CN108165066B - 书画颜料及其制备方法和应用 - Google Patents
书画颜料及其制备方法和应用 Download PDFInfo
- Publication number
- CN108165066B CN108165066B CN201711464244.5A CN201711464244A CN108165066B CN 108165066 B CN108165066 B CN 108165066B CN 201711464244 A CN201711464244 A CN 201711464244A CN 108165066 B CN108165066 B CN 108165066B
- Authority
- CN
- China
- Prior art keywords
- painting
- calligraphy
- powder
- pigment
- rice flour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种书画颜料，组成该书画颜料的成分为：米粉、硅藻泥、檀香粉、松香粉、艾蒿叶粉、余量为水。本发明以米粉作为主料完全代替了传统水性颜料或者油性颜料，在克服了现有的丙烯颜料各种毒害性的基础之上，本发明利用了米粉中富含的表面蛋白和淀粉，在米粉糊化后，使得本发明中的书画颜料成为糊状，表面蛋白以及米粉特有的芳香，使得本发明的书画颜料具有持久的复合芳香，并在米粉中混合硅藻泥、檀香粉、胶、艾蒿叶粉和清水以糊化调和形成书画颜料，采用该书画颜料完成的书画作品干燥后具有三维立体凸起效果，用本发明书画颜料创作的书画作品具有更好的观赏性和装饰性，芳香持久，易于保存。本发明还提供一种书画颜料的制备方法。
Description
技术领域
本发明涉及书画颜料技术领域，尤其涉及一种书画颜料及其制备方法和应用。
背景技术
中国绘画有悠久辉煌的历史，几千年来，经过很多画家的钻研创作，已形成独持的形式与风格。随着现代绘画工艺的发展，对书画颜料的需求已经不同以往，在追求特色书画作品的同时，对书画颜料提出了新的要求。例如，在绘制具有一定立体感的三维书画作品时，原有的平面颜料无法满足书画要求，采用水性或者油性颜料时，只能在纸张或者纸板上形成平面的书画作品，无法得到具有一定凸显效果的立体书画作品。
并且现代书画艺术形式多样，除了以纸张作为书画载体之外，逐渐出现以厚纸板、玻璃、大理石和人造石英板等载体进行艺术创作，在这类硬质光滑的载体上进行书画艺术创作时，由于这类材料表面较光滑且吸水性能不好，因此使用传统的平面颜料如墨水、水粉、油性颜料等创作时，不仅创作得到的作品不稳定，经过擦拭就能抹掉，并且得到的只是与采用纸张进行艺术创作得到的作品一样，无法形成具有明显凹凸不平的立体触感的三维书画作品。
因此，在采用例如玻璃、大理石、人造石英板等硬质光滑载体进行立体书画座屏创作时，现有技术中缺少粘接力强、性能稳定且能形成具有明显凹凸特征的三维书画颜料。
本申请人于2017年7月25日提出了两件中国发明专利申请，申请号分别为201710617396.8和201710616505.4，均请求保护一种书画颜料及其制备方法和应用，在提出专利申请后，申请继续进行研发，以寻求采用其他替代材料完全代替传统的丙烯颜料，在不断的理论研究和试验之后，形成了本发明专利的方案，业内反响十分可观，效果显著。其中仍然采用了丙烯颜料作为颜料成分，但是丙烯颜料是用一种化学合成胶乳剂(含丙烯酸酯、甲基丙烯酸酯、丙烯酸、甲基丙烯酸，以及增稠剂、填充剂等)与颜色微粒混合而成的新型绘画颜料。丙烯颜料属于人工合成的聚合颜料，发明于20世纪50年代，是颜料粉调和丙烯酸乳胶制成的，丙烯颜料虽然用于油画创作十分普遍，但是丙烯颜料具有潜在的致癌性、神经毒性、遗传毒性和生殖毒性，人体可通过消化道，呼吸道，皮肤黏膜等多种途径接触，其中以经消化道吸收最快，丙烯酰胺还可通过胎盘和乳汁进入胎儿和婴幼儿体内，进入体内后，丙烯酰胺在细胞色素P450的作用下，生成活性环氧丙酰胺，这种物质比丙烯酰胺更容易与DNA结合，形成加合物，导致细胞内遗传物质损伤和基因突变，从而发挥致癌作用。
因此，不仅要研发一种三维书画颜料，更要研发一种可以完全取代丙烯并不会对人体到来病害的三维书画颜料。
发明内容
本发明的目的是针对现有技术的不足提供一种书画颜料，以解决现有技术中以丙烯为颜料成分的三维书画颜料对人体存在病害的技术问题。
为实现上述目的，本发明所采用的技术方案是：
一种书画颜料，组成该书画颜料的成分及各成分质量百分比为：米粉30-40份、硅藻泥硅藻泥7-13％、檀香粉6-9％、松香粉5-7％、艾蒿叶粉3-5％、余量为水。
与现有技术相比，本发明具有以下有益效果：
本发明提供的书画颜料，以米粉作为主料完全代替了传统水性颜料或者油性颜料，由于丙烯颜料具有潜在的致癌性、神经毒性、遗传毒性和生殖毒性，人体可通过消化道，呼吸道，皮肤黏膜等多种途径接触，其中以经消化道吸收最快，丙烯酰胺还可通过胎盘和乳汁进入胎儿和婴幼儿体内，进入体内后，丙烯酰胺在细胞色素P450的作用下，生成活性环氧丙酰胺，这种物质比丙烯酰胺更容易与DNA结合，形成加合物，导致细胞内遗传物质损伤和基因突变，从而发挥致癌作用，本发明中的书画颜料以米粉完全替代了现有技术中的丙烯颜料组分，克服了丙烯颜料的上述缺陷，突出的，本发明在克服了现有的丙烯颜料各种毒害性的基础之上，本发明利用了米粉中富含的表面蛋白和淀粉，在米粉糊化后，使得本发明中的书画颜料成为糊状，表面蛋白以及米粉特有的芳香，使得本发明的书画颜料具有持久的复合芳香，用本发明中的书画颜料完成的书画作品，可以给创作者和品赏者提供视觉、触觉和嗅觉多个感官上品赏性；除此之外，在米粉中中混合硅藻泥、檀香粉、胶、艾蒿叶粉和清水以调和形成干燥后具有一定形状特征的书画颜料，使得采用本发明中的书画颜料完成书画作品后，能够在书画创作载体上形成具有凸起特征的书画作品，从而丰富书画作品的立体触感，提高书画作品的艺术美感，给观赏者提供无限思考的空间，与传统平面书画作品相比，具有更好的装饰性和艺术性；并且由于檀香粉和松香粉的混入，不仅可以对书画作品周围的空气进行净化，还能散发持久芳香，改善书画作品附近的空气质量；由于松香粉的强粘接力，与糊化后的米粉结合形成粘接性能好的书画颜料，这使得在硬质光滑的书画创造载体上进行创作书画作品时，书画颜料在干燥后能够稳定的粘接在这类载体上；另外，由于檀香粉具有较好的杀菌作用，能够起到保护书画作品的效果，使创作得到的书画作品可以持久保存；而艾蒿叶粉与檀香粉结合，补充起到防虫防菌的作用，由于艾蒿具有天然的防虫效果，可以防止在长期存放过程中，虫子对本发明中的书画颜料进行破坏。
本发明的另一个目的是提供一种书画颜料的制备方法，其采用的技术方案是：
上述书画颜料的制备方法，包括以下制备步骤：
①取一定量的精抛大米过程中打磨出的糠粉用清水浸泡40-60分钟后，充分搅拌得到糠粉悬浊液；
②将檀香粉、松香粉、艾蒿叶粉分别充分研磨并分别过400目的目筛筛分，分别取筛下物；
③取称量后的硅藻泥、筛分后的檀香粉、松香粉和艾蒿叶粉倒入所述糠粉悬浊液中并搅拌均匀形成糠粉混合物；
④对所述糠粉混合物进行加热，加热时缓慢搅拌使糠粉混合物完全糊化得到书画颜料。
本发明提供的书画颜料的制备方法，先将米粉用清水浸泡，由于糠粉中含有大量的表面蛋白和淀粉，需要足够时间的浸泡才能使米粉完全吸水，在浸泡40-60分钟后充分搅拌得到糠粉悬浊液，再将硅藻泥和筛分好的檀香粉和松香粉倒入糠粉悬浊液中进行充分混合得到糠粉混合物，最后对糠粉混合物进行加热得到书画颜料，使得各种成分的混合十分均匀，粉料细腻，加热后得到的书画颜料均匀有光泽，自带纹理，具有更好的书画效果；该制备方法还具有过程简单，制作方便的特点，可根据实际需要灵活制作，保证书画颜料的活性。
本发明的其它优点、目标和特征将部分通过下面的说明体现，部分还将通过对本发明的研究和实践而为本领域的技术人员所理解。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与作用更加清楚及易于了解，下面结合具体实施方式对本发明作进一步阐述：
实施例1
一种书画颜料，组成该书画颜料的各成分质量百分比为：米粉40％、硅藻泥7％、檀香粉8％、松香粉7％,、艾蒿叶粉3％、余量为水，其中所述米粉粒径为400-500目。
上述方案中采用的硅藻泥具有净化空气的作用，书画艺术作品多陈列在展柜或者悬挂在室内墙壁上，因此加入硅藻泥能够对室内空气起到良好的生物净化作用；檀香粉具有持久芳香且具有杀菌作用，不仅可以对室内空气起到净化作用，还能对书画作品本身起到保护作用，防止蚊虫破坏书画作品；松香则充分发挥了其良好的粘接性能，使该书画颜料在书写后粘接紧密，与书画载体无法拆分；由于本发明中采用了米粉，因此需要采取较好的防虫措施，防止书画作品在长期存放过程中，米粉被蚊虫破坏，而本发明中添加的艾蒿叶粉正起到这个作用，艾蒿的主要成分有1,8-氨树脑、A-守酮、乙酰胆碱、胆碱等，能起到良好的防虫作用，以保证采用本发明提供的书画颜料完成书画作品后，能够长久保存而不被蚊虫破坏；通过上述比例的原料得到的书画颜料在玻璃、大理石、人造石英板上书画后形成的书画作品具有明显的凹凸特征，具有较好的三维立体效果，且书画作品散发着芳香，使得书画作品具有较好的嗅觉美、视觉美和触觉美，给观赏者提供了多维度的欣赏方式，用上述书画颜料绘制的书画作品用在室内装饰中效果显著。
上述方案中书画颜料的制备方法，包括以下制备步骤：
①取一定量的米粉用清水浸泡40-60分钟，充分搅拌得到米粉悬浊液；
②将檀香粉、松香粉和艾蒿叶粉分别充分研磨并分别过400目的目筛筛分，分别取筛下物；
③取称量后的硅藻泥、筛分后的檀香粉、松香粉和艾蒿叶粉倒入所述米粉悬浊液中并搅拌均匀形成米粉混合物；
④对所述米粉混合物进行水浴加热，加热时缓慢搅拌，且加热温度控制在53-65℃之间，米粉混合物完全糊化得到书画颜料；
⑤将④所得书画颜料自然冷却至22-34℃后使用。
上述制备方法中，由于米粉不溶于水，先将米粉浸泡后再将其他组分混入，可以使得米粉先进行吸水充分膨胀，这样在加热的过程中，米粉可以快速糊化；采用水浴加热起到以下作用：①水浴加热可以防止混合物沸腾从而混入气泡，进一步影响书画颜料制备完成以后的使用，保证了书画颜料制备后的纯度，保证使用效果；②水浴加热保证了热量传递的均匀性，防止采用明火加热出现局部温度过高导致书画颜料中产生气泡或者米粉、檀香粉和松香粉的活性被完全破坏，从而达不到预期效果；加热温度为53-65℃起到保护书画颜料中各种成分的活性的作用，因加热的目的是使得米粉糊化得到具有一定粘度和粘接度且具有芳香的书画颜料，65℃是米粉糊化的最佳温度，因此将加热温度控制在53-65℃之间能够均衡的达到以上效果；在冷却时，必须采用自然冷却，如果采用风机等风冷方式，由于米粉糊化后粘度较高，热量传递速度较慢，因此会出现外层温度下降后其内部温度仍然很高的情况，不适宜书画创作，自然冷却速度慢，但是可以保证书画颜料内外温度同时降低，保证了书画效果；另外冷却到22-34℃之间，书画颜料内分子活跃性高、流动性好，在使用后，每一个笔画留下的书画颜料的分子能够自由活动补偿因创作工作带来的不光滑性，从而使得使用上述书画颜料时，书画创作得到的作品表层光滑细腻、富有光泽。上述方法制备的书画颜料在书画作品完成且完全干燥后，具有较好的弹性。
实施例2
一种书画颜料，组成该书画颜料的各成分质量百分比为：糠粉35％、硅藻泥13％、檀香粉6％、松香粉5％、艾蒿叶粉4％、生漆7％，余量为水，其其中所述米粉粒径为700-800目。
上述方案中书画颜料的制备方法，包括以下制备步骤：
①取体积比为1:3的糠粉和清水浸泡50分钟后，充分搅拌混合得到糠粉悬浊液；
②将檀香粉、松香粉和艾蒿叶粉分别充分研磨并分别过400目的目筛筛分，分别取筛下物；
③取称量后的硅藻泥、筛分后的檀香粉、松香粉和艾蒿叶粉倒入所述糠粉悬浊液中并搅拌均匀得到糠粉混合物；
④对所述糠粉混合物进行水浴加热，且加热温度控制在53-65℃之间，加热时沿着顺时针或者逆时针缓慢搅拌使糠粉混合物完全糊化，加热完成后缓慢搅拌并从一个注入点加入7％的生漆，搅拌均匀得到书画颜料；
⑤将④所得书画颜料自然冷却至22-34℃，可用于玻璃或大理石或人造石英板上进行书画创作。
上述方案制成的书画颜料散发自然的芳香，可以使用类似蛋糕袋的书画工具进行书画创作，在进行书画创作完成且充分干燥后，得到的书画作品不仅凸起特征明显，且用手触摸凸起部的顶端，具有明显弹性。该实施例制得的书画颜料与实施例1相比，香味较淡、更稀。
实施例3
一种书画颜料，组成该书画颜料的各成分质量百分比为：糠粉30％、硅藻泥10％、檀香粉9％、松香粉6％、艾蒿叶粉5％、生漆5％，余量为水，其中所述米粉粒径为500-600目。
上述方案中书画颜料的制备方法，包括以下制备步骤：
①取一定量的糠粉用清水浸泡60分钟后，充分搅拌得到糠粉悬浊液；
②将檀香粉、松香粉和艾蒿叶粉充分研磨并分别过400目的目筛筛分，分别取筛下物；
③取称量后的硅藻泥、筛分后的檀香粉、松香粉和艾蒿叶粉倒入所述糠粉悬浊液中并搅拌均匀形成糠粉混合物；
④对所述米粉混合物进行水浴加热，且加热温度控制在53-65℃之间，加热时缓慢搅拌使糠粉混合物完全糊化，加热完成后缓慢搅拌并从一个注入点缓慢注入5％的生漆，混合均匀得到书画颜料；
⑤将④所得书画颜料自然冷却至22-34℃，可用于玻璃或大理石或人造石英板上进行书画创作。
上述制备方法中，由于糠粉是微溶于水，因此在浸泡60分钟后加入其它组分混合均匀，然后进行加热糊化，在糊化的过程中，采用水浴加热可以均匀的进行加热，防止气泡的产生，该实施例制得的书画颜料相对实施例1和实施例2制得的书画颜料弹性更好，在书画作品完成后，触摸作品痕迹的顶部，可见明显变形；突出的是，本实施例中在加热步骤后注入的生漆能够在书画颜料中形成流线型的色彩纹理，通过搅拌方向和轨迹可以使得加入的生漆形成固定图案，可以大大提高书画颜料创作后的观赏性和艺术性。
通过该实施例制得的书画颜料在使用得到书画作品并充分干燥后，书画作品本身香气浓郁，凸起特征明显，凸起部柔软性好，由于加入了生漆，生漆的色彩使得创作者使用不同的书画轨迹完成书画作品时会留下不同的色彩纹理，且色彩纹理是按照完成书画的先后顺序和书画方向留下的，使得观赏者能够根据该书画痕迹推出作者书画的思路，通过该方案制备的书画颜料完成的书画作品，观赏性和装饰性更好。
突出说明的是，本发明中的实施例2和实施例3中，采用的米粉为大米精加工过程中抛光精磨出的糠粉。大米在加工过程中，稻谷经脱壳后成为糙米，糙米去除绝大部分皮层和一部分胚后成为白米，白米米粒表面还会带有大量糠粉。现代加工工艺中，为了大米的外观、储存性和制成米饭的口感，生产上会采用“抛光”工序去掉这部分糠粉，抛光精磨掉的糠粉成为了工艺废料，在大米加工过程中，一公斤大米会有0.1-0.3公斤糠粉被磨掉，而这部分糠粉中，仍然富含表面蛋白和淀粉，本发明以大米生产过程中产生的废料作为书画颜料的主要成分，有效的利用了大米生产过程中产生的废料，成本低，突出的是，这种抛光精磨下来的糠粉仍然因为富含表面蛋白和淀粉，并且具有独特的芳香，糊化后具有表面光滑、富有弹性的特点，这是现有技术中任意一种书画颜料都无法达到的效果，本发明中的米粉是难得的可以完全替代对人体具有毒害作用的丙烯颜料的替代颜料成分。
以上三种实施例制备得到的书画颜料，均可以采用传统书写工具如毛笔等，或者新型书写工具在玻璃、大理石或人造石英板等硬质光滑的载体上完成书画作品。在进行书画创作时，先将载体表面擦拭干净，可用酒精棉擦拭，然后在载体上进行书画创作，创作完成以后可水平放置自然风干，待完全干燥后即可进行书画作品的陈列摆放。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (6)
1.书画颜料，其特征在于：组成该书画颜料的各成分质量百分比为：大米精加工过程中抛光精磨出的糠粉30-40％、硅藻泥7-13％、檀香粉6-9％、松香粉5-7％、艾蒿叶粉3-5％、生漆5-7％，余量为水。
2.权利要求1所述的书画颜料，其特征在于：所述糠粉粒径为400-800目。
3.权利要求1所述书画颜料的制备方法，其特征在于：包括以下制备步骤：①取一定量的精抛大米过程中打磨出的糠粉用清水浸泡40-60分钟后，充分搅拌得到糠粉悬浊液；②将檀香粉、松香粉、艾蒿叶粉分别充分研磨并分别过400目的目筛筛分，分别取筛下物；③取称量后的硅藻泥、筛分后的檀香粉、松香粉和艾蒿叶粉倒入所述糠粉悬浊液中并搅拌均匀形成糠粉混合物；④对所述糠粉混合物进行加热，加热时缓慢搅拌，使糠粉混合物完全糊化，加热完成后缓慢搅拌并加入生漆混合均匀，得到书画颜料。
4.根据权利要求3所述的书画颜料的制备方法，其特征在于：步骤④中的加热温度为53-65℃。
5.根据权利要求3所述的书画颜料的制备方法，其特征在于：将步骤④中得到所述书画颜料冷却至22-34℃后使用。
6.权利要求3制得的书画颜料的应用，其特征在于：将步骤④制得的书画颜料用于玻璃或大理石或人造石英板上进行书画创作。