CN108104471A - 一种抗震复合被动式墙体施工方法及装饰复合墙体 - Google Patents
一种抗震复合被动式墙体施工方法及装饰复合墙体 Download PDFInfo
- Publication number
- CN108104471A CN108104471A CN201711381065.5A CN201711381065A CN108104471A CN 108104471 A CN108104471 A CN 108104471A CN 201711381065 A CN201711381065 A CN 201711381065A CN 108104471 A CN108104471 A CN 108104471A
- Authority
- CN
- China
- Prior art keywords
- parts
- wall
- powder
- antidetonation
- construction method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种抗震复合被动式墙体施工方法及装饰复合墙体,涉及建筑技术领域。该抗震复合被动式墙体施工方法包括:采用空心砖搭建基墙,并在基墙的剪力墙及顶部墙体配筋得到高强度基墙;在高强度基墙上涂覆保温粉体层,待保温粉体层晾干后再涂覆外墙涂料。保温粉体层通过黏土、胶粉、耐水调和粉、中空玻璃微珠、聚丙烯纤维以及混合添加剂的较优配比,尤其是中空玻璃微珠和聚丙烯纤维的配合起到很好地保温隔热的效果;外墙涂料采用了具有较优配比的水、灰钙、重钙、金属粉末以及涂料树脂的外墙涂料。该装饰复合墙体采用上述施工方法施工得到,具有抗震、保温的性能,也是一种被动式的墙体,适合于推广应用。
Description
技术领域
本发明涉及一种建筑技术领域,且特别涉及一种抗震复合被动式墙体施工方法及装饰复合墙体。
背景技术
现有的房屋修建或者房屋装修过程施工得到的墙体,由于施工方式不佳或施工选用的材料不好,导致施工得到的墙体难以兼具多种性能,即使兼具多种性能,其性能也都难以达到较佳的效果。
尤其对于地震频发的地带,对抗震的要求越来越强烈,并且随着科技的发展对于能够被动式地保温隔热提出了更好地要求。
发明内容
本发明的目的在于提供一种抗震复合被动式墙体施工方法,方法简便易行,得到的墙体具备很好地抗震和保温效果,是一种被动式墙体。
本发明的另一目的在于提供一种装饰复合墙体,其具有很好地抗震能力和保温隔热效果。
本发明解决其技术问题是采用以下技术方案来实现的。
本发明提出了一种抗震复合被动式墙体施工方法,包括如下步骤:
采用空心砖搭建基墙,并在基墙的剪力墙及顶部墙体配筋得到高强度基墙;
在高强度基墙上涂覆保温粉体层,待保温粉体层晾干后再涂覆外墙涂料;
按重量份数计,保温粉体层包括70-90份黏土、23-28份胶粉、35-45份耐水调和粉、35-50份中空玻璃微珠、10-18份聚丙烯纤维以及3-7份混合添加剂;
外墙涂料包括10-25份水、10-25份灰钙、20-50份重钙、1-10份金属粉末以及8-15份涂料树脂。
本发明还提出一种装饰复合墙体,应用上述抗震复合被动式墙体施工方法制备而得。
本发明实施例提供一种抗震复合被动式墙体施工方法的有益效果是:其采用空心砖砌基墙,并在基墙的剪力墙及顶部墙体配筋提升基墙了的抗震强度;在基墙完成后在基墙上涂覆保温粉体层,本涂层通过黏土、胶粉、耐水调和粉、中空玻璃微珠、聚丙烯纤维以及混合添加剂的较优配比,尤其是中空玻璃微珠和聚丙烯纤维的配合起到很好地保温隔热的效果,还能防止粉体涂覆后的分层和开裂,耐水调和粉的加入显著改善了墙体的防水性能;外墙涂料由于采用了具有较优配比的水、灰钙、重钙、金属粉末以及涂料树脂的外墙涂料,使得墙体的保温性能更有优异。
本发明还提供了一种装饰复合墙体,其采用本发明抗震复合被动式墙体施工方法施工得到,具有抗震、保温的性能,也是一种被动式的墙体,适合于推广应用。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚,下面将对本发明实施例中的技术方案进行清楚、完整地描述。实施例中未注明具体条件者,按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者,均为可以通过市售购买获得的常规产品。
下面对本发明实施例提供的抗震复合被动式墙体施工方法及装饰复合墙体进行具体说明。
本发明实施例提供的一种抗震复合被动式墙体施工方法,其包括如下步骤:
S1、基墙的构建。
采用空心砖搭建基墙,并在基墙的剪力墙及顶部墙体配筋得到高强度基墙。基墙的搭建采用常规的砌砖方法,根据具体墙面的尺寸进行构建,在基墙的剪力墙及顶部墙体处配筋,来增强墙体的抗震强度和力学性能。
具体地,空心砖为标准尺寸的市购空心砖,保温性能较好。
在高强度基墙上涂覆保温粉体层之前还包括清理基墙的墙面,清理墙面的过程使得墙面表面平整,更有利于后续涂覆过程使得表面均匀且防止开裂现象的产生。
S2、保温粉体层的涂覆。
在高强度基墙上涂覆保温粉体层,按重量份数计,保温粉体层包括70-90份黏土、23-28份胶粉、35-45份耐水调和粉、35-50份中空玻璃微珠、10-18份聚丙烯纤维以及3-7份混合添加剂;优选地,保温粉体层包括70-80份黏土、25-28份胶粉、38-43份耐水调和粉、43-48份中空玻璃微珠、15-18份聚丙烯纤维以及3-5份混合添加剂。
需要说明的是,保温粉体层的各个原料采用上述比例能够保证制备得到的粉体墙面的质感的同时,各组分起到很好地协同增效作用,尤其是中空玻璃微珠和聚丙烯纤维的协同增效作用对于提升粉体的保温隔热的效果具有重要作用。发明人发现聚丙烯纤维和中空玻璃微珠混合使得聚丙烯纤维包覆在中空玻璃微珠的表面,能够增强其保温和抗震的效果。耐水调和粉为自制调和助剂,用于增强粉体的防水性能,黏土作为主要成分,保证得到的粉体的质感和色状,胶粉和混合添加剂的加入能够保证粉体与墙面的贴合力,防止出现开裂现象。若各原料使用的比例超过或低于本发明实施例中记载的比例,则可能导致制备得到的粉体的质感差且节能防水性能不理想,容易出现脱色或开裂现象。
中空玻璃微珠是一种中空的圆球粉末状性能优异的超轻质无机非金属新材料,其真密度在0.20-0.60/cm,粒径在2-125微米之间。具有重量轻、体积大,导热系数低,抗压强度高、吸油率低、分散性和流动性好、化学稳定性高等特点。在本发明实施例中,中空玻璃微珠主要起到增强粉体的保温隔热效果的作用,其中空的圆球结构能够起到真空隔离的效果,显著降低传热效果,增强粉体保温和隔热的性能。
聚丙烯纤维是以聚丙烯为原材料,通过特殊工艺制造而成的。聚丙烯纤维具有质轻、高强度、高弹性、耐磨耐腐蚀的作用,更为重要的是其本身具有不错的保暖性能和绝缘性。在发明实施例中,聚丙烯纤维首先起到一定的保温和抗震效果,更为重要的是,发明人发现聚丙烯纤维和中空玻璃微珠的在上述比例下配合起到的保温和抗震效果最佳,聚丙烯纤维的长度为14~20mm更适合于作为涂料功能性原料应用到墙体的施工工艺过程中。
耐水调和粉和混合助剂为发明人经过试验筛选出的,其配置过程的工艺参数也是经过试验得到的优选方案。耐水调和粉的加入主要是起到增强粉体的防水性能的作用。
具体地,耐水调和粉包括耐水胶粉和聚氨酯,且耐水胶粉和聚氨酯的质量比为2-5:1。耐水胶粉和聚氨酯起到很好地协同增效作用,和上述原料混合制成混合粉体可以显著提升粉体的防水性能。耐水胶粉和聚氨酯采用上述的比例也是为了增强其协同作用,最大程度地增强粉体的防水性能。
混合添加剂包括消泡剂、粘结剂和催干剂,且消泡剂和粘结剂的质量比为1-2:1-2:1。采用上述比例可以使混合粉体的消泡性能达到较佳水平,同时可以加快涂层的干燥速率,缩短施工周期。
具体地,消泡剂、粘结剂和催干剂可以为常用的功能性添加剂,但是发明人发现采用聚二甲基硅氧烷为消泡剂,氰基丙烯酸酯为粘结剂,硫化锰为催干剂的情况下可以使粉体涂层的涂覆性能更佳,如均匀性、干燥速率并且达到无气泡产生的效果。
S3、外墙涂料的涂覆。
待保温粉体层晾干后再涂覆外墙涂料,外墙涂料的涂覆使得墙体整体具有很好的抗震性和力学性能。
具体地,外墙涂料包括10-25份水、10-25份灰钙、20-50份重钙、1-10份金属粉末以及8-15份涂料树脂。优选地,外墙涂料包括15-20份水、13-23份灰钙、30-40份重钙、3-5份金属粉末以及10-12份涂料树脂。
在外墙涂料层中添加金属粉末使得墙面能够将部分中远红外线反射回室内增加室内温度,优选地,为降低制作成本,金属粉末包括铜粉、铁粉和铝粉中的至少一种。涂料树脂即以合成树脂为主要成膜物质的涂料,其用于分散介质中,溶解性或分散性良好,并且具有优良的成膜性。优选地,涂料树脂为丙烯酸乳液。保温墙面涂料的各成分相互配合作用,在配比在上述范围内时涂抹与墙面的颜色色泽较佳和保温性能好。
优选地,外墙涂料还包括10-30份乳胶粉,优选为15-30份。乳胶粉的加入可以增强外墙涂料的黏结性能,使涂料形成表面平整的涂层结构。
本发明实施例还提供了一种装饰复合墙体,其应用上述抗震复合被动式墙体施工方法施工得到。该复合墙体具有很好地抗震性能和保温性能,是一种被动式的复合墙体。
以下结合实施例对本发明的特征和性能作进一步的详细描述。
实施例1
本实施例提供一种抗震复合被动式墙体施工方法,其包括以下步骤:
采用空心砖搭建基墙,并在基墙的剪力墙及顶部墙体配筋得到高强度基墙;清理上述高强度基墙后,在高强度基墙上涂覆保温粉体层,待保温粉体层晾干后再涂覆外墙涂料。
其中,保温粉体层包括70份黏土、23份胶粉、35份耐水调和粉、35份中空玻璃微珠、10份长度为14mm的聚丙烯纤维以及3份混合添加剂;外墙涂料包括10份水、10份灰钙、20份重钙、1份铜粉以及8份丙烯酸乳液;耐水调和粉包括23.33份耐水胶粉和11.67份聚氨酯,混合添加剂包括1份聚二甲基硅氧烷、1份氰基丙烯酸酯和1份硫化锰。
本实施例还提供了一种装饰复合墙体,其通过上述施工方法施工而得。
实施例2
本实施例提供一种抗震复合被动式墙体施工方法,其包括以下步骤:
采用空心砖搭建基墙,并在基墙的剪力墙及顶部墙体配筋得到高强度基墙;清理上述高强度基墙后,在高强度基墙上涂覆保温粉体层,待保温粉体层晾干后再涂覆外墙涂料。
其中,保温粉体层包括90份黏土、28份胶粉、45份耐水调和粉、50份中空玻璃微珠、18份长度为20mm的聚丙烯纤维以及7份混合添加剂;外墙涂料包括25份水、25份灰钙、50份重钙、10份铁粉、10份乳胶粉以及15份丙烯酸乳液;耐水调和粉包括37.5份耐水胶粉和7.5份聚氨酯,混合添加剂包括2.8份聚二甲基硅氧烷、2.8份氰基丙烯酸酯和1.4份硫化锰。
本实施例还提供了一种装饰复合墙体,其通过上述施工方法施工而得。
实施例3
本实施例提供一种抗震复合被动式墙体施工方法,其包括以下步骤:
采用空心砖搭建基墙,并在基墙的剪力墙及顶部墙体配筋得到高强度基墙;清理上述高强度基墙后,在高强度基墙上涂覆保温粉体层,待保温粉体层晾干后再涂覆外墙涂料。
其中,保温粉体层包括80份黏土、25份胶粉、38份耐水调和粉、43份中空玻璃微珠、15份长度为16mm的聚丙烯纤维以及5份混合添加剂;外墙涂料包括15份水、13份灰钙、30份重钙、3份铝粉、30份乳胶粉以及10份丙烯酸乳液;耐水调和粉包括28.5份耐水胶粉和9.5份聚氨酯,混合添加剂包括1.25份聚二甲基硅氧烷、2.5份氰基丙烯酸酯和1.25份硫化锰。
本实施例还提供了一种装饰复合墙体,其通过上述施工方法施工而得。
实施例4
本实施例提供一种抗震复合被动式墙体施工方法,其包括以下步骤:
采用空心砖搭建基墙,并在基墙的剪力墙及顶部墙体配筋得到高强度基墙;清理上述高强度基墙后,在高强度基墙上涂覆保温粉体层,待保温粉体层晾干后再涂覆外墙涂料。
其中,保温粉体层包括80份黏土、25份胶粉、43份耐水调和粉、48份中空玻璃微珠、15份长度为16mm的聚丙烯纤维以及5份混合添加剂;外墙涂料包括20份水、23份灰钙、40份重钙、5份铝粉、15份乳胶粉以及12份丙烯酸乳液;耐水调和粉包括28.67份耐水胶粉和14.33份聚氨酯,混合添加剂包括1.25份聚二甲基硅氧烷、2.5份氰基丙烯酸酯和1.25份硫化锰。
本实施例还提供了一种装饰复合墙体,其通过上述施工方法施工而得。
对比例1-3
一般室内墙体,选取3处墙体。
试验例1
将实施例1-4和对比例1-3中的墙体进行抗压能力测试,测试方法参见GB/T50081-2002。将测得的抗压强度值记录至表格1。
表1抗压强度(MPa)测试结果
实施例 | 1 | 2 | 3 | 4 | 对比例1 | 对比例2 | 对比例3 |
抗压强度 | 29.3 | 29.6 | 29.5 | 29.6 | 25.4 | 26.2 | 24.5 |
根据表1可知,本发明实施例施工得到的墙体的抗压强度达到29MPa以上明显优于一般室内墙体,可见本发明中的施工方法得到的墙体的抗震能力较强,适合于在地震频发地带广泛采用。
试验例2
将实施例1-4和对比例1-3中得到的墙体的分别进行导热系数测定,具体的操作参见GB/T10294-2008防护热板法,将测得的结果记录入表2。
表2导热系数(W/m℃)测试结果
实施例 | 1 | 2 | 3 | 4 | 对比例1 | 对比例2 | 对比例3 |
抗压强度 | 0.112 | 0.112 | 0.114 | 0.108 | 0.372 | 0.357 | 0.346 |
由表2可知,采用本发明施工方法得到的墙体的导热系数明显低于普通室内墙体,具有不错的保温隔热的性能,是一种多功能的复合墙体。
综上所述,本发明提供的一种抗震复合被动式墙体施工方法,其采用空心砖砌基墙,并在基墙的剪力墙及顶部墙体配筋提升基墙了的抗震强度;在基墙完成后在基墙上涂覆保温粉体层,本涂层通过黏土、胶粉、耐水调和粉、中空玻璃微珠、聚丙烯纤维以及混合添加剂的较优配比,尤其是中空玻璃微珠和聚丙烯纤维的配合起到很好地保温隔热的效果,还能防止粉体涂覆后的分层和开裂,耐水调和粉的加入显著改善了墙体的防水性能;外墙涂料由于采用了具有较优配比的水、灰钙、重钙、金属粉末以及涂料树脂的外墙涂料,使得墙体的保温性能更有优异。
本发明还提供了一种装饰复合墙体,其采用本发明抗震复合被动式墙体施工方法施工得到,具有抗震、保温的性能,也是一种被动式的墙体,适合于推广应用。
以上所描述的实施例是本发明一部分实施例,而不是全部的实施例。本发明的实施例的详细描述并非旨在限制要求保护的本发明的范围,而是仅仅表示本发明的选定实施例。基于本发明中的实施例,本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
Claims (10)
1.一种抗震复合被动式墙体施工方法,其特征在于,包括如下步骤:
采用空心砖搭建基墙,并在所述基墙的剪力墙及顶部墙体配筋得到高强度基墙;
在所述高强度基墙上涂覆保温粉体层,待所述保温粉体层晾干后再涂覆外墙涂料;
按重量份数计,所述保温粉体层包括70-90份黏土、23-28份胶粉、35-45份耐水调和粉、35-50份中空玻璃微珠、10-18份聚丙烯纤维以及3-7份混合添加剂;
所述外墙涂料包括10-25份水、10-25份灰钙、20-50份重钙、1-10份金属粉末以及8-15份涂料树脂。
2.根据权利要求1所述的抗震复合被动式墙体施工方法,其特征在于,所述保温粉体层包括70-80份黏土、25-28份胶粉、38-43份耐水调和粉、43-48份中空玻璃微珠、15-18份聚丙烯纤维以及3-5份混合添加剂;
所述外墙涂料包括15-20份水、13-23份灰钙、30-40份重钙、3-5份金属粉末以及10-12份涂料树脂。
3.根据权利要求1或2中所述的抗震复合被动式墙体施工方法,其特征在于,所述外墙涂料还包括10-30份乳胶粉,优选为15-30份。
4.根据权利要求3所述的抗震复合被动式墙体施工方法,其特征在于,所述耐水调和粉包括耐水胶粉和聚氨酯,且所述耐水胶粉和所述聚氨酯的质量比为2-5:1。
5.根据权利要求1或2中所述的抗震复合被动式墙体施工方法,其特征在于,所述混合添加剂包括消泡剂、粘结剂和催干剂,且所述消泡剂和所述粘结剂的质量比为1-2:1-2:1。
6.根据权利要求1或2中所述的抗震复合被动式墙体施工方法,其特征在于,所述金属粉末包括铜粉、铁粉和铝粉中的至少一种。
7.根据权利要求6所述的抗震复合被动式墙体施工方法,其特征在于,所述涂料树脂为丙烯酸乳液。
8.根据权利要求1所述的抗震复合被动式墙体施工方法,其特征在于,所述聚丙烯纤维的长度为14~20mm。
9.根据权利要求1所述的抗震复合被动式墙体施工方法,其特征在于,在所述高强度基墙上涂覆所述保温粉体层之前还包括清理所述基墙的墙面。
10.一种装饰复合墙体,其特征在于,应用权利要求1-9中任一项所述的抗震复合被动式墙体施工方法制备而得。