CN108218645A - A kind of high precision tungsten type delay composition of delay detonating detonator and preparation method thereof - Google Patents
A kind of high precision tungsten type delay composition of delay detonating detonator and preparation method thereof Download PDFInfo
- Publication number
- CN108218645A CN108218645A CN201810109385.3A CN201810109385A CN108218645A CN 108218645 A CN108218645 A CN 108218645A CN 201810109385 A CN201810109385 A CN 201810109385A CN 108218645 A CN108218645 A CN 108218645A
- Authority
- CN
- China
- Prior art keywords
- drying
- delay
- parts
- sieved
- high precision
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
High precision tungsten type delay composition the invention discloses a kind of delay detonating detonator and preparation method thereof, according to the mass fraction, composition of raw materials is the delay powder:1000 parts of di-iron trioxide, 340 540 parts of potassium hyperchlorate, 500 700 parts of tungsten powder, 60 90 parts of industrial silicon, 44 64 parts of manganese dioxide.The step of preparing the delay powder be:First with stainless steel ball and industrial alcohol, it is mixed by mixing machine;Dry again by the screening of the sieve of 20 mesh and for the first time, then by polyvinyl alcohol water solution kneading and second dry and etc. obtain the delay powder.The delay powder by breakthrough improves formula, has reached the extension to Nonel detonator high precision, is very suitable for high-accuracy explosion and uses;The preparation method of the delay powder is sufficiently mixed the ingredient of the delay powder completely, to enhance the accuracy of its delayed effect by multiple mixing and drying using alcohol and polyvinyl alcohol water solution.
Description
Technical field
The present invention relates to a kind of delay powders of delay detonating detonator, and in particular to a kind of delay detonating detonator
High precision tungsten type delay composition and preparation method thereof.
Background technology
Explosive is a kind of substance that quickly can be burnt or decompose, and a large amount of heat can be generated in very short time
And gas, typical explosive include explosive and corresponding apparatus to cause bursting, usually also have corresponding shell, be by detonator
After heat or impact energy triggering, explosive will be chemically reacted quickly, i.e. fully burning or decomposition.It is chemically reacting
In, compound, which is decomposed, generates multiple gases, between each not homoatomic of reactant (original chemical compound), with chemical bond
Form stores big energy, and when compound molecule decomposes, product (gas of generation) is possibly also with some of which energy
(rather than whole energy) forms new keys.The energy of most of " residues " can form high temperature heat.The gas of concentration is greatly being pressed
Rapid expanding under power, heat can accelerate the movement velocity of each gas particle so that pressure higher, in high explosive, and gas
Pressure is very big, it is sufficient to destroy building, cause people's injures and deaths.If gas expansion speed is faster than velocity of sound, powerful shock wave will be generated.
This pressure can also promote solid fragment to go out at a high speed, with huge strength strike people or building.
Explosive is due to that can make surrounding medium fierce destruction work(, and be often otherwise known as high explosive, and common high explosive is pressed
Composition can be divided into 2 class of single compound explosive and composite explosives.Wherein, the very high explosive of also a kind of sensitivity, is changed into detonation from burning
Time it is extremely short, be usually not directly used for making destruction work(, but for igniting or igniting other explosive wastewaters, referred to as priming.It is fried
By the effect of certain extraneous excitation momentum, detonation is that the spread speed of chemical reaction zone in explosive is more than explosive for the explosion of medicine
Explosion phenomenon during the middle velocity of sound is the typical energy releasing pattern of explosive.Actually in two stages, most of destroy is for explosion
Caused by initial expansion, it can also manufacture a very low region of pressure around explosive source, and gas is quickly displaced outwardly, from
And from explosion, " " center " is inhaled outward, and outward after impact, gas regurgitates the central area of partial vacuum, shape by most of gas
It is smaller interior to energy wave into second destructive power.Chemical reaction velocity is very fast during due to explosive charge, and height is formed in moment
Warm high pressure gas, and with high power (every kilogram of explosive detonation moment output power is up to 5 × 10 kilowatts) to extraneous work done,
Surrounding medium is made to be deformed by strong impact, compression or fragmentation.The process of explosive reaction necessarily leads to a large amount of gases, explosive
Explosion time generates hundreds of to thousands of times that gas volume is explosion front volume, is consumingly compressed in the moment of explosion a large amount of gases
Within intimate original volume, thus the high pressure of hundreds thousand of a atmospheric pressure is generated, along with the exothermicity of reaction, high temperature and pressure
For gas rapidly to surrounding medium expansion working, this has resulted in power possessed by explosive.
Explosive because its with it is of low cost, save manpower, engineering construction can be accelerated, because due to it is more and more extensive be applied to state
The economic each department of the people.In terms of mining, Large-scale blasting is carried out using explosive, to exploit metallic ore and open coal mine;Profit
The petroleum perforation charge of explosive is loaded with energy-gathering jetting effect, available for oil exploitation;In terms of geological prospecting, made of explosive
Explosive-source explosive post is used for seismic prospecting;In machine building industry, explosive is used for explosive forming, the techniques such as cutting metal, explosive welding;
In hydraulic and electric engineering engineering, explosive is used to build dam, dredging river, level land;In railway, highway construction, explosive is used to split
Mountain is opened a way, and digs tunnel, chamber etc.;Explosive is also largely used to exploit various building stones.Explosive militarily can be used as shell, aviation
The explosive charge of the ammunitions such as bomb, guided missile, land mine, torpedo, grenade, it can also be used to the apparatus to cause bursting and military blasting of nuclear bomb.
Industrially it is widely used in digging up mine, builds the road, build water conservancy projects, engineering explosion, intermetallic composite coating etc., is also widely used for seismic prospecting
Etc. science and technology fields.
Priming system is equipped with the miniaturized component or device of explosive, can (such as heat, machinery, electricity and light by certain initial punching
Punching can) effect is incendivity or explosion, to generate expected function, common priming system have Nonel detonator, fuse cord, lead it is quick-fried
Rope, igniter cap, fire in a stove before fuel is added etc..Wherein, Nonel detonator is the abbreviation of plastic detonating tube detonator, it is to rush energy by the shock wave of detonator
Quick-fried detonator is led in the industry of excitation, is assemblied by detonator and blasting cap, for the blasting engineering of explosion danger.Nonel detonator
Include wink hair Nonel detonator and delay detonating detonator again.It sends out Nonel detonator in wink and refers to the detonator having an effect in moment
Thunder, delay detonating detonator refer to the Nonel detonator for playing time-lag action.Delay detonating detonator by action time be divided into millisecond,
Half second, second delay Nonel detonator etc..Nonel detonator has antistatic, anti lightning, anti-radio frequency, water resistant, anti-stray current
Ability, it is safe and reliable, it is simple and practicable.
In civil explosive industry now, half second delay series of delay detonating detonator is mainly using silicon systems or black powder
Formula, such Delay Tube is with regard to long, and again because being pipe male extension mode, so production and use are very inconvenient;Together
When, precision of the formula of silicon systems or black powder in the time of delaying has had reached bottleneck now, time deviation can ±
25ms/mm or so, for best situation also only in ± 20ms/mm, this is for some high-accuracy explosions or inadequate,
Therefore, it is necessary to be directed to the accuracy of delay detonating detonator to be improved.
Invention content
(1) technical problems to be solved
In view of the deficiencies of the prior art, the technical problem to be solved in the present invention is to provide a kind of delay detonating detonators
High precision tungsten type delay composition and preparation method thereof, the delay powder by breakthrough improve formula, have reached to detonator thunder
The extension of pipe high precision is very suitable for high-accuracy explosion and uses;The preparation method of the delay powder by multiple mixing and
Drying, and the ingredient of the delay powder is made to be sufficiently mixed completely using alcohol and polyvinyl alcohol water solution, enhance its delayed effect
Accuracy.
(2) technical solution
In order to solve the above technical problem, the present invention provides the high precision tungsten of such a delay detonating detonator
It is delay powder, according to the mass fraction, composition of raw materials is:1000 parts of di-iron trioxide, 340-540 parts of potassium hyperchlorate, tungsten powder
500-700 parts, 60-90 parts of industrial silicon, 44-64 parts of manganese dioxide.
Preferably, according to the mass fraction, composition of raw materials is:1000 parts of di-iron trioxide, 440 parts of potassium hyperchlorate, tungsten powder
600 parts, 75 parts of industrial silicon, 54 parts of manganese dioxide.
A kind of preparation method of the high precision tungsten type delay composition of delay detonating detonator, step are:
A. raw material di-iron trioxide, potassium hyperchlorate, tungsten powder, industrial silicon and manganese dioxide are weighed respectively, and raw material is distinguished
It is added in mixing machine, then the stainless steel ball of the Φ 20mm of quality, Φ 16mm, Φ 12mm such as is separately added into mixing machine, no
The mass ratio of steel ball gross mass of becoming rusty and raw material gross mass is 2:1, then it is raw material gross mass 4.6- to add in quality into mixing machine
5.2% 95% industrial alcohol, and pass through mixing machine and mixed, mixing rotating speed is 34-42r/min, continuously mixes 24-48h;
B. mixture is poured into the sieve of 20 mesh and sieved, obtain being sieved through material, then carry out to being sieved through material
It dries for the first time, drying temperature is 45-55 DEG C, drying time 24-36h;
C. the polyvinyl alcohol water solution that mass concentration is 4% is added in into first time drying material, according to the gross mass of raw material,
130-170ml polyvinyl alcohol water solutions are added in every kilogram of raw material, and are integrated uniformly, then second of drying is carried out to it, are dried
Temperature is 45-55 DEG C, drying time 30-40min;
D. second of drying material is positioned on the sieve of 40 mesh, its surface is wiped using rubber, so as to carry out
It is granulated, then third time drying is carried out to it, drying temperature is 45-55 DEG C, is dried for the third time when its water content is less than 0.15%
It completes, then is poured into the sieve of 20 mesh and is sieved, it is the obtained height of delay detonating detonator to be sieved through material
Accuracy tungsten type delay composition.
Preferably, in stepb, mixture is poured into the sieve of 20 mesh and sieved, obtain being sieved through material, then right
It is sieved through material and carries out first time drying, drying temperature is 50 DEG C, drying time 30h.
Preferably, in step C, the polyvinyl alcohol water solution that mass concentration is 4%, root are added in into first time drying material
According to the gross mass of raw material, 150ml polyvinyl alcohol water solutions are added in every kilogram of raw material, and integrate uniformly, then second is carried out to it
Secondary drying, drying temperature are 50 DEG C, drying time 35min.
(3) advantageous effect
Compared with prior art, the present invention proportioning of the delay powder by science, is formulated improvement, utilizes tungsten powder breakthroughly
It is improved breakthroughly to its raw material, while accordingly with two iron of oxidation, potassium hyperchlorate, tungsten powder, industrial silicon and titanium dioxide
Manganese, and it is corresponding science refinement specifically done to its proportional quantity had adjusted, so as to breach matching for silicon systems or black powder
Side's limitation, has reached the extension to Nonel detonator high precision, wherein, the accuracy of silicon systems or black powder formula normally only exists
± 25ms/mm or so, and the accuracy of tungsten type delay composition formula of the present invention can reach ± 10ms/mm or so, be very suitable for high-precision
Close explosion uses, and has splendid practical value.
The preparation method of the delay powder combines alcohol and polyvinyl alcohol water solution conduct by multiple mixing and drying
Medium is merged, the various composition of delay powder is made to be sufficiently mixed completely, makes between its internal particle that there are a certain distance guarantee is loose
Property, be not susceptible to it is hardened, while enhancing its delayed effect accuracy, moreover it is possible to improve its ignition success rate.
In general, which by breakthrough improves formula, has reached and Nonel detonator high precision is prolonged
Phase is very suitable for high-accuracy explosion and uses;The preparation method of the delay powder utilizes alcohol by multiple mixing and drying
Being sufficiently mixed the ingredient of the delay powder with polyvinyl alcohol water solution completely, enhances the accuracy of its delayed effect.
Specific embodiment
It, below will be right to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention
Technical solution in the embodiment of the present invention carries out clear, complete description, with the present invention is further explained, it is clear that described
Embodiment is only the part of the embodiment of the present invention, instead of all the embodiments.
Embodiment 1
The preparation method of the high precision tungsten type delay composition of this batch delay detonating detonator, its step are as follows:
A. raw material di-iron trioxide 1000g, potassium hyperchlorate 340g, tungsten powder 700g, industrial silicon 90g and titanium dioxide are weighed respectively
Manganese 44g, and raw material is added separately in mixing machine, then be separately added into mixing machine 1450g Φ 20mm stainless steel balls,
The Φ 16mm stainless steel balls of 1450g, the Φ 12mm stainless steel balls of 1450g, then add in into mixing machine the 95% industrial wine of 100g
Essence, and pass through mixing machine and mixed, mixing rotating speed is 34r/min, continuously mixes 48h;
B. mixture is poured into the sieve of 20 mesh and sieved, obtain being sieved through material, then carry out to being sieved through material
It dries for the first time, drying temperature is 45 DEG C, drying time 36h;
C. the polyvinyl alcohol water solution 283ml that mass concentration is 4% is added in into first time drying material, kneading is uniform, then
Second of drying is carried out to it, drying temperature is 45 DEG C, drying time 40min;
D. second of drying material is positioned on the sieve of 40 mesh, its surface is wiped using rubber, so as to carry out
It is granulated, then third time drying is carried out to it, drying temperature is 45 DEG C, has been dried for the third time when its water content is less than 0.15%
Into, then be poured into the sieve of 20 mesh and sieved, it is sieved through the high-precision of the delay detonating detonator that material as obtains
True property tungsten type delay composition sample 1.
Embodiment 2
The preparation method of the high precision tungsten type delay composition of this batch delay detonating detonator, its step are as follows:
A. raw material di-iron trioxide 1000g, potassium hyperchlorate 540g, tungsten powder 500g, industrial silicon 60g and titanium dioxide are weighed respectively
Manganese 64g, and raw material is added separately in mixing machine, then be separately added into mixing machine 1443g Φ 20mm stainless steel balls,
The Φ 16mm stainless steel balls of 1443g, the Φ 12mm stainless steel balls of 1443g, then add in into mixing machine the 95% industrial wine of 113g
Essence, and pass through mixing machine and mixed, mixing rotating speed is 42r/min, and continuous mixing is for 24 hours;
B. mixture is poured into the sieve of 20 mesh and sieved, obtain being sieved through material, then carry out to being sieved through material
It dries for the first time, drying temperature is 55 DEG C, and drying time is for 24 hours;
C. the polyvinyl alcohol water solution 367ml that mass concentration is 4% is added in into first time drying material, kneading is uniform, then
Second of drying is carried out to it, drying temperature is 55 DEG C, drying time 30min;
D. second of drying material is positioned on the sieve of 40 mesh, its surface is wiped using rubber, so as to carry out
It is granulated, then third time drying is carried out to it, drying temperature is 55 DEG C, has been dried for the third time when its water content is less than 0.15%
Into, then be poured into the sieve of 20 mesh and sieved, it is sieved through the high-precision of the delay detonating detonator that material as obtains
True property tungsten type delay composition sample 2.
Embodiment 3
The preparation method of the high precision tungsten type delay composition of this batch delay detonating detonator, its step are as follows:
A. raw material di-iron trioxide 1000g, potassium hyperchlorate 440g, tungsten powder 600g, industrial silicon 75 and titanium dioxide are weighed respectively
Manganese 54g, and raw material is added separately in mixing machine, then be separately added into mixing machine 1446g Φ 20mm stainless steel balls,
The Φ 16mm stainless steel balls of 1446g, the Φ 12mm stainless steel balls of 1446g, then add in into mixing machine the 95% industrial wine of 106g
Essence, and pass through mixing machine and mixed, mixing rotating speed is 38r/min, continuously mixes 36h;
B. mixture is poured into the sieve of 20 mesh and sieved, obtain being sieved through material, then carry out to being sieved through material
It dries for the first time, drying temperature is 50 DEG C, drying time 30h;
C. the polyvinyl alcohol water solution 325ml that mass concentration is 4% is added in into first time drying material, kneading is uniform, then
Second of drying is carried out to it, drying temperature is 50 DEG C, drying time 35min;
D. second of drying material is positioned on the sieve of 40 mesh, its surface is wiped using rubber, so as to carry out
It is granulated, then third time drying is carried out to it, drying temperature is 50 DEG C, has been dried for the third time when its water content is less than 0.15%
Into, then be poured into the sieve of 20 mesh and sieved, it is sieved through the high-precision of the delay detonating detonator that material as obtains
True property tungsten type delay composition sample 3.
Experimental Comparison and result:
Extension detonator 1, extension detonator 2, the extension detonator produced by sample 1, sample 2, sample 3 is now taken respectively
3 and the existing extension detonator 4 produced by silicon series prescription and the extension detonator 5 that is produced by black powder formula, point
This five kinds of extension detonators theoretical and real time deviation in ignition is not tested.
It can be obtained by experimental data, the time deviation of 1 test of many times of extension detonator is average in ± 11ms/mm;Prolong
The time deviation of 2 test of many times of phase detonator is average in ± 10ms/mm;The time deviation of 3 test of many times of extension detonator is averaged
In ± 9ms/mm;And the time deviation of 4 test of many times of extension detonator is average in ± 22ms/mm;5 test of many times of extension detonator
Time deviation it is average in ± 25ms/mm;It is possible thereby to become apparent from, the extension produced by the defering medicine prescription is led quick-fried
Pipe, accuracy obtained the raising of matter, reached the extension to Nonel detonator high precision, is very suitable for high-accuracy quick-fried
It is broken to use.
The foregoing describe the technical characteristics and basic principle and associated advantages of the present invention, for those skilled in the art
For, it is clear that the present invention is not limited to the details of above-mentioned exemplary embodiment, and it is in the design without departing substantially from the present invention or substantially special
In the case of sign, the present invention can be realized in other specific forms.It therefore, in all respects, should all be by embodiment
Regard exemplary as, and be non-limiting, the scope of the invention being indicated by the appended claims rather than by the foregoing description,
It is intended that all changes falling within the meaning and scope of the equivalent requirements of the claims are included within the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in each embodiment can also be properly combined, forms those skilled in the art
The other embodiment being appreciated that.
Claims (5)
1. a kind of high precision tungsten type delay composition of delay detonating detonator, which is characterized in that according to the mass fraction, raw material
It is formulated and is:1000 parts of di-iron trioxide, 340-540 parts of potassium hyperchlorate, 500-700 parts of tungsten powder, 60-90 parts of industrial silicon, titanium dioxide
44-64 parts of manganese.
2. the high precision tungsten type delay composition of delay detonating detonator according to claim 1, which is characterized in that by matter
Number meter is measured, composition of raw materials is:1000 parts of di-iron trioxide, 440 parts of potassium hyperchlorate, 600 parts of tungsten powder, 75 parts of industrial silicon, two
54 parts of manganese oxide.
3. a kind of method of high precision tungsten type delay composition for preparing delay detonating detonator as described in claim 1,
It is characterized in that, its step are as follows:
A. raw material di-iron trioxide, potassium hyperchlorate, tungsten powder, industrial silicon and manganese dioxide are weighed respectively, and raw material is separately added into
Into mixing machine, then the stainless steel ball of the Φ 20mm of quality, Φ 16mm, Φ 12mm, the stainless steel such as it is separately added into mixing machine
The mass ratio of ball gross mass and raw material gross mass is 2:1, then it is raw material gross mass 4.6-5.2%'s to add in quality into mixing machine
95% industrial alcohol, and pass through mixing machine and mixed, mixing rotating speed is 34-42r/min, continuously mixes 24-48h;
B. mixture is poured into the sieve of 20 mesh and sieved, obtain being sieved through material, then first is carried out to being sieved through material
Secondary drying, drying temperature are 45-55 DEG C, drying time 24-36h;
C. the polyvinyl alcohol water solution that mass concentration is 4%, according to the gross mass of raw material, every thousand are added in into first time drying material
130-170ml polyvinyl alcohol water solutions are added in gram raw material, and integrate uniform, then second of drying, drying temperature are carried out to it
It is 45-55 DEG C, drying time 30-40min;
D. second of drying material is positioned on the sieve of 40 mesh, its surface is wiped using rubber, so as to be granulated,
Third time drying is carried out to it again, drying temperature is 45-55 DEG C, dries and completes for the third time when its water content is less than 0.15%,
It is poured into the sieve of 20 mesh and is sieved again, it is the obtained high precision of delay detonating detonator to be sieved through material
Tungsten type delay composition.
4. the method for high precision tungsten type delay composition according to claim 3 for preparing delay detonating detonator, special
Sign is, in stepb, mixture is poured into the sieve of 20 mesh and is sieved, and obtains being sieved through material, then to being sieved through
Material carries out first time drying, and drying temperature is 50 DEG C, drying time 30h.
5. the method for high precision tungsten type delay composition according to claim 3 for preparing delay detonating detonator, special
Sign is, in step C, the polyvinyl alcohol water solution that mass concentration is 4% is added in into first time drying material, according to raw material
Gross mass adds in 150ml polyvinyl alcohol water solutions in every kilogram of raw material, and integrates uniform, then carries out second of drying to it, dries
Dry temperature is 50 DEG C, drying time 35min.