CN108130160A - A kind of steel wire dry drawing powder and preparation method thereof - Google Patents
A kind of steel wire dry drawing powder and preparation method thereof Download PDFInfo
- Publication number
- CN108130160A CN108130160A CN201711426914.4A CN201711426914A CN108130160A CN 108130160 A CN108130160 A CN 108130160A CN 201711426914 A CN201711426914 A CN 201711426914A CN 108130160 A CN108130160 A CN 108130160A
- Authority
- CN
- China
- Prior art keywords
- steel wire
- powder
- drawing powder
- wire dry
- dry drawing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of steel wire dry drawing powder, its component are：Stearic acid 20%, organic zinc phosphide 5%, other compound anti-extreme pressure agents 2%, remaining is pulverized limestone, dry drawing powder composition is mixed by regulation component, certain pressure, at a temperature of react uniform, after drying, moisture is less than 1.5%, using powder is beaten, is finally ground into fine powder again.Drawing powder fat content of the present invention is low, and less than 30%, using the steel wire of drawing of the present invention without greasy dirt, surface is clean, good antirust property.
Description
Technical field
The present invention relates to a kind of steel wire dry drawing powder and preparation method thereof, belong to chemicals technical field.
Background technology
Common drawing powder is mainly calcium system and sodium system during steel wire dry drawing, but the steel wire after this two classes drawing powder drawing
Surface is not clean, all there are surface it is dirty the problem of, the present invention develops a kind of novel drawing powder so that the steel wire table after drawing
Face is very clean, steel wire surface good antirust property.
Invention content
The purpose of the invention is to overcome the deficiencies of the prior art and provide a kind of steel wire dry drawing powder and its preparation side
Method solves the problems, such as drawn steel wire surface contaminants, it is ensured that steel wire surface is clean, improves steel wire surface rustless property.
A kind of steel wire dry drawing powder of the present invention, its component（Weight percent）For：Stearic acid 20%, organic phosphatization
Zinc 5%, other compound anti-extreme pressure agents 2%, remaining is pulverized limestone.
The preparation method of the steel wire dry drawing powder of the present invention, the dry drawing powder composition is mixed by regulation component
Close, certain pressure, at a temperature of react uniform, after drying, moisture is less than 1.5%, using powder is beaten, is finally ground into again carefully
Powder.
The drawing powder fat content of the present invention is few, and fat content is less than 30%.And common drawing powder fat content is 40%-
60%, while drawing powder is processed into powdering, and common drawing powder is graininess, while adds other additives, that is, be ensure that
Lubricity, while ensure that steel wire surface is clean.
The present invention adds in organic zinc phosphide in drawing powder for the first time so that and not only the greasy property of drawing powder is good, but also
It can guarantee steel wire surface non-corrosive.
In drawn steel wire, by the drawing powder of the present invention for wire drawing machine most latter two drawing diaphragm capsule, it is ensured that steel wire
Surface is clean.
The advantageous effect of patent of the present invention
1st, the steel wire surface of drawing is very clean, user's free from dust in use, environmental protection.
2nd, with commodity steel wire since surface is clean, steel wire will not skid spring during around spring since surface is dirty,
Solve the problems, such as height spring occur around spring.
3rd, for needing the follow-up steel wire for carrying out coating processing, surface is totally handled convenient for cleaning before copper plating, ensure that coating
Quality.
4th, the steel wire through the drawing powder drawing, surface good antirust property.
Specific embodiment
A kind of steel wire dry drawing powder of the present invention, its component（Weight percent）For：Stearic acid 20%, organic phosphatization
Zinc 5%, other compound anti-extreme pressure agents 2%, remaining is pulverized limestone.
The preparation method of the steel wire dry drawing powder of the present invention, the dry drawing powder composition is mixed by regulation component
Close, certain pressure, at a temperature of react uniform, after drying, moisture is less than 1.5%, using powder is beaten, is finally ground into again carefully
Powder.
The drawing powder fat content of the present invention is few, and fat content is less than 30%.And common drawing powder fat content is 40%-
60%, while drawing powder is processed into powdering, and common drawing powder is graininess, while adds other additives, that is, be ensure that
Lubricity, while ensure that steel wire surface is clean.
The present invention adds in organic zinc phosphide in drawing powder for the first time so that and not only the greasy property of drawing powder is good, but also
It can guarantee steel wire surface non-corrosive.
In drawn steel wire, by the drawing powder of the present invention for wire drawing machine most latter two drawing diaphragm capsule, it is ensured that steel wire
Surface is clean.
Claims (3)
1. a kind of steel wire dry drawing powder, it is characterized in that：Its component（Weight percent）For：Stearic acid 20%, organic zinc phosphide
5%, other compound anti-extreme pressure agents 2%, remaining is pulverized limestone.
2. steel wire dry drawing powder as described in claim 1, it is characterized in that：The drawing powder fat content is less than 30%.
3. the preparation method of steel wire dry drawing powder as claimed in claim 1 or 2, it is characterized in that：By the steel wire dry type
Drawing powder composition by regulation component mixing, certain pressure, at a temperature of react uniform, after drying, moisture is less than 1.5%, then
By beating powder, it is finally ground into fine powder again.