CN108166077A - A kind of production method of antistatic silk core - Google Patents
A kind of production method of antistatic silk core Download PDFInfo
- Publication number
- CN108166077A CN108166077A CN201810143815.3A CN201810143815A CN108166077A CN 108166077 A CN108166077 A CN 108166077A CN 201810143815 A CN201810143815 A CN 201810143815A CN 108166077 A CN108166077 A CN 108166077A
- Authority
- CN
- China
- Prior art keywords
- silk
- layer
- cocoon
- core
- antistatic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of antistatic silk core, belong to bedding processing technique field.The production method of the antistatic silk core includes selecting silkworm, drying, softening, a pocket is made in silk cocoon after softening, silk pocket is pulled into rectangle silk screen, silk screen layer stackup is put, silk is pulled out from four angles of every pull spring net and the midpoint of four edges, and the silk twist-on that will be pulled out in adjacent silk screen, then mulberry silk layer will be obtained from the silk twist-on pulled out positioned at top layer and on undermost silk screen, finally one layer of reticulated conductive fibrous layer is sutured in the outer surface of mulberry silk layer.Present invention process is simple, while ensureing comfortable, warming, ventilative, can also prevent electrostatic, substantially increase the sleep quality of people.
Description
Technical field
The present invention relates to bedding processing technique fields, and in particular to a kind of production method of antistatic silk core.
Background technology
Silk quilt that is, using silk as the quilt of filler, has personal warming, fluffy soft, Breathable healthcare and helps sleep
Advantageous quality and the advantages such as dormancy, therefore the silk quilt being fabricated to using silk is favored by consumers in general very much.Silk
Mainly included the silk core made of silk, at present, the production method of silk core is mainly first that silk net is simple
It is superimposed to form silk core, then silk quilt core retainer plate is sewed in the outer layer of silk core, so as to make mulberry silk layer and silk
It is bonded by core retainer plate, but the silk core made in this way is easier loosely, the guarantor that will substantially reduce silk quilt in this way
It warms up ventilative and other effects.In addition, current silk core does not have anti-static effect, in day, the season of cool-drying, silk quilt hold very much
Generate electrostatic easily due to the friction with human body, human body can be made one under static radiation for a long time lather, headache, it is uncomfortable in chest and
Expiratory dyspnea etc., so as to influence to sleep.Therefore, it is necessary to a kind of silk core is provided securely and can antistatic silk core
Production method.
Invention content
The goal of the invention of the present invention is：In view of the above problems, a kind of making of antistatic silk core is provided
Method by being screened to silk cocoon, drying, the processes such as softening, then silk screen from level to level is made, will pull out silk on each layer silk screen
And the silk twist-on with being pulled out on adjacent bed silk screen, make to connect more securely between each layer silk screen, finally be stitched on the surface of mulberry silk layer
One layer of reticulated conductive fibrous layer is made, so as to play anti-static effect.
To achieve these goals, the technical solution adopted by the present invention is as follows：
A kind of production method of antistatic silk core, includes the following steps：
(1) bonscocoons is selected in silk cocoon, then bonscocoons is put into screening machine and is sieved, obtains big cocoon and small cocoon, by institute
State raw material of the big cocoon as silk core；
(2) the big cocoon in above-mentioned steps (1) is put into drying machine and be dried, the drying is：First, big cocoon is existed
6-10min is dried under conditions of 90-100 DEG C, big cocoon at a temperature of 55-65 DEG C is then dried into 10-15min, obtains dried cocoon；
(3) dried cocoon obtained in above-mentioned steps (2) is put and is impregnated into bating liquor, the temperature of the bating liquor is 85-92
DEG C, mixed aqueous solution of the bating liquor for fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perborate, the fatty alcohol polyoxy
The mass ratio of vinethene, sodium bicarbonate and sodium perborate is 1-1.5:2-3:1, after impregnating 50-70min, bating liquor is filtered out
It goes, is then washed repeatedly with 50-60 DEG C of cleaning solution, obtain softening cocoon；
(4) the softening cocoon obtained in above-mentioned steps (3) is torn, takes out silkworm chrysalis, then the softening cocoons by multiple taking-up silkworm chrysalises
It is sleeved on dilator and is strutted, dry 1-2h is to get to silk pocket at 90-100 DEG C；
(5) each pocket obtained in above-mentioned steps (4) is pulled into rectangle silk screen along four direction, it will be described in every
Long silk screen layer stacking is put, and silk is pulled out, and will be pulled out in adjacent silk screen from four angles of every pull spring net and the midpoint of four edges
The silk twist-on, then by from the silk twist-on pulled out positioned at top layer and on undermost silk screen, obtain rectangular
Body mulberry silk layer；
(6) reticulated conductive fibrous layer is woven into using conductive fiber, cut out described made from six pieces and above-mentioned steps (5)
Six pieces of reticulated conductive fibrous layers are layered on the silkworm by six faces reticulated conductive fibrous layer of the same size of mulberry silk layer
On six faces of silk layer, by four sides of the every piece of reticulated conductive fibrous layer reticulated conductive fiber adjacent with four pieces respectively
Layer suture, obtains fluffy silk core；
(7) carry out rubbing pressure respectively to the two sides of fluffy silk core that above-mentioned steps (6) obtain to get to antistatic silk
Core.
Further, the sieve diameter of screening machine described in step (1) is 3cm.
Further, the temperature of bating liquor described in step (3) is 90 DEG C, the fatty alcohol polyoxyethylene ether, bicarbonate
The mass ratio of sodium and sodium perborate is 1.2:2.5:1.
Further, cleaning solution described in step (3) is the ethanol solution that volume fraction is 68%-72%.
Further, the mesh diameter of reticulated conductive fibrous layer described in step (6) is 5-10mm, and the reticulated conductive is fine
The thickness for tieing up layer is 0.5-1mm.
Further, fiber is complexed for carbon composite fibre or acrylic fibers copper in the conductive fiber.
Further, rubbed described in step (7) briquetting include to the fluffy silk core rub on one side pressure 12-15min after,
Pressure 12-15min is rubbed another side again.
In conclusion by adopting the above-described technical solution, the beneficial effects of the invention are as follows：
1. present invention process is simple, the processes such as screened, dried, being softened to silk cocoon first, by being sieved to silk cocoon
Choosing, and using making raw material of the big cocoon as silk core, using fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perborate
Mixed aqueous solution is as bating liquor, since the fatty alcohol polyoxyethylene ether of addition is surfactant, silk in sodium bicarbonate and
More fluffy softness under the action of sodium perborate, and the mutual deadlocked power of silk weakens pulls into silk pocket in next step rectangular
Be more prone to during shape silk screen, and on rectangle silk screen be easier pull out silk carry out twist-on, twist-on more securely, and
The silk toughness for the big cocoon selected is more preferable, and the rectangle silk screen of pull-out is more secured.
2. the present invention is using the silk by suturing one layer of reticulated conductive fibrous layer in the outer surface of mulberry silk layer obtained
It during core, will not influence to sleep because electrostatic is generated, and thin layer of the reticulated conductive fibrous layer for 1mm or so, have no effect on and sleep
To the experience of silk quilt during feel, while ensureing comfortable, warming, ventilative, it can also prevent electrostatic, substantially increase people
Sleep quality.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated.
Embodiment 1
A kind of production method of antistatic silk core, includes the following steps：
(1) bonscocoons is selected in silk cocoon, then bonscocoons is put into screening machine and is sieved, in order to meet big cocoon and small cocoon
Size, the sieve diameter of screening machine are chosen as 3cm, obtain big cocoon and small cocoon, using the big cocoon as the raw material of silk core.
(2) the big cocoon in above-mentioned steps (1) is put into drying machine and be dried, the drying is：First, big cocoon is existed
6min is dried under conditions of 90 DEG C, big cocoon at a temperature of 55 DEG C is then dried into 10min, obtains dried cocoon.
(3) dried cocoon obtained in above-mentioned steps (2) to be put and is impregnated into bating liquor, the temperature of the bating liquor is 85 DEG C,
Mixed aqueous solution of the bating liquor for fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perborate, the fatty alcohol polyoxy second
The mass ratio of alkene ether, sodium bicarbonate and sodium perborate is 1:2:1, after impregnating 50min, bating liquor is filtered out, is then with temperature
50 DEG C of cleaning solution washs repeatedly, obtains softening cocoon.Wherein, cleaning solution is the ethanol water that volume fraction is 68%, fat
Alcohol polyoxyethylene ether is dissolved in ethyl alcohol, is then cleaned, and water cleans sodium bicarbonate and sodium perborate, so as to not influence the matter of silk
Amount.
(4) the softening cocoon obtained in above-mentioned steps (3) is torn, takes out silkworm chrysalis, then the softening cocoons by multiple taking-up silkworm chrysalises
It is sleeved on dilator and is strutted, dry 1h is to get to silk pocket at 90 DEG C.Drying process also can be by not clean ethyl alcohol and fat
Fat alcohol polyoxyethylene ether is volatilized, and makes a pocket noresidue chemical substance.
(5) each pocket obtained in above-mentioned steps (4) is pulled into rectangle silk screen along four direction, it will be described in every
Rectangle silk screen layer stackup is put, and silk is pulled out, and will be adjacent from four angles of every rectangle silk screen and the midpoint of four edges
The silk twist-on pulled out in rectangle silk screen, then will be pulled out from positioned at top layer and on undermost rectangle silk screen
The silk twist-on come, obtains cuboid mulberry silk layer.
(6) reticulated conductive fibrous layer is woven into using conductive fiber, wherein, conductive fiber is carbon composite fibre or acrylic fibers
Fiber is complexed in copper, and the mesh diameter of reticulated conductive fibrous layer is 5mm, thickness 0.5mm.Cut out six pieces and above-mentioned steps (5)
Six faces reticulated conductive fibrous layer of the same size of the mulberry silk layer obtained, by six pieces of reticulated conductive fibrous layers
It is layered on six faces of the mulberry silk layer, by four sides of the every piece of reticulated conductive fibrous layer net adjacent with four pieces respectively
Shape conductive fiber layer sutures, and obtains fluffy silk core.
(7) two sides of fluffy silk core that above-mentioned steps (6) obtain is carried out rubbing pressure respectively, wherein, first to fluffy
Silk core rub pressure 12min on one side after, then rub another side pressure 12min to get to antistatic silk core.
Embodiment 2
A kind of production method of antistatic silk core, includes the following steps：
(1) bonscocoons is selected in silk cocoon, then bonscocoons is put into screening machine and is sieved, in order to meet big cocoon and small cocoon
Size, the sieve diameter of screening machine are chosen as 3cm, obtain big cocoon and small cocoon, using the big cocoon as the raw material of silk core.
(2) the big cocoon in above-mentioned steps (1) is put into drying machine and be dried, the drying is：First, big cocoon is existed
8min is dried under conditions of 95 DEG C, big cocoon at a temperature of 60 DEG C is then dried into 14min, obtains dried cocoon.
(3) dried cocoon obtained in above-mentioned steps (2) to be put and is impregnated into bating liquor, the temperature of the bating liquor is 90 DEG C,
Mixed aqueous solution of the bating liquor for fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perborate, the fatty alcohol polyoxy second
The mass ratio of alkene ether, sodium bicarbonate and sodium perborate is 1.2:2.5:1, after impregnating 60min, bating liquor is filtered out, then with temperature
The cleaning solution spent for 55 DEG C washs repeatedly, obtains softening cocoon.Wherein, cleaning solution is the ethanol water that volume fraction is 70%,
Fatty alcohol polyoxyethylene ether is dissolved in ethyl alcohol, is then cleaned, and water cleans sodium bicarbonate and sodium perborate, so as to not influence silk
Quality.
(4) the softening cocoon obtained in above-mentioned steps (3) is torn, takes out silkworm chrysalis, then the softening cocoons by multiple taking-up silkworm chrysalises
It is sleeved on dilator and is strutted, dry 1.5h is to get to silk pocket at 95 DEG C.Drying process also can by not clean ethyl alcohol and
Fatty alcohol polyoxyethylene ether is volatilized, and makes a pocket noresidue chemical substance.
(5) each pocket obtained in above-mentioned steps (4) is pulled into rectangle silk screen along four direction, it will be described in every
Rectangle silk screen layer stackup is put, and silk is pulled out, and will be adjacent from four angles of every rectangle silk screen and the midpoint of four edges
The silk twist-on pulled out in rectangle silk screen, then will be pulled out from positioned at top layer and on undermost rectangle silk screen
The silk twist-on come, obtains cuboid mulberry silk layer.
(6) reticulated conductive fibrous layer is woven into using conductive fiber, wherein, conductive fiber is carbon composite fibre or acrylic fibers
Fiber is complexed in copper, and the mesh diameter of reticulated conductive fibrous layer is 8mm, thickness 0.6mm.Cut out six pieces and above-mentioned steps (5)
Six faces reticulated conductive fibrous layer of the same size of the mulberry silk layer obtained, by six pieces of reticulated conductive fibrous layers
It is layered on six faces of the mulberry silk layer, four sides of every piece of reticulated conductive fibrous layer are adjacent described netted with four pieces respectively
Conductive fiber layer sutures, and obtains fluffy silk core.
(7) two sides of fluffy silk core that above-mentioned steps (6) obtain is carried out rubbing pressure respectively, wherein, first to fluffy
Silk core rub pressure 13min on one side after, then rub another side pressure 13min to get to antistatic silk core.
Embodiment 3
A kind of production method of antistatic silk core, includes the following steps：
(1) bonscocoons is selected in silk cocoon, then bonscocoons is put into screening machine and is sieved, in order to meet big cocoon and small cocoon
Size, the sieve diameter of screening machine are chosen as 3cm, obtain big cocoon and small cocoon, using the big cocoon as the raw material of silk core.
(2) the big cocoon in above-mentioned steps (1) is put into drying machine and be dried, the drying is：First, big cocoon is existed
10min is dried under conditions of 100 DEG C, big cocoon at a temperature of 65 DEG C is then dried into 15min, obtains dried cocoon.
(3) dried cocoon obtained in above-mentioned steps (2) to be put and is impregnated into bating liquor, the temperature of the bating liquor is 92 DEG C,
Mixed aqueous solution of the bating liquor for fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perborate, the fatty alcohol polyoxy second
The mass ratio of alkene ether, sodium bicarbonate and sodium perborate is 1.5:3:1, after impregnating 70min, bating liquor is filtered out, then uses temperature
It is washed repeatedly for 60 DEG C of cleaning solutions, obtains softening cocoon.Wherein, cleaning solution is the ethanol water that volume fraction is 72%, fat
Fat alcohol polyoxyethylene ether is dissolved in ethyl alcohol, is then cleaned, and water cleans sodium bicarbonate and sodium perborate, so as to not influence silk
Quality.
(4) the softening cocoon obtained in above-mentioned steps (3) is torn, takes out silkworm chrysalis, then the softening cocoons by multiple taking-up silkworm chrysalises
It is sleeved on dilator and is strutted, dry 2h is to get to silk pocket at 100 DEG C.Drying process also can by not clean ethyl alcohol and
Fatty alcohol polyoxyethylene ether is volatilized, and makes a pocket noresidue chemical substance.
(5) each pocket obtained in above-mentioned steps (4) is pulled into rectangle silk screen along four direction, it will be described in every
Rectangle silk screen layer stackup is put, and silk is pulled out, and will be adjacent from four angles of every rectangle silk screen and the midpoint of four edges
The silk twist-on pulled out in rectangle silk screen, then will be pulled out from positioned at top layer and on undermost rectangle silk screen
The silk twist-on come, obtains cuboid mulberry silk layer.
(6) reticulated conductive fibrous layer is woven into using conductive fiber, wherein, conductive fiber is carbon composite fibre or acrylic fibers
Fiber is complexed in copper, and the mesh diameter of reticulated conductive fibrous layer is 10mm, thickness 1mm.Six pieces are cut out to make with above-mentioned steps (5)
Six faces reticulated conductive fibrous layer of the same size of the mulberry silk layer obtained spreads six pieces of reticulated conductive fibrous layers
It is on six faces of the mulberry silk layer, four sides of every piece of reticulated conductive fibrous layer are adjacent described netted with four pieces respectively
Conductive fiber layer sutures, and obtains fluffy silk core.
(7) two sides of fluffy silk core that above-mentioned steps (6) obtain is carried out rubbing pressure respectively, wherein, first to fluffy
Silk core rub pressure 15min on one side after, then rub another side pressure 15min to get to antistatic silk core.
Comparative example 1
Comparative example 1 is differed only in embodiment 1：The bating liquor and cleaning solution used in the step of comparative example 1 (3) is equal
For water, remaining step and embodiment 1 are consistent.
Comparative example 2
Comparative example 2 is differed only in embodiment 1：The bating liquor used in the step of comparative example 2 (3) is volumetric concentration
For 25% sodium bicarbonate solution, cleaning solution is water, remaining step is consistent with embodiment 1.
Comparative example 3
Comparative example 3 is differed only in embodiment 1：Rectangle silk screen layer stackup is put in the step of comparative example 3 (5), no
By pulling out the process of silk and twist-on, remaining step is consistent with embodiment 1.
Comparative example 4
Comparative example 4 is differed only in embodiment 1：Comparative example 4 lacks step (6), remaining step and embodiment 1 one
It causes.
Comparative example 5
Comparative example 5 is differed only in embodiment 1：The bating liquor and cleaning solution used in the step of comparative example 5 (3) is equal
For water, rectangle silk screen only stacks layer by layer in step (5), without pulling out silk and twist-on, and lack step (6).
Applicant also experiences silk core made from each embodiment and each comparative example.
Silk quilt core retainer plate obtained in embodiment 1-3 and comparative example 1-5 is entered into core respectively, and carries out sense organ and sleep body
It tests, it is as follows to obtain result：
Silk core soft texture in embodiment 1-3, without other impurities and peculiar smell in core, during use silk core compared with
To be secured, sleep quality is good, wherein, the sense organ of embodiment 1 and sleep experience are best；And in comparative example 1 step (3) due to the use of
For water as bating liquor, compared with the silk core in embodiment 1-3, the pliability of silk core is low, and has in core a little miscellaneous
Matter, each rectangle silk screen of silk core is not secured enough during use, is susceptible to fracture of wire phenomenon, and sleep quality reduces；It is right
In ratio 2 step (3) due to the use of volumetric concentration be 25% sodium bicarbonate solution as in cleaning solution, with embodiment 1-3
Silk core is compared, and sense organ and sleep experience are between comparative example 1 and embodiment 1-3；It is rectangular in the step of comparative example 3 (5)
Shape silk screen layer stackup is put, and without the process for pulling out silk and twist-on, is caused between each rectangle silk screen of silk core easily
Separation, silk core fastness can be poor, remaining effect is consistent with embodiment 1-3；Comparative example 4 lacks step (6), so as to make silk
The anti-static effect of core is poor, and sleep quality reduces, remaining effect is consistent with embodiment 1-3；Make in the step of comparative example 5 (3)
Bating liquor and cleaning solution are water, and rectangle silk screen only stacks layer by layer in step (5), without pulling out silk and twist-on,
And lack step (6), and causing silk core pliability poor, there are other impurities in core, silk core is insecure during use, and
Hold easy to produce static electricity, cause sleep quality poor.
To sum up, antistatic silk core soft texture made from the embodiment of the present invention, no other impurities, silk quilt during use
The secured performance of core is good, and plays the role of antistatic, so as to substantially increase sleep quality.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, that is made any repaiies
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (7)
1. a kind of production method of antistatic silk core, it is characterised in that：Include the following steps：
(1) bonscocoons is selected in silk cocoon, then bonscocoons is put into screening machine and is sieved, obtains big cocoon and small cocoon, it will be described big
Raw material of the cocoon as silk core；
(2) the big cocoon in above-mentioned steps (1) is put into drying machine and be dried, the drying is：First, by big cocoon in 90-
6-10min is dried under conditions of 100 DEG C, big cocoon at a temperature of 55-65 DEG C is then dried into 10-15min, obtains dried cocoon；
(3) dried cocoon obtained in above-mentioned steps (2) is put and is impregnated into bating liquor, the temperature of the bating liquor is 85-92 DEG C, institute
State the mixed aqueous solution that bating liquor is fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perborate, the aliphatic alcohol polyethenoxy
The mass ratio of ether, sodium bicarbonate and sodium perborate is 1-1.5:2-3:1, after impregnating 50-70min, bating liquor is filtered away, so
The cleaning solution for being afterwards 50-60 DEG C with temperature washs repeatedly, obtains softening cocoon；
(4) the softening cocoon obtained in above-mentioned steps (3) is torn, takes out silkworm chrysalis, then multiple softening cocoons for taking out silkworm chrysalis are sleeved on
It is strutted on dilator, dry 1-2h is to get to silk pocket at 90-100 DEG C；
(5) each pocket obtained in above-mentioned steps (4) is pulled into rectangle silk screen along four direction, by every silk screen
It stacks layer by layer, silk is pulled out from four angles of every pull spring net and the midpoint of four edges, and described in being pulled out in adjacent silk screen
Silk twist-on, then by from the silk twist-on pulled out positioned at top layer and on undermost silk screen, obtain cuboid silk
Layer；
(6) reticulated conductive fibrous layer is woven into using conductive fiber, cuts out the silk made from six pieces and above-mentioned steps (5)
Six pieces of reticulated conductive fibrous layers are layered on the mulberry silk layer by six faces reticulated conductive fibrous layer of the same size of layer
Six faces on, adjacent with the four pieces reticulated conductive fibrous layer seam respectively by four sides of every piece of reticulated conductive fibrous layer
It closes, obtains fluffy silk core；
(7) carry out rubbing pressure respectively to the two sides of fluffy silk core that above-mentioned steps (6) obtain to get to antistatic silk quilt
Core.
2. the production method of antistatic silk core according to claim 1, it is characterised in that：Step is sieved described in (1)
The sieve diameter of extension set is 3cm.
3. the production method of antistatic silk core according to claim 1, it is characterised in that：It is soft described in step (3)
The temperature for changing liquid is 90 DEG C, and the mass ratio of the fatty alcohol polyoxyethylene ether, sodium bicarbonate and sodium perborate is 1.2:2.5:1.
4. the production method of antistatic silk core according to claim 1, it is characterised in that：Step is washed described in (3)
It is the ethanol solution that volume fraction is 68%-72% to wash liquid.
5. the production method of antistatic silk core according to claim 1, it is characterised in that：Net described in step (6)
The mesh diameter of shape conductive fiber layer is 5-10mm, and the thickness of the reticulated conductive fibrous layer is 0.5-1mm.
6. the production method of antistatic silk core according to claim 1, it is characterised in that：The conductive fiber is carbon
Plain composite fibre or acrylic fibers copper complexing fiber.
7. the production method of antistatic silk core according to claim 1, it is characterised in that：Step is rubbed described in (7)
Briquetting include to the fluffy silk core rub on one side pressure 12-15min after, then to another side rub pressure 12-15min.