CN108374217A - The Preparation method and use of graphene-superhigh molecular weight polyethylene fibers coating cotton thread - Google Patents

The Preparation method and use of graphene-superhigh molecular weight polyethylene fibers coating cotton thread Download PDF

Info

Publication number
CN108374217A
CN108374217A CN201810037240.7A CN201810037240A CN108374217A CN 108374217 A CN108374217 A CN 108374217A CN 201810037240 A CN201810037240 A CN 201810037240A CN 108374217 A CN108374217 A CN 108374217A
Authority
CN
China
Prior art keywords
graphene
molecular weight
weight polyethylene
polyethylene fibers
superhigh molecular
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201810037240.7A
Other languages
Chinese (zh)
Inventor
沙嫣
沙晓林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Johnson Security Polytron Technologies Inc
Original Assignee
Nantong Johnson Security Polytron Technologies Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Johnson Security Polytron Technologies Inc filed Critical Nantong Johnson Security Polytron Technologies Inc
Priority to CN201810037240.7A priority Critical patent/CN108374217A/en
Publication of CN108374217A publication Critical patent/CN108374217A/en
Pending legal-status Critical Current

Abstract

The present invention provides a kind of preparation methods of graphene superhigh molecular weight polyethylene fibers coating cotton thread comprising following steps：Using spandex thread as core wire, with a graphene superhigh molecular weight polyethylene fibers and a nylon yarn or dacron thread to the core wire coated to get.Compared with prior art, the present invention has following advantageous effect：1, the dipped gloves prepared using the anti-cutting coating cotton thread obtained by the present invention, meeting 4 grades of European Union EN388 standards wear-resisting property, 5 grades of anti-cutting performance, 4 grades of tear resistance, penetration-resistant can be 4 grade, meet 2 grades of European Union EN407 standard heat exposures performance simultaneously, meets 4 grades of ANSI anti-cuttings performance；Oversleeve meets 6 grades of ANSI anti-cuttings performance.

Description

The Preparation method and use of graphene-superhigh molecular weight polyethylene fibers coating cotton thread
Technical field
The present invention relates to a kind of Preparation method and uses of graphene-superhigh molecular weight polyethylene fibers coating cotton thread, belong to In fibrous material technical field.
Background technology
Safety protection glove is frequently used in complicated work situation or in dangerous sports, can Play the role of protecting labourer or sportsman's hand.Therefore, safety protection glove has been requested to preferable resistance to when in use Grind performance and anti-cutting performance, but in the prior art, influenced by thread material and weaving method, safety protection glove it is wear-resisting Property, anti-cutting, tear resistance and penetration-resistant are insufficient.
Invention content
For the defects in the prior art, it is fine that the object of the present invention is to provide a kind of graphene-ultra-high molecular weight polyethylenes Tie up the Preparation method and use of coating cotton thread.
The present invention is achieved by the following technical solutions：
The present invention provides a kind of preparation method of graphene-superhigh molecular weight polyethylene fibers coating cotton thread comprising such as Lower step：
Using spandex thread as core wire, with a graphene-superhigh molecular weight polyethylene fibers and a nylon yarn or dacron thread To the core wire coated to get.
Preferably, the spandex thread, graphene-superhigh molecular weight polyethylene fibers and nylon yarn or dacron thread Weight percent is respectively：5~15%, 55~70%, 15~30%.
Preferably, the graphene-superhigh molecular weight polyethylene fibers, nylon yarn or dacron thread, spandex thread Line density is respectively 380~420D, 130~160D, 130~150D.
Preferably, the twist of the graphene-superhigh molecular weight polyethylene fibers is 180~220 twirls, twist direction It is twisted for Z, the twist of nylon yarn or dacron thread is 360~540 twirls, and twist direction is twisted for S.
Preferably, in the graphene-superhigh molecular weight polyethylene fibers graphene content be 0.5~ 10wt%.
Preferably, also contain filler in the graphene-superhigh molecular weight polyethylene fibers, the filler contains Amount is 5~20wt%, and the filler includes silicon carbide, diamond, glass microballoon, ceramic fibre, glass fibre, basalt fibre At least one of dimension, metallic fiber.
Preferably, include graphene that content is 0.1~5wt% in the nylon yarn or dacron thread, it is described The Lapie of spandex thread is 1.6~2, includes the graphene that content is 0.1~5wt% in the spandex thread.
A kind of Anti-cutting covered yarn line prepared by aforementioned preparation process.
Preferably, the curling coefficient of the Anti-cutting covered yarn line is 96~99.
A kind of purposes of Anti-cutting covered yarn line as the aforementioned in gloves or oversleeve.
A kind of preparation method of gloves as the aforementioned comprising following steps：
Gloves base is made using Anti-cutting covered yarn line, after the gloves base is impregnated in slurry, carries out being solidified into coating, Obtain gloves；
Wherein, the slurry includes at least one of PU, butyronitrile, natural emulsion, PVC or neoprene；
The preparation method of the gloves base is：The Anti-cutting covered yarn line is inputted to the braider of 7 needles, 10 needles or 13 needles In, braided parameter is set, is woven；
The braided parameter is specially：It is with technical parameter of the braider of 13 needle when weaving 9 yards of gloves：
Determine that grammes per square metre is 710~730g, lower captain's degree is 24~25cm；
The convolution number for controlling little finger of toe is 56, and nameless convolution number is 76, and the convolution number of middle finger is 82, the convolution number of index finger It is 72, the convolution number of thumb is 56, and the convolution number of four fingers and palms is 32, and the convolution number of five fingers and palms is 44, the convolution number of threaded portion It is 66.
Preferably, the oversleeve is the small tubular knitting of 260~320 needles, using 6 anti-cuttings claddings when knitting Yarn manufactures.
Compared with prior art, the present invention has following advantageous effect：
1, the dipped gloves prepared using the anti-cutting coating cotton thread obtained by the present invention, it is wear-resisting to meet European Union's EN388 standards 4 grades of performance, 5 grades of anti-cutting performance, 4 grades of tear resistance, penetration-resistant can be 4 grades, while meeting European Union EN407 standard heat exposures 2 grades of performance meets 4 grades of ANSI anti-cuttings performance；Oversleeve meets 6 grades of ANSI anti-cuttings performance；
2, the Comprehensive Characteristics and performance that the anti-cutting of high-performance and heat resistanceheat resistant gloves are made in the application have been more than that other are main in the world Gloves brand；Gloves or oversleeve as made of Du Pont's Kevlar yarns, heat resistance is remarkable, but anti-cutting is insufficient；Royal DSM Gloves made of Dyneema yarns, anti-cutting can reach 5 grades of standards of Europe superscript, but only 3 grades of American Standard cutting, heat resistanceheat resistant are also less It is good；Yarn of the present invention and manufactured dipped gloves or oversleeve, not only solar heat protection contact performance is close to Kevlar yarn gloves, anti-cutting Also it is combine above-mentioned two famous brand excellent to have reached 5 grades of Europe superscript, 6 grades of standards of American Standard or even oversleeve and reached 9 grades of American Standard Point；
3, meet particular market demand, it is suitable for large-scale promotion.
Specific implementation mode
With reference to specific embodiment, the present invention is described in detail.Following embodiment will be helpful to the technology of this field Personnel further understand the present invention, but the invention is not limited in any way.It should be pointed out that the ordinary skill of this field For personnel, without departing from the inventive concept of the premise, various modifications and improvements can be made.These belong to the present invention Protection domain.
In the present invention：" twist " refers to possessed number of twists in every meter of long filament.
" braiders of 10 needles ", practical is circular knitting machine, and glove knitting machine is also one kind of circular knitting machine.
" convolution number ", refers to the a-circle-by-a-circle quantity of braider in knitted glove base.
Embodiment 1
A kind of preparation method of graphene-superhigh molecular weight polyethylene fibers coating cotton thread is present embodiments provided, is wrapped Include following steps：
Using spandex thread as core wire, with a graphene-superhigh molecular weight polyethylene fibers and a nylon yarn or dacron thread To the core wire coated to get.
Preferably, the spandex thread, graphene-superhigh molecular weight polyethylene fibers and nylon yarn or dacron thread Weight percent is respectively：5~15%, 55~70%, 15~30%.
Preferably, the graphene-superhigh molecular weight polyethylene fibers, nylon yarn or dacron thread, spandex thread Line density is respectively 380~420D, 130~160D, 130~150D.
Preferably, the twist of the graphene-superhigh molecular weight polyethylene fibers is 180~220 twirls, twist direction It is twisted for Z, the twist of nylon yarn or dacron thread is 360~540 twirls, and twist direction is twisted for S.
Preferably, in the graphene-superhigh molecular weight polyethylene fibers graphene content be 0.5~ 10wt%.
Preferably, also contain filler in the graphene-superhigh molecular weight polyethylene fibers, the filler contains Amount is 5~18wt%, and the filler includes silicon carbide, diamond, ceramic fibre, glass fibre, basalt fibre, metallic fiber At least one of.
Preferably, include graphene that content is 0.1~5wt% in the nylon yarn or dacron thread, it is described The Lapie of spandex thread is 1.6~2, includes the graphene that content is 0.1~5wt% in the spandex thread.
The curling coefficient of cutting-resisting yarn manufactured in the present embodiment is 96~99.
Embodiment 2
A kind of method that the Anti-cutting covered yarn line prepared by 1 method of embodiment prepares gloves is present embodiments provided, specifically Include the following steps：
Gloves base is made using Anti-cutting covered yarn line, after the gloves base is impregnated in slurry, carries out being solidified into coating, Obtain gloves；
Wherein, the slurry includes at least one of PU, butyronitrile, natural emulsion, PVC or neoprene；
The preparation method of the gloves base is：The Anti-cutting covered yarn line is inputted to the braider of 7 needles, 10 needles or 13 needles In, braided parameter is set, is woven；
The braided parameter is specially：It is with technical parameter of the braider of 13 needle when weaving 9 yards of gloves：
Determine that grammes per square metre is 710~730g, lower captain's degree is 24~25cm；
The convolution number for controlling little finger of toe is 56, and nameless convolution number is 76, and the convolution number of middle finger is 82, the convolution number of index finger It is 72, the convolution number of thumb is 56, and the convolution number of four fingers and palms is 32, and the convolution number of five fingers and palms is 44, the convolution number of threaded portion It is 66.
Embodiment 3
A kind of method that the Anti-cutting covered yarn line prepared by 1 method of embodiment prepares oversleeve is present embodiments provided, it is described Oversleeve is the small tubular knitting of 260~320 needles, using 6 Anti-cutting covered yarn lines manufactures when knitting.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited in above-mentioned Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow Ring the substantive content of the present invention.

Claims (12)

1. a kind of preparation method of graphene-superhigh molecular weight polyethylene fibers coating cotton thread, which is characterized in that including walking as follows Suddenly：
Using spandex thread as core wire, with a graphene-superhigh molecular weight polyethylene fibers and a nylon yarn or dacron thread to institute State core wire coated to get.
2. the preparation method of graphene as described in claim 1-superhigh molecular weight polyethylene fibers coating cotton thread, feature exist In the spandex thread, graphene-superhigh molecular weight polyethylene fibers and the weight percent of nylon yarn or dacron thread are respectively：5 ~15%, 55~70%, 15~30%.
3. the preparation method of graphene as described in claim 1-superhigh molecular weight polyethylene fibers coating cotton thread, feature exist In, the line density of the graphene-superhigh molecular weight polyethylene fibers, nylon yarn or dacron thread, spandex thread be respectively 380~ 420D, 130~160D, 130~150D.
4. the preparation method of graphene as described in claim 1-superhigh molecular weight polyethylene fibers coating cotton thread, feature exist In the twist of the graphene-superhigh molecular weight polyethylene fibers is 180~220 twirls, and twist direction is twisted for Z, nylon yarn or terylene The twist of silk is 360~540 twirls, and twist direction is twisted for S.
5. the preparation method of graphene as described in claim 1-superhigh molecular weight polyethylene fibers coating cotton thread, feature exist In the content of graphene is 0.5~10wt% in the graphene-superhigh molecular weight polyethylene fibers.
6. the preparation method of graphene as claimed in claim 5-superhigh molecular weight polyethylene fibers coating cotton thread, feature exist In also containing filler in the graphene-superhigh molecular weight polyethylene fibers, the content of the filler is 5~20wt%, described Filler include in silicon carbide, diamond, glass microballoon, ceramic fibre, glass fibre, basalt fibre, metallic fiber at least It is a kind of.
7. the preparation method of graphene as described in claim 1-superhigh molecular weight polyethylene fibers coating cotton thread, feature exist In, include the graphene that content is 0.1~5wt% in the nylon yarn or dacron thread, the Lapie of the spandex thread is 1.6~ 2, include the graphene that content is 0.1~5wt% in the spandex thread.
8. a kind of Anti-cutting covered yarn line prepared by any one of claim 1~7 preparation method.
9. Anti-cutting covered yarn line as described in claim 8, which is characterized in that curling coefficient is 96~99.
10. a kind of purposes of Anti-cutting covered yarn line as claimed in claim 8 in gloves, oversleeve or clothes.
11. a kind of preparation method of gloves as claimed in claim 10, which is characterized in that include the following steps：
Gloves base is made using Anti-cutting covered yarn line, after the gloves base is impregnated in slurry, carries out being solidified into coating, obtain Gloves；
Wherein, the slurry includes at least one of PU, butyronitrile, natural emulsion, PVC or neoprene；
The preparation method of the gloves base is：The Anti-cutting covered yarn line is inputted in the braider of 7 needles, 10 needles or 13 needles, if Determine braided parameter, is woven；
The braided parameter is specially：It is with technical parameter of the braider of 13 needle when weaving 9 yards of gloves：
Determine that grammes per square metre is 710~730g, lower captain's degree is 24~25cm；
The convolution number for controlling little finger of toe is 56, and nameless convolution number is 76, and the convolution number of middle finger is 82, and the convolution number of index finger is 72, the convolution number of thumb is 56, and the convolution number of four fingers and palms is 32, and the convolution number of five fingers and palms is 44, and the convolution number of threaded portion is 66。
12. a kind of preparation method of oversleeve as claimed in claim 10, which is characterized in that the oversleeve is that 260-320 needles are small Tubular knitting, using 6 Anti-cutting covered yarn lines manufactures when knitting.
CN201810037240.7A 2018-01-15 2018-01-15 The Preparation method and use of graphene-superhigh molecular weight polyethylene fibers coating cotton thread Pending CN108374217A (en)