CN108221154A - A kind of method of knitted glove - Google Patents
A kind of method of knitted glove Download PDFInfo
- Publication number
- CN108221154A CN108221154A CN201711195591.2A CN201711195591A CN108221154A CN 108221154 A CN108221154 A CN 108221154A CN 201711195591 A CN201711195591 A CN 201711195591A CN 108221154 A CN108221154 A CN 108221154A
- Authority
- CN
- China
- Prior art keywords
- cotton thread
- coating cotton
- convolution number
- sth
- nylon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of methods of knitted glove, include the following steps：The first coating cotton thread and the second coating cotton thread are prepared respectively；By first coating cotton thread and the second coating cotton thread circular machine knitting into gloves.Compared with prior art, gloves of the invention have the advantages that：4 grades of European Union EN388 standards wear-resisting property, 5 grades of anti-cutting performance, 4 grades of tear resistance, penetration-resistant can be reached can be 4 grades, can reach 5 grades of U.S.'s ansi standard anti-cutting performance；It is of low cost, it is suitable for large-scale promotion.
Description
Technical field
The present invention relates to a kind of methods of knitted glove, belong to the knitting skill field of gloves.
Background technology
Safety protection glove is frequently used in complicated work situation or in dangerous sports, can
Play the role of protecting labourer or sportsman's hand.Therefore, safety protection glove has been requested to preferable resistance to when in use
Grind performance and anti-cutting performance, but in the prior art, influenced by thread material and weaving method, safety protection glove it is wear-resisting
Property, anti-cutting, tear resistance and penetration-resistant are insufficient.
Invention content
For the defects in the prior art, the object of the present invention is to provide a kind of methods of knitted glove.
The present invention is achieved by the following technical solutions：
A kind of method of knitted glove, includes the following steps：
The first coating cotton thread and the second coating cotton thread are prepared respectively；
By first coating cotton thread and the second coating cotton thread circular machine knitting into gloves；
Wherein, first coating cotton thread is made of polyethylene and spandex；Second coating cotton thread is by interior packet nylon or washs
Synthetic fibre, outsourcing nylon and glass fibre composition.
The weaving method of the gloves further includes the braiding of gloves threaded portion, and threaded portion need to mix rubber latex thread in braiding.
Preferably, the preparation method of first coating cotton thread is：
Using the spandex of 67-73D as the first core wire, first core wire is wrapped with the 194-206D polyethylenes after reeling
Cover, the first coating cotton thread be made, the twist is 165-225 sth. made by twisting during cladding, and twist direction is twisted with the fingers for Z or S, it is described made from the first wrap yarn
The curling coefficient of line is 96.8.
Preferably, the mass fraction of the polyethylene and spandex be respectively 80.11~90.11% and 9.89~
19.89%.
Preferably, the preparation method of second coating cotton thread is：
S1：Using the glass fibre of 97-103D as the second core wire, with packet nylon in the 67-73D after reeling to first core
Line is coated, and the second coating cotton thread semi-finished product are made, and the twist is 544-736 sth. made by twisting during cladding, and twist direction is Z sth. made by twisting；
S2：The second coating cotton thread semi-finished product are coated with the 67-73D outsourcings nylon after reeling, are made second
Coating cotton thread, the twist is 493-667 sth. made by twisting during cladding, and twist direction is S sth. made by twisting, it is described made from the curling coefficient of the second coating cotton thread be
96.8 Lapie 2.2-2.8.
Preferably, the mass fraction of the glass fibre, interior packet nylon and outsourcing nylon be respectively 36.66~
46.66%th, 24.17~34.17% and 24.17~34.17%.
Preferably, using the glove knitting machine of 13 needles.
Preferably, it is with technical parameter of the braider of 13 needle when weaving 9 yards of gloves：
Grammes per square metre is determined as 710~730g, lower captain's degree is 24~25cm；
The convolution number for controlling little finger of toe is 56, and nameless convolution number is 76, and the convolution number of middle finger is 82, the convolution number of forefinger
It is 72, the convolution number of thumb is 56, and the convolution number of four fingers and palms is 32, and the convolution number of five fingers and palms is 44, the convolution number of threaded portion
It is 66.
Meanwhile when carrying out the braiding of 6~13 yards of gloves with the braider, the size of gloves often increases or decreases 1 yard, gram
50g is increased or decreased again, and lower captain's degree increases or decreases 1cm, and convolution number increases or decreases 2 units.
Compared with prior art, gloves of the invention have the advantages that：
1st, 4 grades of European Union EN388 standards wear-resisting property, 5 grades of anti-cutting performance, 4 grades of tear resistance, penetration-resistant can be reached
Can be 4 grades, 5 grades of U.S.'s ansi standard anti-cutting performance can be reached；
2nd, it is of low cost, it is suitable for large-scale promotion.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail.Following embodiment will be helpful to the technology of this field
Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill to this field
For personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.These belong to the present invention
Protection domain.
A kind of method of knitted glove, includes the following steps：
The first coating cotton thread and the second coating cotton thread are prepared respectively；
By first coating cotton thread and the second coating cotton thread circular machine knitting into gloves；
Wherein, first coating cotton thread is made of polyethylene and spandex；Second coating cotton thread is by interior packet nylon, outsourcing
Nylon and glass fibre composition.
The weaving method of the gloves further includes the braiding of gloves threaded portion, and threaded portion need to mix rubber latex thread in braiding.
Preferably, the preparation method of first coating cotton thread is：
Using the spandex of 70D as the first core wire, first core wire is coated with the 200D polyethylenes after reeling, is made the
One coating cotton thread, the twist is 195 sth. made by twisting during cladding, and twist direction is twisted with the fingers for Z, it is described made from the curling coefficient of the first coating cotton thread be
96.8。
Preferably, the mass fraction of the polyethylene and spandex be respectively 80.11~90.11% and 9.89~
19.89%.
Preferably, the preparation method of second coating cotton thread is：
S1：Using the glass fibre of 100D as the second core wire, first core wire is carried out with packet nylon in the 70D after reeling
The second coating cotton thread semi-finished product are made in cladding, and the twist is 640 sth. made by twisting during cladding, and twist direction is Z sth. made by twisting；
S2：The second coating cotton thread semi-finished product are coated with the 70D outsourcings nylon after reeling, the second cladding is made
Yarn, the twist is 580 sth. made by twisting during cladding, and twist direction is twisted with the fingers for S, and the curling coefficient of second coating cotton thread obtained is 96.8.
Preferably, the mass fraction of the glass fibre, interior packet nylon and outsourcing nylon be respectively 36.66~
46.66%th, 24.17~34.17% and 24.17~34.17%.
Preferably, using 10 needles or the braider of 13 needles.
Preferably, it is with technical parameter of the braider of 13 needle when weaving 9 yards of gloves：
Grammes per square metre is determined as 710~730g, lower captain's degree is 24~25cm；
The convolution number for controlling little finger of toe is 56, and nameless convolution number is 76, and the convolution number of middle finger is 82, the convolution number of forefinger
It is 72, the convolution number of thumb is 56, and the convolution number of four fingers and palms is 32, and the convolution number of five fingers and palms is 44, the convolution number of threaded portion
It is 66.
Meanwhile when carrying out the braiding of 6~13 yards of gloves with the braider, the size of gloves often increases or decreases 1 yard, gram
50g is increased or decreased again, and lower captain's degree increases or decreases 1cm, and convolution number increases or decreases 2 units.
Embodiment 1
A kind of method of knitted glove that the present embodiment is related to, includes the following steps：
First, the first coating cotton thread and the second coating cotton thread are prepared respectively；
The preparation method of first coating cotton thread is：
Using the spandex of 70D as the first core wire, first core wire is coated with the 200D polyethylenes after reeling, is made the
One coating cotton thread, the twist is 195 sth. made by twisting during cladding, and twist direction is twisted with the fingers for Z, it is described made from the curling coefficient of the first coating cotton thread be
96.8, the mass fraction of the polyethylene and spandex is respectively 80.11 and 19.89%.
The preparation method of second coating cotton thread is：
S1：Using the glass fibre of 100D as the second core wire, first core wire is carried out with packet nylon in the 70D after reeling
The second coating cotton thread semi-finished product are made in cladding, and the twist is 640 sth. made by twisting during cladding, and twist direction is Z sth. made by twisting；
S2：The second coating cotton thread semi-finished product are coated with the 70D outsourcings nylon after reeling, the second cladding is made
Yarn, the twist is 580 sth. made by twisting during cladding, and twist direction is twisted with the fingers for S, and the curling coefficient of second coating cotton thread obtained is 96.8.
The mass fraction of the glass fibre, interior packet nylon and outsourcing nylon is respectively 36.66%, 34.17% and
29.17%.
Two, the braider of 13 needles of first coating cotton thread and the second coating cotton thread is subjected to positive and negative and weaves 9 yards
Gloves, specific technical parameter are：
Grammes per square metre is determined as 710~730g, lower captain's degree is 24~25cm.
The convolution number that little finger of toe need to be controlled is 56, and nameless convolution number is 76, and the convolution number of middle finger is 82, the convolution of forefinger
Number is 72, and the convolution number of thumb is 56, and the convolution number of four fingers and palms is 32, and the convolution number of five fingers and palms is 44, the convolution of threaded portion
Number is 66.
Embodiment 2
A kind of method of knitted glove that the present embodiment is related to, includes the following steps：
First, the first coating cotton thread and the second coating cotton thread are prepared respectively；
The preparation method of first coating cotton thread is：
Using the spandex of 70D as the first core wire, first core wire is coated with the 200D polyethylenes after reeling, is made the
One coating cotton thread, the twist is 195 sth. made by twisting during cladding, and twist direction is twisted with the fingers for Z, it is described made from the curling coefficient of the first coating cotton thread be
96.8, the mass fraction of the polyethylene and spandex is respectively 90.11% and 9.89%.
The preparation method of second coating cotton thread is：
S1：Using the glass fibre of 100D as the second core wire, first core wire is carried out with packet nylon in the 70D after reeling
The second coating cotton thread semi-finished product are made in cladding, and the twist is 640 sth. made by twisting during cladding, and twist direction is Z sth. made by twisting；
S2：The second coating cotton thread semi-finished product are coated with the 70D outsourcings nylon after reeling, the second cladding is made
Yarn, the twist is 580 sth. made by twisting during cladding, and twist direction is twisted with the fingers for S, and the curling coefficient of second coating cotton thread obtained is 96.8.
The mass fraction of the glass fibre, interior packet nylon and outsourcing nylon is respectively 46.66%, 24.17% and
29.17%.
Two, the braider of 13 needles of first coating cotton thread and the second coating cotton thread is subjected to positive and negative and weaves 8 yards
Gloves, specific technical parameter are：
Grammes per square metre is determined as 660~680g, lower captain's degree is 23~24cm.
The convolution number that little finger of toe need to be controlled is 54, and nameless convolution number is 74, and the convolution number of middle finger is 80, the convolution of forefinger
Number is 70, and the convolution number of thumb is 54, and the convolution number of four fingers and palms is 30, and the convolution number of five fingers and palms is 42, the convolution of threaded portion
Number is 64.
Embodiment 3
A kind of method of knitted glove that the present embodiment is related to, includes the following steps：
First, the first coating cotton thread and the second coating cotton thread are prepared respectively；
The preparation method of first coating cotton thread is：
Using the spandex of 70D as the first core wire, first core wire is coated with the 200D polyethylenes after reeling, is made the
One coating cotton thread, the twist is 195 sth. made by twisting during cladding, and twist direction is twisted with the fingers for Z, it is described made from the curling coefficient of the first coating cotton thread be
96.8, the mass fraction of the polyethylene and spandex is respectively 85.11% and 14.89%.
The preparation method of second coating cotton thread is：
S1：Using the glass fibre of 100D as the second core wire, first core wire is carried out with packet nylon in the 70D after reeling
The second coating cotton thread semi-finished product are made in cladding, and the twist is 640 sth. made by twisting during cladding, and twist direction is Z sth. made by twisting；
S2：The second coating cotton thread semi-finished product are coated with the 70D outsourcings nylon after reeling, the second cladding is made
Yarn, the twist is 580 sth. made by twisting during cladding, and twist direction is twisted with the fingers for S, and the curling coefficient of second coating cotton thread obtained is 96.8.
The mass fraction of the glass fibre, interior packet nylon and outsourcing nylon is respectively 41.66%, 29.17% and
29.17%.
Two, the braider of 13 needles of first coating cotton thread and the second coating cotton thread is subjected to positive and negative and weaves 10 yards
Gloves, specific technical parameter is：
Grammes per square metre is determined as 760~780g, lower captain's degree is 25~26cm.
The convolution number that little finger of toe need to be controlled is 58, and nameless convolution number is 78, and the convolution number of middle finger is 84, the convolution of forefinger
Number is 74, and the convolution number of thumb is 58, and the convolution number of four fingers and palms is 34, and the convolution number of five fingers and palms is 46, the convolution of threaded portion
Number is 68.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring the substantive content of the present invention.
Claims (7)
- A kind of 1. method of knitted glove, which is characterized in that include the following steps：The first coating cotton thread and the second coating cotton thread are prepared respectively；By first coating cotton thread and the second coating cotton thread circular machine knitting into gloves；Wherein, first coating cotton thread is made of polyethylene and spandex；Second coating cotton thread is by interior packet nylon or terylene, outer Packet nylon and glass fibre composition.
- 2. the method for the gloves woven as described in claim 1, which is characterized in that the preparation method of first coating cotton thread For：Using the spandex of 67-73D as the first core wire, first core wire is coated with the 194-206D polyethylenes after reeling, is made The first coating cotton thread, the twist is 165-225 sth. made by twisting during cladding, twist direction is twisted with the fingers for Z or S, it is described made from the first coating cotton thread It is 96.8 to crimp coefficient.
- 3. the method for knitted glove as claimed in claim 2, which is characterized in that the mass fraction of the polyethylene and spandex is distinguished For 80.11~90.11% and 9.89~19.89%.
- 4. the method for knitted glove as described in claim 1, which is characterized in that the preparation method of second coating cotton thread For：S1：Using the glass fibre of 97-103D as the second core wire, with packet nylon in the 67-73D after reeling to first core wire into Row cladding, is made the second coating cotton thread semi-finished product, and the twist is 544-736 sth. made by twisting during cladding, and twist direction is Z sth. made by twisting；S2：The second coating cotton thread semi-finished product are coated with the 67-73D outsourcings nylon after reeling, the second cladding is made Yarn, the twist is 493-667 sth. made by twisting during cladding, and twist direction is S sth. made by twisting, it is described made from the curling coefficient of the second coating cotton thread be 96.8, Lapie 2.2-2.8.
- 5. the method for knitted glove as claimed in claim 4, which is characterized in that the glass fibre, interior packet nylon and outsourcing The mass fraction of nylon is respectively 36.66~46.66%, 24.17~34.17% and 24.17~34.17%.
- 6. the method for knitted glove as described in claim 1, which is characterized in that using the glove knitting machine of 13 needles.
- 7. the method for the gloves woven as described in claim 1, which is characterized in that with the braider of 13 needle in braiding 9 Code gloves when technical parameter be：Grammes per square metre is determined as 710~730g, lower captain's degree is 24~25cm；The convolution number for controlling little finger of toe is 56, and nameless convolution number is 76, and the convolution number of middle finger is 82, and the convolution number of forefinger is 72, the convolution number of thumb is 56, and the convolution number of four fingers and palms is 32, and the convolution number of five fingers and palms is 44, and the convolution number of threaded portion is 66。