 parts of magnetic iron powder, 3 parts of magnesia, 2 parts of zinc oxide, 2 parts of ramulus et uncus uncariae, 2 parts of mistletoe, melia toosendan
2 parts of son, 2 parts of ox rattan, 2 parts of moutan bark, 2 parts of madder, 2 parts of Radix Astragali.
The special spandex thread is prepared using following methods：S1. macro is milled：By tourmaline powder, glass microballoon, magnet
It is 0.02 micron of the first mixed-powder that powder, magnesia, zinc oxide wear into grain size with precision lapping machine, then by ramulus et uncus uncariae, mistletoe,
Fructus meliae toosendan, Niu Teng, moutan bark, madder and Radix Astragali wear into the second mixed-powder that grain size is 0.03 micron with precision lapping machine；S2.
Melting mixing：Under vacuum, the first mixed-powder is heated to 1700 DEG C, becomes molten condition, added after being cooled to 245 DEG C
Enter the second mixed-powder, add polyurethanes, form molten mixture；S3. by molten mixture extruser
It squeezes out, be granulated and then special spandex thread is made after spinning, stretching.
As the preferred embodiment of the present invention, the grain size of special spandex thread of the present invention is 0.07 micron, silk
Grain size is 0.03 micron, and the grain size of soybean fiber silk is 0.06 micron.
Embodiment 3：
A kind of healthcare face fabric of far infrared, the healthcare face fabric are formed by following parts by weight material is blended：Special 30 parts of spandex thread,
55 parts of silk, 45 parts of soybean fiber silk；Contain following parts by weight of component in the special spandex thread：50 parts of polyurethanes,
3 parts of tourmaline powder, 2 parts of glass microballoon, 3 parts of magnetic iron powder, 4 parts of magnesia, 2 parts of zinc oxide, 2 parts of ramulus et uncus uncariae, 3 parts of mistletoe, melia toosendan
2 parts of son, 3 parts of ox rattan, 3 parts of moutan bark, 2 parts of madder, 2 parts of Radix Astragali.
The special spandex thread is prepared using following methods：S1. macro is milled：By tourmaline powder, glass microballoon, magnet
It is 0.02 micron of the first mixed-powder that powder, magnesia, zinc oxide wear into grain size with precision lapping machine, then by ramulus et uncus uncariae, mistletoe,
Fructus meliae toosendan, Niu Teng, moutan bark, madder and Radix Astragali wear into the second mixed-powder that grain size is 0.03 micron with precision lapping machine；S2.
Melting mixing：Under vacuum, the first mixed-powder is heated to 1800 DEG C, becomes molten condition, added after being cooled to 260 DEG C
Enter the second mixed-powder, add polyurethanes, form molten mixture；S3. by molten mixture extruser
It squeezes out, be granulated and then special spandex thread is made after spinning, stretching.
As the preferred embodiment of the present invention, the grain size of special spandex thread of the present invention is 0.08 micron, silk
Grain size is 0.04 micron, and the grain size of soybean fiber silk is 0.07 micron.
For those of ordinary skill in the art to which the present invention belongs, without departing from the inventive concept of the premise,
Several simple deduction or replace can also be made, should all be considered as belonging to protection scope of the present invention.
Claims (6)
1. a kind of healthcare face fabric of far infrared, which is characterized in that the healthcare face fabric is formed by following parts by weight material is blended：It is special
20 ~ 30 parts of spandex thread processed, 45 ~ 55 parts of silk, 35 ~ 45 parts of soybean fiber silk；Contain following parts by weight in the special spandex thread
Component：40 ~ 50 parts of polyurethanes, 2 ~ 3 parts of tourmaline powder, 1 ~ 2 part of glass microballoon, 1 ~ 3 part of magnetic iron powder, 2 ~ 4 parts of magnesia,
1 ~ 2 part of zinc oxide, 1 ~ 2 part of ramulus et uncus uncariae, 1 ~ 3 part of mistletoe, 1 ~ 2 part of Fructus meliae toosendan, 1 ~ 3 part of ox rattan, 1 ~ 3 part of moutan bark, madder 1 ~ 2
Part, 1 ~ 2 part of Radix Astragali.
2. healthcare face fabric according to claim 1, which is characterized in that the healthcare face fabric is blended by following parts by weight material
It forms：Special 25 parts of spandex thread, 50 parts of silk, 40 parts of soybean fiber silk；Contain following parts by weight group in the special spandex thread
Point：45 parts of polyurethanes, 2 parts of glass microballoon, 2 parts of magnetic iron powder, 3 parts of magnesia, 2 parts of zinc oxide, hooks 3 parts of tourmaline powder
2 parts of rattan, 2 parts of mistletoe, 2 parts of Fructus meliae toosendan, 2 parts of ox rattan, 2 parts of moutan bark, 2 parts of madder, 2 parts of Radix Astragali.
3. healthcare face fabric according to claim 1, which is characterized in that the special spandex thread is prepared using following methods：
S1. macro is milled：Tourmaline powder, glass microballoon, magnetic iron powder, magnesia, zinc oxide are worn into grain size with precision lapping machine is
0.01 ~ 0.02 micron of the first mixed-powder, then ramulus et uncus uncariae, mistletoe, Fructus meliae toosendan, Niu Teng, moutan bark, madder and Radix Astragali is smart
Close grinder wears into the second mixed-powder that grain size is 0.02 ~ 0.03 micron；S2. melting mixing：Under vacuum, by first
Mixed-powder is heated to 1600 ~ 1800 DEG C, becomes molten condition, the second mixed-powder is added in after being cooled to 230 ~ 260 DEG C, then add
Enter polyurethanes, form molten mixture；S3. molten mixture with extruser is squeezed out, be granulated and then through spinning
Special spandex thread is made after stretching in silk.
4. healthcare face fabric according to claim 3, which is characterized in that the special spandex thread is prepared using following methods：
S1. macro is milled：Tourmaline powder, glass microballoon, magnetic iron powder, magnesia, zinc oxide are worn into grain size with precision lapping machine is
0.01 ~ 0.02 micron of the first mixed-powder, then ramulus et uncus uncariae, mistletoe, Fructus meliae toosendan, Niu Teng, moutan bark, madder and Radix Astragali is smart
Close grinder wears into the second mixed-powder that grain size is 0.02 ~ 0.03 micron；S2. melting mixing：Under vacuum, by first
Mixed-powder is heated to 1700 DEG C, becomes molten condition, and the second mixed-powder is added in after being cooled to 245 DEG C, adds poly- amino
Formic acid esters forms molten mixture；S3. molten mixture with extruser is squeezed out, be granulated and then after spinning, stretching
Special spandex thread is made.
5. healthcare face fabric according to claim 1, which is characterized in that the grain size of the special spandex thread is 0.06 ~ 0.08
Micron, the grain size of silk is 0.02 ~ 0.04 micron, and the grain size of soybean fiber silk is 0.05 ~ 0.07 micron.
6. healthcare face fabric according to claim 1, which is characterized in that the grain size of the special spandex thread is 0.07 micron,
The grain size of silk is 0.03 micron, and the grain size of soybean fiber silk is 0.06 micron.