CN108113803A - 医用石膏绷带 - Google Patents

医用石膏绷带 Download PDF

Info

Publication number
CN108113803A
CN108113803A CN201711380961.XA CN201711380961A CN108113803A CN 108113803 A CN108113803 A CN 108113803A CN 201711380961 A CN201711380961 A CN 201711380961A CN 108113803 A CN108113803 A CN 108113803A
Authority
CN
China
Prior art keywords
parts
plaster bandage
medical plaster
antibiotic layer
extraction
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201711380961.XA
Other languages
English (en)
Other versions
CN108113803B (zh
Inventor
陈国平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU PROVINCE JIAN'ERKANG PHARMACEUTICAL SURGICAL DRESSING CO Ltd
Original Assignee
JIANGSU PROVINCE JIAN'ERKANG PHARMACEUTICAL SURGICAL DRESSING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU PROVINCE JIAN'ERKANG PHARMACEUTICAL SURGICAL DRESSING CO Ltd filed Critical JIANGSU PROVINCE JIAN'ERKANG PHARMACEUTICAL SURGICAL DRESSING CO Ltd
Priority to CN201711380961.XA priority Critical patent/CN108113803B/zh
Publication of CN108113803A publication Critical patent/CN108113803A/zh
Application granted granted Critical
Publication of CN108113803B publication Critical patent/CN108113803B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及医疗用品技术领域，尤其是一种医用石膏绷带；所述抗菌层的厚度为10‑18μm，所述抗菌层中填充的抗菌剂的质量份组成如下：缓凝剂2‑18份、纤维素环糊精8‑20份、硝酸银2‑8份、薄荷4‑8份、石榴皮提取物1‑6份、薰衣草油1‑2份，所述纤维素环糊精为改性β‑环糊精接枝硝化纤维素；本发明中的医用石膏绷带透气性好，能有效确保肌体外伤骨折处的皮肤通气干燥，湿度或潮气消除或减轻，从而可以消除或减轻由石膏固定后不透气所造成的不适。

Description

医用石膏绷带
技术领域
本发明涉及医疗用品技术领域，尤其是一种医用石膏绷带。
背景技术
骨科骨折固定，畸形矫正，炎症肢体制动，骨髓炎，骨结核，骨肿瘤术以及骨关节成形术肢体固定及模具模型制作等，在必要的情况情况下，都需要有绷带的固定，才能得到完全的康复，目前，石膏绷带缠绕时，交叠的面积应在上一周石膏绷带的下1/3，这样才可使整个石膏绷带形成一体，在缠绕过程中，助手必须以手掌扶体，避免用手指扶持，以防造成石膏压凹，使局部皮肤受压，这种常用的石膏绷带，因其自身的特点和常用的缠绕方式的弊端，造成其透气性差，容易导致伤口处的血液流通不畅，皮肤肿胀、瘙痒，甚至泛白，对患者的康复极为不利，同时造成了药物的浪费。
发明内容
本发明的目的是：提供一种透气效果好、使用舒适性高的医用石膏绷带。
为解决上述技术问题，本发明采用的技术方案如下：
一种医用石膏绷带，所述石膏绷带中填充有抗菌层，所述抗菌层的厚度为10-18μm，所述抗菌层中填充的抗菌剂的质量份组成如下：缓凝剂2-18份、纤维素环糊精8-20份、硝酸银2-8份、薄荷4-8份、石榴皮提取物1-6份、薰衣草油1-2份，所述纤维素环糊精为改性β-环糊精接枝硝化纤维素；
所述石榴皮提取物采用以下方法制得：将石榴皮洗净切碎，置于乙醇和乙酸乙酯的混合溶剂中回流提取1-3次，提取后进行浓缩得到1.5g/cm3的胶状物，即石榴皮提取物。
优选的，所述缓凝剂采用硼酸钠和柠檬酸盐的混合物，其质量比为1:1-3。
优选的，所述缓凝剂采用硼酸钠和柠檬酸盐的混合物，其质量比为1:2。
优选的，所述石榴皮提取物中安石榴苷的重量含量在45％以上。
优选的，所述薰衣草油采用超临界二氧化碳流体技术萃取。
优选的，所述萃取的温度为45-50℃，萃取的压力为10-15MPa。
采用本发明的技术方案的有益效果是：
本发明中的医用石膏绷带透气性好，能有效确保肌体外伤骨折处的皮肤通气干燥，湿度或潮气消除或减轻，从而可以消除或减轻由石膏固定后不透气所造成的不适。
具体实施方式
下面结合具体实施方式对本发明作进一步说明。
实施例1
一种医用石膏绷带，石膏绷带中填充有抗菌层，抗菌层的厚度为10μm，抗菌层中填充的抗菌剂的质量份组成如下：缓凝剂2份、纤维素环糊精8份、硝酸银2份、薄荷4份、石榴皮提取物1份、薰衣草油1份，所述纤维素环糊精为改性β-环糊精接枝硝化纤维素；缓凝剂采用硼酸钠和柠檬酸盐的混合物，其质量比为1:1；本实施例中石榴皮提取物采用以下方法制得：将石榴皮洗净切碎，置于乙醇和乙酸乙酯的混合溶剂中回流提取1-3次，提取后进行浓缩得到1.5g/cm3的胶状物，即石榴皮提取物；石榴皮提取物中安石榴苷的重量含量在45％以上。
本实施例中薰衣草油采用超临界二氧化碳流体技术萃取，萃取的温度为45℃，萃取的压力为10MPa。
实施例2
一种医用石膏绷带，石膏绷带中填充有抗菌层，抗菌层的厚度为15μm，抗菌层中填充的抗菌剂的质量份组成如下：缓凝剂15份、纤维素环糊精15份、硝酸银5、薄荷6份、石榴皮提取物3份、薰衣草油1.5份，所述纤维素环糊精为改性β-环糊精接枝硝化纤维素；缓凝剂采用硼酸钠和柠檬酸盐的混合物，其质量比为1:2；本实施例中石榴皮提取物采用以下方法制得：将石榴皮洗净切碎，置于乙醇和乙酸乙酯的混合溶剂中回流提取1-3次，提取后进行浓缩得到1.5g/cm3的胶状物，即石榴皮提取物；石榴皮提取物中安石榴苷的重量含量在45％以上。
本实施例中薰衣草油采用超临界二氧化碳流体技术萃取，萃取的温度为50℃，萃取的压力为12MPa。
实施例3
一种医用石膏绷带，石膏绷带中填充有抗菌层，抗菌层的厚度为18μm，抗菌层中填充的抗菌剂的质量份组成如下：缓凝剂18份、纤维素环糊精20份、硝酸银8份、薄荷8份、石榴皮提取物6份、薰衣草油2份，所述纤维素环糊精为改性β-环糊精接枝硝化纤维素；缓凝剂采用硼酸钠和柠檬酸盐的混合物，其质量比为1:3；本实施例中石榴皮提取物采用以下方法制得：将石榴皮洗净切碎，置于乙醇和乙酸乙酯的混合溶剂中回流提取1-3次，提取后进行浓缩得到1.5g/cm3的胶状物，即石榴皮提取物；石榴皮提取物中安石榴苷的重量含量在45％以上。
本实施例中薰衣草油采用超临界二氧化碳流体技术萃取，萃取的温度为50℃，萃取的压力为15MPa。
本发明中的医用石膏绷带透气性好，能有效确保肌体外伤骨折处的皮肤通气干燥，湿度或潮气消除或减轻，从而可以消除或减轻由石膏固定后不透气所造成的不适。
以上述依据本发明的理想实施例为启示，通过上述的说明内容，相关工作人员完全可以在不偏离本项发明技术思想的范围内，进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容，必须要根据权利要求范围来确定其技术性范围。

Claims (6)

1.一种医用石膏绷带，所述石膏绷带中填充有抗菌层，其特征在于：所述抗菌层的厚度为10-18μm，所述抗菌层中填充的抗菌剂的质量份组成如下：缓凝剂2-18份、纤维素环糊精8-20份、硝酸银2-8份、薄荷4-8份、石榴皮提取物1-6份、薰衣草油1-2份，所述纤维素环糊精为改性β-环糊精接枝硝化纤维素；
所述石榴皮提取物采用以下方法制得：将石榴皮洗净切碎，置于乙醇和乙酸乙酯的混合溶剂中回流提取1-3次，提取后进行浓缩得到1.5g/cm3的胶状物，即石榴皮提取物。
2.根据权利要求1所述的医用石膏绷带，其特征在于：所述缓凝剂采用硼酸钠和柠檬酸盐的混合物，其质量比为1:1-3。
3.根据权利要求2所述的医用石膏绷带，其特征在于：所述缓凝剂采用硼酸钠和柠檬酸盐的混合物，其质量比为1:2。
4.根据权利要求1所述的医用石膏绷带，其特征在于：所述石榴皮提取物中安石榴苷的重量含量在45％以上。
5.根据权利要求1所述的医用石膏绷带，其特征在于：所述薰衣草油采用超临界二氧化碳流体技术萃取。
6.根据权利要求5所述的医用石膏绷带，其特征在于：所述萃取的温度为45-50℃，萃取的压力为10-15MPa。
CN201711380961.XA 2017-12-20 2017-12-20 医用石膏绷带 Active CN108113803B (zh)