CN108166162A - A kind of preparation method of non-woven fabrics western-style clothes set - Google Patents
A kind of preparation method of non-woven fabrics western-style clothes set Download PDFInfo
- Publication number
- CN108166162A CN108166162A CN201711448109.1A CN201711448109A CN108166162A CN 108166162 A CN108166162 A CN 108166162A CN 201711448109 A CN201711448109 A CN 201711448109A CN 108166162 A CN108166162 A CN 108166162A
- Authority
- CN
- China
- Prior art keywords
- western
- style clothes
- woven fabrics
- preparation
- drier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation methods of non-woven fabrics western-style clothes set, by the way that antiseptic, UV resistant agent and drier are added in terylene chips, the non-woven fabrics western-style clothes set being prepared not only has extraordinary durable antibiotic, uvioresistant, indeformable performance, but also can ensure that the western-style clothes in western-style clothes set keeps dry for a long time, prevent that western-style clothes is mouldy, situations such as peculiar smell occurs;Using nano silver antimicrobials, it can achieve the effect that durable antibiotic;Spinel powder is added in, not only uvioresistant effect is good, and safe and environment-friendly;Expanded vermiculite powder and carbon molecular sieve are used in conjunction with, as drier, since its density is low, the surface of terylene chips is largely distributed in, can effectively adsorb the moisture in air, peculiar smell can also be adsorbed, effect is good, and clean, dry after can be iteratively repeated use.
Description
Technical field
The present invention relates to the preparation methods that daily necessities technical field more particularly to a kind of non-woven fabrics western-style clothes cover.
Background technology
Non-woven fabrics (English name:Non Woven Fabric or Nonwoven cloth) nonwoven fabric is also known as, it is by orienting
Or random fiber and form.Cloth is called due to the appearance with cloth and certain performances.
Non-woven fabrics have it is moisture-proof, ventilative, flexible, light, not combustion-supporting, easy decompose, it is nontoxic it is nonirritant, rich in color,
The features such as cheap, recyclable.If used polypropylene (pp materials) pellet as raw material, through high-temperature fusion, spinneret, paving more
Guiding principle, hot pressing are batched continuous one-step and are produced.
Non-woven fabrics has the following advantages that:
It is 1. light:Using acrylic resin as main production raw material, proportion only 0.9, only 3/5ths of cotton have fluffy
Property, good hand touch.
It is 2. soft:(2~3D) is formed by fine fibre and dubs the molding of shape hot melting cohesion.Finished product pliability is moderate, has comfort.
3. water repellent is breathed freely:Polypropylene chip does not absorb water, and moisture content zero, finished product water-repellancy is good, and tool is formed by 100% fiber
Porosity, gas permeability is good, and easy holding cloth cover is dry and comfortable, uncomplicated laundering.
It is 4. nontoxic, nonirritant:Product is using the production of FDA food grade materials is met, and without other chemical compositions, performance is steady
Fixed, nontoxic, free from extraneous odour does not stimulate skin.
5. antibacterial, anti-chemical agent:Polypropylene category inactivity substance, does not damage by worms, and can be isolated that there are liquid Endophytic bacterias
And the erosion of insects;Antibacterial, caustic corrosion, finished product do not influence intensity due to erosion.
6. antibiotic property.Product tool pull out it is aqueous, it is not mouldy, and the erosion there are liquid Endophytic bacteria and insects can be isolated, it is not mould
Moth.
7. physical property is good.Net hot adhesion is directly paved by polypropylene spinning to form, the relatively general short fine product of product strength is preferred,
Intensity is non-directional, and vertical transverse strength is close.
8. in terms of environmental protection, the raw material of most of non-woven fabrics used are polypropylene, and the raw material of polybag are poly-
Ethylene although two kinds of substance names are similar, differs greatly in chemical constitution.The chemical molecular structure of polyethylene has phase
When strong stability, it is extremely difficult to degrade, so polybag needs 300 years ability decomposable asymmetric choice nets to finish;And polyacrylic chemical constitution is loosely
Gu strand is easy for be broken, so as to effectively degrade, and followed in nontoxic form into next step environment
Ring, a non-woven fabric shopping bag can be decomposed thoroughly in 90 days.And reusable 10 times of non-woven fabric shopping bag or more,
Also there was only the 10% of polybag after discarded to the dustiness of environment.
Non-woven fabrics is applied to the important use that daily necessities are non-woven fabrics, the present invention provides a kind of non-woven fabrics western-style clothes
The preparation method of set.
Invention content
Technical problems based on background technology, the present invention propose a kind of preparation method of non-woven fabrics western-style clothes set.
Technical scheme is as follows:
A kind of preparation method of non-woven fabrics western-style clothes set, includes the following steps:
A, prepared by slice:Antiseptic, UV resistant agent and drier are put into the DTY formative memory terylene chips of molten state
In, after stirring evenly, room temperature is reduced to, obtains hybrid slicing;
B, hybrid slicing conveys:Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder;
C, it squeezes:Hybrid slicing enters twin (double) screw extruder, hybrid slicing melted by heating, vacuum suction melt institute by gravity
Containing excess polymer, final uniformly mixed and discharging of pressurizeing;
D, fondant filter filters:The melt for going out extruder first removes impurity, and through static mixer through pot strainer
It is further uniformly mixed, subsequently into spinning system;
E, spinning:On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, again through spinneret after filtering, even pressure
Plate is sprayed in thread shape, and silk is consolidated into the cooling of quenching area;
F, networking:Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, spreads
Silk networking, and it is fed forward to spun lacing area;
G, spun lacing:It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing;
H, it is dehydrated:Carry out prebake dehydration;
I, cutting is batched:The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
Preferably, in the step A, the antiseptic is nano silver antimicrobials.
Preferably, in the step A, the UV resistant agent is inorganic UV resistant agent.
Preferably, in the step A, the UV resistant agent is spinel powder.
Preferably, in the step A, the drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
Preferably, in the step A, antiseptic, UV resistant agent and drier are in the DTY forms note for adding in molten state
Before recalling terylene chips, drying to moisture content is needed to be less than 1%.
Preferably, in the step A, the addition of antiseptic, UV resistant agent and drier is respectively 0.01-
0.05%th, 0.2-0.8%, 1-5%.
The invention has the beneficial effects that:The present invention provides a kind of preparation method of non-woven fabrics western-style clothes set, by that will resist
Microbial inoculum, UV resistant agent and drier are added in terylene chips, and it is very good that the non-woven fabrics western-style clothes set being prepared not only has
Durable antibiotic, uvioresistant, indeformable performance, but also can ensure that the western-style clothes in western-style clothes set keeps dry for a long time,
Prevent that western-style clothes is mouldy, situations such as peculiar smell occurs;Using nano silver antimicrobials, it can achieve the effect that durable antibiotic;It is brilliant to add in point
Mountain flour, not only uvioresistant effect is good, and safe and environment-friendly;Expanded vermiculite powder and carbon molecular sieve are used in conjunction with, as drying
Agent since its density is low, is largely distributed in the surface of terylene chips, can effectively adsorb the moisture in air, can also adsorb
Peculiar smell, effect is good, and clean, dry after can be iteratively repeated use.
Specific embodiment
Embodiment 1:
A kind of preparation method of non-woven fabrics western-style clothes set, includes the following steps:
A, prepared by slice:Antiseptic, UV resistant agent and drier are put into the DTY formative memory terylene chips of molten state
In, after stirring evenly, room temperature is reduced to, obtains hybrid slicing;
B, hybrid slicing conveys:Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder;
C, it squeezes:Hybrid slicing enters twin (double) screw extruder, hybrid slicing melted by heating, vacuum suction melt institute by gravity
Containing excess polymer, final uniformly mixed and discharging of pressurizeing;
D, fondant filter filters:The melt for going out extruder first removes impurity, and through static mixer through pot strainer
It is further uniformly mixed, subsequently into spinning system;
E, spinning:On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, again through spinneret after filtering, even pressure
Plate is sprayed in thread shape, and silk is consolidated into the cooling of quenching area;
F, networking:Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, spreads
Silk networking, and it is fed forward to spun lacing area;
G, spun lacing:It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing;
H, it is dehydrated:Carry out prebake dehydration;
I, cutting is batched:The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
In the step A, the antiseptic is nano silver antimicrobials.
In the step A, the UV resistant agent is spinel powder.
In the step A, the drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
In the step A, antiseptic, UV resistant agent and drier are in the DTY formative memory terylene for adding in molten state
Before slice, drying to moisture content is needed to be less than 1%.
In the step A, the addition of antiseptic, UV resistant agent and drier is respectively 0.03%, 0.5%,
2.5%.
Embodiment 2:
A kind of preparation method of non-woven fabrics western-style clothes set, includes the following steps:
A, prepared by slice:Antiseptic, UV resistant agent and drier are put into the DTY formative memory terylene chips of molten state
In, after stirring evenly, room temperature is reduced to, obtains hybrid slicing;
B, hybrid slicing conveys:Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder;
C, it squeezes:Hybrid slicing enters twin (double) screw extruder, hybrid slicing melted by heating, vacuum suction melt institute by gravity
Containing excess polymer, final uniformly mixed and discharging of pressurizeing;
D, fondant filter filters:The melt for going out extruder first removes impurity, and through static mixer through pot strainer
It is further uniformly mixed, subsequently into spinning system;
E, spinning:On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, again through spinneret after filtering, even pressure
Plate is sprayed in thread shape, and silk is consolidated into the cooling of quenching area;
F, networking:Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, spreads
Silk networking, and it is fed forward to spun lacing area;
G, spun lacing:It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing;
H, it is dehydrated:Carry out prebake dehydration;
I, cutting is batched:The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
In the step A, the antiseptic is nano silver antimicrobials.
In the step A, the UV resistant agent is spinel powder.
In the step A, the drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
In the step A, antiseptic, UV resistant agent and drier are in the DTY formative memory terylene for adding in molten state
Before slice, drying to moisture content is needed to be less than 1%.
In the step A, the addition of antiseptic, UV resistant agent and drier is respectively 0.01%, 0.8%,
1%.
Embodiment 3:
A kind of preparation method of non-woven fabrics western-style clothes set, includes the following steps:
A, prepared by slice:Antiseptic, UV resistant agent and drier are put into the DTY formative memory terylene chips of molten state
In, after stirring evenly, room temperature is reduced to, obtains hybrid slicing;
B, hybrid slicing conveys:Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder;
C, it squeezes:Hybrid slicing enters twin (double) screw extruder, hybrid slicing melted by heating, vacuum suction melt institute by gravity
Containing excess polymer, final uniformly mixed and discharging of pressurizeing;
D, fondant filter filters:The melt for going out extruder first removes impurity, and through static mixer through pot strainer
It is further uniformly mixed, subsequently into spinning system;
E, spinning:On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, again through spinneret after filtering, even pressure
Plate is sprayed in thread shape, and silk is consolidated into the cooling of quenching area;
F, networking:Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, spreads
Silk networking, and it is fed forward to spun lacing area;
G, spun lacing:It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing;
H, it is dehydrated:Carry out prebake dehydration;
I, cutting is batched:The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
In the step A, the antiseptic is nano silver antimicrobials.
In the step A, the UV resistant agent is spinel powder.
In the step A, the drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
In the step A, antiseptic, UV resistant agent and drier are in the DTY formative memory terylene for adding in molten state
Before slice, drying to moisture content is needed to be less than 1%.
In the step A, the addition of antiseptic, UV resistant agent and drier is respectively 0.05%, 0.2%,
5%.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (7)
1. a kind of preparation method of non-woven fabrics western-style clothes set, which is characterized in that include the following steps:
A, prepared by slice:Antiseptic, UV resistant agent and drier are put into the DTY formative memory terylene chips of molten state,
After stirring evenly, room temperature is reduced to, obtains hybrid slicing;
B, hybrid slicing conveys:Hybrid slicing is transported to by air-flow in the feed stock chip hopper above extruder;
C, it squeezes:Hybrid slicing enters twin (double) screw extruder by gravity, and hybrid slicing melted by heating is sucked by vacuum more contained by melt
Remaining polymer, final uniformly mixed and discharging of pressurizeing;
D, fondant filter filters:Go out the melt of extruder and first remove impurity through pot strainer, and through static mixer into one
Step is uniformly mixed, subsequently into spinning system;
E, spinning:On the spinning-drawing machine of spinning system, melt is introduced into filament spinning component, is in through spinneret after filtering, even pressure again
Thread shape sprays, and silk is consolidated into the cooling of quenching area;
F, networking:Tow imports draft nozzle pneumatically and carries out high speed drawing-off, is then uniformly layered on transmission net, piddler into
Net, and it is fed forward to spun lacing area;
G, spun lacing:It first carries out wire side to prewet, subsequently into positive and negative multiple tracks spun lacing and decorative pattern spun lacing;
H, it is dehydrated:Carry out prebake dehydration;
I, cutting is batched:The drying that absorbs water again is cut by the breadth of setting, reaches automatic last volume during set amount.
2. the preparation method of non-woven fabrics western-style clothes set as described in claim 1, which is characterized in that described in the step A
Antiseptic is nano silver antimicrobials.
3. the preparation method of non-woven fabrics western-style clothes set as described in claim 1, which is characterized in that described in the step A
UV resistant agent is inorganic UV resistant agent.
4. the preparation method of non-woven fabrics western-style clothes set as claimed in claim 3, which is characterized in that described in the step A
UV resistant agent is spinel powder.
5. the preparation method of non-woven fabrics western-style clothes set as described in claim 1, which is characterized in that described in the step A
Drier is carbon molecular sieve and the mixture of expanded vermiculite powder.
6. the preparation method of non-woven fabrics western-style clothes set as described in claim 1, which is characterized in that in the step A, antibacterial
Agent, UV resistant agent and drier need drying to moisture content to be less than before the DTY formative memory terylene chips of molten state are added in
1%.
7. the preparation method of non-woven fabrics western-style clothes set as described in claim 1, which is characterized in that in the step A, antibacterial
The addition of agent, UV resistant agent and drier is respectively 0.01-0.05%, 0.2-0.8%, 1-5%.