CN108149109A - 金属陶瓷材料 - Google Patents

金属陶瓷材料 Download PDF

Info

Publication number
CN108149109A
CN108149109A CN201711448900.2A CN201711448900A CN108149109A CN 108149109 A CN108149109 A CN 108149109A CN 201711448900 A CN201711448900 A CN 201711448900A CN 108149109 A CN108149109 A CN 108149109A
Authority
CN
China
Prior art keywords
parts
cermet material
component
present
cobalt
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711448900.2A
Other languages
English (en)
Inventor
贾留宽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
LUOYANG SHENJIA KILN CO Ltd
Original Assignee
LUOYANG SHENJIA KILN CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by LUOYANG SHENJIA KILN CO Ltd filed Critical LUOYANG SHENJIA KILN CO Ltd
Priority to CN201711448900.2A priority Critical patent/CN108149109A/zh
Publication of CN108149109A publication Critical patent/CN108149109A/zh
Pending legal-status Critical Current

Abstract

一种金属陶瓷材料，其组分及各组分的质量份数为：碳化硅20‑30份、镍2‑5份、钴2‑5份、镁2‑5份、铜1‑5份、铝2‑5份、氮化钛1‑3份、锌1‑3份、钙2‑5份。借由上述技术方案，本发明一种金属陶瓷材料，具有良好的耐磨性以及韧性，可以用于制造精密轴承。

Description

金属陶瓷材料
技术领域
本发明属于陶瓷材料领域，特别是涉及一种金属陶瓷材料。
背景技术
普通轴承钢AISI52100(GCr15)、不锈钢AISI440(9Cr18)、氮化硅(Si3N4)和氧化锆(ZrO2)四种轴承材料性能对照情况，陶瓷轴承作为一种重要的机械基础件，由于其具有金属轴承所无法比拟的优良性能，抗高温、超强度等在新材料世界独领风骚。近十多年来，在国计民生的各个领域中得到了日益广泛的应用。
发明内容
本发明的目的在于提出一种金属陶瓷材料，所要解决的技术问题是使其具有良好的耐磨性和韧性，从而更加适于实用。
本发明的目的及解决其技术问题是采用以下技术方案来实现。依据本发明提出的一种金属陶瓷材料，其组分及各组分的质量份数为：碳化硅20-30份、镍2-5份、钴2-5份、镁2-5份、铜1-5份、铝2-5份、氮化钛1-3份、锌1-3份、钙2-5份。
本发明一种金属陶瓷材料，具有良好的耐磨性以及韧性，可以用于制造精密轴承。
上述说明仅是本发明技术方案的概述，为了能够更清楚了解本发明的技术手段，而可依照说明书的内容予以实施，并且为了让本发明的上述和其他目的、特征和优点能够更明显易懂，以下特举较佳实施例详细说明。
具体实施方式
实施例一：
金属陶瓷材料，其组分及各组分的质量份数为：碳化硅20份、镍2份、钴2份、镁2份、铜1份、铝2份、氮化钛1份、锌1份、钙2份。
实施例二：
金属陶瓷材料，其组分及各组分的质量份数为：碳化硅30份、镍5份、钴5份、镁5份、铜5份、铝5份、氮化钛3份、锌3份、钙5份。
实施例三：
金属陶瓷材料，其组分及各组分的质量份数为：碳化硅25份、镍3份、钴3份、镁3份、铜3份、铝3份、氮化钛2份、锌2份、钙3份。
以上所述，仅是本发明的较佳实施例而已，并非对本发明做任何形式上的限制，虽然本发明已以较佳实施例揭露如上，然而并非用以限定本发明，任何熟悉本专业的技术人员，在不脱离本发明技术方案范围内，当可利用上述揭示的技术内容做出些许更动或修饰为等同变化的等效实施例，但凡是未脱离本发明技术方案的内容，依据本发明的技术实质对以上实施例所做的任何简单修改、等同变化与修饰，均仍属于本发明技术方案的范围内。

Claims (1)

1.金属陶瓷材料，其特征在于：其组分及各组分的质量份数为：碳化硅20-30份、镍2-5份、钴2-5份、镁2-5份、铜1-5份、铝2-5份、氮化钛1-3份、锌1-3份、钙2-5份。
CN201711448900.2A 2017-12-27 2017-12-27 金属陶瓷材料 Pending CN108149109A (zh)