CN108203231A - A kind of brown-green mat glass lampshade made using frosting liquor frosting technique - Google Patents
A kind of brown-green mat glass lampshade made using frosting liquor frosting technique Download PDFInfo
- Publication number
- CN108203231A CN108203231A CN201611171231.4A CN201611171231A CN108203231A CN 108203231 A CN108203231 A CN 108203231A CN 201611171231 A CN201611171231 A CN 201611171231A CN 108203231 A CN108203231 A CN 108203231A
- Authority
- CN
- China
- Prior art keywords
- brown
- green
- frosting
- sent
- glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of brown-green mat glass lampshade made using frosting liquor frosting technique, which belongs to glass manufacturing area;The raw material that the present invention uses includes:Real estate quartz sand 32% 34%, sodium carbonate 10% 12%, purchase brown cullet 15%, the green cullet 15% of purchase, calcite 11%, aluminium hydroxide 10%, sodium nitrate 2%, barium carbonate 1%, oxygen sodium metasilicate 0.7%, anhydrous sodium sulphate 0.3%, selenium powder 0.9%, cobalt powder 0.1%, by the way that brown-green elen shade is made after the mixing of raw material, melting, molding, annealing, frosted, tempering, this method has the series of advantages such as simple for process, raw material sources are convenient, production cost is low, pollution-free, suitable industrialized production;Product has many advantages, such as exquisite in workmanship, specious, smooth easy clean with dim sense, hardness height, stable chemical performance, surface.
Description
Technical field
The invention belongs to glass manufacturing areas more particularly to one kind to use frosting liquor frosting work by raw material of real estate quartz sand
The brown-green mat glass lampshade that skill makes.
Background technology
Glass is a kind of transparent or semitransparent solid matter, the formation contiguous network structure in melting, in cooling procedure
Viscosity gradually increases and hardens and non crystallized silicates nonmetallic materials.It using quartz sand, soda ash is main that simple glass, which is,
Raw material, through 1500 DEG C -1600 DEG C of high-temperature fusion, molding and amorphous non-crystalline solid material prepared by through being quickly cooled down,
Wherein dioxide-containing silica is between 55%-65%, the calcium oxide also containing 15% sodium oxide molybdena and 10%, its main feature is that hard texture and
It is crisp, water white transparency, low production cost, easily molded.Glass can be made different shapes and have different purposes, Glass lamp
Cover is one kind of glassware, it is after the working process of surface to obtain finished product after tempering again using glass as basic material,
Feature is that hardness height, stable chemical performance, surface are smooth easy clean, environmentally friendly.It is different to be made that different materials can also be added
Color, can be by putting-out system into frosted, frosting, applique colour etc..Product of the present invention is a kind of brown-green mat glass lamp
The manufacturing method of cover, it is to add purchase brown and green cullet in dispensing as primary raw material using real estate quartz sand, then add
Auxiliary material is added to be mixed, is melted, brown-green mat glass lampshade is made through being molded, annealing, after frosting, tempering again.Brown-green covers
Tempering must be carried out after sand glass lamp shade forming, the tempering method used is gas medium tempering method, and operating procedure is will to be molded
When brown-green glass lamp shade after cooling is heated to close to 650~700 DEG C of its softening temperature, its all part is blown simultaneously suddenly
It is made to cool down rapidly with cold wind, the mechanical strength and thermal stability of brown-green glass lamp shade, basic demand can be increased after cooling
It is quickly and uniformly to cool down, to obtain equally distributed stress.Brown-green glass lamp shade and simple glass lampshade after tempering
Compared to having the following advantages:1. intensity improves several times compared with simple glass;2. safe to use, bearing capacity increase improves glass
The frangible property of glass lampshade, in the fractionlet of no acute angle destruction;3. glass resistance to thermal shocks matter after tempering compared with
Simple glass can improve 3-5 times, can generally bear 220 degree or more of difference variation.
Invention content:
Present invention mainly solves the problem of be to provide a kind of brown-green mat glass lampshade made using frosting liquor frosting technique,
The raw material that the present invention uses is by weight ratio:Real estate quartz sand 32%-34%, sodium carbonate 10%-12%, purchase brown cullet
15%th, green cullet 15%, calcite 11%, aluminium hydroxide 10%, sodium nitrate 2%, barium carbonate 1%, oxygen sodium metasilicate 0.7%, member are purchased
Bright powder 0.3%, selenium powder 0.9%, cobalt powder 0.1%.
The present invention can be achieved through the following technical solutions:
(1)By the real estate quartz sand of formula ratio, sodium carbonate, purchase brown cullet, the green cullet of purchase, calcite, hydrogen-oxygen
Change aluminium, sodium nitrate, barium carbonate, oxygen sodium metasilicate, anhydrous sodium sulphate, selenium powder, cobalt powder and be sent into blender blending uniformly, it will be mixed by conveyer
It closes material and is sent into continuous induction melting furnace, power transmission heats after sealing, makes between the temperature of mixture reaches 1530 DEG C -1550 DEG C, to keep this temperature
23-25 hours, mixture is made to reach molten condition, obtain brown-green glass melt;
(2)Brown-green glass melt is sent into mold, brown-green glass lamp shade is made, by brown-green glass lamp shade Temperature fall
Annealing kiln is sent into conveyer after to 600 DEG C of hardening, the time of 2-2.5 hours is passed through in annealing kiln, temperature is dropped from 600 DEG C
To 150 DEG C, annealing at this time finishes, and brown-green glass lamp shade is sent into air, naturally cools to room temperature in air;
(3)Brown-green glass lamp shade is sent into frosting pond and sprays black glass lampshade 4-5 minutes with frosting liquor, frosting technique knot
Beam is cleaned up brown-green glass lamp shade with water after frosting;
(4)Brown-green mat glass lampshade after frosting is sent into tempering case, brown-green mat glass lampshade is first heated to 660
Between DEG C -680 DEG C, stop heating, be sent into cold wind from all directions immediately, be rapidly cooled to brown-green mat glass lampshade often
Wen Hou, tempering terminate, and brown-green mat glass lampshade from tempering case is taken out, obtains finished product.
Above-mentioned steps(1)Described in continuous induction melting furnace be electric smelter.
The beneficial effects of the invention are as follows:Provide a kind of brown-green mat glass lamp made using frosting liquor frosting technique
Cover, the production method have simple for process, raw material sources are convenient, production cost is low, it is pollution-free, be suitble to industrialized production etc. one
Number of advantages;Product is a kind of refined lampshade, with it is exquisite in workmanship, specious, hardness is high, with it is dim sense, chemically
Can be stable, surface is smooth easy clean the advantages that.
Specific embodiment
With reference to specific embodiment, the present invention is described in further detail.
Embodiment 1
Real estate quartz sand that total amount is 32% will be accounted for, sodium carbonate that total amount is 12% is accounted for, accounts for the broken glass of purchase brown that total amount is 15%
Glass, account for green cullet of purchase that total amount is 15%, account for calcite that total amount is 11%, account for aluminium hydroxide that total amount is 10%, account for it is total
It measures the sodium nitrate for 2%, account for total amount the barium carbonate for being 1%, account for that oxygen sodium metasilicate that total amount is 0.7%, to account for the member that total amount is 0.3% bright
Powder accounts for that selenium powder that total amount is 0.9%, accounting for the cobalt powder that total amount is 0.1%, to be sent into blender blending uniform, by conveyer by mixture
Continuous induction melting furnace is sent into, power transmission heats after sealing, and the temperature of mixture is made to reach 1530 DEG C, keeps this temperature 25 hours, makes mixture
Reach molten condition, obtain brown-green glass melt;Brown-green glass melt is sent into mold, brown-green Glass lamp is made
Brown-green glass lamp shade is naturally cooling to be sent into annealing kiln with conveyer after 600 DEG C of hardening by cover, small by 2 in annealing kiln
When time, temperature is down to 150 DEG C from 600 DEG C, at this time annealing finish, by brown-green glass lamp shade be sent into air in, in sky
Room temperature is naturally cooled in gas;Brown-green glass lamp shade is sent into frosting pond and is divided with frosting liquor spray black glass lampshade 4-5
Clock, frosting technique terminate, and are cleaned up brown-green glass lamp shade with water after frosting;By the brown-green mat glass lamp after frosting
Cover is sent into tempering case, and brown-green mat glass lampshade first is heated to 660 DEG C, stops heating, is sent into immediately from all directions cold
Wind, after brown-green mat glass lampshade is cooled to room temperature rapidly, tempering terminates, by brown-green mat glass lampshade from tempering case
Middle taking-up, obtains finished product.
Embodiment 2
Real estate quartz sand that total amount is 33% will be accounted for, sodium carbonate that total amount is 11% is accounted for, accounts for the broken glass of purchase brown that total amount is 15%
Glass, account for green cullet of purchase that total amount is 15%, account for calcite that total amount is 11%, account for aluminium hydroxide that total amount is 10%, account for it is total
It measures the sodium nitrate for 2%, account for total amount the barium carbonate for being 1%, account for that oxygen sodium metasilicate that total amount is 0.7%, to account for the member that total amount is 0.3% bright
Powder accounts for that selenium powder that total amount is 0.9%, accounting for the cobalt powder that total amount is 0.1%, to be sent into blender blending uniform, by conveyer by mixture
Continuous induction melting furnace is sent into, power transmission heats after sealing, and the temperature of mixture is made to reach 1540 DEG C, keeps this temperature 24 hours, makes mixture
Reach molten condition, obtain brown-green glass melt;Brown-green glass melt is sent into mold, brown-green Glass lamp is made
Brown-green glass lamp shade is naturally cooling to be sent into annealing kiln with conveyer after 600 DEG C of hardening by cover, small by 2 in annealing kiln
When time, temperature is down to 150 DEG C from 600 DEG C, at this time annealing finish, by brown-green glass lamp shade be sent into air in, in sky
Room temperature is naturally cooled in gas;Brown-green glass lamp shade is sent into frosting pond and is divided with frosting liquor spray black glass lampshade 4-5
Clock, frosting technique terminate, and are cleaned up brown-green glass lamp shade with water after frosting;By the brown-green mat glass lamp after frosting
Cover is sent into tempering case, and brown-green mat glass lampshade first is heated to 670 DEG C, stops heating, is sent into immediately from all directions cold
Wind, after brown-green mat glass lampshade is cooled to room temperature rapidly, tempering terminates, by brown-green mat glass lampshade from tempering case
Middle taking-up, obtains finished product.
Embodiment 3
Real estate quartz sand that total amount is 34% will be accounted for, sodium carbonate that total amount is 10% is accounted for, accounts for the broken glass of purchase brown that total amount is 15%
Glass, account for green cullet of purchase that total amount is 15%, account for calcite that total amount is 11%, account for aluminium hydroxide that total amount is 10%, account for it is total
It measures the sodium nitrate for 2%, account for total amount the barium carbonate for being 1%, account for that oxygen sodium metasilicate that total amount is 0.7%, to account for the member that total amount is 0.3% bright
Powder accounts for that selenium powder that total amount is 0.9%, accounting for the cobalt powder that total amount is 0.1%, to be sent into blender blending uniform, by conveyer by mixture
Continuous induction melting furnace is sent into, power transmission heats after sealing, and the temperature of mixture is made to reach 1550 DEG C, keeps this temperature 25 hours, makes mixture
Reach molten condition, obtain brown-green glass melt;Brown-green glass melt is sent into mold, brown-green Glass lamp is made
Brown-green glass lamp shade is naturally cooling to be sent into annealing kiln with conveyer after 600 DEG C of hardening by cover, small by 2 in annealing kiln
When time, temperature is down to 150 DEG C from 600 DEG C, at this time annealing finish, by brown-green glass lamp shade be sent into air in, in sky
Room temperature is naturally cooled in gas;Brown-green glass lamp shade is sent into frosting pond and is divided with frosting liquor spray black glass lampshade 4-5
Clock, frosting technique terminate, and are cleaned up brown-green glass lamp shade with water after frosting;By the brown-green mat glass lamp after frosting
Cover is sent into tempering case, and brown-green mat glass lampshade first is heated to 680 DEG C, stops heating, is sent into immediately from all directions cold
Wind, after brown-green mat glass lampshade is cooled to room temperature rapidly, tempering terminates, by brown-green mat glass lampshade from tempering case
Middle taking-up, obtains finished product.
Claims (2)
1. a kind of brown-green mat glass lampshade made using frosting liquor frosting technique, composition of raw materials is by weight percentage
It calculates, including:Real estate quartz sand 32%-34%, sodium carbonate 10%-12%, purchase brown cullet 15%, the green cullet 15% of purchase,
Calcite 11%, aluminium hydroxide 10%, sodium nitrate 2%, barium carbonate 1%, oxygen sodium metasilicate 0.7%, anhydrous sodium sulphate 0.3%, selenium powder 0.9%, cobalt powder
0.1%;It is characterized in that:
(1)By the real estate quartz sand of formula ratio, sodium carbonate, purchase brown cullet, the green cullet of purchase, calcite, hydrogen-oxygen
Change aluminium, sodium nitrate, barium carbonate, oxygen sodium metasilicate, anhydrous sodium sulphate, selenium powder, cobalt powder and be sent into blender blending uniformly, it will be mixed by conveyer
It closes material and is sent into continuous induction melting furnace, power transmission heats after sealing, makes between the temperature of mixture reaches 1530 DEG C -1550 DEG C, to keep this temperature
23-25 hours, mixture is made to reach molten condition, obtain brown-green glass melt;
(2)Brown-green glass melt is sent into mold, brown-green glass lamp shade is made, by brown-green glass lamp shade Temperature fall
Annealing kiln is sent into conveyer after to 600 DEG C of hardening, the time of 2-2.5 hours is passed through in annealing kiln, temperature is dropped from 600 DEG C
To 150 DEG C, annealing at this time finishes, and brown-green glass lamp shade is sent into air, naturally cools to room temperature in air;
(3)Brown-green glass lamp shade is sent into frosting pond and sprays black glass lampshade 4-5 minutes with frosting liquor, frosting technique knot
Beam is cleaned up brown-green glass lamp shade with water after frosting;
(4)Brown-green mat glass lampshade after frosting is sent into tempering case, brown-green mat glass lampshade is first heated to 660
Between DEG C -680 DEG C, stop heating, be sent into cold wind from all directions immediately, be rapidly cooled to brown-green mat glass lampshade often
Wen Hou, tempering terminate, and brown-green mat glass lampshade from tempering case is taken out, obtains finished product.
2. a kind of brown-green mat glass lampshade made using frosting liquor frosting technique according to claim 1, special
Sign is:Step(1)Described in continuous induction melting furnace electric smelter.