CN108166155A - A kind of preparation method of non-woven fabrics shower cap - Google Patents
A kind of preparation method of non-woven fabrics shower cap Download PDFInfo
- Publication number
- CN108166155A CN108166155A CN201711449688.1A CN201711449688A CN108166155A CN 108166155 A CN108166155 A CN 108166155A CN 201711449688 A CN201711449688 A CN 201711449688A CN 108166155 A CN108166155 A CN 108166155A
- Authority
- CN
- China
- Prior art keywords
- shower cap
- woven fabrics
- drier
- preparation
- antiseptic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of non-woven fabrics shower cap, by the way that antiseptic and drier are added in terylene chips, the non-woven fabrics shower cap being prepared not only has extraordinary durable antibiotic, uvioresistant, indeformable performance, even if but also it can ensure during bathing, hair in shower cap keeps dry for a long time, prevents hair from itching, situations such as peculiar smell occurs；Using nano silver antimicrobials, it can achieve the effect that durable antibiotic；Aqueous polyurethane waterproofing agent is added in, not only good water-proof effect, and be added without organic solvent is safe and environment-friendly；Expanded vermiculite powder and carbon molecular sieve are used in conjunction with, as drier, since its density is low, a large amount of surfaces for being distributed in terylene chips, the moisture in shower cap can be effectively adsorbed, peculiar smell can also be adsorbed, effect is good, and clean, dry after can be iteratively repeated use, overcome the shortcomings that traditional shower cap is disposable.
Description
Technical field
The present invention relates to daily necessities technical field more particularly to a kind of preparation methods of non-woven fabrics shower cap.
Background technology
Non-woven fabrics (English name：Non Woven Fabric or Nonwoven cloth) nonwoven fabric is also known as, it is by orienting
Or random fiber and form.Cloth is called due to the appearance with cloth and certain performances.
Non-woven fabrics have it is moisture-proof, ventilative, flexible, light, not combustion-supporting, easy decompose, it is nontoxic it is nonirritant, rich in color,
The features such as cheap, recyclable.If used polypropylene (pp materials) pellet as raw material, through high-temperature fusion, spinneret, paving more
Guiding principle, hot pressing are batched continuous one-step and are produced.
Non-woven fabrics has the following advantages that：
It is 1. light：Using acrylic resin as main production raw material, proportion only 0.9, only 3/5ths of cotton have fluffy
Property, good hand touch.
It is 2. soft：(2~3D) is formed by fine fibre and dubs the molding of shape hot melting cohesion.Finished product pliability is moderate, has comfort.
3. water repellent is breathed freely：Polypropylene chip does not absorb water, and moisture content zero, finished product water-repellancy is good, and tool is formed by 100% fiber
Porosity, gas permeability is good, and easy holding cloth cover is dry and comfortable, uncomplicated laundering.
It is 4. nontoxic, nonirritant:Product is using the production of FDA food grade materials is met, and without other chemical compositions, performance is steady
Fixed, nontoxic, free from extraneous odour does not stimulate skin.
5. antibacterial, anti-chemical agent：Polypropylene category inactivity substance, does not damage by worms, and can be isolated that there are liquid Endophytic bacterias
And the erosion of insects；Antibacterial, caustic corrosion, finished product do not influence intensity due to erosion.
6. antibiotic property.Product tool pull out it is aqueous, it is not mouldy, and the erosion there are liquid Endophytic bacteria and insects can be isolated, it is not mould
Moth.
7. physical property is good.Net hot adhesion is directly paved by polypropylene spinning to form, the relatively general short fine product of product strength is preferred,
Intensity is non-directional, and vertical transverse strength is close.
8. in terms of environmental protection, the raw material of most of non-woven fabrics used are polypropylene, and the raw material of polybag are poly-
Ethylene although two kinds of substance names are similar, differs greatly in chemical constitution.The chemical molecular structure of polyethylene has phase
When strong stability, it is extremely difficult to degrade, so polybag needs 300 years ability decomposable asymmetric choice nets to finish；And polyacrylic chemical constitution is loosely
Gu strand is easy for be broken, so as to effectively degrade, and followed in nontoxic form into next step environment
Ring, a non-woven fabric shopping bag can be decomposed thoroughly in 90 days.And reusable 10 times of non-woven fabric shopping bag or more,
Also there was only the 10% of polybag after discarded to the dustiness of environment.
Non-woven fabrics is applied to the important use that daily necessities are non-woven fabrics, the present invention provides a kind of showers of non-woven fabrics
The preparation method of cap.
Invention content
Technical problems based on background technology, the present invention propose a kind of preparation method of non-woven fabrics shower cap.
Technical scheme is as follows：
A kind of preparation method of non-woven fabrics shower cap, includes the following steps：
A, prepared by slice：Antiseptic and drier are put into the DTY formative memory terylene chips of molten state, stirred evenly
Afterwards, room temperature is reduced to, obtains hybrid slicing；
B, hybrid slicing conveys：Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder；
C, it squeezes：Hybrid slicing enters twin (double) screw extruder, hybrid slicing melted by heating, vacuum suction melt institute by gravity
Containing excess polymer, final uniformly mixed and discharging of pressurizeing；
D, fondant filter filters：The melt for going out extruder first removes impurity, and through static mixer through pot strainer
It is further uniformly mixed, subsequently into spinning system；
E, spinning：On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, again through spinneret after filtering, even pressure
Plate is sprayed in thread shape, and silk is consolidated into the cooling of quenching area；
F, networking：Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, spreads
Silk networking, and it is fed forward to spun lacing area；
G, spun lacing：It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing；
H, water-proofing treatment：It carries out prebake dehydration and water-proofing treatment is carried out using waterproofing agent in nonwoven surface；
I, cutting is batched：The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
Preferably, in the step A, the antiseptic is nano silver antimicrobials.
Preferably, in the step A, the drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
Preferably, in the step A, antiseptic and drier are in the DTY formative memory terylene chips for adding in molten state
Before, drying to moisture content is needed to be less than 1%.
Preferably, in the step A, the addition of antiseptic and drier is respectively 0.01-0.05% and 1-5%.
Preferably, in the step H, the waterproofing agent is aqueous polyurethane.
The invention has the beneficial effects that：The present invention provides a kind of preparation method of non-woven fabrics shower cap, by that will resist
Microbial inoculum and drier are added in terylene chips, the non-woven fabrics shower cap being prepared not only have extraordinary durable antibiotic,
Uvioresistant, indeformable performance, even if but also can ensure during bathing, the hair holding long-time in shower cap
It is dry, it prevents hair from itching, situations such as peculiar smell occur；Using nano silver antimicrobials, it can achieve the effect that durable antibiotic；Add in water
Property polyurethane water-proof agent, not only good water-proof effect, and be added without organic solvent are safe and environment-friendly；By expanded vermiculite powder and carbon point
Son sieve is used in conjunction with, and as drier, since its density is low, is largely distributed in the surface of terylene chips, can effectively be adsorbed and wash one's hair
Moisture in bathing cap can also adsorb peculiar smell, and effect is good, and clean, dry after can be iteratively repeated use, overcome tradition
Shower cap it is disposable lack.
Specific embodiment
Embodiment 1：
A kind of preparation method of non-woven fabrics shower cap, includes the following steps：
A, prepared by slice：Antiseptic and drier are put into the DTY formative memory terylene chips of molten state, stirred evenly
Afterwards, room temperature is reduced to, obtains hybrid slicing；
B, hybrid slicing conveys：Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder；
C, it squeezes：Hybrid slicing enters twin (double) screw extruder, hybrid slicing melted by heating, vacuum suction melt institute by gravity
Containing excess polymer, final uniformly mixed and discharging of pressurizeing；
D, fondant filter filters：The melt for going out extruder first removes impurity, and through static mixer through pot strainer
It is further uniformly mixed, subsequently into spinning system；
E, spinning：On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, again through spinneret after filtering, even pressure
Plate is sprayed in thread shape, and silk is consolidated into the cooling of quenching area；
F, networking：Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, spreads
Silk networking, and it is fed forward to spun lacing area；
G, spun lacing：It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing；
H, water-proofing treatment：It carries out prebake dehydration and water-proofing treatment is carried out using waterproofing agent in nonwoven surface；
I, cutting is batched：The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
In the step A, the antiseptic is nano silver antimicrobials.
In the step A, the drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
In the step A, antiseptic and drier need before the DTY formative memory terylene chips of molten state are added in
Drying to moisture content is less than 1%.
In the step A, the addition of antiseptic and drier is respectively 0.03% and 2.5%.
In the step H, the waterproofing agent is aqueous polyurethane.
Embodiment 2：
A kind of preparation method of non-woven fabrics shower cap, includes the following steps：
A, prepared by slice：Antiseptic and drier are put into the DTY formative memory terylene chips of molten state, stirred evenly
Afterwards, room temperature is reduced to, obtains hybrid slicing；
B, hybrid slicing conveys：Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder；
C, it squeezes：Hybrid slicing enters twin (double) screw extruder, hybrid slicing melted by heating, vacuum suction melt institute by gravity
Containing excess polymer, final uniformly mixed and discharging of pressurizeing；
D, fondant filter filters：The melt for going out extruder first removes impurity, and through static mixer through pot strainer
It is further uniformly mixed, subsequently into spinning system；
E, spinning：On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, again through spinneret after filtering, even pressure
Plate is sprayed in thread shape, and silk is consolidated into the cooling of quenching area；
F, networking：Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, spreads
Silk networking, and it is fed forward to spun lacing area；
G, spun lacing：It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing；
H, water-proofing treatment：It carries out prebake dehydration and water-proofing treatment is carried out using waterproofing agent in nonwoven surface；
I, cutting is batched：The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
In the step A, the antiseptic is nano silver antimicrobials.
In the step A, the drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
In the step A, antiseptic and drier need before the DTY formative memory terylene chips of molten state are added in
Drying to moisture content is less than 1%.
In the step A, the addition of antiseptic and drier is respectively 0.01% and 1%.
In the step H, the waterproofing agent is aqueous polyurethane.
Embodiment 3：
A kind of preparation method of non-woven fabrics shower cap, includes the following steps：
A, prepared by slice：Antiseptic and drier are put into the DTY formative memory terylene chips of molten state, stirred evenly
Afterwards, room temperature is reduced to, obtains hybrid slicing；
B, hybrid slicing conveys：Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder；
C, it squeezes：Hybrid slicing enters twin (double) screw extruder, hybrid slicing melted by heating, vacuum suction melt institute by gravity
Containing excess polymer, final uniformly mixed and discharging of pressurizeing；
D, fondant filter filters：The melt for going out extruder first removes impurity, and through static mixer through pot strainer
It is further uniformly mixed, subsequently into spinning system；
E, spinning：On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, again through spinneret after filtering, even pressure
Plate is sprayed in thread shape, and silk is consolidated into the cooling of quenching area；
F, networking：Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, spreads
Silk networking, and it is fed forward to spun lacing area；
G, spun lacing：It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing；
H, water-proofing treatment：It carries out prebake dehydration and water-proofing treatment is carried out using waterproofing agent in nonwoven surface；
I, cutting is batched：The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
In the step A, the antiseptic is nano silver antimicrobials.
In the step A, the drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
In the step A, antiseptic and drier need before the DTY formative memory terylene chips of molten state are added in
Drying to moisture content is less than 1%.
In the step A, the addition of antiseptic and drier is respectively 0.05% and 5%.
In the step H, the waterproofing agent is aqueous polyurethane.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. a kind of preparation method of non-woven fabrics shower cap, which is characterized in that include the following steps：
A, prepared by slice：Antiseptic and drier are put into the DTY formative memory terylene chips of molten state, after stirring evenly,
Room temperature is reduced to, obtains hybrid slicing；
B, hybrid slicing conveys：Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder；
C, it squeezes：Hybrid slicing enters twin (double) screw extruder by gravity, and hybrid slicing melted by heating is sucked by vacuum more contained by melt
Remaining polymer, final uniformly mixed and discharging of pressurizeing；
D, fondant filter filters：Go out the melt of extruder and first remove impurity through pot strainer, and through static mixer into one
Step is uniformly mixed, subsequently into spinning system；
E, spinning：On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, is in through spinneret after filtering, even pressure again
Thread shape sprays, and silk is consolidated into the cooling of quenching area；
F, networking：Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, piddler into
Net, and it is fed forward to spun lacing area；
G, spun lacing：It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing；
H, water-proofing treatment：It carries out prebake dehydration and water-proofing treatment is carried out using waterproofing agent in nonwoven surface；
I, cutting is batched：The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
2. the preparation method of non-woven fabrics shower cap as described in claim 1, which is characterized in that described in the step A
Antiseptic is nano silver antimicrobials.
3. the preparation method of non-woven fabrics shower cap as described in claim 1, which is characterized in that described in the step A
Drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
4. the preparation method of non-woven fabrics shower cap as described in claim 1, which is characterized in that in the step A, antiseptic
With drier before the DTY formative memory terylene chips of molten state are added in, drying to moisture content is needed to be less than 1%.
5. the preparation method of non-woven fabrics shower cap as described in claim 1, which is characterized in that in the step A, antiseptic
Addition with drier is respectively 0.01-0.05%, 1-5%.
6. the preparation method of non-woven fabrics shower cap as described in claim 1, which is characterized in that described in the step H
Waterproofing agent is aqueous polyurethane.