CN108106897A - 风电轴承热喷锌拉拔力检测方法 - Google Patents

风电轴承热喷锌拉拔力检测方法 Download PDF

Info

Publication number
CN108106897A
CN108106897A CN201711407805.8A CN201711407805A CN108106897A CN 108106897 A CN108106897 A CN 108106897A CN 201711407805 A CN201711407805 A CN 201711407805A CN 108106897 A CN108106897 A CN 108106897A
Authority
CN
China
Prior art keywords
pulling capacity
wind power
capacity detection
power bearing
sample block
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711407805.8A
Other languages
English (en)
Inventor
谢彦龙
姜万录
李智
王在莉
王振
李洋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wafangdian Bearing Group National Bearing Engineering Technology Research Center Co Ltd
Wafangdian Bearing Group Corp
Original Assignee
Wafangdian Bearing Group National Bearing Engineering Technology Research Center Co Ltd
Wafangdian Bearing Group Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wafangdian Bearing Group National Bearing Engineering Technology Research Center Co Ltd, Wafangdian Bearing Group Corp filed Critical Wafangdian Bearing Group National Bearing Engineering Technology Research Center Co Ltd
Priority to CN201711407805.8A priority Critical patent/CN108106897A/zh
Publication of CN108106897A publication Critical patent/CN108106897A/zh
Pending legal-status Critical Current

Abstract

本发明提供一种风电轴承热喷锌拉拔力检测方法，制作与风电轴承相同材料的拉拔力检测样块，检测样块形状与风电轴承安装孔相配合；将拉拔力检测样块安装到风电轴承安装孔内；拉拔力检测样块随风电轴承一起进行喷砂处理；喷砂后，拉拔力检测样块随产品一起进行喷锌处理；喷锌后，将拉拔力检测铆钉粘接到拉拔力检测样块上；预定时间后，进行拉拔力检测。此拉拔力检测样块可作为产品的一部分进行加工，无需单独处理，可随机进行检测每一套风电轴承喷涂加工后的结合力情况，数据真实有效，准确度高，可反映加工过程中的实际情况，根据实际检测情况可实时进行调整。

Description

风电轴承热喷锌拉拔力检测方法
技术领域
本发明涉及一种风电轴承热喷锌拉拔力检测方法，属于风电轴承防腐领域。
背景技术
由于风电轴承所处的工作环境恶劣，寿命时间长，所以风电轴承防腐表面喷涂结合力有着严格的要求。以往检测风电轴承喷涂表面附着力时，均采用与风电轴承相同材料的钢板，进行热喷锌处理，然后使用拉拔力检测铆钉进行拉拔力检测，检测过程具有目的性，达不到对所有产品随机抽取检测目的，做不到所有产品表面结合力真实有效，而且在钢板进行热喷锌处理时，喷砂的强度、喷锌的厚度、温度等人为因素和环境因素无法保证与风电轴承进行喷锌处理时完全一样，因此检测出来的拉拔力与风电轴承真实的拉拔力也会有所差异，检测结果不够准确。
发明内容
根据现有技术存在的问题，本发明提供一种风电轴承热喷锌拉拔力检测方法，包括以下步骤：
步骤一：制作与风电轴承相同材料的拉拔力检测样块，检测样块形状与风电轴承安装孔相配合；
步骤二：将拉拔力检测样块安装到风电轴承安装孔内；
步骤三：拉拔力检测样块随风电轴承一起进行喷砂处理；
步骤四：喷砂后，拉拔力检测样块随产品一起进行喷锌处理；
步骤五：喷锌后，将拉拔力检测铆钉粘接到拉拔力检测样块上；
步骤六：预定时间后，进行拉拔力检测。
进一步地，所述拉拔力检测样块带有倒角，倒角与安装孔边缘形状相配合。
进一步地，所述拉拔力检测样块的直径略小于风电轴承安装孔直径。
进一步地，所述步骤六中预定时间为12小时。
风电轴承现通用安装孔的直径为39mm，检测样块直径略小于39mm ，通常为38.5mm-38.7mm，可与安装孔紧密配合，倒角防止了在加工过程中由于外力作用进入安装孔的可能。
本发明的有益效果为：此拉拔力检测样块可作为产品的一部分进行加工，无需单独处理，可随机进行检测每一套风电轴承喷涂加工后的结合力情况，数据真实有效，准确度高，可反映加工过程中的实际情况，根据实际检测情况可实时进行调整。
附图说明
图1为拉拔力检测样块安装位置示意图，
图中：1、拉拔力检测样块， 2、安装孔。
具体实施方式
一种风电轴承热喷锌拉拔力检测方法，包括以下步骤：
步骤一：制作与风电轴承相同材料且带有倒角的拉拔力检测样块，检测样块形状与风电轴承安装孔相配合，拉拔力检测样块的直径略小于风电轴承安装孔直径；
步骤二：将拉拔力检测样块安装到风电轴承安装孔内；
步骤三：拉拔力检测样块随风电轴承一起进行喷砂处理；
步骤四：喷砂后，拉拔力检测样块随产品一起进行喷锌处理；
步骤五：喷锌后，将拉拔力检测铆钉粘接到拉拔力检测样块上；
步骤六：等待12小时后，使用铆钉拉拔仪进行拉拔力检测。
进行验证实验对上述拉拔力检测实验的结果进行验证，验证方法包括以下步骤：
步骤一：设计可与实验风电轴承安装孔配合的拉拔力检测样块；
步骤二：将拉拔力检测样块安装到实验轴承上，同时进行防腐喷砂喷锌处理；
步骤三：对拉拔力检测样块及实验轴承分别粘接拉拔力检测铆钉；
步骤四：等待12小时后，使用铆钉拉拔仪进行拉拔力检测后。
实验结果：检测结果接近相同,证实此检测结果真实有效，接近实际产品加工情况。

Claims (4)

1.一种风电轴承热喷锌拉拔力检测方法，其特征在于：包括以下步骤：
步骤一：制作与风电轴承相同材料的拉拔力检测样块，检测样块形状与风电轴承安装孔相配合；
步骤二：将拉拔力检测样块安装到风电轴承安装孔内；
步骤三：拉拔力检测样块随风电轴承一起进行喷砂处理；
步骤四：喷砂后，拉拔力检测样块随产品一起进行喷锌处理；
步骤五：喷锌后，将拉拔力检测铆钉粘接到拉拔力检测样块上；
步骤六：预定时间后，进行拉拔力检测。
2.根据权利要求1所述的一种风电轴承热喷锌拉拔力检测方法，其特征在于：所述拉拔力检测样块带有倒角，倒角与安装孔边缘形状相配合。
3.根据权利要求1所述的一种风电轴承热喷锌拉拔力检测方法，其特征在于：所述拉拔力检测样块的直径略小于风电轴承安装孔直径。
4.根据权利要求1所述的一种风电轴承热喷锌拉拔力检测方法，其特征在于：所述步骤六中预定时间为12小时。
CN201711407805.8A 2017-12-22 2017-12-22 风电轴承热喷锌拉拔力检测方法 Pending CN108106897A (zh)