CN108238754A - Wall face finishing mucilage - Google Patents
Wall face finishing mucilage Download PDFInfo
- Publication number
- CN108238754A CN108238754A CN201611214771.6A CN201611214771A CN108238754A CN 108238754 A CN108238754 A CN 108238754A CN 201611214771 A CN201611214771 A CN 201611214771A CN 108238754 A CN108238754 A CN 108238754A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- powder
- wall face
- finishing mucilage
- face finishing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wall face finishing mucilage, the component including mass parts is：The dispersed latex powder of 16 20 mass parts, the Portland cement of 200 240 mass parts, the coal fly ash hollow micro bead of 40 50 mass parts, the glass fibre of 46 mass parts, the heat preservation powder of 15 30 mass parts, the fire prevention powder of 20 35 mass parts, the hard calcium carbonate of 40 80 mass parts, the metal powder of 10 20 mass parts and 150 200 mass parts water.Coal fly ash hollow micro bead and heat preservation powder are increased in the present invention, it can not only keep suitable with using the intensity of neat cement, the rubber cement intensity that even higher than neat cement makes, so as to save the usage amount of cement, processing cost is reduced, while can also effectively improve compression strength and adhesion strength, it may have the performance of cracking resistance intensity height and good flame resistance, fire line is strong, applied widely.
Description
Technical field
The invention belongs to wall face insulated fire technical fields, and in particular to a kind of wall face finishing mucilage.
Background technology
With the maturation of China's Building technology, various construction materials are quickly grown, in order to ensure wall on wallboard wall face
The heat insulating ability and fire protecting performance of plate, generally all can be in exterior wall using float coat, and the float coat of traditional technology is predominantly by polymer
Rubber cement, fire prevention and guarantor's high-temperature behavior are relatively limited, there are certain hidden danger safe to use, while for the grade for ensureing rubber cement
It needs using a large amount of cement, so as to which the cement waste compared with large resource can be caused, so applicability and practicability are restricted.
Invention content
The wall face finishing mucilage big and strong fire line the object of the present invention is to provide a kind of adhesion strength.
The technical solution for realizing the object of the invention is a kind of wall face finishing mucilage, and the component including mass parts is：16-
The dispersed latex powder of 20 mass parts, the Portland cement of 200-240 mass parts, the fly ash hollow of 40-50 mass parts are micro-
Pearl, the glass fibre of 4-6 mass parts, the heat preservation powder of 15-30 mass parts, the fire prevention powder of 20-35 mass parts, 40-80 mass
The hard calcium carbonate, the metal powder of 10-20 mass parts and the water of 150-200 mass parts of part.
Or the component including mass parts is：The normal silicate water of the dispersed latex powder of 18 mass parts, 220 mass parts
Mud, the coal fly ash hollow micro bead of 45 mass parts, the glass fibre of 5 mass parts, the heat preservation powder of 26 mass parts, 30 mass parts it is anti-
Fiery powder, the hard calcium carbonate of 50-60 mass parts, the metal powder of 15 mass parts and 180 mass parts water.
Further include the FDN water-reducing agents of 25-30 mass parts.
A diameter of 2-5um of the coal fly ash hollow micro bead.
The heat preservation powder is alumina silicate powder.
The length of the glass fibre is 10-15mm.
The fire prevention powder is polyvinyl chloride powder body.
The present invention has positive effect：Coal fly ash hollow micro bead and heat preservation powder are increased in the present invention, due to fine coal
Grey cenosphere can replace the usage amount of part of cement, can not only keep suitable or even high with using the intensity of neat cement
In the rubber cement intensity that neat cement makes, so as to save the usage amount of cement, processing cost is reduced, while can also effectively carry
High compressive strength and adhesion strength, it may have the performance of cracking resistance intensity height and good flame resistance, fire line is strong, applied widely.
Specific embodiment
A kind of wall face finishing mucilage, the component including mass parts are：The dispersed latex powder of 16-20 mass parts, 200-
The Portland cement of 240 mass parts, the coal fly ash hollow micro bead of 40-50 mass parts, 4-6 mass parts glass fibre, 15-
The heat preservation powder of 30 mass parts, the fire prevention powder of 20-35 mass parts, the hard calcium carbonate of 40-80 mass parts, 10-20 mass parts
Metal powder and 150-200 mass parts water, when in use by being sufficiently mixed and stir evenly.Metal powder in the present embodiment
End is iron powder.
Coal ash cenosphere be by flyash by impurity elimination, sedimentation is selected obtains, sedimentation is selected including by the powder after impurity elimination
Coal ash is put into gas medium, since the relative density of coal fly ash hollow micro bead is smaller, is completed according to its terminal velocity degree selected.
Further include the FDN water-reducing agents of 25-30 mass parts.
A diameter of 2-5um of the coal fly ash hollow micro bead.
The heat preservation powder is alumina silicate powder.
The length of the glass fibre is 10-15mm.
The fire prevention powder is polyvinyl chloride powder body.
(embodiment 2)
Component including mass parts is：The dispersed latex powder of 18 mass parts, the Portland cement of 220 mass parts, 45
The coal fly ash hollow micro bead of mass parts, the glass fibre of 5 mass parts, 26 mass parts heat preservation powder, 30 mass parts fire prevention powder
The water at end, the hard calcium carbonate of 50-60 mass parts, the metal powder of 15 mass parts and 180 mass parts, when in use by abundant
It is mixed and stirred for uniformly.
Coal fly ash hollow micro bead and heat preservation powder are increased in the present invention, since coal fly ash hollow micro bead can replace part
The usage amount of cement can not only keep the rubber cement intensity suitable with using the intensity of neat cement, even higher than neat cement makes,
So as to save the usage amount of cement, processing cost is reduced, while can also effectively improve compression strength and adhesion strength,
High and good flame resistance the performance with cracking resistance intensity, fire line is strong, applied widely.
Obviously, the above embodiment of the present invention be only to clearly illustrate example of the present invention, and not be pair
The restriction of embodiments of the present invention.For those of ordinary skill in the art, may be used also on the basis of the above description
To make other variations or changes in different ways.There is no necessity and possibility to exhaust all the enbodiments.And these
The obvious changes or variations that the connotation for belonging to of the invention is extended out still fall within protection scope of the present invention.
Claims (7)
1. a kind of wall face finishing mucilage, it is characterised in that：Component including mass parts is：The dispersion breast of 16-20 mass parts
Rubber powder, the Portland cement of 200-240 mass parts, the coal fly ash hollow micro bead of 40-50 mass parts, 4-6 mass parts glass
Glass fiber, 15-30 mass parts heat preservation powder, 20-35 mass parts fire prevention powder, 40-80 mass parts hard calcium carbonate,
The metal powder of 10-20 mass parts and the water of 150-200 mass parts.
2. wall face finishing mucilage according to claim 1, it is characterised in that：Component including mass parts is：18 matter
Measure the dispersed latex powder of part, the Portland cement of 220 mass parts, the coal fly ash hollow micro beads of 45 mass parts, 5 mass parts
Glass fibre, the heat preservation powder of 26 mass parts, the fire prevention powder of 30 mass parts, the hard calcium carbonate of 50-60 mass parts, 15 mass
The metal powder of part and the water of 180 mass parts.
3. the wall face finishing mucilage according to claim 1 or claim 2, it is characterised in that：Further include 25-30 matter
Measure the FDN water-reducing agents of part.
4. wall face finishing mucilage according to claim 3, it is characterised in that：The diameter of the coal fly ash hollow micro bead
For 2-5um.
5. wall face finishing mucilage according to claim 4, it is characterised in that：The heat preservation powder is aluminium silicate powder
End.
6. wall face finishing mucilage according to claim 5, it is characterised in that：The length of the glass fibre is 10-
15mm。
7. wall face finishing mucilage according to claim 6, it is characterised in that：The fire prevention powder is polyvinyl chloride powder
Opisthosoma.