CN108148309A - A kind of corrosion resistant graphite polystyrene board - Google Patents
A kind of corrosion resistant graphite polystyrene board Download PDFInfo
- Publication number
- CN108148309A CN108148309A CN201711174390.4A CN201711174390A CN108148309A CN 108148309 A CN108148309 A CN 108148309A CN 201711174390 A CN201711174390 A CN 201711174390A CN 108148309 A CN108148309 A CN 108148309A
- Authority
- CN
- China
- Prior art keywords
- parts
- corrosion resistant
- graphite
- resin
- aging agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of corrosion resistant graphite polystyrene board is related to fitting up, decorateing technical field, it is characterised in that：It is made up of the following materials in parts by weight, 17 24 parts of polystyrene, 15 21 parts of graphite, 6 12 parts of magnesium hydroxide, 7 12 parts of resin, 59 parts of sepiolite powder, 7 13 parts of modified kaolin, 28 parts of anti-aging agent, 49 parts of polyvinyl alcohol, 36 parts of biomass additive, 27 33 parts of clear water.The method of the present invention is reasonable, it is easy to operate, being capable of anti-corrosion and wear-resisting.
Description
Technical field
The present invention relates to finishing, decoration technical fields, and in particular to a kind of corrosion resistant graphite polystyrene board.
Background technology
Graphite (graphite) is a kind of crystalline carbon.Hexagonal crystal system, for iron mass colour to Dark grey.2.25 gram/li of density
Rice 3, hardness 1.5,3652 DEG C of molten point, 4827 DEG C of boiling point.Matter is soft, there is soapy feeling, electrically conductive.Chemical property torpescence, it is corrosion-resistant,
It is not easy to react with acid, alkali etc..Strengthen heat in air or oxygen, incendivity simultaneously generates carbon dioxide.Strong oxidizer can be by its oxygen
It is melted into organic acid.As antifriction additive and lubriation material, crucible, electrode, dry cell, pencil-lead are made.High purity graphite can be in core
Make neutron moderator on reactor.It is commonly referred to as carbon or blacklead.
Styrofoam is used as the protective layer of waterproof layer, full name polystyrene foam plate also known as cystosepiment or EPS sheet.Be by
Expandable polystyrene bead containing volatile fluid foaming agent, after heated pre- hair in a mold hot briquetting have it is micro-
The white solid of thin hole-closing structure.
And the range used and the frequency used due to styrofoam, it often often will appear in many places and be subjected to corruption
The problem of losing and being broken, crack thus causes and good can not use and need to disassemble and install again, can be very numb
It is tired, it can also waste a large amount of time and human and material resources.
Invention content
The technical problems to be solved by the invention be to overcome existing technological deficiency provide a kind of method rationally, operation side
It just, being capable of anti-corrosion and a kind of wear-resisting corrosion resistant graphite polystyrene board.
The technical problems to be solved by the invention are realized using following technical solution：
A kind of corrosion resistant graphite polystyrene board, it is characterised in that：It is made up of the following materials in parts by weight,
17-24 parts of polystyrene, 15-21 parts of graphite, 6-12 parts of magnesium hydroxide, 7-12 parts of resin, 5-9 parts of sepiolite powder,
7-13 parts of modified kaolin, 2-8 parts of anti-aging agent, 4-9 parts of polyvinyl alcohol, 3-6 parts of biomass additive, 27-33 parts of clear water；
The resin is epoxy resin, one kind of phenolic resin, polyvinyl resin, alkyd resin；
The anti-aging agent is antioxidant A W, one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD；
The preparation method of the modified kaolin is that kaolin is ground to and crossed 500-600 mesh sieve, is then placed on 45 DEG C
Then oven for baking 30 minutes adds in the clear water of 0.7 times of its weight, is then warming up to 50 DEG C and constant temperature, then carries out 25
The stirring of minute adds in methyl diphenylene diisocyanate, and is warming up to 55 DEG C, is then stirred 1.8 hours, then do
It is dry, re-grind, obtain modified kaolin；
The methyl diphenylene diisocyanate is 1 with kaolinic mass ratio：3.5；
The biomass additive is made up of the following materials in parts by weight,
1 part of Rhizoma Et Radix Notopterygii, 2 parts of monkshood, 3 parts of the flower bud of lily magnolia, 4 parts of rhizoma atractylodis, 5 parts of pawpaw, 6 parts of turpentine, 1 part of eupatorium, 7 parts of the root of Chinese clematis, thunder
Public 2 parts of rattan, 3 parts of lycopodium calvatum, 4 parts of berba aristolochiae mollissimae, 5 parts of caulis piperis futokadsurae, 6 parts of Fructus Liquidambaris, 7 parts of the achene of Siberian cocklebur；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant
It 4-5 hour of middle baking, is then placed in equipment and grinds and cross 400-500 mesh sieve, the clear water for adding 0.7 times of quality of materials stirs
1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
A kind of preparation method of corrosion resistant graphite polystyrene board is,
I is put into polystyrene, graphite, magnesium hydroxide, resin, sepiolite powder, modified kaolin, clear water in reaction kettle,
2 hours are mixed at a temperature of 65-75 DEG C；
During anti-aging agent, polyvinyl alcohol, biomass additive are added to I by II, and 75-85 DEG C is warming up to, continues mixing 1.5
A hour；
III takes out the material in reaction kettle, is then placed in mold, heating mold is carried out according to the usual manner of styrofoam,
Then molding is taken out.
Beneficial effects of the present invention are：Above-mentioned material is combined mixing, react, heat up, by way of mold
And processing, the performance of product has obtained more powerful optimization and release, and almost non-toxic pollution-free, for environment, human body
All it is not injure and destroy, and is added to the material of biomass, is also one very good with biological coating now
Selection, nontoxic and pollution-free and of low cost, product has good anti-corrosion, moisture-proof, thermal insulation, heat-insulated effect, and can increase
Add the service life used.The method of the present invention is reasonable, it is easy to operate, being capable of anti-corrosion and wear-resisting.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below into
One step illustrates the present invention.
Embodiment 1
A kind of corrosion resistant graphite polystyrene board, it is characterised in that：It is made up of the following materials in parts by weight,
17 parts of polystyrene, 15 parts of graphite, 6 parts of magnesium hydroxide, 7 parts of resin, 5 parts of sepiolite powder, 7 parts of modified kaolin,
2 parts of anti-aging agent, 4 parts of polyvinyl alcohol, 3 parts of biomass additive, 27 parts of clear water；
The resin is epoxy resin, one kind of phenolic resin, polyvinyl resin, alkyd resin；
The anti-aging agent is antioxidant A W, one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD；
The preparation method of the modified kaolin is that kaolin is ground to and crossed 500-600 mesh sieve, is then placed on 45 DEG C
Then oven for baking 30 minutes adds in the clear water of 0.7 times of its weight, is then warming up to 50 DEG C and constant temperature, then carries out 25
The stirring of minute adds in methyl diphenylene diisocyanate, and is warming up to 55 DEG C, is then stirred 1.8 hours, then do
It is dry, re-grind, obtain modified kaolin；
The methyl diphenylene diisocyanate is 1 with kaolinic mass ratio：3.5；
The biomass additive is made up of the following materials in parts by weight,
1 part of Rhizoma Et Radix Notopterygii, 2 parts of monkshood, 3 parts of the flower bud of lily magnolia, 4 parts of rhizoma atractylodis, 5 parts of pawpaw, 6 parts of turpentine, 1 part of eupatorium, 7 parts of the root of Chinese clematis, thunder
Public 2 parts of rattan, 3 parts of lycopodium calvatum, 4 parts of berba aristolochiae mollissimae, 5 parts of caulis piperis futokadsurae, 6 parts of Fructus Liquidambaris, 7 parts of the achene of Siberian cocklebur；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant
It 4-5 hour of middle baking, is then placed in equipment and grinds and cross 400-500 mesh sieve, the clear water for adding 0.7 times of quality of materials stirs
1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
A kind of preparation method of corrosion resistant graphite polystyrene board is,
I is put into polystyrene, graphite, magnesium hydroxide, resin, sepiolite powder, modified kaolin, clear water in reaction kettle,
2 hours are mixed at a temperature of 65-75 DEG C；
During anti-aging agent, polyvinyl alcohol, biomass additive are added to I by II, and 75-85 DEG C is warming up to, continues mixing 1.5
A hour；
III takes out the material in reaction kettle, is then placed in mold, heating mold is carried out according to the usual manner of styrofoam,
Then molding is taken out.
Embodiment 2
A kind of corrosion resistant graphite polystyrene board, it is characterised in that：It is made up of the following materials in parts by weight,
24 parts of polystyrene, 21 parts of graphite, 12 parts of magnesium hydroxide, 12 parts of resin, 9 parts of sepiolite powder, modified kaolin 13
Part, 8 parts of anti-aging agent, 9 parts of polyvinyl alcohol, 6 parts of biomass additive, 33 parts of clear water；
The resin is epoxy resin, one kind of phenolic resin, polyvinyl resin, alkyd resin；
The anti-aging agent is antioxidant A W, one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD；
The preparation method of the modified kaolin is that kaolin is ground to and crossed 500-600 mesh sieve, is then placed on 45 DEG C
Then oven for baking 30 minutes adds in the clear water of 0.7 times of its weight, is then warming up to 50 DEG C and constant temperature, then carries out 25
The stirring of minute adds in methyl diphenylene diisocyanate, and is warming up to 55 DEG C, is then stirred 1.8 hours, then do
It is dry, re-grind, obtain modified kaolin；
The methyl diphenylene diisocyanate is 1 with kaolinic mass ratio：3.5；
The biomass additive is made up of the following materials in parts by weight,
1 part of Rhizoma Et Radix Notopterygii, 2 parts of monkshood, 3 parts of the flower bud of lily magnolia, 4 parts of rhizoma atractylodis, 5 parts of pawpaw, 6 parts of turpentine, 1 part of eupatorium, 7 parts of the root of Chinese clematis, thunder
Public 2 parts of rattan, 3 parts of lycopodium calvatum, 4 parts of berba aristolochiae mollissimae, 5 parts of caulis piperis futokadsurae, 6 parts of Fructus Liquidambaris, 7 parts of the achene of Siberian cocklebur；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant
It 4-5 hour of middle baking, is then placed in equipment and grinds and cross 400-500 mesh sieve, the clear water for adding 0.7 times of quality of materials stirs
1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
A kind of preparation method of corrosion resistant graphite polystyrene board is,
I is put into polystyrene, graphite, magnesium hydroxide, resin, sepiolite powder, modified kaolin, clear water in reaction kettle,
2 hours are mixed at a temperature of 65-75 DEG C；
During anti-aging agent, polyvinyl alcohol, biomass additive are added to I by II, and 75-85 DEG C is warming up to, continues mixing 1.5
A hour；
III takes out the material in reaction kettle, is then placed in mold, heating mold is carried out according to the usual manner of styrofoam,
Then molding is taken out.
Embodiment 3
A kind of corrosion resistant graphite polystyrene board, it is characterised in that：It is made up of the following materials in parts by weight,
20 parts of polystyrene, 19 parts of graphite, 8 parts of magnesium hydroxide, 9 parts of resin, 6 parts of sepiolite powder, 10 parts of modified kaolin,
5 parts of anti-aging agent, 6 parts of polyvinyl alcohol, 4 parts of biomass additive, 31 parts of clear water；
The resin is epoxy resin, one kind of phenolic resin, polyvinyl resin, alkyd resin；
The anti-aging agent is antioxidant A W, one kind in anti-aging agent RD, antioxidant A, antioxidant D, anti-aging agent CPPD；
The preparation method of the modified kaolin is that kaolin is ground to and crossed 500-600 mesh sieve, is then placed on 45 DEG C
Then oven for baking 30 minutes adds in the clear water of 0.7 times of its weight, is then warming up to 50 DEG C and constant temperature, then carries out 25
The stirring of minute adds in methyl diphenylene diisocyanate, and is warming up to 55 DEG C, is then stirred 1.8 hours, then do
It is dry, re-grind, obtain modified kaolin；
The methyl diphenylene diisocyanate is 1 with kaolinic mass ratio：3.5；
The biomass additive is made up of the following materials in parts by weight,
1 part of Rhizoma Et Radix Notopterygii, 2 parts of monkshood, 3 parts of the flower bud of lily magnolia, 4 parts of rhizoma atractylodis, 5 parts of pawpaw, 6 parts of turpentine, 1 part of eupatorium, 7 parts of the root of Chinese clematis, thunder
Public 2 parts of rattan, 3 parts of lycopodium calvatum, 4 parts of berba aristolochiae mollissimae, 5 parts of caulis piperis futokadsurae, 6 parts of Fructus Liquidambaris, 7 parts of the achene of Siberian cocklebur；
Preparation method is：Above-mentioned material is exposed to the sun 4 hours in the sunlight, is then placed in 85-95 DEG C of roasting plant
It 4-5 hour of middle baking, is then placed in equipment and grinds and cross 400-500 mesh sieve, the clear water for adding 0.7 times of quality of materials stirs
1 hour is mixed, is then warming up to 75-85 DEG C, continues to stir 1.5 hours, then dries, re-grind；
A kind of preparation method of corrosion resistant graphite polystyrene board is,
I is put into polystyrene, graphite, magnesium hydroxide, resin, sepiolite powder, modified kaolin, clear water in reaction kettle,
2 hours are mixed at a temperature of 65-75 DEG C；
During anti-aging agent, polyvinyl alcohol, biomass additive are added to I by II, and 75-85 DEG C is warming up to, continues mixing 1.5
A hour；
III takes out the material in reaction kettle, is then placed in mold, heating mold is carried out according to the usual manner of styrofoam,
Then molding is taken out.
By experiment, 1-3 of the embodiment of the present invention and common expansion polyphenyl plate performance and effect, such as following table are measured：
The basic principles, main features and the advantages of the invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (2)
1. a kind of corrosion resistant graphite polystyrene board, it is characterised in that：It is made up of the following materials in parts by weight,
17-24 parts of polystyrene, 6-12 parts of magnesium hydroxide, 7-12 parts of resin, 5-9 parts of sepiolite powder, is modified 15-21 parts of graphite
7-13 parts of kaolin, 2-8 parts of anti-aging agent, 4-9 parts of polyvinyl alcohol, 3-6 parts of biomass additive, 27-33 parts of clear water.
2. a kind of corrosion resistant graphite polystyrene board according to claim 1, it is characterised in that：A kind of corrosion resistant stone
The preparation method of black styrofoam is,
I is put into polystyrene, graphite, magnesium hydroxide, resin, sepiolite powder, modified kaolin, clear water in reaction kettle, in 65-
2 hours are mixed at a temperature of 75 DEG C；
During anti-aging agent, polyvinyl alcohol, biomass additive are added to I by II, and 75-85 DEG C is warming up to, it is 1.5 small to continue mixing
When；
III takes out the material in reaction kettle, is then placed in mold, carries out heating mold according to the usual manner of styrofoam, then
Molding is taken out.