CN108193508A - A kind of nylon-cotton fabric flame retardant type textile technology - Google Patents
A kind of nylon-cotton fabric flame retardant type textile technology Download PDFInfo
- Publication number
- CN108193508A CN108193508A CN201611123832.8A CN201611123832A CN108193508A CN 108193508 A CN108193508 A CN 108193508A CN 201611123832 A CN201611123832 A CN 201611123832A CN 108193508 A CN108193508 A CN 108193508A
- Authority
- CN
- China
- Prior art keywords
- nylon
- cotton fabric
- cotton
- fabric
- flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of nylon-cotton fabric flame retardant type textile technology, point comb：Bright and beautiful cotton block is resolved into single fiber state, improves straightening of fibers, parastate；Removal of impurities：Removes cotton fine impurities in the block and short flannel make fiber further full and uniform mixing；Winder：Process carries out on bobbin-winding machine, and the nylon-cotton fabric obtained in Textile Engineering is continued, and is wound into even density, shapes the good, bobbin convenient for moving back solution；It pads：Nylon-cotton fabric after cleaning is put into pad in working solution, an immersing and rolling processing is carried out by padding machine；The scrim surfaces got ready are coated into flame-retardant expanded coating.The invention uses coating good flame retardation effect, it is a kind of green product, suitable for industrial-scale production, and the cottons brocade fabric such as antiseptic, deodorant, antistatic agent by being added in process is padded be not only able to it is antistatic convenient for dress and also have the functions such as antibacterial, deodorization, effectively improve the practical performance of cotton brocade fabric.
Description
Technical field
The invention belongs to textile technology field, more particularly, to a kind of nylon-cotton fabric flame retardant type textile technology.
Background technology
Conventional fabrics function is single at present, especially in particular circumstances, functional fabric is required just increasingly stronger；
Although traditional fabric also has flame-retardant nature, thermal insulation is not strong；So a kind of not only fire-retardant but also heat-insulated fabric is just needed,
To protect the personal safety of people.Meanwhile the dyeing method of existing fabric, it is not environmentally friendly enough, and dyeing is uneven, is also easy to
Color.Therefore good textile should have following factor：Comfort type, taste, different appearance fabrics, the fabric for meeting fashion trends
Physical property, sale label etc..Ideal fabric is that some combines this, this means that the various fibrous roots of mixing
Best product is made according to our requirement.With the continuous development of textile technology, textile fabric is just from economical and practical to structure
Lightening, style trends are developed using functionalization, health environment-friendlyization, thus mix the exploitation of flame retardant type textile technology
It is the inexorable trend of weaving development.
Invention content
In view of this, the invention is directed to a kind of nylon-cotton fabric flame retardant type textile technology, to solve conventional fabrics
The shortcomings of function is single, and anti-flaming thermal-insulation effect is poor, and comfort level is poor, of high cost.
In order to achieve the above objectives, the technical solution of the invention is realized in：
A kind of nylon-cotton fabric flame retardant type textile technology, 1. divides comb：Bright and beautiful cotton block is resolved into single fiber state, improves fiber and stretches
Directly, parastate；2. it cleans：Removes cotton fine impurities in the block and short flannel make fiber further full and uniform mixing；3. network
Cylinder：Process carries out on bobbin-winding machine, and the nylon-cotton fabric obtained in Textile Engineering is continued, and in the process, makes to knit
Object obtains appropriate, uniform tension；By defined requirement, flaw, impurity and dust, clear flaw mistake are checked and removed
Small and strong tieing is formed in journey；Be wound into even density, capacity fully, forming is good, the bobbin convenient for moving back solution；4. by bright and beautiful
Cotton fabric carries out pretreatment work, spare as base fabric；5. it dyes：Base fabric is subjected to dyeing processing, is specially put into base fabric
In the clear water of overflow dyeing machine, active dye liquor is gradually added into clear water, after carrying out fixation treatment, dyeing semi-finished product are made；It 6. will dye
Color semi-produced fabric merging bath raio is 1:In 2 dye vat, when water temperature rises to 50 DEG C, the ricinoleic acid butyl ester sulfuric acid of 8g/L is added in
Sodium, the natural dye of 14g/L, 4g/L methyltrimethoxysilane, PH adjusted to 3.6, heated up with the heating rate of 6 DEG C/min
To 66 DEG C, 2 hours are kept the temperature, completes dyeing；7. it cleans：Nylon-cotton fabric is put into 45-50 DEG C of liquid of soaping and soaped, soaped
Time is 18-28min；8. it pads：Nylon-cotton fabric after cleaning is put into pad in working solution, an immersing and rolling is carried out by padding machine
Processing, pads 45-55 DEG C of the temperature of working solution, pH 5-6, and an immersing and rolling is that the rotating speed of padding machine is 13-17r/min, pick-up
80%；9. it is coated with flame-retardant expanded coating：Flame-retardant expanded coating is coated in ready scrim surfaces.
Further, the working solution that pads contains：Waterproofing agent：3.5g/L；Penetrating agent JFC：4.5g/L；Softening agent：1.9g/
L；Antiseptic：1.4g/L；HAC：2g/L；Deodorant 1g/L；Antistatic agent：2g/L.
Further, the deodorant is activated carbon, and the antistatic agent is the cruel amine of oxygroup bay.
Further, dewatered drying is carried out after flame-retardant expanded coating is coated with, nylon-cotton fabric is dried using dryer,
98~130 DEG C of drying temperature, 1.5~2 hours time.
Further, the flame-retardant expanded coating is Flame-retardant acrylic acid esters lotion.
Further, the Flame-retardant acrylic acid esters lotion is coated in using spraying method on nylon-cotton fabric.
Further, after being dried to nylon-cotton fabric, sizing treatment, 115 DEG C of setting temperature are carried out, locomotive rotating speed is
65m/min。
Further, after sizing treatment, clot processing is carried out, the nylon-cotton fabric is subjected to clot by coiler.
Relative to the prior art, a kind of nylon-cotton fabric flame retardant type textile technology described in the invention has following excellent
Gesture：
(1) flame-retardant expanded coating effect is good used in this technique, and the body of energy effective protection people escapes injury, elasticity
Good, at low cost, washing fastness and color fastness are excellent.
(2) in this technique manufacturing process, do not discharge harmful substance, be not only a kind of green product, and finished product
Flexible, breathable, production efficiency is high, and simple for process, simple operation can promote the use of.
(3) present invention by cottons brocade fabrics such as the antiseptics, deodorant, antistatic agent that are added in process is padded not
But can be antistatic convenient for wearing and having the functions such as antibacterial, deodorization, effectively improve the practical performance of cotton brocade fabric.
Description of the drawings
The attached drawing for forming the part of the invention is used for providing further understanding the invention, present invention wound
The illustrative embodiments and their description made do not form the improper restriction to the invention for explaining the invention.
In attached drawing：
Fig. 1 is the process flow diagram of the invention.
Specific embodiment
It should be noted that in the absence of conflict, the feature in embodiment and embodiment in the invention can
To be combined with each other.
In the description of the invention, it is to be understood that term " " center ", " longitudinal direction ", " transverse direction ", " on ", " under ",
The orientation or position relationship of the instructions such as "front", "rear", "left", "right", " vertical ", " level ", " top ", " bottom ", " interior ", " outer " are
Based on orientation shown in the drawings or position relationship, it is for only for ease of description the invention and simplifies description rather than instruction
Or imply that signified device or element there must be specific orientation, with specific azimuth configuration and operation, therefore be not understood that
For the limitation to the invention.In addition, term " first ", " second " etc. are only used for description purpose, and it is not intended that instruction
Or imply relative importance or the implicit quantity for indicating indicated technical characteristic." first ", " second " etc. are defined as a result,
Feature can express or implicitly include one or more this feature.In the description of the invention, unless separately
It is described, " multiple " are meant that two or more.
In the description of the invention, it should be noted that unless otherwise clearly defined and limited, term " peace
Dress ", " connected ", " connection " should be interpreted broadly, for example, it may be being fixedly connected or being detachably connected or integrally
Connection；Can be mechanical connection or electrical connection；It can be directly connected, can also be indirectly connected by intermediary,
It can be the connection inside two elements.For the ordinary skill in the art, on being understood by concrete condition
State concrete meaning of the term in the invention.
The present invention will be described in detail below with reference to the accompanying drawings and in conjunction with the embodiments creates.
A kind of nylon-cotton fabric flame retardant type textile technology, 1. divides comb：Bright and beautiful cotton block is resolved into single fiber state, improves fiber and stretches
Directly, parastate；2. it cleans：Removes cotton fine impurities in the block and short flannel make fiber further full and uniform mixing；3. network
Cylinder：Process carries out on bobbin-winding machine, and the nylon-cotton fabric obtained in Textile Engineering is continued, and in the process, makes to knit
Object obtains appropriate, uniform tension；By defined requirement, flaw, impurity and dust, clear flaw process are checked and removed
It is middle to form small and strong tieing；Be wound into even density, capacity fully, forming is good, the bobbin convenient for moving back solution；4. by bright and beautiful cotton
Fabric carries out pretreatment work, spare as base fabric；5. it dyes：Base fabric is subjected to dyeing processing, base fabric is specially put into dye
In the clear water of color machine, active dye liquor is gradually added into clear water, after carrying out fixation treatment, dyeing semi-finished product are made；It 6. will dyeing
Semi-produced fabric merging bath raio is 1:In 2 dye vat, when water temperature rises to 50 DEG C, add in 8g/L ricinoleic acid butyl ester sodium sulphate,
The natural dye of 14g/L, the methyltrimethoxysilane of 4g/L, PH are adjusted to 3.6, are warming up to the heating rate of 6 DEG C/min
66 DEG C, 2 hours are kept the temperature, completes dyeing；7. it cleans：Nylon-cotton fabric is put into 45-50 DEG C of liquid of soaping and soaped, when soaping
Between be 18-28min；8. it pads：Nylon-cotton fabric after cleaning is put into pad in working solution and is carried out at an immersing and rolling by padding machine
Reason, pads 45-55 DEG C of the temperature of working solution, pH 5-6, and an immersing and rolling is that the rotating speed of padding machine is 13-17r/min, pick-up
80%；9. it is coated with flame-retardant expanded coating：Flame-retardant expanded coating is coated in ready scrim surfaces.
Wherein, the working solution that pads contains：Waterproofing agent：3.5g/L；Penetrating agent JFC：4.5g/L；Softening agent：1.9g/L；
Antiseptic：1.4g/L；HAC：2g/L；Deodorant 1g/L；Antistatic agent：2g/L.
It should be noted that the deodorant is activated carbon, the antistatic agent is the cruel amine of oxygroup bay.
Wherein, dewatered drying is carried out after flame-retardant expanded coating is coated with, nylon-cotton fabric is dried using dryer, dried
Dry 98~130 DEG C of temperature, 1.5~2 hours time.
Wherein, the flame-retardant expanded coating is Flame-retardant acrylic acid esters lotion.
Wherein, the Flame-retardant acrylic acid esters lotion is coated in using spraying method on nylon-cotton fabric.
Separately it should be noted that, after being dried to nylon-cotton fabric, sizing treatment, 115 DEG C of setting temperature are carried out, locomotive turns
Speed is 65m/min.
Wherein, after sizing treatment, clot processing is carried out, the nylon-cotton fabric is subjected to clot by coiler.
The foregoing is merely the preferred embodiments of the invention, are not intended to limit the invention creation, all at this
Within the spirit and principle of innovation and creation, any modification, equivalent replacement, improvement and so on should be included in the invention
Protection domain within.
Claims (8)
1. a kind of nylon-cotton fabric flame retardant type textile technology, it is characterised in that：
1. divide comb：Bright and beautiful cotton block is resolved into single fiber state, improves straightening of fibers, parastate；
2. it cleans：Removes cotton fine impurities in the block and short flannel make fiber further full and uniform mixing；
3. winder：Process carries out on bobbin-winding machine, and the nylon-cotton fabric obtained in Textile Engineering is continued, in this process
In, fabric is made to obtain appropriate, uniform tension；By defined requirement, check and remove flaw, impurity and dust, clearly
Small and strong tieing is formed during flaw；Be wound into even density, capacity fully, forming is good, the bobbin convenient for moving back solution；
4. nylon-cotton fabric is carried out into pretreatment work, it is spare as base fabric；
5. it dyes：Base fabric is subjected to dyeing processing, specially base fabric is put into the clear water of overflow dyeing machine, is gradually added into clear water
After carrying out fixation treatment, dyeing semi-finished product are made in active dye liquor；
6. it is 1 by dyeing semi-produced fabric merging bath raio:In 2 dye vat, when water temperature rises to 50 DEG C, the ricinoleic acid of 8g/L is added in
Butyl ester sodium sulphate, the natural dye of 14g/L, 4g/L methyltrimethoxysilane, PH adjusted to 3.6, with the heating of 6 DEG C/min
Speed is warming up to 66 DEG C, keeps the temperature 2 hours, completes dyeing；
7. it cleans：Nylon-cotton fabric is put into 45-50 DEG C of liquid of soaping and soaped, the time of soaping is 18-28min；
8. it pads：Nylon-cotton fabric after cleaning is put into pad in working solution, an immersing and rolling processing is carried out by padding machine, pad work
Make 45-55 DEG C of the temperature of liquid, pH 5-6, an immersing and rolling is that the rotating speed of padding machine is 13-17r/min, pick-up 80%；
9. it is coated with flame-retardant expanded coating：Flame-retardant expanded coating is coated in ready scrim surfaces.
2. a kind of nylon-cotton fabric flame retardant type textile technology according to claim 1, it is characterised in that：It is described to pad working solution
Contain：Waterproofing agent：3.5g/L；Penetrating agent JFC：4.5g/L；Softening agent：1.9g/L；Antiseptic：1.4g/L；HAC：2g/L；Deodorization
Agent 1g/L；Antistatic agent：2g/L.
3. a kind of nylon-cotton fabric flame retardant type textile technology according to claim 2, it is characterised in that：The deodorant is lives
Property charcoal, the antistatic agent be the cruel amine of oxygroup bay.
4. a kind of nylon-cotton fabric flame retardant type textile technology according to claim 1, it is characterised in that：It is flame-retardant expanded being coated with
Dewatered drying is carried out after coating, nylon-cotton fabric is dried using dryer, 98~130 DEG C of drying temperature, the time 1.5~2
Hour.
5. a kind of nylon-cotton fabric flame retardant type textile technology according to claim 1, it is characterised in that：The flame-retardant expanded painting
Expect for Flame-retardant acrylic acid esters lotion.
6. a kind of nylon-cotton fabric flame retardant type textile technology according to claim 4, it is characterised in that：The flame retardant type propylene
Esters of gallic acid lotion is coated in using spraying method on nylon-cotton fabric.
7. a kind of nylon-cotton fabric flame retardant type textile technology according to claim 1, it is characterised in that：To nylon-cotton fabric into
After row drying, sizing treatment, 115 DEG C of setting temperature are carried out, locomotive rotating speed is 65m/min.
8. a kind of nylon-cotton fabric flame retardant type textile technology according to claim 7, it is characterised in that：After sizing treatment, into
Row clot is handled, and the nylon-cotton fabric is carried out clot by coiler.