CN108239263B - 利用含水杨醛基的铝配合物催化己内酯聚合的方法 - Google Patents

利用含水杨醛基的铝配合物催化己内酯聚合的方法 Download PDF

Info

Publication number
CN108239263B
CN108239263B CN201711314930.4A CN201711314930A CN108239263B CN 108239263 B CN108239263 B CN 108239263B CN 201711314930 A CN201711314930 A CN 201711314930A CN 108239263 B CN108239263 B CN 108239263B
Authority
CN
China
Prior art keywords
reaction
ligand
catalyst
aluminum complex
salicylaldehyde
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201711314930.4A
Other languages
English (en)
Other versions
CN108239263A (zh
Inventor
姚伟
高爱红
张永芳
王洪宾
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Jinan
Original Assignee
University of Jinan
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Jinan filed Critical University of Jinan
Priority to CN201711314930.4A priority Critical patent/CN108239263B/zh
Publication of CN108239263A publication Critical patent/CN108239263A/zh
Application granted granted Critical
Publication of CN108239263B publication Critical patent/CN108239263B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种利用含水杨醛基的铝配合物催化己内酯聚合的方法，包括以下步骤：将催化剂、有机溶剂、苄醇助催化剂和己内酯混合，在无水无氧和惰性气体保护下进行开环聚合反应，反应后将反应物进行处理得聚己内酯。本发明以自行研发的含水杨醛基的铝配合物作为催化剂进行己内酯开环聚合反应，含水杨醛基的铝配合物催化剂制备方法简单，成本低，产品收率高，催化剂结构变化多样，金属中心铝与配体的二价N，N，O，O配位，催化活性高、立体选择性高、反应速率快，得到的聚合物是苄氧基封端的聚合物，分子量分布窄，分子量可控、产率高，满足市场需求。

Description

利用含水杨醛基的铝配合物催化己内酯聚合的方法
技术领域
本发明涉及一种催化己内酯聚合的方法，具体涉及一种利用含水杨醛基的铝配合物催化己内酯聚合的方法。
背景技术
以石油为原料的传统塑料从上世纪40年代开始在工业中有非常大的影响，这些传统塑料有无可比拟的优点，但有两个致命的缺点：不可再生性和不可降解性。在石油作为不可再生资源面临枯竭的情况下，依赖石油原料的高分子塑料材料的快速发展受到很大制约，而且高分子聚合塑料材料难以降解，大量的高分子聚合塑料材料废弃物长期积存在现实生活中对人类生存环境造成的污染也逐渐加重。寻找代替石油的可再生资源，开发环境友好型、可生物降解型的新材料成为未来高分子聚合塑料材料发展的趋势。
聚酯为生物可降解型的绿色环保型的高分子材料，其作为石油产品的替代物越来越受到人们的关注。在自然生活环境中，废弃的聚内酯材料能被土壤中的微生物彻底的分解成水和二氧化碳，环保并且可再生。因为聚酯无毒、无刺激性，且具有良好的生物相容性，因此被广泛应用于医学和环保领域，例如手术缝合线、包装、药物控制释放和组织工程支架等。聚内酯优良的生物相容性、生物降解性以及可持续发展利用的性能，使其已经成为21世纪最具有发展前景的高分子材料。
便捷的合成聚酯的方法是环内酯的开环聚合法，这种合成方法的优点是：聚合的可控性、较窄的分子量分布。目前常用的催化剂多是配体和金属形成的配合物，催化剂中的金属包括镁、钙、锗、锡、铝、锌、铁、钛、锆、镧系等。在金属配合物催化剂中，配体和金属的选择催化剂的选择对于开环聚合反应的快慢、所得产品的性能都十分关键，在同一金属的情况下，往往配体的替换和选择会表现出意料之外的催化效果，在同一配体的情况下，金属的替换也会产生不同的催化效果，因此研究新的、性能好的催化剂十分必要。
发明内容
本发明提供了一种利用含水杨醛基的铝配合物催化己内酯聚合的方法，该方法操作简单，以自行研发的含水杨醛基的铝配合物为催化剂，反应可控性好，得到的聚己内酯分子量可控、产率高。
本发明是在国家自然基金委青年项目（No 21104026）的资助下完成的，本发明技术方案如下：
本发明提供了一种结构特殊的含水杨醛基的铝配合物催化剂，该催化剂的结构式如下式（Ⅰ）所示：
Figure 595590DEST_PATH_IMAGE001
。
本发明含水杨醛基的铝配合物为配合物，通过对配体结构的选择和与金属铝的配位具有优异的性能，本发明配体结构特殊，配体中取代基的选择对于该铝配合物作为环内酯开环聚合反应催化剂的催化性能有较大影响。其中，R为氢、C1-C4的烷烃或卤素，所述卤素为氟、氯、溴或碘。进一步的，R为溴时催化活性最佳。
本发明含水杨醛基的铝配合物是由配体和三甲基铝反应得到，其制备方法包括以下步骤：将配体A加入有机溶剂中，在-10～0 oC下加入三甲基铝，加完后使反应温度自然升至室温，然后将温度升至30～110oC进行反应，反应后真空抽干溶剂、洗涤、过滤，得式Ⅰ所述的含水杨醛基的铝配合物。
配体A与三甲基铝反应的方程式如下，其中配体A的结构式如下式所示，R为氢、C1-C4的烷烃或卤素，所述卤素为氟、氯、溴、碘；R优选为溴；
Figure 615630DEST_PATH_IMAGE002
上述制备方法中，配体A的制备方法包括以下步骤：将对甲苯磺酸溶解到二甲苯中，先慢慢加入对甲苯磺酸等摩尔量的乙二胺，再加入对甲苯磺酸等摩尔量的邻苯二甲酸酐，然后加热进行回流反应，反应结束后冷却至室温，过滤，得对甲苯磺酸和邻苯二甲酸酐保护的乙二胺；将对甲苯磺酸和邻苯二甲酸酐保护的乙二胺溶解到二氯甲烷中，缓慢滴加饱和碳酸氢钠水溶液进行反应以脱去对甲苯磺酸，反应结束后分液，将所得有机相用无水硫酸镁干燥，然后旋干溶剂，得单边邻苯二甲酸酐保护的乙二胺；
将单边邻苯二甲酸酐保护的乙二胺和等摩尔量的水杨醛或其衍生物溶解在甲醇中，加热进行回流反应，反应结束后冷却、过滤，所得固体用冷甲醇洗涤、干燥，得配体A；所述水杨醛衍生物的结构式如下式B所示，其中R为氢、C1-C4的烷烃或卤素，优选为叔丁基或溴；
Figure 791396DEST_PATH_IMAGE003
。
上述制备方法中，配体A和三甲基铝发生加成反应，三甲基铝的烷基加成到化合物A中的C=O双键上，C=O双键变成C-O单键。通过核磁表征发现在δ= 1.5-2.0 附近有一组CH3的特征峰，此特征峰就是NC(O)(Ar)CH 3中CH3的特征峰。
上述制备方法中，配体A与三甲基铝的摩尔比1：1～1.3，优选1：1～1.05。
上述制备方法中，所述有机溶剂为干燥的己烷、甲苯和环己烷中的一种或两种，优选为干燥的己烷或甲苯。
上述制备方法中，有机溶剂用量为反应原料（配体A和三甲基铝）总质量的5～40倍。
上述制备方法中，反应在气体保护下进行，所述气体为惰性气体或氮气。
上述制备方法中，反应自然升到室温以后再升至30～110oC进行反应，例如30oC、40oC、50oC、60oC、70oC、80oC、90oC、100oC、110oC，优选40～60oC。在30～110oC（优选40～60oC）进行反应的时间为1～12小时，优选为3～6小时。反应后，用正己烷对沉淀进行洗涤。
本发明所述的含水杨醛基的铝配合物是制备式Ⅱ所述的化合物的中间产物，含水杨醛基的铝配合物对水比较敏感，在配体A与三甲基铝反应后的反应液中加入水充分搅拌能使铝化合物水解，经分液、收集有机相、有机相回收溶剂处理，所得剩余物经重结晶即为式Ⅱ所述的化合物。因此，制备铝化合物要在无水及质子溶剂的情况下进行。此外，以式Ⅱ所述的化合物为原料，将配体A替换为式Ⅱ所述的化合物，按照上述含水杨醛基的铝配合物的制备方法也能再得到式Ⅰ含水杨醛基的铝配合物。
Figure 1
以式Ⅱ所述的化合物制备含水杨醛基的铝配合物时，有机溶剂为干燥的己烷、甲苯和环己烷中的一种或两种，优选为己烷或甲苯。有机溶剂用量为反应原料（式Ⅱ所述的化合物和三甲基铝）总质量的5～40倍。反应结束以后用干燥己烷进行重结晶，得到纯度高的式Ⅰ含水杨醛基的铝配合物。
本发明含水杨醛基的铝配合物为配合物，配体的N、N、O、O与铝进行配位，配合物的结构和经典的环内酯催化剂（salenAl）的结构非常类似，催化效果好，具有较高的立体选择性，是一种很好的环内酯开环聚合反应的催化剂。
本发明含水杨醛基的铝配合物作为环内酯开环聚合反应的催化剂时，可以催化环己内酯的开环聚合，得到一系列的聚己内酯。本发明具体提供了一种利用该含水杨醛基的铝配合物催化己内酯聚合的方法，包括以下步骤：将含水杨醛基的铝配合物催化剂、有机溶剂、苄醇助催化剂和己内酯混合，在无水无氧和惰性气体保护下进行开环聚合反应，反应后将反应物进行处理得聚己内酯。
本发明含水杨醛基的铝配合物用作己内酯开环聚合反应的催化剂时， R为溴时催化活性最佳。
上述开环聚合反应中，己内酯与含水杨醛基的铝配合物催化剂的摩尔比为50～1500：1，例如50:1、100：1、150:1、200:1、300:1、400:1、500:1、600：1、800:1、1000:1、1200:1、1500：1。
上述开环聚合反应中，反应所用有机溶剂为甲苯或四氢呋喃，优选甲苯。
上述开环聚合反应中，醇助催化剂为苄醇。苄醇助催化剂与含水杨醛基的铝配合物催化剂的摩尔比为1～3：1。
上述开环聚合反应中，聚合反应温度为20～110℃，例如20℃、30℃、40℃、50℃、60℃、70℃、80℃、90℃、100℃、110℃。随着聚合反应温度的升高，催化剂的立体选择性有降低的趋势，催化活性有升高的趋势。
上述开环聚合反应中，聚合反应时间为1-60分钟，例如1分钟、4分钟、10分钟、30分钟、40分钟、60分钟等。
上述开环聚合反应中，反应后加入冷甲醇或乙醇纯化聚内酯，得纯化后的聚内酯。所得聚己内酯的分子量可控性高，可以在1-16万范围内调整。
本发明以自行研发的含水杨醛基的铝配合物作为催化剂进行己内酯开环聚合反应，含水杨醛基的铝配合物催化剂制备方法简单，成本低，产品收率高，催化剂结构变化多样，金属中心铝与配体的二价N，N，O，O配位，催化活性高、立体选择性高、反应速率快，得到的聚合物是苄氧基封端的聚合物，分子量分布窄，分子量可控、产率高，满足市场需求。
具体实施方式
下面通过具体实施例进一步说明本发明，但本发明并不限于此，具体保护范围见权利要求。
制备单边保护的乙二胺(a)
将0.50 g对甲苯磺酸溶解到二甲苯中，先慢慢加入对甲苯磺酸等摩尔量的乙二胺，再加入对甲苯磺酸等摩尔量的邻苯二甲酸酐，加热回流反应8h，反应结束以后冷却到室温，过滤，洗涤，干燥得到对甲苯磺酸和邻苯二甲酸酐保护的乙二胺。将对甲苯磺酸和邻苯二甲酸酐保护的乙二胺溶解到二氯甲烷中，室温慢慢滴加过量的碳酸氢钠饱和水溶液进行反应，以脱去对甲苯磺酸，反应结束后分液，用无水硫酸镁干燥，旋干溶剂，得到单边邻苯二甲酸酐保护的乙二胺0.48 g，产率87.3%。
Figure 550722DEST_PATH_IMAGE005
制备含水杨醛基的配体（A）
含水杨醛基的配体是由单边保护的乙二胺和水杨醛或其衍生物通过缩合反应得到的，下面对合成不同的配体A进行举例。
Figure 425268DEST_PATH_IMAGE006
实施例1
所合成配体结构式如上式（A），其中R为氢，反应过程为：将单边保护的乙二胺（a）0.20 g和等摩尔量的水杨醛加入10 mL甲醇中，加热回流反应12小时,反应结束以后冷却过滤并用冷的甲醇洗涤，过滤，收集并干燥称重，得0.27 g固体，产率87.1%。
对所得产品进行表征，结果如下：
1H NMR (400 MHz, CDCl3) δ 12.85 (s, 1H, OH), 8.26 (s, 1H, ArHC=N),7.80 (d, J = 5.4 Hz, 2H, Ar–H), 7.68 (d, J = 5.4Hz, 2H, Ar–H), 7.24–7.16 (m,1H, Ar–H), 7.11 (m, 1H, Ar–H), 6.97 (d, J = 8.3 Hz, 1H, Ar–H), 6.75 (td, J =7.5, 1.0 Hz, 1H, Ar–H), 4.20 (m, 2H, NCH 2), 4.10 (m, 2H, NCH 2). HRESI-MS: m/zcacld. C17H14N2O3 [M-H]-; 293.0927, found: 293.0931.
从以上表征结果可以看出，所得产品即为上式（A）中R为氢的配体。
实施例2
所合成配体结构式如上式（A），其中R为甲基，反应过程为：将单边保护的乙二胺（a）0.25 g和等摩尔量的3,5-二甲基水杨醛加入20 mL甲醇中，加热回流反应12小时,反应结束以后冷却过滤并用冷的甲醇洗涤，过滤，收集并干燥称重，得0.38 g固体，产率90.5%。
对所得产品进行表征，结果如下：
1H NMR (400 MHz, CDCl3) δ 12.61 (s, 1H, OH), 8.20 (s, 1H, ArHC=N),7.73 (d, J = 5.5 Hz, 2H, Ar–H), 7.66 (d, J = 5.4 Hz, 2H, Ar–H), 6.96 (s, 1H,Ar–H), 6.75 (s, 1H, Ar–H), 4.31– 4.28(m, 2H, NCH 2), 4.20–4.15 (m, 2H, NCH 2),2.17 (s, 3H, CH 3), 2.15 (s, 3H, CH 3)。HRESI-MS: m/z cacld. C19H18N2O3 [M-H]-;321.1238, found: 321.1236.
从以上表征结果可以看出，所得产品即为上式（A）中R为甲基的配体。
实施例3
所合成配体结构式如上式（A），其中R为溴，反应过程为：将单边保护的乙二胺（a）0.22 g和等摩尔量的3,5-二溴水杨醛加入15 mL甲醇中，加热回流反应12小时,反应结束以后冷却过滤并用冷的甲醇洗涤，过滤，收集并干燥称重，得0.46 g固体，产率88.5%。
对所得产品进行表征，结果如下：
1H NMR (400 MHz, CDCl3) δ 13.90 (s, 1H, OH), 8.19 (s, 1H, ArHC=N),7.82–7.74(m, 2H, Ar–H), 7.67–7.60 (m, 2H, Ar–H), 7.54 (s, 1H, Ar–H), 7.15 (s,1H, Ar–H), 4.30–4.27 (m, 2H, NCH 2), 4.25–4.20 (m, 2H, NCH 2)。HRESI-MS: m/zcacld. C17H12Br2N2O3 [M-H]-; 448.9136, found: 448.9138.
从以上表征结果可以看出，所得产品即为上式（A）中R为溴的配体。
实施例4
所合成配体结构式如上式（A），其中R为叔丁基，反应过程为：将单边保护的乙二胺（a）0.30 g和等摩尔量的3,5-二叔丁基水杨醛加入20 mL甲醇中，加热回流反应12小时,反应结束以后冷却过滤并用冷的甲醇洗涤，过滤，收集并干燥称重，得0.53 g固体，产率82.8%。
对所得产品进行表征，结果如下：
1H NMR (400 MHz, CDCl3) δ13.27 (s, 1H, OH), 8.23 (s, 1H, ArHC=N),7.70–7.68 (m, 2H, Ar–H) ), 7.64–7.59 (m, 2H, Ar–H), 7.30 (s, 1H, Ar–H)), 6.95(s, 2H, Ar–H)), 4.34–4.29 (m, 2H, NCH 2), 4.13–4.10 (m, 2H, NCH 2), 1.37 (s, 9H,CH3), 1.26(s, 9H, CH3)。HRESI-MS: m/z cacld. C25H30N2O3 [M-H]-; 405.2175, found:405.2173.
从以上表征结果可以看出，所得产品即为上式（A）中R为叔丁基的配体。
以配体A为原料制备铝配合物（I）
式（I）所示铝配合物由配体A和三甲基铝通过烷基消除和烷基加成反应生成，反应式如下。
Figure 506357DEST_PATH_IMAGE002
实施例5
所用配体结构式如上式（A），其中R为氢，反应过程为：在氮气气氛下,将配体A0.21 g溶于8 mL干燥甲苯中，在-10℃下加入配体A 1.0倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到100℃反应1小时,反应结束以后真空抽干溶剂，加入干燥的正己烷过滤并用干燥的正己烷洗涤，过滤，收集并干燥称重，得0.22 g固体，产率88.0%。
所得产物核磁信息如下，从核磁信息可以看出，R为氢的化合物（I）合成成功。
1H NMR (400 MHz, CDCl3) δ 8.22 (s, 1H, ArHC=N), 7.61 (d, J = 6.7 Hz,1H, Ar–H), 7.53 (d, J = 6.7 Hz, 1H, Ar–H), 7.41 (t, J = 7.1 Hz, 1H, Ar–H),7.33 (d, J = 6.3 Hz, 1H, Ar–H), 7.08 (d, J = 7.1 Hz, 1H, Ar–H), 6.76–6.62 (m,3H, Ar–H), 4.25–4.20 (m, 2H, NCH 2), 4.13–4.08 (m, 2H, NCH 2), 1.65 (s, 3H,CH 3),–0.50(s, 3H, AlCH3). Anal. Calcd for C19H19AlN2O3: C 65.14, H 5.47, N 8.00.Found: C 65.16, H 5.49, N 8.05.
实施例6
所用配体结构式如上式（A），其中R为甲基，反应过程为：在氮气氛下,将配体A0.41 g溶于12 mL干燥环己烷中，在0℃下加入配体A 1.05倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热反应温度到60℃反应4小时, 反应结束以后真空抽干溶剂，加入干燥的正己烷过滤并用干燥的正己烷洗涤，过滤，收集并干燥称重，得到0.39 g固体，产率81.2%。
所得产物核磁信息如下，从核磁信息可以看出，R为甲基的化合物（I）合成成功。
1H NMR (400 MHz, CDCl3) δ 8.17 (s, 1H, ArHC=N), 7.68 (s, 1H, Ar–H),7.61–7.57 (m, 2H, Ar–H), 7.13 (s, 1H, Ar–H), 6.30 (s, 1H, Ar–H), 4.32 (m, 2H,NCH2), 4.13 (m, 2H, NCH2), 2.14–2.10 (m, 2H, CH2CH 2), 2.10 (s, 3H, ArCH 3),2.08 (s, 3H, ArCH 3), 1.67 (s, 3H, CCH 3), –0.50 (s, 3H, AlCH 3). Anal. Calcd forC21H23AlN2O3: C 66.66, H 6.13, N 7.40. Found: C 66.61, H 6.18, N 7.45.
实施例7
所用配体结构式如上式（A），其中R为溴，反应过程为：在氮气氛下,将配体A 0.24g溶于10 mL干燥甲苯中，在-5℃下加入配体A 1.1倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到50℃反应5小时, 反应结束以后真空抽干溶剂，加入干燥的正己烷过滤并用干燥的正己烷洗涤，过滤，收集并干燥称重，得到0.24 g固体,产率88.9%。
所得产品的核磁信息如下所示，由此可以看出R为溴的化合物（I）合成成功。
1H NMR (400 MHz, CDCl3) δ 8.21 (s, 1H, ArHC=N), 7.84 (d, J = 6.7 Hz,1H, Ar–H), 7.66 (s, 2H, Ar–H), 7.64–7.55 (m, 2H, Ar–H), 7.40–7.33 (m, 1H, Ar–H), 4.27 (m, 2H, NCH 2), 4.10–4.06 (m, 2H, NCH 2), 1.67 (s, 1H, CCH 3), –0.50 (s,3H, AlCH 3). Anal. Calcd for C19H17AlBr2N2O3: C 44.91, H 3.37, N 5.51. Found: C44.93, H 3.41, N 5.55.
实施例8
所用配体结构式如上式（A），其中R为叔丁基，反应过程为：在氮气氛下,将配体A0.23 g溶于10 mL干燥正己烷中，在-10℃下加入配体A 1.0倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到40℃反应12小时,过滤并用干燥的正己烷洗滤饼，收集并干燥称重，得0.24 g固体, 产率92.3%.
所得产物的核磁信息如下所示，由此可以看出R为叔丁基的化合物（I）合成成功。
1H NMR (400 MHz, CDCl3) δ 8.17 (s, 1H, ArHC=N), 7.80 (d, J = 6.7 Hz,1H, Ar–H), 7.67 (s, 2H, Ar–H), 7.60–7.53 (m, 2H, Ar–H), 7.41–7.32 (m, 1H, Ar–H), 4.33–4.29 (m, 2H, NCH 2), 3.93–3.86 (m, 2H, NCH 2), 1.66 (s, 3H, CCH 3), 1.31(s, 9H, CH3), 1.24(s, 9H, CH3), –0.52 (s, 3H, AlCH 3). Anal. Calcd forC27H35AlN2O3: C 70.11, H 7.63, N 6.06. Found: C 70.12, H 7.65, N 6.12.
以配体Ⅱ为原料制备铝配合物（I）
实施例9
R为氢的配体Ⅱ合成：在氮气气氛下,将配体A （R为氢）0.30 g溶于10 mL干燥甲苯中，在-10℃下加入配体A 1.0倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到60℃反应4小时,反应结束以后，加入55微升水停止反应，分液收集有机相，无水硫酸钠干燥，旋干溶剂，得粗产品，将粗产品经甲醇重结晶，得纯产品0.27 g, 产率84.4 %。
对所得产品进行表征，结果如下：
1H NMR (400 MHz, CDCl3) δ12.85 (s, 1H, OH), 8.31 (s, 1H, CH=N), 7.61(d, J = 7.5 Hz, 1H, Ar–H), 7.55–7.47 (m, 4H, Ar–H), 7.15 (d, J = 7.4 Hz, 1H,Ar–H), 6.88 (d, J = 8.2 Hz, 1H, Ar–H), 6.65 (t, J = 7.4 Hz, 1H, Ar–H), 4.41–4.32 (m, 2H, NCH 2), 4.16–4.10 (m, 2H, NCH), 1.61 (s, 3H, CH3).
HRESI-MS: m/z cacld. C18H18N2O3 [M-H]-; 309.1238, found: 309.1236.
从以上表征结果可以看出，所得产品即为上式（Ⅱ）中R为氢的配体。
所用配体结构式如上式（II），其中R为氢，反应过程为：在氮气气氛下,将配体II0.30 g溶于10 mL干燥环己烷中，在-10℃下加入配体II 1.2倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到40℃反应6小时,反应结束以后过滤并用干燥的正己烷洗涤，过滤，收集并干燥称重，得0.29 g固体，产率85.3%。产物结构式如式Ⅰ所示， R为氢。
实施例10
R为甲基的配体Ⅱ合成：在氮气氛下,将配体A（R为甲基） 0.40 g溶于10 mL干燥环己烷中，在0℃下加入配体A 1.05倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热反应温度到40℃反应6小时，反应后加入67微升水停止反应，分液收集有机相，无水硫酸钠干燥，旋干溶剂，得粗产品，将粗产品经甲醇重结晶，得纯产品0.36 g, 产率85.7%。
对所得产品进行表征，结果如下：
1H NMR (400 MHz, CDCl3) δ13.01 (s, 1H，OH), 8.27 (s, 1H, CH=N), 7.64(d, J = 7.4 Hz, 1H, Ar–H), 7.55–7.44 (m, 3H, Ar–H), 6.98–6.88 (m, 1H, Ar–H),6.81–6.72 (m, 1H, Ar–H), 4.38–4.31 (m, 2H, NCH2), 4.18–4.09 (m, 2H, NCH2),2.21 (s, 6H, ArCH3), 1.61 (s, 3H, CH3). HRESI-MS: m/z cacld. C20H22N2O3 [M-H]-;337.1553, found: 337.1556.
从以上表征结果可以看出，所得产品即为上式（Ⅱ）中R为甲基的配体。
所用配体结构式如上式（II），其中R为甲基，反应过程为：在氮气氛下,将配体II0.25 g溶于10 mL干燥甲苯中，在0℃下加入配体II 1.1倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热反应温度到110℃反应1小时, 反应结束以后真空抽干溶剂，加入干燥的正己烷过滤并用干燥的正己烷洗涤，过滤，收集并干燥称重，得到0.20 g固体，产率71.4%。产物结构式如式Ⅰ所示， R为甲基。
实施例11
R为溴的配体Ⅱ合成：在氮气氛下,将配体A （R为溴）0.30 g溶于10 mL干燥甲苯中，在-5℃下加入配体A 1.1倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到110℃反应1小时, 反应结束以后加入36微升水停止反应，分液收集有机相，无水硫酸钠干燥，旋干溶剂，得粗产品，将粗产品经乙醇重结晶，得纯产品0.26 g, 产率83.9%。
对所得产品进行表征，结果如下：
1H NMR (400 MHz, CDCl3) δ12.56 (s, 1H，OH), 8.27 (s, 1H, CH=N), 7.63–7.58 (m, 2H, Ar–H), 7.41–7.30 (m, 2H, Ar–H), 7.16 (d, J = 7.2 Hz, 1H, Ar–H),7.12 (d, J = 7.2 Hz, 1H, Ar–H), 4.45–4.32 (m, 2H, NCH 2), 4.23–4.14 (m, 2H,NCH 2), 1.60 (s, 3H, CH3).
HRESI-MS: m/z cacld. C18H16Br2N2O3 [M-H]-; 464.9448, found: 464.9452.
从以上表征结果可以看出，所得产品即为上式（Ⅱ）中R为溴的配体。
所用配体结构式如上式（II），其中R为溴，反应过程为：在氮气氛下,将配体II0.45 g溶于15 mL干燥己烷中，在-5℃下加入配体II 1.0倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到60℃反应3小时, 反应结束以后过滤并用干燥的正己烷洗涤，过滤，收集并干燥称重，得到0.41 g固体,产率83.7%。产物结构式如式Ⅰ所示， R为溴。
实施例12
R为叔丁基的配体Ⅱ合成：在氮气氛下,将配体A （R为叔丁基）0.20 g溶于8 mL干燥正己烷中，在-5℃下加入配体A 1.3倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到30℃反应8小时,反应后加入27微升水停止反应，分液收集有机相，无水硫酸钠干燥，旋干溶剂，得粗产品，将粗产品经甲醇重结晶，得纯产品0.17 g, 产率81.0%。
对所得产品进行表征，结果如下：
1H NMR (300 MHz, CDCl3) δ13.02 (s, 1H，OH), 8.24 (s, 1H, CH=N), 7.76–7.65 (m, 1H, Ar–H), 7.63–7.52 (m, 3H, Ar–H), 7.50–7.42(m, 1H, Ar–H), 7.40 (d,J = 7.2 Hz, 1H, Ar–H), 7.18 (d, J = 7.0 Hz, 1H, Ar–H), 7.08–7.00 (m, 1H, Ar–H), 4.35–4.21 (m, 2H, NCH 2), 4.14–4.06 (m, 2H, NCH 2), 1.62(s, 3H, CH3), 1.38(s, 9H, CH3), 1.24 (s, 9H, CH3).
HRESI-MS: m/z cacld. C26H34N2O3 [M-H]-; 421.2492, found: 421.2487.
从以上表征结果可以看出，所得产品即为上式（Ⅱ）中R为叔丁基的配体。
所用配体结构式如上式（II），其中R为叔丁基，反应过程为：在氮气氛下,将配体II0.40 g溶于12 mL干燥甲苯中，在0℃下加入配体II 1.1倍摩尔量的三甲基铝，待反应温度自然升到室温后，加热到60℃反应2小时, 反应结束以后过滤并用干燥的正己烷洗涤，过滤，收集并干燥称重，得到0.40 g固体,产率90.9%。产物结构式如式Ⅰ所示， R为叔丁基。
制备聚ε-己内酯
实施例13
在无水无氧和惰性气体保护下进行反应，首先在用高纯氮气洗气烘烤后的安瓶中顺序加入100 µmol催化剂（式Ⅰ所示铝配合物, R为氢）、100 µmol 苄醇、10 mL甲苯以及10mmol的己内酯，然后置于110oC的油浴中，反应5分钟后加入少量水终止反应，用乙醇沉淀、洗涤数次，室温下真空干燥，得1.11 g产品，收率97.4%，分子量2.4万。
实施例14
按照实施例13的方法制备聚己内酯，不同的是：所用的催化剂为式Ⅰ所示铝配合物, R为甲基。反应6分钟以后所得产品的质量为1.10 g，产率为96.5%，分子量为2.0万。
实施例15
按照实施例13的方法制备聚己内酯，不同的是：所用的催化剂为式Ⅰ所示铝配合物, R为溴。反应1.5分钟以后所得产品的质量为1.12 g，产率为98.2%，分子量为2.2万。
实施例16
按照实施例13的方法制备聚己内酯，不同的是：所用的催化剂为式Ⅰ所示铝配合物, R为叔丁基。反应7分钟以后所得产品的质量为1.10 g，产率为96.5%，分子量为2.3万。
实施例17
在无水无氧和惰性气体保护下进行反应，首先在用高纯氮气洗气烘烤后的安瓶中顺序加入100 µmol催化剂（式Ⅰ所示铝配合物, R为溴）、100 µmol苄醇、10 mL甲苯以及10mmol的己内酯，然后分别在20oC、40oC、60oC、80oC和100oC下反应，反应结束后加入少量水终止反应，用甲醇沉淀、洗涤数次，室温下真空干燥。
其中，在20℃反应35分钟，得1.10 g产品，产率96.5%，分子量2.0万。
在40℃反应18分钟，得1.10 g产品，产率96.5%，分子量2.3万。
在60℃反应12分钟，得1.11 g产品，产率97.4%，分子量2.1万。
在80℃反应9分钟，得1.11 g产品，产率97.4%，分子量2.2万。
在100℃反应3分钟，得1.12 g产品，产率98.2%，分子量2.4万。
实施例18
在无水无氧和惰性气体保护下进行反应，首先在用高纯氮气洗气烘烤后的安瓶中顺序加入10 µmol催化剂（式Ⅰ所示铝配合物, R为氢）、30 µmol苄醇、10 mL四氢呋喃以及5mmol的ε-己内酯，然后30oC反应50分钟后加入少量水终止反应，用乙醇沉淀、洗涤数次，室温下真空干燥，得0.54 g产品，收率94.7%，分子量5.8万。
实施例19
在无水无氧和惰性气体保护下进行反应，首先在用高纯氮气洗气烘烤后的安瓶中顺序加入10 µmol催化剂（式Ⅰ所示铝配合物, R为甲基）、30 µmol 苄醇、10 mL甲苯以及10mmol的ε-己内酯，然后50oC反应20分钟后加入少量水终止反应，用乙醇沉淀、洗涤数次，室温下真空干燥，得1.12 g产品，收率98.2%，分子量7.4万。
实施例20
在无水无氧和惰性气体保护下进行反应，首先在用高纯氮气洗气烘烤后的安瓶中顺序加入10 µmol催化剂（式Ⅰ所示铝配合物, R为叔丁基）、20 µmol 苄醇、15 mL甲苯以及15 mmol的ε-己内酯，然后置于90oC的油浴中，反应9分钟后加入少量水终止反应，用乙醇沉淀、洗涤数次，室温下真空干燥，得1.63 g产品，收率95.3%，分子量15.8万。
实施例21
在无水无氧和惰性气体保护下进行反应，首先在用高纯氮气洗气烘烤后的安瓶中顺序加入100 µmol催化剂（式Ⅰ所示铝配合物, R为氢）、100 µmol 苄醇、10 mL甲苯以及5mmol的ε-己内酯，然后置于70oC的油浴中，反应11分钟后加入少量水终止反应，用乙醇沉淀、洗涤数次，室温下真空干燥，得0.55 g产品，收率96.5%，分子量1.0万。
对比例1
镍催化剂的制备：所用配体结构式如上式（II），R为溴，反应过程为：将配体0.40 g溶于20 mL无水乙醇中，室温下加入1.0倍配体摩尔量的醋酸镍，加热回流反应12小时,反应结束以后真空浓缩溶剂,加入二氯甲烷析出固体，过滤并用己烷洗涤，干燥得镍催化剂，其结构式如下所示。
Figure 715621DEST_PATH_IMAGE007
按照实施例13的方法制备聚己内酯，不同的是：所用的催化剂为上述镍催化剂。反应24小时后加入少量水终止反应，用甲醇沉淀、洗涤数次，室温下真空干燥，得0.45 g，产率39.5 %，分子量1.1万。该镍催化剂对己内酯的聚合活性太低，没有价值。
对比例2
铝催化剂的制备：所用配体结构式如下式（LH2），反应过程为：在无水无氧和惰性气体保护下，将配体0.20 g溶于10 mL甲苯中，-5℃下加入加入1.0倍配体摩尔量的三甲基铝，缓慢升至室温后加热到80℃反应12小时,反应结束以后真空浓缩溶剂,加入干燥己烷析出固体，过滤并用己烷洗涤，干燥得铝催化剂，其结构式如下所示LAlMe。
Figure 288161DEST_PATH_IMAGE008
按照实施例13的方法制备聚己内酯，不同的是：所用的催化剂为该铝催化剂。反应15分钟后加入少量水终止反应，用乙醇沉淀、洗涤数次，室温下真空干燥，得0.94克，收率82.5%，分子量1.3万。
对比例3
按照实施例13的方法制备聚己内酯，不同的是：所用的催化剂为专利201410609375.8中实施例10所用的催化剂。反应15分钟后加入少量水终止反应，用乙醇沉淀、洗涤数次，室温下真空干燥，得0.98克，收率86.0%，分子量1.5万。
对比例4
在氮气氛下,将配体A （R为叔丁基）0.20 g溶于8 mL干燥正己烷中，在-5℃下加入配体A 1.3倍摩尔量的三异丙基铝，待反应温度自然升到室温后，加热到30℃反应24小时,反应后加入27微升水停止反应，分液收集有机相，无水硫酸钠干燥，旋干溶剂，发现得到化合物没有发生变化（异丙基没有进行C=O加成反应）。三异丙基铝无法进行加成反应。
对比例5
按照实施例13的方法制备聚己内酯，不同的是：所用的催化剂为式Ⅰ所示铝配合物, R为甲氧基。反应12min以后所得产品的质量为0.97 g，产率为85.1%，分子量为2.1万。
对比例6
将对甲苯磺酸溶解到二甲苯中，先慢慢加入对甲苯磺酸等摩尔量的1，3-丙二胺，再加入对甲苯磺酸等摩尔量的邻苯二甲酸酐，加热回流反应，反应结束以后冷却到室温将固体过滤，洗涤，干燥，得到对甲苯磺酸和邻苯二甲酸酐保护的1，3-丙二胺。将对甲苯磺酸和邻苯二甲酸酐保护的1，3-丙二胺溶解到二氯甲烷中，室温下慢慢滴加过量的碳酸氢钠饱和水溶液进行反应，以脱去对甲苯磺酸，反应结束后分液，用无水硫酸镁干燥，旋干溶剂，得到单边邻苯二甲酸酐保护的1，3-丙二胺。单边邻苯二甲酸酐保护的丙二胺和等摩尔量的3，5-二溴水杨醛在甲醇中加热回流，反应结束以后放到冰箱中冷却，析出固体，过滤，用冷的甲醇洗涤，干燥，得到化合物LD。
铝催化剂的制备：在氮气氛下,将下式化合物LD 0.20 g溶于10 mL干燥甲苯中，在-10℃下加入1.0倍化合物LD摩尔量的三甲基铝，待反应温度自然升到室温后，加热到110℃反应1小时, 反应结束以后真空抽干溶剂，加入干燥的正己烷洗涤、过滤、干燥，得到0.18g固体,产率81.8%,该铝化合物经水解以后做质谱表征发现该类配体只能单边发生加成反应得到LDAlMe2（HRESI-MS: m/z cacld. C18H14Br2N2O3 [M-H]-; 462.9294, found:462.9292）。
按照实施例13的方法制备聚己内酯，不同的是：所用的催化剂为该铝催化剂。反应后所得产品的质量为0.57 g，产率为50.0%，分子量为1.6万。
Figure 266481DEST_PATH_IMAGE009

Claims (14)

1.一种利用含水杨醛基的铝配合物催化己内酯聚合的方法，其特征是包括以下步骤：将催化剂、有机溶剂、苄醇助催化剂和己内酯混合，在无水无氧和惰性气体保护下进行开环聚合反应，反应后将反应物进行处理得聚己内酯；所述催化剂为含水杨醛基的铝配合物，其结构式如下式Ⅰ所示，其中，R为氢、C1-C4的烷基或卤素；
Figure 181845DEST_PATH_IMAGE002
。
2.根据权利要求1所述的方法，其特征是：R为溴。
3.根据权利要求1所述的方法，其特征是：催化剂制备方法为：将配体A或配体Ⅱ加入有机溶剂中，在-10～0 oC下加入三甲基铝，加完后使反应温度自然升至室温，然后将温度升至30～110oC进行反应，反应后真空抽干溶剂、洗涤、过滤，得式Ⅰ所述的含水杨醛基的铝配合物；配体A和配体Ⅱ结构式如下，其中，R均为氢、C1-C4的烷基或卤素；
Figure 909630DEST_PATH_IMAGE004
。
4.根据权利要求3所述的方法，其特征是：配体A和配体Ⅱ中，R均为溴。
5.根据权利要求3所述的方法，其特征是：催化剂制备过程中，配体A或配体Ⅱ与三甲基铝的摩尔比为1：1～1.3。
6.根据权利要求5所述的方法，其特征是：催化剂制备过程中，配体A或配体Ⅱ与三甲基铝的摩尔比为1：1～1.05。
7.根据权利要求3所述的方法，其特征是：催化剂制备过程中，所述有机溶剂为干燥的己烷、甲苯和环己烷中的一种或两种；有机溶剂用量为反应原料总质量的5～40倍。
8.根据权利要求3所述的方法，其特征是：催化剂制备过程中，升到室温以后再将温度升至30～110oC反应1～12小时。
9.根据权利要求8所述的方法，其特征是：催化剂制备过程中，升到室温以后再将温度升至40～60oC反应3～6小时。
10.根据权利要求3所述的方法，其特征是：催化剂制备过程中，反应在惰性气体保护下进行。
11.根据权利要求1-10中任一项所述的方法，其特征是：开环聚合反应时，己内酯与催化剂的摩尔比为50～1500：1。
12.根据权利要求1-10中任一项所述的方法，其特征是：开环聚合反应时，卞醇助催化剂与催化剂的摩尔比为1～3：1。
13.根据权利要求1-10中任一项所述的方法，其特征是：开环聚合反应时，所述有机溶剂为甲苯或四氢呋喃。
14.根据权利要求1-10中任一项所述的方法，其特征是：开环聚合反应时，反应温度为20～110℃，反应时间为1-60分钟。
CN201711314930.4A 2017-12-12 2017-12-12 利用含水杨醛基的铝配合物催化己内酯聚合的方法 Active CN108239263B (zh)